CN107743788A - A kind of discarded admaic earth brick powder ceramic flowerpot - Google Patents
A kind of discarded admaic earth brick powder ceramic flowerpot Download PDFInfo
- Publication number
- CN107743788A CN107743788A CN201711087570.9A CN201711087570A CN107743788A CN 107743788 A CN107743788 A CN 107743788A CN 201711087570 A CN201711087570 A CN 201711087570A CN 107743788 A CN107743788 A CN 107743788A
- Authority
- CN
- China
- Prior art keywords
- discarded
- admaic earth
- brick powder
- earth brick
- flowerpot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ceramic flowerpot prepared by the use of discarded admaic earth brick powder as primary raw material, category is construction refuse regenerated to utilize field.The flowerpot is molded using gypsum mould grouting method, and using discarded admaic earth brick powder as primary raw material, other components include its slurry:The auxiliary agents such as water, suspending agent, reinforcing agent, water reducer, preservative, grinding aid, colouring agent.Obtained flowerpot gas permeability and breathable properties are good, and bending strength is high, and production cost is low, has beautified gardens or home environment, realizes the regeneration of waste and old resource.
Description
Technical field
Field is utilized the present invention relates to construction refuse regenerated, and in particular to a kind of discarded admaic earth brick powder ceramic flowerpot.
Background technology
Discarded admaic earth brick is one kind in building waste, due to reconstruction of the old city town, dilapidated house removal, new Urbanization Construction
Etc. having removed substantial amounts of old low rise buildings, many garbage mountains are formd, although many departments have all been concerned about building waste
Recycling, but current utilization is also very limited, largely discarded admaic earth brick be still concentrate take up an area stockpiling or
Landfill yard landfill is sent to, a large amount of rare land resources is not only taken up, soil and air can also be polluted.
What the discarded admaic earth brick of building waste was utilized at present is limited in that the intensity after it is broken is relatively low, Wu Faman
It is largely used foot as the equicohesive requirement of construction material or roadbed material, can only small volume addition use.
Discarded admaic earth brick powder main component is sintered clay, it has also become clinker, has the characteristic of poor material, normal
Do not have adhesive property under temperature or low temperature, i.e., soak adhesive aggregation shaping after can not adding water as natural clay.Broken is discarded
Admaic earth brick particulate material can only be used as aggregate to be molded reluctantly by adding substantial amounts of wet adhesive aid, and broken fine powder is also necessary
It can just be made or extruded, compressing by note prize, modeling by adding shaping assistant.But this discarded admaic earth brick powder or particulate material
During composition as ceramic batch with surmount clay brick firing temperature it is suitable at a high temperature of sintering character and production can be presented
Raw a certain amount of liquid phase.
Analyzed based on more than, by substantial amounts of experimental exploration, invented a kind of ceramic flower made using discarded admaic earth brick powder
Basin.At present, the relevant report that ceramic flowerpot is made using discarded conventional red clay brick powder is not seen.The present invention glues discarded conventional red
Used after cob brick crushing as a kind of main raw material(s) of flowerpot making, one is provided to discard the regeneration of admaic earth brick
The beneficial approach of bar.
The content of the invention
To reduce environmental pollution, present invention aims at provide a kind of discarded admaic earth brick powder ceramic flowerpot to make to discard red glue
Cob brick can be utilized largely, make its regeneration, improve its value.,
To realize the purpose of the present invention, the present invention crushes discarded admaic earth brick, as the primary raw material of flowerpot, adds it
Its component is configured to pour into a mould slurry, is molded using gypsum mould grouting method, so as to prepare discarded admaic earth brick powder ceramic flowerpot.
Present invention cast slurry takes following component, and each component is by weight percentage:
Described discarded admaic earth brick powder is to be crushed to form by discarded conventional red clay brick, and its main component is SiO2、
Al2O3、Fe2O3。
The composite assistant is selected from the Guilin Qi Hong Science and Technology Ltd.s production type products of Disper 365, is commercially available product.
The Zhecheng Brown crake comes from Henan Province Shangqiu Zhecheng County, is local mineral raw material, is that one kind mainly picks up from bottom of trench and river
The cohesive soil of bed, main component are:SiO2、Al2O3、Fe2O3, CaO and igloss amount, wherein key component content is SiO249~
67%th, Al2O314~15%, Fe2O35.5~6.5%, CaO 2~10%, igloss amount 6~13%.
