CN107739934A - 一种高韧性铝合金 - Google Patents
一种高韧性铝合金 Download PDFInfo
- Publication number
- CN107739934A CN107739934A CN201711048269.7A CN201711048269A CN107739934A CN 107739934 A CN107739934 A CN 107739934A CN 201711048269 A CN201711048269 A CN 201711048269A CN 107739934 A CN107739934 A CN 107739934A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- alloy
- titanium
- high toughness
- lanthanum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高韧性铝合金,其包括的化学元素成分及其质量百分比为:铜0.8‑2.3%、镧0.6‑1.2%、钛3.2‑3.5%、镁2.1‑2.6%、钇1.1‑1.5%、铬0.6‑0.9%、余量为铝。本发明的有益效果在于提供一种高韧性的铝合金,通过加入钛使得铝合金的强度得到提高,并且提高了铝合金的韧性。
Description
技术领域
本发明涉及材料领域,具体的说,涉及一种高韧性铝合金。
背景技术
铝是一种银白色的轻金属,有较好的延展性,在潮湿空气中能形成一层防止金属腐蚀的氧化膜,铝元素在地壳中的含量仅次于氧和硅,居第三位,是地壳中含量最丰富的金属元素。航空、建筑、汽车三大重要工业的发展,要求材料特性具有铝及其合金的独特性质。
因而提供一种具有高韧性性能的铝合金是现在应用市场所需要的。
发明内容
本发明所要解决的技术问题是提供一种高韧性铝合金。
本发明解决上述技术问题的技术方案如下:
一种高韧性铝合金,其包括的化学元素成分及其质量百分比为:铜3-6%、镧0.6-1.2%、钛3.2-3.5%、镁2.1-2.6%、钇1.1-1.5%、铬0.6-0.9%、余量为铝。
本发明的有益效果是:提供一种高韧性的铝合金,通过加入钛使得铝合金的强度得到提高,并且提高了铝合金的韧性。
在上述技术方案的基础上,本发明还可以做如下改进:
进一步,其包括的化学元素成分及其质量百分比为:铜3%、镧0.6%、钛3.2%、镁2.1%、钇1.1%、铬0.6%、余量为铝。
进一步,其包括的化学元素成分及其质量百分比为:铜5%、镧1.2%、钛3.5%、镁2.6%、钇1.5%、铬0.9%、余量为铝。
进一步,其包括的化学元素成分及其质量百分比为:铜6%、镧1.1%、钛3.3%、镁2.4%、钇1.3%、铬0.78%、余量为铝。
进一步,所述铝合金的制备方法包括如下步骤:先将铝热容,按比例再加入其他元素,保温4小时后成型得到。
具体实施方式
以下结合实施例对本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
实施例1
一种高韧性的铝合金,其包括的化学元素成分及其质量百分比为:铜3%、镧0.6%、钛3.2%、镁2.1%、钇1.1%、铬0.6%、余量为铝。
所述铝合金的制备方法包括如下步骤:先将铝热容,按比例再加入其他元素,保温4小时后成型得到。
实施例2
一种高韧性的铝合金,其包括的化学元素成分及其质量百分比为:铜6%、镧1.2%、钛3.5%、镁2.6%、钇1.5%、铬0.9%、余量为铝。
所述铝合金的制备方法包括如下步骤:先将铝热容,按比例再加入其他元素,保温4小时后成型得到。
实施例3
一种高韧性的铝合金,其包括的化学元素成分及其质量百分比为:铜5%、镧1.1%、钛3.3%、镁2.4%、钇1.3%、铬0.78%、余量为铝。
所述铝合金的制备方法包括如下步骤:先将铝热容,按比例再加入其他元素,保温4小时后成型得到。
对比例1
市售普通铝合金材料。
对上述实施例1-3和对比例1中的金属材料进行机械性能测试,结果见下表。
硬度HB | 抗压强度/MPa | 韧性性能 | |
实施例1 | 126 | 361 | 优秀 |
实施例2 | 125 | 358 | 优秀 |
实施例3 | 123 | 355 | 优秀 |
对比例1 | 69 | 215 | 一般 |
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (5)
1.一种高韧性铝合金,其特征在于,其包括的化学元素成分及其质量百分比为:铜3-6%、镧0.6-1.2%、钛3.2-3.5%、镁2.1-2.6%、钇1.1-1.5%、铬0.6-0.9%、余量为铝。
2.根据权利要求1所述一种高韧性铝合金,其特征在于,其包括的化学元素成分及其质量百分比为:铜3%、镧0.6%、钛3.2%、镁2.1%、钇1.1%、铬0.6%、余量为铝。
3.根据权利要求1所述一种高韧性铝合金,其特征在于,其包括的化学元素成分及其质量百分比为:铜6%、镧1.2%、钛3.5%、镁2.6%、钇1.5%、铬0.9%、余量为铝。
4.根据权利要求1所述一种高韧性铝合金,其特征在于,其包括的化学元素成分及其质量百分比为:铜5%、镧1.1%、钛3.3%、镁2.4%、钇1.3%、铬0.78%、余量为铝。
5.根据权利要求1-4任一所述一种高韧性铝合金,其特征在于,所述铝合金的制备方法包括如下步骤:先将铝热容,按比例再加入其他元素,保温4小时后成型得到。