CN107675554A - 一种防伪环保转移纸及其制作工艺 - Google Patents
一种防伪环保转移纸及其制作工艺 Download PDFInfo
- Publication number
- CN107675554A CN107675554A CN201711126650.0A CN201711126650A CN107675554A CN 107675554 A CN107675554 A CN 107675554A CN 201711126650 A CN201711126650 A CN 201711126650A CN 107675554 A CN107675554 A CN 107675554A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- paper
- transfer paper
- environmental security
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防伪环保转移纸及其制作工艺,该防伪环保转移纸具有菲涅尔透镜结构,本发明根据菲涅尔透镜的特定结构,创新地开发新型树脂涂料,并通过工艺的改进与创新,利用紫外光固化技术的优势,将紫外光固化技术和模压工艺结合,最后得到复制有菲涅尔透镜结构的防伪环保转移纸,并且使该防伪环保转移纸具有菲涅尔透镜结构清晰、视觉效果好、环保、防伪特性强等优点。
Description
技术领域
本发明涉及特种防伪材料邻域,尤其涉及一种防伪环保转移纸及其制作工艺。
背景技术
菲涅尔透镜是由像厚透镜弯曲或反射光的小平面所组成的微结构。它们可以被聚焦或散开光线。菲涅尔透镜有线状的,也有圆形的。前者镜面集中在一条轴上,看上去像一个圆柱;后者看上去则像一个圆球。有聚透镜和发散透镜,前者焦点在镜头的前方;后者当光从镜头后方射过来时,有一个虚拟焦点在镜头后方。所以,两个紧挨着的聚透镜和发散透镜,前者的实焦点在胶片上面,后者的虚拟焦点在胶片后面,移动时两个焦点向相反方向,会给人造成视觉上的错觉。这些透镜使用金刚石车床制作,利用金刚石工具将小平面切割成金属模具。在最早的时候,菲涅尔透镜一边是平的,一边是凸的,常被安装在房车的后部,这样驾驶员就能够看到更广的范围。制作菲涅尔透镜首先从金属板模具开始,金属板可以用铜或者镍,先平整切割,确保所有切过的地方纹路清晰。切割好后,其像面镜子。然后,把这些切割好的面放进模具,这些面和角将决定菲涅尔透镜的光的反射。在这个阶段,金属片将会成为原始母版,在它的基础上再复制更多模具。接下来,将紫外光固化聚合物应用于聚酯胶片,然后再与圆柱状的轴承(指母版的复制品)相结合,圆柱上的图像便可转移到胶片上。然后,将胶片放进喷镀金属器,涂上铝,这样它变得不透明但能反光。如果没有涂层,图像将消失在胶粘剂中。最终,将其连同相应的设计颜色和菲涅尔透镜等一起放在印刷机器中,生产出菲涅尔透镜包装产品。将菲涅尔透镜引入包装中,可以显示包装所在的区域,如果您站在商店的某个区域,有人在您和包装之间走动,包装将看起来具有均匀的运动,抓住你的视角,把你带到包装之中。为确保图像清晰并具有防伪的特性,可以将全息图技术与菲涅尔透镜结合起来,这样可以使图像具有菲涅尔透镜结构的同时又有彩虹一样的光泽。这种菲涅尔透镜技术以及全息图技术的高技术门槛以及不可复制性可以增加图像的防伪特性。