Preferably, preservative is selected from blue peak brand lfk23 type products, is commercially available product.
Preferably, described discarded admaic earth brick powder particles are less than 20 mesh.
In slurry, bentonite is as suspending agent, and iron oxide red is as colouring agent, Zhecheng Brown crake and dextrine powder as shaping
Reinforcing agent, play a part of bonding enhancing semi-finished product and product intensity in blank forming, drying, sintering, composite assistant is by dividing
Powder, water reducer, grinding aid are combined, and preservative, which plays, prevents that slurries are putrid and deteriorated, function of breed bacteria.
Preferably, slurry each component percentage by weight is as follows:
A kind of discarded admaic earth brick powder ceramic flowerpot provided by the invention, its preparation section operating procedure are as follows:
(1) raw material are weighed by above-mentioned slurry each component percentage by weight, by discarded admaic earth brick powder, bentonite, Zhecheng
Brown crake, iron oxide red, dextrine powder, water, composite assistant add grinder, using grinder speed lapping, extract slurry.
(2) above-mentioned slurry is moved into the stirring pool of mixer, preservative is added and is stirred, continue high-speed stirred;
(3) slurry being stirred is transferred in container and deposited, it is old, cast slurry is made;
(4) obtained cast slurry is prepared into ceramic flowerpot base substrate according to ceramic grout technique, by the demoulding, repaired biscuit or portion
Repaired biscuit, drying after part bonding, enter kiln;
Burnt till using the temperature schedule of oxidizing flame as shown in Figure 2, in maximum sintering temperature, 970~1020 DEG C are incubated 2~4h,
System cools, and is taken out after cooling and produces ceramic flowerpot.
Beneficial effect of the present invention:
1st, it is environmentally friendly
It is that primary raw material prepares ceramic flowerpot using discarded conventional red clay brick, is a kind of admaic earth brick recycling discarded well
Utilization ways, it can rationally and effectively clear up discarded admaic earth brick resource.Can solve filling out for building waste to a certain extent
Transport and cost of floor space problem are buried, and can promotion is construction refuse regenerated to be recycled, and makes the attached of discarded admaic earth brick reconstituted product
Value added to be greatly improved, comprehensive benefit is preferable.
2nd, natural resources is saved
According to of the present invention, it can be used to manufacture ceramic flowerpot using discarded conventional red clay brick in large quantities, not only make discarded red
Clay brick fundamentally finds a kind of reliable resolution utilization ways, while can be subject to profit instead of natural clay with large dosage
With can save substantial amounts of natural resources, improve the comprehensive utilization ratio of waste resources.
3rd, manufactured discarded red brick powder ceramic flowerpot intensity height, good permeability
Discarded conventional red clay brick pulverized powder is the clay by roasting, has the property of clinker and poor material, but is contained using it
There is SiO2、Al2O3、Fe2O3There is the characteristics of sintering character under isoreactivity composition high temperature, by the exploration to formula, add other
Ceramic flowerpot carcass strength is high made of making after material, and still contains the higher porosity, the porosity between 12~15%,
With preferable water penetration and breathable properties so that not only improve plant using ceramic flowerpot made of discarded admaic earth brick powder
Growth can also adjust the wettability of air.
4th, the living environment of people is beautified
The ceramic flowerpot of different types can be prepared by method of the present invention, color is traditional brick red colour system, surface
It can be not added with decorating, or simply impose low temperature bristol glaze or use low temperature raw mineral materials colored drawing, the lucky temperature of nature can be showed
Fragrant atmosphere, different potted plants, with releasing negative oxygen ion, can beautify our inhabitation, trip or mining area nature ring in kind
Border, reach the effect that harmonious co-existence between man and nature is appealed to both the more and the less cultured.
Brief description of the drawings
Fig. 1 is the flow chart of the discarded admaic earth brick powder ceramic flowerpot preparation method of the present invention.
Fig. 2 is the discarded admaic earth brick powder ceramic flowerpot sintering curve of the present invention.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described.It should be understood that following examples are merely to illustrate this
Invention is not for restriction the scope of the present invention.
