CN107746246A - 一种环保负离子瓷砖及其生产工艺 - Google Patents

一种环保负离子瓷砖及其生产工艺 Download PDF

Info

Publication number
CN107746246A
CN107746246A CN201710811685.1A CN201710811685A CN107746246A CN 107746246 A CN107746246 A CN 107746246A CN 201710811685 A CN201710811685 A CN 201710811685A CN 107746246 A CN107746246 A CN 107746246A
Authority
CN
China
Prior art keywords
glaze
ceramic body
environmentally friendly
powder
graphene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710811685.1A
Other languages
English (en)
Inventor
林柱权
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FOSHAN CITY GAOMING DISTRICT XINYUEFENG BUILDING MATERIAL Co Ltd
Original Assignee
FOSHAN CITY GAOMING DISTRICT XINYUEFENG BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FOSHAN CITY GAOMING DISTRICT XINYUEFENG BUILDING MATERIAL Co Ltd filed Critical FOSHAN CITY GAOMING DISTRICT XINYUEFENG BUILDING MATERIAL Co Ltd
Priority to CN201710811685.1A priority Critical patent/CN107746246A/zh
Publication of CN107746246A publication Critical patent/CN107746246A/zh
Pending legal-status Critical Current

Abstract

本发明所述一种环保负离子瓷砖及其生产工艺，包括陶瓷坯体和釉料，所述陶瓷坯体包括硅藻土、粘土、砂石、电气石粉、黑磷和石墨烯，所述釉料包括钠长石粉、滑石粉、二氧化硅溶胶、微晶石、微晶玻璃、稀土材料、石墨烯和玛瑙石粉。本发明所生产的陶瓷具有良好的负离子释放能力，释放的负离子能够改善空气质量，改善人体健康，提高人体免疫力，是一种健康环保的新产品。

Description

一种环保负离子瓷砖及其生产工艺
技术领域
本发明属于陶瓷技术领域，具体地说，涉及一种环保负离子瓷砖及其生产工艺。
背景技术
随着社会的发展和人们生活水平的提高，越来越注重环保与健康，特别是在日用品方面，普通的瓷砖已经不能满足人们对保健性能的要求，而负离子陶瓷材料由于其独特的负离子释放功能，可更好地应用于健康和环保领域。
负离子的主要功能：负离子有镇静、镇痛、镇咳、止痒、利尿、增食欲、降血压之效。比如雷雨过后，空气的负离子增多，人们感到心情舒畅。而在空调房间，因空气中负离子经过一系列空调净化处理和漫长通风管道后几乎全部消失，人们在其中长期停留会感到胸闷、头晕、乏力、工作效率和健康状况下降，被称之为“空调综合症”。
发明内容
本发明克服了现有技术中的缺点，提供了一种环保负离子瓷砖及其生产工艺，可释放负离子，解决现有技术负离子释放浓度低的问题。
为了解决上述技术问题，本发明是通过以下技术方案实现的：
一种环保负离子瓷砖，包括陶瓷坯体和釉料，所述陶瓷坯体包括硅藻土、粘土、砂石、电气石粉、黑磷和石墨烯，所述釉料包括钠长石粉、滑石粉、二氧化硅溶胶、微晶石、微晶玻璃、稀土材料、石墨烯和玛瑙石粉。
进一步，按照重量百分比：所述陶瓷坯体包括硅藻土10-20％、粘土35-45％、砂石粉10-20％、电气石粉25-35％、黑磷1-2％和石墨烯1-3％。
进一步，按照重量百分比：所述釉料包括钠长石粉70-80％、滑石粉10-15％、二氧化硅溶胶2-5％、微晶石2-3％、微晶玻璃2-3％、稀土材料1-2％、石墨烯1-2％和玛瑙石粉1-2％。
进一步，所述稀土材料为氧化镧或独居石。
一种环保负离子瓷砖的生产工艺，包括以下步骤：
1)制备泥浆，按照陶瓷坯体的原料称料各种原料，进行球磨得到泥浆；
2)制备陶瓷坯体，将上述泥浆过筛，压滤得到泥饼，泥饼经真空练泥，陈腐7-10天，制成陶瓷坯体；
3)制备釉料；按照原料配比称量，进行球磨，球磨至釉料细度过250目筛；
4)烧制：将涂覆有釉料的陶瓷坯体在氮气气氛下进行烧结。
进一步，步骤4)烧制时，将涂覆有釉料的陶瓷坯体先再350-400℃进行加热，在1280-1300℃氮气气氛下进行烧结。
与现有技术相比，本发明的有益效果是：
本发明所述一种环保负离子瓷砖及其生产工艺所生产的陶瓷具有良好的负离子释放能力，释放的负离子能够改善空气质量，改善人体健康，提高人体免疫力，是一种健康环保的新产品。
具体实施方式
以下对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例1：
本发明所述一种环保负离子瓷砖，包括陶瓷坯体和釉料，按照重量百分比：陶瓷坯体包括硅藻土15％、粘土42％、砂石粉12％、电气石粉28％、黑磷1.2％和石墨烯1.8％。
釉料包括钠长石粉73.2％、滑石粉14％、二氧化硅溶胶4％、微晶石2.1％、微晶玻璃2.1％、稀土材料2.1％、石墨烯1.2％和玛瑙石粉1.3％，稀土材料选用氧化镧。
电气石粉、微晶石和稀土材料实现负离子的释放，黑磷和石墨烯增加负离子的释放量，而且石墨烯对釉层进行增强，提高其耐磨性。
一种环保负离子瓷砖的生产工艺，包括以下步骤：
1)制备泥浆，按照陶瓷坯体的原料称料各种原料，进行球磨得到泥浆；
2)制备陶瓷坯体，将上述泥浆过筛，压滤得到泥饼，泥饼经真空练泥，陈腐7-10天，制成陶瓷坯体；
3)制备釉料；按照原料配比称量，进行球磨，球磨至釉料细度过250目筛；
4)烧制：将涂覆有釉料的陶瓷坯体先再350-400℃进行加热，在1280-1300℃氮气气氛下进行烧结，由于黑磷和石墨烯在有氧高温下容易分解，因此在氮气气氛下进行烧结。
本发明申请一种环保负离子瓷砖，陶瓷表面测得负离子平均释放浓度为1800个/cm3，在距离瓷砖表面1米位置，测得负离子平均释放浓度为1350个/cm3。
实施例2：
本发明所述一种环保负离子瓷砖，包括陶瓷坯体和釉料，按照重量百分比：所述陶瓷坯体包括硅藻土12％、粘土40％、砂石粉15％、电气石粉30％、黑磷1.5％和石墨烯1.5％。
釉料包括钠长石粉75％、滑石粉12.5％、二氧化硅溶胶3％、微晶石2.5％、微晶玻璃2.5％、稀土材料1.5％、石墨烯1.5％和玛瑙石粉1.5％。
稀土材料采用独居石，其具有电磁性和放射性--产生离子--激活电气石粉，进而产生更多的负离子和远红外。
最后应说明的是：以上仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，但是凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (6)