紫外光固化技术是二十世纪60年代以来开发的一种高效节能环保的高新固化技术,它是指在高能量的紫外光作为固化能源的照射下,由体系中的光引发剂吸收紫外光产生自由基,引发光敏树脂(预聚物)和活性稀剂分子发生连锁聚合反应,使得液相体系在瞬间进行聚合、交联和固化的过程。紫外光固化技术具有低挥发性有机物排放量,固化速度快,节省能源,固化膜综合性能好,降低可燃性,减少液态废弃物,适合高速自动化生产线和对热敏感基材的涂布等诸多优点。紫外光固化材料由于应用了紫外光固化技术,防止了溶剂挥发造成的污染,节约了能源,大大缩短了固化时间,从而增加经济效益。
然而,由于菲涅尔结构的结构深度大的特性决定了其用传统方法复制得到的只能是覆膜纸,覆膜纸会对环境造成污染。出于环保方面的需要,制作具有菲涅尔透镜结构的防伪环保转移纸是十分必要的。这需要通过大量的创造性工作,根据菲涅尔透镜的特定结构,创新地开发新型树脂涂料,并通过工艺的改进与创新,利用紫外光固化技术的优势,将紫外光固化技术和模压工艺结合,最后得以复制菲涅尔透镜结构和其它全息图文,制作具有菲涅尔透镜结构的防伪环保转移纸。
发明内容
本发明的目的是针对现有技术存在的缺陷,提供一种防伪环保转移纸及其制作工艺,这种工艺得到的转移纸具有清晰的菲涅尔透镜结构且拥有视觉效果好、环保、防伪特性强等优点。
本发明的目的是这样实现的:
本发明的一种防伪环保转移纸上具有菲涅尔透镜结构;该防伪环保转移纸包括保护层、紫外光转移层、紫外光固化层、粘结涂料层、铝层、胶粘层和纸张;纸张设置在胶粘层的下表面;胶粘层设置在铝层的下表面;铝层设置在粘结涂料层的下表面;粘结涂料层设置在紫外光固化层的下表面;紫外光固化层设置在紫外光转移层的下表面;紫外光转移层设置在保护层的下表面;。
上述的一种防伪环保转移纸,其中,纸张为白卡纸、铜版纸、灰卡纸、黑卡纸、红卡纸、黄卡纸、蓝卡纸、绿卡纸、哑粉纸及特种纸中的一种。
上述的一种防伪环保转移纸的制作工艺,包括以下步骤:
步骤一:制作具有菲涅尔透镜结构的模压工作板,并将模压工作板安装于模压辊上;
步骤二:在基膜的下表面依次涂布紫外光转移涂料、紫外光固化涂料,并在基膜的下表面依次形成紫外光转移层和紫外光固化层;
步骤三:将步骤二中的涂布后的基膜放置在模压工作板上,使紫外光固化层与模压工作板上的模压辊紧密接触,并将紫外光固化涂料在压力的作用下填满模压工作板中的菲涅尔透镜结构,然后使用紫外光照射基膜的表面,使紫外光固化涂料固化,从而使基膜的下表面上复制有菲涅尔透镜结构;
步骤四:在步骤三中的具有菲涅尔透镜结构的紫外光固化层的下表面上涂布粘结涂料,得到具有菲涅尔透镜结构的粘结涂料层;
步骤五:在步骤四中具有菲涅尔透镜结构的粘结涂料层的下表面上进行真空镀铝,得到具有所述菲涅尔透镜结构的铝层;
步骤六:在步骤五中具有所述菲涅尔透镜结构的铝层的下表面上涂布胶粘涂料,得到胶粘层,并通过胶粘层与纸张复合;随后将基膜剥离,在紫外光离心层的上表面上涂布保护涂料,形成保护层,得到具有菲涅尔透镜结构的防伪环保转移纸。
上述的一种防伪环保转移纸的制作工艺,其中,步骤一中的模压工作板的制备工艺包括以下步骤:
S1:利用金刚石车床制作菲涅尔透镜;
S2:将S1中得到的菲涅尔透镜结构复制于基材上,然后进行固化处理;
