CN107695613A - 螺母加工工艺 - Google Patents

螺母加工工艺 Download PDF

Info

Publication number
CN107695613A
CN107695613A CN201610639642.5A CN201610639642A CN107695613A CN 107695613 A CN107695613 A CN 107695613A CN 201610639642 A CN201610639642 A CN 201610639642A CN 107695613 A CN107695613 A CN 107695613A
Authority
CN
China
Prior art keywords
nut
processing technology
nut body
cold headers
cold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610639642.5A
Other languages
English (en)
Inventor
莫宁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610639642.5A priority Critical patent/CN107695613A/zh
Publication of CN107695613A publication Critical patent/CN107695613A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种螺母加工工艺，包括以下步骤：用冷镦机将原料冷镦成形，使螺母本体的角部饱满一致；用冷镦机在螺母本体的中心处冲出通孔；用攻丝机在螺母本体的中心孔内加工出内螺纹，形成螺母；打磨加工好的毛坯；检验尺寸；车削毛坯表面；检验尺寸；自然冷却2‑3小时。本发明的有益效果在于：本发明生产的螺母抗压耐磨，使用寿命长。

Description

螺母加工工艺
技术领域
本发明属于工艺领域，具体涉及一种螺母加工工艺。
背景技术
焊接螺母属于五金类标准件，常用于各种精密零件、机箱、机柜、汽车构件等，焊接螺母的一个端面上设有多个焊接点，各焊接点的高度一致。现有的焊接螺母的加工工艺如下：1.螺母本体整形，用冷镦机将坯料镦成形，一般需连续冷镦2～3次，主要是为了螺母本体的 4 个对角饱满一致；2.拉角，用冷镦机将成形后的螺母本体一个端面边缘处镦出高度一致的焊接点；3.冲孔，用冷镦机在螺母本体的中心处冲出通孔；4.攻丝用攻丝机在螺母本体的中心孔内加工出内螺纹。上述工艺生产的螺母抗压耐磨性能不足。
发明内容
本发明所采用的技术方案是：一种螺母加工工艺，包括以下步骤：
用冷镦机将原料冷镦成形，使螺母本体的角部饱满一致；
用冷镦机在螺母本体的中心处冲出通孔；
用攻丝机在螺母本体的中心孔内加工出内螺纹，形成螺母；
打磨加工好的毛坯；
检验尺寸；
车削毛坯表面；
检验尺寸；
自然冷却2-3小时。
作为优选，最佳升温速率为每小时升温 70 摄氏度。
作为优选，冷却时间为3小时。
本发明的有益效果在于：本发明生产的螺母抗压耐磨，使用寿命长。
具体实施方式
下面将结合具体实施例对本发明作进一步详细说明。
一种螺母加工工艺，包括以下步骤：
用冷镦机将原料冷镦成形，使螺母本体的角部饱满一致；
用冷镦机在螺母本体的中心处冲出通孔；
用攻丝机在螺母本体的中心孔内加工出内螺纹，形成螺母；
打磨加工好的毛坯；
检验尺寸；
车削毛坯表面；
检验尺寸；
自然冷却2-3小时。
作为优选，最佳升温速率为每小时升温 70 摄氏度。
作为优选，冷却时间为3小时。
本发明生产的螺母抗压耐磨，使用寿命长。

Claims (3)

1.一种螺母加工工艺，其特征在于：包括以下步骤：
用冷镦机将原料冷镦成形，使螺母本体的角部饱满一致；
用冷镦机在螺母本体的中心处冲出通孔；
用攻丝机在螺母本体的中心孔内加工出内螺纹，形成螺母；
打磨加工好的毛坯；
检验尺寸；
车削毛坯表面；
检验尺寸；
自然冷却2-3小时。
2.根据权利要求1所述的螺母加工工艺，其特征在于：最佳升温速率为每小时升温 70摄氏度。
3.根据权利要求1所述的螺母加工工艺，其特征在于：冷却时间为3小时。
CN201610639642.5A 2016-08-08 2016-08-08 螺母加工工艺 Pending CN107695613A (zh)