CN107780788A - 一种复合防火玻璃及其制备方法 - Google Patents
一种复合防火玻璃及其制备方法 Download PDFInfo
- Publication number
- CN107780788A CN107780788A CN201710981894.0A CN201710981894A CN107780788A CN 107780788 A CN107780788 A CN 107780788A CN 201710981894 A CN201710981894 A CN 201710981894A CN 107780788 A CN107780788 A CN 107780788A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite fireproof
- glass
- fire
- potassium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种复合防火玻璃及其制备方法，复合防火玻璃包括两块平行相对设置的玻璃本体和填充在两块所述玻璃本体之间密封空间的防火液；所述防火液包括如下重量份的原料：20‑40份多元醇、50‑70份丙烯酰胺、3份‑5份亚甲基双丙烯酰胺、3‑6份三乙氧基硅烷、4‑7份成碳剂、5‑12份改性有机硅聚合物、1‑2份钾明矾、4‑7份氯化镁、5‑8份甲基丙烯酸甲酯、5‑10份丙烯酸丁酯、3‑12份氢氧化钠、8‑12份过硫酸钾、7‑12份去离子水、6‑12份消泡剂、4‑12份流平剂。本发明的复合防火玻璃能够有效防火隔热，还能避免防火液固化过程中产生气泡和杂质。
Description
技术领域
本发明涉及玻璃生产制造技术领域，具体涉及一种复合防火玻璃及其制备方法。
背景技术
安全玻璃是一种重要的新型建筑材料，防火玻璃是一种具有防火功能的门窗玻璃，它在高温火焰的冲击下仍然能够保持较长时间不炸裂，从而有效组织火焰与烟雾的蔓延。目前的防火玻璃存在较多不足，当被火烤时容易产生大量微泡，直接影响复合防火玻璃的表观质量等，严重影响了防火玻璃的使用寿命和效果。
发明内容
本发明所要解决的技术问题是针对现有技术的不足，提供一种复合防火玻璃及其制备方法。
本发明解决上述技术问题的技术方案如下：一种复合防火玻璃，包括两块平行相对设置的玻璃本体和填充在两块所述玻璃本体之间密封空间的防火液；所述防火液包括如下重量份的原料：20-40份多元醇、50-70份丙烯酰胺、3份-5份亚甲基双丙烯酰胺、3-6份三乙氧基硅烷、4-7份成碳剂、5-12份改性有机硅聚合物、1-2份钾明矾、4-7份氯化镁、5-8份甲基丙烯酸甲酯、5-10份丙烯酸丁酯、3-12份氢氧化钠、8-12份过硫酸钾、7-12份去离子水、6-12份消泡剂、4-12份流平剂。
本发明的有益效果是：本发明的复合防火玻璃能够有效防火隔热，还能避免防火液固化过程中产生气泡和杂质。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，所述防火液包括如下重量份的原料：30份多元醇、60份丙烯酰胺、4份亚甲基双丙烯酰胺、5份三乙氧基硅烷、5份成碳剂、9份改性有机硅聚合物、1.5份钾明矾、6份氯化镁、6份甲基丙烯酸甲酯、7份丙烯酸丁酯、8份氢氧化钠、10份过硫酸钾、10份去离子水、10份消泡剂、8份流平剂。