S3:将S2中固化后的基材进行两次电镀处理,得到复制有上述菲涅尔透镜结构的模压工作板,或直接使用S2中固化后的基材作为模压工作板。
上述的一种防伪环保转移纸的制作工艺,其中,步骤一中的模压工作板的材质为镍板、PET板、BOPP板、PVC板、PC板中的一种。
上述的一种防伪环保转移纸的制作工艺,其中,步骤二中的基膜为BOPP基膜、PET基膜、PVC基膜、PI基膜、PC基膜中的一种。
上述的一种防伪环保转移纸的制作工艺,其中,步骤二中的紫外光转移涂料包括以下组分及重量份数:甲醚化氨基树脂10-20份,羟基丙烯酸树脂5-15份,聚乙烯醇树脂1-10份,乙酸0.5-3份,助溶剂0.5-10份,溶剂10-40份,去离子水1-30份,苯乙烯-丙烯酸酯共聚物乳液5-40份,水溶性硅溶胶20-30份,润湿剂0.1-2份,消泡剂0.01-0.1份,流平剂0.1-2份,抗静电剂0.1-1份;所述助溶剂为苯甲酸钠、水杨酸钠、对氨基苯甲酸钠中的至少一种;所述溶剂为乙醇、正丙醇、异丙醇、正丁醇、醋酸乙酯、醋酸正丙酯、醋酸丁酯、丙二醇甲醚、丙二醇乙醚中的至少一种。
上述的一种防伪环保转移纸的制作工艺,其中,步骤二中的紫外光固化涂料包括以下组分及重量份数:光固化树脂5-70份,光聚合单体10-90份,溶剂2-70份,光引发剂0.5-40份,助剂0-15份,附着力促进剂3-10份,滑石粉0.1-10份,消静电剂0.5-10份;所述光固化树脂选自环氧丙烯酸酯、聚氨酯丙烯酸酯、聚酯丙烯酸酯、聚醚丙烯酸酯、纯丙烯酸酯、有机硅低聚物、光固化聚丁二烯低聚物、有机-无机杂化树脂中的至少一种;所述光聚合单体为具有1-5个烯属不饱和双键的丙烯酸酯,所述溶剂为乙醇、正丙醇、异丙醇、正丁醇、醋酸乙酯、醋酸正丙酯、醋酸丁酯、丙二醇甲醚、丙二醇乙醚中的至少一种,所述光引发剂为2-羟基-2-甲基-1-苯基-1-丙酮、安息香双甲醚、二苯甲酮、1-羟基-环己基苯基酮、2,4,6-三甲基苯甲酰基二苯基氧化磷中的至少一种;所述助剂为抗划伤剂、流平剂、交联剂、分散剂、增塑剂中的至少一种。
上述的一种防伪环保转移纸的制作工艺,其中,步骤四中的粘结涂料包括以下组分及重量份数:氯醋树脂1-10份,聚丙烯酸酯树脂10-50份,醋酸乙酯10-30份,乙醇1-20份,正丙醇0.1-5份,异丙醇0.1-5份,丁酮5-20份,助剂0.1-20份;所述助剂为流平剂、交联剂、增塑剂中的至少一种。
上述的一种防伪环保转移纸的制作工艺,其中,步骤六中的胶粘涂料包括以下组分及重量份数:丙烯酸酯树脂10-50份,醋酸乙烯酯1-30份,甲基丙烯酸甲酯1-15份,丙烯酰胺1-5份,氢氧化钠0.1-2份,醋酸0.1-2份,乙醇10-40份,丁酮5-20份,乳化剂0.1-5份,助剂0.1-10份,溶剂10-40份;所述助剂为交联剂、增韧剂、增黏剂、消泡剂中的至少一种;所述溶剂为正丙醇、异丙醇、正丁醇、醋酸乙酯、醋酸正丙酯、醋酸丁酯、丙二醇甲醚、丙二醇乙醚中的至少一种。
上述的一种防伪环保转移纸的制作工艺,其中,步骤六中剥离后的基膜,在下一次制作所述具有菲涅尔透镜结构的防伪环保转移纸时在所述步骤二中重复使用。