1.一种环保负离子瓷砖，其特征在于，包括陶瓷坯体和釉料，所述陶瓷坯体包括硅藻土、粘土、砂石、电气石粉、黑磷和石墨烯，所述釉料包括钠长石粉、滑石粉、二氧化硅溶胶、微晶石、微晶玻璃、稀土材料、石墨烯和玛瑙石粉。
2.根据权利要求1所述一种环保负离子瓷砖，其特征在于，按照重量百分比：所述陶瓷坯体包括硅藻土10-20％、粘土35-45％、砂石粉10-20％、电气石粉25-35％、黑磷1-2％和石墨烯1-3％。
3.根据权利要求1所述一种环保负离子瓷砖，其特征在于，按照重量百分比：所述釉料包括钠长石粉70-80％、滑石粉10-15％、二氧化硅溶胶2-5％、微晶石2-3％、微晶玻璃2-3％、稀土材料1-2％、石墨烯1-2％和玛瑙石粉1-2％。
4.根据权利要求1所述一种环保负离子瓷砖，其特征在于，所述稀土材料为氧化镧或独居石。
5.根据权利要求1所述一种环保负离子瓷砖的生产工艺，其特征在于，包括以下步骤：
1)制备泥浆，按照陶瓷坯体的原料称料各种原料，进行球磨得到泥浆；
2)制备陶瓷坯体，将上述泥浆过筛，压滤得到泥饼，泥饼经真空练泥，陈腐7-10天，制成陶瓷坯体；
3)制备釉料；按照原料配比称量，进行球磨，球磨至釉料细度过250目筛；
4)烧制：将涂覆有釉料的陶瓷坯体在氮气气氛下进行烧结。
6.根据权利要求5所述一种环保负离子瓷砖的生产工艺，其特征在于，步骤4)烧制时，将涂覆有釉料的陶瓷坯体先再350-400℃进行加热，在1280-1300℃氮气气氛下进行烧结。
CN201710811685.1A 2017-09-11 2017-09-11 一种环保负离子瓷砖及其生产工艺 Pending CN107746246A (zh)