进一步，所述氢氧化钠的浓度为0.5％-1％。
一种复合防火玻璃的制备方法，包括以下步骤：
(1)取如上所述重量份的原料，将改性有机硅聚合物、三乙氧基硅烷、消泡剂、流平剂、氢氧化钠和去离子水混合均匀，静置水解得到混合物一；
(2)将丙烯酰胺、多元醇、亚甲基双丙烯酰胺、丙烯酸丁酯、甲基丙烯酸甲酯、钾明矾和氯化镁混合均匀得到混合物二；
(3)将混合物二均匀缓慢加入到混合物一中，并搅拌均匀后开始加热，加热过程不停搅拌，最后加入成碳剂和过硫酸钾混合均匀后，真空浓缩得到所述防火液。
进一步，步骤(3)中的加热过程持续通入氮气。
具体实施方式
以下对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1
本实施例的一种复合防火玻璃，包括两块平行相对设置的玻璃本体和填充在两块所述玻璃本体之间密封空间的防火液；所述防火液包括如下重量份的原料：20份多元醇、50份丙烯酰胺、3份亚甲基双丙烯酰胺、3份三乙氧基硅烷、4份成碳剂、5份改性有机硅聚合物、1份钾明矾、4份氯化镁、5份甲基丙烯酸甲酯、5份丙烯酸丁酯、3份氢氧化钠、8份过硫酸钾、7份去离子水、6份消泡剂、4份流平剂。
具体的，所述氢氧化钠的浓度为0.5％。
本实施例的复合防火玻璃的制备方法，包括以下步骤：
(1)取如上所述重量份的原料，将改性有机硅聚合物、三乙氧基硅烷、消泡剂、流平剂、氢氧化钠和去离子水混合均匀，静置水解得到混合物一；
(2)将丙烯酰胺、多元醇、亚甲基双丙烯酰胺、丙烯酸丁酯、甲基丙烯酸甲酯、钾明矾和氯化镁混合均匀得到混合物二；
(3)将混合物二均匀缓慢加入到混合物一中，并搅拌均匀后开始加热，加热过程不停搅拌，最后加入成碳剂和过硫酸钾混合均匀后，真空浓缩得到所述防火液。
具体的，步骤(3)中的加热过程持续通入氮气。
本实施例的复合防火玻璃能够有效防火隔热，还能避免防火液固化过程中产生气泡和杂质。
实施例2
本实施例的一种复合防火玻璃，包括两块平行相对设置的玻璃本体和填充在两块所述玻璃本体之间密封空间的防火液；所述防火液包括如下重量份的原料：30份多元醇、60份丙烯酰胺、4份亚甲基双丙烯酰胺、5份三乙氧基硅烷、5份成碳剂、9份改性有机硅聚合物、1.5份钾明矾、6份氯化镁、6份甲基丙烯酸甲酯、7份丙烯酸丁酯、8份氢氧化钠、10份过硫酸钾、10份去离子水、10份消泡剂、8份流平剂。
进一步，所述氢氧化钠的浓度为0.8％。
本实施例的复合防火玻璃的制备方法，包括以下步骤：
(1)取如上所述重量份的原料，将改性有机硅聚合物、三乙氧基硅烷、消泡剂、流平剂、氢氧化钠和去离子水混合均匀，静置水解得到混合物一；
(2)将丙烯酰胺、多元醇、亚甲基双丙烯酰胺、丙烯酸丁酯、甲基丙烯酸甲酯、钾明矾和氯化镁混合均匀得到混合物二；
(3)将混合物二均匀缓慢加入到混合物一中，并搅拌均匀后开始加热，加热过程不停搅拌，最后加入成碳剂和过硫酸钾混合均匀后，真空浓缩得到所述防火液。
具体的，步骤(3)中的加热过程持续通入氮气。
本实施例的复合防火玻璃能够有效防火隔热，还能避免防火液固化过程中产生气泡和杂质。
实施例3
本实施例的一种复合防火玻璃，包括两块平行相对设置的玻璃本体和填充在两块所述玻璃本体之间密封空间的防火液；所述防火液包括如下重量份的原料：40份多元醇、70份丙烯酰胺、5份亚甲基双丙烯酰胺、6份三乙氧基硅烷、7份成碳剂、12份改性有机硅聚合物、2份钾明矾、7份氯化镁、8份甲基丙烯酸甲酯、10份丙烯酸丁酯、12份氢氧化钠、12份过硫酸钾、12份去离子水、12份消泡剂、12份流平剂。