上述的一种防伪环保转移纸的制作工艺,其中,步骤六中的保护涂料包括以下组分及重量份数:水性丙烯酸酯树脂乳液10-50份,聚四氢呋喃醚二醇5-20份,聚酯二元醇1-15份,氢化苯基甲烷二异氰酸酯1-15份,抗划伤剂0.1-5份,滑石粉0.1-1份,消泡剂0.1-2份,抗静电剂0.1-2份,透明剂0.1-5份,抗氧化剂0.1-1份,乙醇1-20份,去离子水1-25份。
本发明根据菲涅尔透镜的特定结构,创新地开发新型树脂涂料,并通过工艺的改进与创新,利用紫外光固化技术的优势,将紫外光固化技术和模压工艺结合,最后得到复制有菲涅尔透镜结构的防伪环保转移纸,并且使该转移纸具有菲涅尔透镜结构清晰、视觉效果好、环保、防伪特性强等优点。
附图说明
图1是本发明防伪环保转移纸的结构示意图。
具体实施方式
图1示出了实施例1和实施例2的防伪环保转移纸的结构示意图,该防伪环保转移纸上具有菲涅尔透镜结构;该防伪环保转移纸包括保护层1、紫外光转移层2、紫外光固化层3、粘结涂料层4、铝层5、胶粘层6和纸张7;纸张7设置在胶粘层6的下表面;胶粘层6设置在铝层5的下表面;铝层5设置在粘结涂料层4的下表面;粘结涂料层4设置在紫外光固化层3的下表面;紫外光固化层3设置在紫外光转移层2的下表面;紫外光转移层2设置在保护层1的下表面;纸张7为白卡纸、铜版纸、灰卡纸、黑卡纸、红卡纸、黄卡纸、蓝卡纸、绿卡纸、哑粉纸及特种纸中的一种。
下面将结合实施例,对本发明防伪环保转移纸的制作工艺作进一步说明。
实施例1
一种防伪环保转移纸的制作工艺,包括以下步骤:
利用金刚石车床制作中心透镜半径20cm样式的菲涅尔透镜;将得到的菲涅尔透镜结构利用紫外光固化涂料复制于PET基材上,然后使用紫外光固化处理,紫外光波长设置为150-300nm之间,固化时间0.1h;将固化后的PET基材在电铸槽中进行两次电镀处理,得到复制有上述菲涅尔透镜结构的模压工作板。将模压工作板安装于模压辊上。
按照如下组分及重量份数制作紫外光转移涂料:甲醚化氨基树脂15份,羟基丙烯酸树脂10份,聚乙烯醇树脂8份,乙酸2.3份,水杨酸钠5.8份,乙醇26份,正丁醇6份,异丙醇10份,去离子水26份,苯乙烯-丙烯酸酯共聚物乳液34份,水溶性硅溶胶21份,润湿剂1.3份,消泡剂0.08份,流平剂1.2份,抗静电剂0.5份。
将紫外光转移涂料用涂布机涂布至PET基膜的下表面上,PET基膜的膜厚10μm,涂布机网纹辊为300目,输送速度150m/min,干涂布量为0.6g/m2,涂布时紫外光离心涂料的粘度为15秒(涂4-杯,25℃),烘干温度为80℃。
按照如下组分及重量份数制作紫外光固化涂料:环氧丙烯酸酯30份,聚氨酯丙烯酸酯12份,聚醚丙烯酸酯5份,光固化聚丁二烯低聚物8份,光聚合单体45份,乙醇35份,正丙醇12份,正丁醇8份,丙二醇甲醚2份,2-羟基-2-甲基-1-苯基-1-丙酮2份,安息香双甲醚2份,二苯甲酮2份,流平剂2份,附着力促进剂5份,滑石粉0.6份,消静电剂1.5份。
将紫外光固化涂料用涂布机涂布至PET基膜的紫外光离心层的下表面上,涂布机网纹辊为250目,输送速度200m/min,干涂布量为3g/m2,涂布时紫外光固化涂料的粘度为20秒(涂4-杯,25℃),烘干温度为90℃。
将涂布有紫外光固化层的PET基膜进行模压,使PET基膜的被涂布面与模压工作板上的模压辊紧密接触,并将紫外光固化涂料在压力的作用下填满工作板中的菲涅尔透镜结构,然后使用紫外光照射膜面,得到复制有上述菲涅尔透镜结构的PET基膜。其中,模压辊上压力为5kg/cm2,模压辊下压力为5kg/cm2,PET基膜的运行张力为30N,紫外光灯管的功率为25kW、强度120W/cm,波长为150-300nm之间。