Embodiment 1:The discarded admaic earth brick powder ceramic flowerpot of the present invention is prepared with slurry is poured into a mould, and the weight proportion of each component is such as
1 in table 1#It is shown, stage firing temperature is burnt till as 970 DEG C of insulation 4h in product.
Embodiment 2:Prepared by the discarded admaic earth brick powder ceramic flowerpot of the present invention matches somebody with somebody such as table again with cast slurry, each component
2 in 1#It is shown, stage firing temperature is burnt till as 1000 DEG C of insulation 3h in product.
Embodiment 3:The discarded admaic earth brick powder ceramic flowerpot of the present invention is prepared with slurry is poured into a mould, and the weight proportion of each component is such as
3 in table 1#It is shown, stage firing temperature is burnt till as 1020 DEG C of insulation 2h in product.
Flow prepares ceramic flowerpot of the present invention as shown in Figure 1, is matched by the composition weight of listed cast slurry in table 1
Weigh raw material;
(1) discarded admaic earth brick powder, bentonite, Zhecheng Brown crake, iron oxide red, dextrine powder, water, composite assistant are added
Grinder, 2h is ground under 400r/min high speeds, be ground to 200 mesh fineness, component is uniform, no caking, extracts slurry;
(2) above-mentioned slurry is transferred in the stirring pool of mixer, preservative is added into stirring pool, continue high-speed stirred
30min;
(3) slurry being stirred is transferred in suitable container and deposited, old more than 24h, obtained cast slurry;
(4) obtained cast slurry is prepared into ceramic flowerpot carcass according to ceramic grout technique, by the demoulding, repaired biscuit or portion
Repaired biscuit, drying after part bonding, or surface apply low temperature bristol glaze or use low temperature coloring earth colored drawing, dry again, enter kiln and use oxygen
Change the temperature schedule of flame as shown in Figure 2 to burn till, 2~4h of soak, system cooling, ceramic flowerpot is made.
The performance of discarded admaic earth brick powder ceramic flowerpot:
The discarded admaic earth brick powder ceramic flowerpot prepared according to embodiments of the present invention, its performance test results are shown in Table 2.Detection
Methods and techniques index according to《Make pottery in QB/T 3732.1-1999 ordinary potteries gardens》Requirement carry out.
The cast slurry component proportion that the embodiment of the present invention of table 1 uses
The main performance testing result for the discarded admaic earth brick powder ceramic flowerpot that the embodiment of the present invention of table 2 makes
As seen from the results in Table 2, the water absorption rate of discarded admaic earth brick powder ceramic flowerpot produced by the present invention and bending strength are equal
Meet《Make pottery in QB/T 3732.1-1999 ordinary potteries gardens》Index request, its bending strength is in 25MPa or so higher than minimum
More than limit value 15MPa50%, water absorption rate is near 11%, better than the index request that flowerpot class is not more than 15%, and with certain
Water penetration.The added value of flowerpot of the present invention is high, can beautify the natural environment of ours at one's side, phase of enhancing harmony between man and nature
Raw, appearance color meets the traditional aesthetic temperament and interest of people, great marketing application value.
Claims (2)
1. a kind of discarded admaic earth brick powder ceramic flowerpot, it is characterised in that be molded using gypsum mould grouting method, its slurry is by following
Component forms, each component percentage by weight meter:
Discarded admaic earth brick powder 40 ~ 50%
Bentonite 3 ~ 10%
Water 40 ~ 50%
Iron oxide red 0 ~ 3%
Zhecheng Brown crake 5 ~ 10%
Dextrine powder 0.5 ~ 1.0%
Composite assistant 0.3 ~ 1.5%
Preservative 0.3 ~ 1.5%,
The composite assistant is selected from the type products of Disper 365 of Guilin Qi Hong Science and Technology Ltd.s production.
2. discarded admaic earth brick powder ceramic flowerpot as claimed in claim 1, it is characterised in that each component weight hundred of its slurry
Divide ratio as follows:
Discarded admaic earth brick powder 44 ~ 48%
Bentonite 3 ~ 6%
Water 40 ~ 45%
Iron oxide red 0 ~ 3%
Zhecheng Brown crake 5 ~ 8%
Dextrine powder 0.5 ~ 1.0%
Composite assistant 0.3 ~ 1.0%
Preservative 0.3 ~ 0.5%.