具体的，所述氢氧化钠的浓度为1％。
本实施例的复合防火玻璃的制备方法，包括以下步骤：
(1)取如上所述重量份的原料，将改性有机硅聚合物、三乙氧基硅烷、消泡剂、流平剂、氢氧化钠和去离子水混合均匀，静置水解得到混合物一；
(2)将丙烯酰胺、多元醇、亚甲基双丙烯酰胺、丙烯酸丁酯、甲基丙烯酸甲酯、钾明矾和氯化镁混合均匀得到混合物二；
(3)将混合物二均匀缓慢加入到混合物一中，并搅拌均匀后开始加热，加热过程不停搅拌，最后加入成碳剂和过硫酸钾混合均匀后，真空浓缩得到所述防火液。
具体的，步骤(3)中的加热过程持续通入氮气。
本实施例的复合防火玻璃能够有效防火隔热，还能避免防火液固化过程中产生气泡和杂质。
对实施例1、实施例2和实施例3中的防火玻璃的防火性能进行检测，取相同大小和厚度的实施例1、实施例2和实施例3的防火玻璃，分别为A、B、C。再取未添加有改性有机硅聚合物和丙烯酰胺的防火玻璃D；再取添加物质与本实施例的相同，但是添加量少的防火玻璃E。分别对A、B、C、D、E的一个侧面进行加热，对A、B、C、D、E的另一个侧面进行温度测量，检测结果如表1所示。
表1不同防火玻璃的隔热性能
| 防火玻璃 | A | B | C | D | E |
| 温度℃ | 25 | 28 | 24 | 50 | 60 |
由表1可知，本实施例1-3的防火玻璃的防火性能远远好于防火玻璃D和E的隔热效果。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (5)
1.一种复合防火玻璃，其特征在于，包括两块平行相对设置的玻璃本体和填充在两块所述玻璃本体之间密封空间的防火液；所述防火液包括如下重量份的原料：20-40份多元醇、50-70份丙烯酰胺、3份-5份亚甲基双丙烯酰胺、3-6份三乙氧基硅烷、4-7份成碳剂、5-12份改性有机硅聚合物、1-2份钾明矾、4-7份氯化镁、5-8份甲基丙烯酸甲酯、5-10份丙烯酸丁酯、3-12份氢氧化钠、8-12份过硫酸钾、7-12份去离子水、6-12份消泡剂、4-12份流平剂。
2.根据权利要求1所述一种复合防火玻璃，其特征在于，所述防火液包括如下重量份的原料：30份多元醇、60份丙烯酰胺、4份亚甲基双丙烯酰胺、5份三乙氧基硅烷、5份成碳剂、9份改性有机硅聚合物、1.5份钾明矾、6份氯化镁、6份甲基丙烯酸甲酯、7份丙烯酸丁酯、8份氢氧化钠、10份过硫酸钾、10份去离子水、10份消泡剂、8份流平剂。
3.根据权利要求1或2所述一种复合防火玻璃，其特征在于，所述氢氧化钠的浓度为0.5％-1％。
4.一种复合防火玻璃的制备方法，其特征在于，包括以下步骤：
(1)取权利要求1至3任一项所述重量份的原料，将改性有机硅聚合物、三乙氧基硅烷、消泡剂、流平剂、氢氧化钠和去离子水混合均匀，静置水解得到混合物一；
(2)将丙烯酰胺、多元醇、亚甲基双丙烯酰胺、丙烯酸丁酯、甲基丙烯酸甲酯、钾明矾和氯化镁混合均匀得到混合物二；
(3)将混合物二均匀缓慢加入到混合物一中，并搅拌均匀后开始加热，加热过程不停搅拌，最后加入成碳剂和过硫酸钾混合均匀后，真空浓缩得到所述防火液。
5.根据权利要求4所述一种复合防火玻璃的制备方法，其特征在于，步骤(3)中的加热过程持续通入氮气。