按照如下组分及重量份数制作粘结涂料:氯醋树脂8份,聚丙烯酸酯树脂45份,醋酸乙酯25份,乙醇20份,正丙醇2.5份,异丙醇3.5份,丁酮5份,流平剂3份,交联剂2份。
将粘结涂料用涂布机涂布至紫外光固化层的下表面上,涂布机网纹辊为100目,输送速度150m/min,干涂布量为1g/m2,涂布时粘结涂料的粘度为10秒(涂4-杯,25℃),烘干温度为100℃。
将上述步骤后得到的粘结涂料层的下表面上进行真空镀铝,车速为500m/min,铝层厚度为50nm,得到具有所述菲涅尔透镜结构的铝层。
按照如下组分及重量份数制作胶粘涂料:丙烯酸酯树脂35份,醋酸乙烯酯25份,甲基丙烯酸甲酯10份,丙烯酰胺3份,氢氧化钠1.3份,醋酸1.5份,乙醇35份,丁酮10份,乳化剂4份,消泡剂2份,增粘剂2份,交联剂2份,正丙醇5份,醋酸丁酯10份。
将胶粘涂料用涂布机涂布至铝层的下表面上,涂布机网纹辊为300目,输送速度200m/min,干涂布量为2g/m2,涂布时胶粘层涂料的粘度为8秒(涂4-杯,25℃),烘干温度为80℃。
通过胶粘层将PET基膜与纸张用复合机复合,纸张选用白卡纸,车速400m/min。
复合后将纸张表面的PET基膜单独剥离,剥离速度300m/min,剥离后的PET基膜,可在下一次制作该防伪环保转移纸时重复使用,或做其它用途。
按照如下组分及重量份数制作保护涂料:水性丙烯酸酯树脂乳液45份,聚四氢呋喃醚二醇15份,聚酯二元醇13份,氢化苯基甲烷二异氰酸酯13份,抗划伤剂2.5份,滑石粉0.8份,消泡剂1.2份,抗静电剂0.8份,透明剂3.5份,抗氧化剂0.6份,乙醇20份,去离子水20份。
将保护涂料用涂布机涂布至紫外光离心层的上表面上,涂布机网纹辊为300目,输送速度200m/min,干涂布量为1g/m2,涂布时保护涂料的粘度为4秒(涂4-杯,25℃),烘干温度为120℃。
最终,得到具有中心透镜半径20cm特定、、样式的菲涅尔透镜结构的防伪环保转移纸,可用于包装、印刷、特种防伪、特种光学等邻域。
实施例2
一种防伪环保转移纸的制作工艺,包括以下步骤:
利用金刚石车床制作中心透镜半径30cm样式的菲涅尔透镜;将得到的菲涅尔透镜结构利用紫外光固化涂料复制于PET基材上,然后使用紫外光固化处理,紫外光波长设置为150-300nm之间,固化时间0.15h;将固化后的PET基材在电铸槽中进行两次电镀处理,得到复制有上述菲涅尔透镜结构的模压工作板。将模压工作板安装于模压辊上。
按照如下组分及重量份数制作紫外光转移涂料:甲醚化氨基树脂15份,羟基丙烯酸树脂11份,聚乙烯醇树脂8份,乙酸2.2份,水杨酸钠5.8份,乙醇26份,正丁醇6份,异丙醇10份,去离子水26份,苯乙烯-丙烯酸酯共聚物乳液40份,水溶性硅溶胶21份,润湿剂1.5份,消泡剂0.08份,流平剂1.2份,抗静电剂0.5份。
将紫外光转移涂料用涂布机涂布至PET基膜的下表面上,PET基膜的膜厚为15μm,涂布机网纹辊为300目,输送速度200m/min,干涂布量为0.5g/m2,涂布时紫外光离心涂料的粘度为15秒(涂4-杯,25℃),烘干温度为90℃。
按照如下组分及重量份数制作紫外光固化涂料:环氧丙烯酸酯30份,聚氨酯丙烯酸酯13份,聚醚丙烯酸酯5份,光固化聚丁二烯低聚物6份,光聚合单体30份,乙醇35份,正丙醇12份,正丁醇8份,醋酸正丙酯2份,2-羟基-2-甲基-1-苯基-1-丙酮2份,1-羟基-环已基苯甲酮2份,二苯甲酮2份,流平剂2份,附着力促进剂6份,滑石粉0.6份,消静电剂1.5份。
将紫外光固化涂料用涂布机涂布至PET基膜的紫外光离心层的下表面上,涂布机网纹辊为300目,输送速度150m/min,干涂布量为3g/m2,涂布时紫外光固化涂料的粘度为15秒(涂4-杯,25℃),烘干温度为90℃。
将涂布有紫外光固化层的PET基膜进行模压,使PET基膜被涂布面与模压工作板上的模压辊紧密接触,并将紫外光固化涂料在压力的作用下填满工作板中的菲涅尔透镜结构,然后使用紫外光照射膜面,得到复制有中心透镜半径30cm样式的菲涅尔透镜结构的PET基膜。其中,模压辊上压力为6kg/cm2,模压辊下压力为6kg/cm2,PET基膜的运行张力为25N,紫外光灯管的功率为25kW、强度120W/cm,波长为150-300nm之间。
按照如下组分及重量份数制作粘结涂料:氯醋树脂6份,聚丙烯酸酯树脂40份,醋酸乙酯20份,乙醇15份,正丙醇4份,异丙醇5份,丁酮5份,流平剂3份,交联剂2份。
将粘结涂料用涂布机涂布至紫外光固化层的下表面上,涂布机网纹辊为150目,输送速度200m/min,干涂布量为1.5g/m2,涂布时粘结涂料的粘度为15秒(涂4-杯,25℃),烘干温度为100℃。
在上述步骤后得到的粘结涂料层的下表面上进行真空镀铝,车速为550m/min,铝层厚度为40nm,得到具有中心透镜半径30cm样式的菲涅尔透镜结构的铝层。
按照如下组分及重量份数制作胶粘涂料:丙烯酸酯树脂40份,醋酸乙烯酯20份,甲基丙烯酸甲酯8份,丙烯酰胺5份,氢氧化钠1.3份,醋酸1.5份,乙醇40份,丁酮10份,乳化剂4份,消泡剂2份,增粘剂2份,交联剂2份,正丙醇5份,醋酸丁酯10份。
将胶粘涂料用涂布机涂布至铝层的下表面上,涂布机网纹辊为200目,输送速度250m/min,干涂布量为1.5g/m2,涂布时胶粘层涂料的粘度为10秒(涂4-杯,25℃),烘干温度为90℃。
通过胶粘层将PET基膜与纸张用复合机复合,纸张选用白卡纸,车速350m/min。
复合后将纸张表面的PET基膜单独剥离,剥离速度350m/min,剥离后的PET基膜,可在下一次制作该防伪环保转移纸时重复使用,或做其它用途。
按照如下组分及重量份数制作保护涂料:水性丙烯酸酯树脂乳液50份,聚四氢呋喃醚二醇20份,聚酯二元醇13份,氢化苯基甲烷二异氰酸酯13份,抗划伤剂3份,滑石粉0.8份,消泡剂1.2份,抗静电剂0.8份,透明剂3份,抗氧化剂0.6份,乙醇20份,去离子水25份。
将保护涂料用涂布机涂布至紫外光离心层的上表面上,涂布机网纹辊为300目,输送速度250m/min,干涂布量为1.5g/m2,涂布时保护涂料的粘度为5秒(涂4-杯,25℃),烘干温度为120℃。
最终,得到具有中心透镜半径30cm样式的菲涅尔透镜结构的防伪环保转移纸,可用于包装、印刷、特种防伪、特种光学等邻域。
实施例1与实施例2中,PET基膜的重复利用次数为30次以上,在环保的同时降低了企业的生产成本。
实施例1与实施例2中,铝层与纸张的附着牢度根据以下标准进行测试:中华人民共和国包装行业标准:真空镀铝纸(BB/T 0054-2010),测得结果为实施例1与实施例2中的附着牢度均大于99%。
本发明根据菲涅尔透镜的特定结构,研制出新型紫外光固化涂料,通过工艺的改进与创新,将紫外光固化技术与模压工艺结合,使制得的防伪环保转移纸具有清晰的菲涅尔透镜结构;紫外光转移层使基膜可以被单独剥离干净并重复使用,由于基膜被单独剥离后,具有菲涅尔透镜结构的紫外光固化层依然覆盖在纸张上,从而使菲涅尔透镜结构更加清晰,保护层防止了菲涅尔透镜结构被刮花,保证了菲涅尔透镜结构清晰,粘结涂料层、胶粘层和真空镀铝技术使铝层附着牢度更好,铝层的设计使本发明的防伪环保转移纸具有金属光泽。
以上实施例仅供说明本发明之用,而非对本发明的限制,有关技术领域的技术人员,在不脱离本发明的精神和范围的情况下,还可以作出各种变换或变型,因此所有等同的技术方案也应该属于本发明的范畴,应由各权利要求所限定。
Claims (10)
1.一种防伪环保转移纸,其特征在于,所述防伪环保转移纸上具有菲涅尔透镜结构;
所述防伪环保转移纸包括保护层、紫外光转移层、紫外光固化层、粘结涂料层、铝层、胶粘层和纸张;
所述纸张设置在所述胶粘层的下表面;所述胶粘层设置在所述铝层的下表面;所述铝层设置在所述粘结涂料层的下表面;所述粘结涂料层设置在所述紫外光固化层的下表面;所述紫外光固化层设置在所述紫外光转移层的下表面;所述紫外光转移层设置在所述保护层的下表面。
2.如权利要求1所述的一种防伪环保转移纸,其特征在于,所述纸张为白卡纸、铜版纸、灰卡纸、黑卡纸、红卡纸、黄卡纸、蓝卡纸、绿卡纸、哑粉纸及特种纸中的一种。
3.如权利要求1或2所述的任一种防伪环保转移纸的制作工艺,其特征在于,包括以下步骤:
步骤一:制作具有菲涅尔透镜结构的模压工作板,并将模压工作板安装于模压辊上;
步骤二:在基膜的下表面依次涂布紫外光转移涂料、紫外光固化涂料,并在基膜的下表面依次形成紫外光转移层和紫外光固化层;
步骤三:将所述步骤二中的涂布后的基膜放置在模压工作板上,使紫外光固化层与模压工作板上的模压辊紧密接触,并将紫外光固化涂料在压力的作用下填满模压工作板中的菲涅尔透镜结构,然后使用紫外光照射基膜的表面,使紫外光固化涂料固化,从而使基膜的下表面上复制有菲涅尔透镜结构;
步骤四:在所述步骤三中的具有菲涅尔透镜结构的紫外光固化层的下表面上涂布粘结涂料,得到具有菲涅尔透镜结构的粘结涂料层;
步骤五:在所述步骤四中具有菲涅尔透镜结构的粘结涂料层的下表面上进行真空镀铝,得到具有所述菲涅尔透镜结构的铝层;
步骤六:在所述步骤五中具有所述菲涅尔透镜结构的铝层的下表面上涂布胶粘涂料,得到胶粘层,并通过胶粘层与纸张复合;随后将基膜剥离,在紫外光离心层的上表面上涂布保护涂料,形成保护层,得到具有菲涅尔透镜结构的防伪环保转移纸。
4.如权利要求3所述的一种防伪环保转移纸的制作工艺,其特征在于,所述步骤一中的模压工作板的制备工艺包括以下步骤:
S1:利用金刚石车床制作菲涅尔透镜;
S2:将所述S1中得到的菲涅尔透镜结构复制于基材上,然后进行固化处理;
S3:将所述S2中固化后的基材进行两次电镀处理,得到复制有上述菲涅尔透镜结构的模压工作板,或直接使用所述S2中固化后的基材作为模压工作板。
5.如权利要求3所述的一种防伪环保转移纸的制作工艺,其特征在于,所述步骤二中的紫外光转移涂料包括以下组分及重量份数:甲醚化氨基树脂10-20份,羟基丙烯酸树脂5-15份,聚乙烯醇树脂1-10份,乙酸0.5-3份,助溶剂0.5-10份,溶剂10-40份,去离子水1-30份,苯乙烯-丙烯酸酯共聚物乳液5-40份,水溶性硅溶胶20-30份,润湿剂0.1-2份,消泡剂0.01-0.1份,流平剂0.1-2份,抗静电剂0.1-1份;所述助溶剂为苯甲酸钠、水杨酸钠、对氨基苯甲酸钠中的至少一种,所述溶剂为乙醇、正丙醇、异丙醇、正丁醇、醋酸乙酯、醋酸正丙酯、醋酸丁酯、丙二醇甲醚、丙二醇乙醚中的至少一种。
6.如权利要求3所述的一种防伪环保转移纸的制作工艺,其特征在于,所述步骤二中的紫外光固化涂料包括以下组分及重量份数:光固化树脂5-70份,光聚合单体10-90份,溶剂2-70份,光引发剂0.5-40份,助剂0-15份,附着力促进剂3-10份,滑石粉0.1-10份,消静电剂0.5-10份;所述光固化树脂选自环氧丙烯酸酯、聚氨酯丙烯酸酯、聚酯丙烯酸酯、聚醚丙烯酸酯、纯丙烯酸酯、有机硅低聚物、光固化聚丁二烯低聚物、有机-无机杂化树脂中的至少一种;所述光聚合单体为具有1-5个烯属不饱和双键的丙烯酸酯,所述溶剂为乙醇、正丙醇、异丙醇、正丁醇、醋酸乙酯、醋酸正丙酯、醋酸丁酯、丙二醇甲醚、丙二醇乙醚中的至少一种,所述光引发剂为2-羟基-2-甲基-1-苯基-1-丙酮、安息香双甲醚、二苯甲酮、1-羟基-环己基苯基酮、2,4,6-三甲基苯甲酰基二苯基氧化磷中的至少一种,所述助剂为抗划伤剂、流平剂、交联剂、分散剂、增塑剂中的至少一种。
7.如权利要求3所述的一种防伪环保转移纸的制作工艺,其特征在于,所述步骤四中的粘结涂料包括以下组分及重量份数:氯醋树脂1-10份,聚丙烯酸酯树脂10-50份,醋酸乙酯10-30份,乙醇1-20份,正丙醇0.1-5份,异丙醇0.1-5份,丁酮5-20份,助剂0.1-20份;所述助剂为流平剂、交联剂、增塑剂中的至少一种。
8.如权利要求3所述的一种防伪环保转移纸的制作工艺,其特征在于,所述步骤六中的胶粘涂料包括以下组分及重量份数:丙烯酸酯树脂10-50份,醋酸乙烯酯1-30份,甲基丙烯酸甲酯1-15份,丙烯酰胺1-5份,氢氧化钠0.1-2份,醋酸0.1-2份,乙醇10-40份,丁酮5-20份,乳化剂0.1-5份,助剂0.1-10份,溶剂10-40份;所述助剂为交联剂、增韧剂、增黏剂、消泡剂中的至少一种,所述溶剂为正丙醇、异丙醇、正丁醇、醋酸乙酯、醋酸正丙酯、醋酸丁酯、丙二醇甲醚、丙二醇乙醚中的至少一种。
9.如权利要求3所述的一种防伪环保转移纸的制作工艺,其特征在于,所述步骤六中剥离后的基膜,在下一次制作所述防伪环保转移纸时在所述步骤二中重复使用。
10.如权利要求3所述的一种防伪环保转移纸的制作工艺,其特征在于,所述步骤六中的保护涂料包括以下组分及重量份数:水性丙烯酸酯树脂乳液10-50份,聚四氢呋喃醚二醇5-20份,聚酯二元醇1-15份,氢化苯基甲烷二异氰酸酯1-15份,抗划伤剂0.1-5份,滑石粉0.1-1份,消泡剂0.1-2份,抗静电剂0.1-2份,透明剂0.1-5份,抗氧化剂0.1-1份,乙醇1-20份,去离子水1-25份。