CN107652625A - 一种变色三聚氰胺甲醛模塑料及其制备方法 - Google Patents
一种变色三聚氰胺甲醛模塑料及其制备方法 Download PDFInfo
- Publication number
- CN107652625A CN107652625A CN201711027801.7A CN201711027801A CN107652625A CN 107652625 A CN107652625 A CN 107652625A CN 201711027801 A CN201711027801 A CN 201711027801A CN 107652625 A CN107652625 A CN 107652625A
- Authority
- CN
- China
- Prior art keywords
- molding compound
- melamine
- melamine formaldehyde
- discoloration
- formaldehyde molding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种变色三聚氰胺甲醛模塑料及其制备方法，该变色三聚氰胺甲醛模塑料包括以下质量分数的成分：三聚氰胺50%~60%、甲醛20%~30%、纸浆10%~20%、变色材料1%~5%、钛白粉2%~5%、颜色粉1%~10%、脱模剂0.2%~0.6%、固化剂1%~5%；其中，变色材料为隐色染料壳—芯结构，其外壳为固化交联的密胺环氧树脂聚合物，内芯为隐色染料。由本发明制得的三聚氰胺甲醛模塑料，着色工艺简单、热稳定性高，不易掉色或色彩暗淡，外表美观新颖，且无有毒物质产生。
Description
技术领域
本发明属于高分子塑料技术领域，具体涉及一种变色三聚氰胺甲醛模塑料及其制备方法。
背景技术
三聚氰胺甲醛模塑料又称蜜胺模塑料，是一种高性能复合材料，以三聚氰胺甲醛树脂为基体，有机或无机填料为增强体，加入各类助剂，通过一定塑化工艺制备而来。由于原料价格低廉，制品色泽鲜艳，外观光滑，无臭无味，具有自熄及耐电弧性、耐热、阻燃、制品尺寸稳定，因而广泛应用于电子、电器、汽车、日用品等行业。
但目前三聚氰胺甲醛模塑粉着色工艺比较单一，且在高温高湿下稳定性差，在后续的三聚氰胺甲醛模塑粉成型阶段，压制的模温一般在150℃到180℃之间，易引起三聚氰胺甲醛模塑粉的颜色迁移，当温度降低时，制得的成品灰暗且没有光泽，因此，本发明改变三聚氰胺甲醛模塑粉的着色工艺，使三聚氰胺甲醛模塑粉具有较强的热稳定性、透明性以及着色力，是本领域技术人员亟待解决的技术问题。
发明内容
本发明的目的在于：为了解决上述背景技术中的现有技术存在的问题，提供一种着色工艺简单、外表美观新颖的三聚氰胺甲醛模塑料，且无有毒物质产生，可以实现从“有色—无色” “有色—有色” “无色—无色”状态的颜色变化。
本发明解决其技术问题所采用的技术方案是：
一种变色三聚氰胺甲醛模塑料，包括以下质量分数的成分：三聚氰胺50%~60%、甲醛20%~30%、纸浆10%~20%、变色材料1%~5%、钛白粉2%~5%、颜色粉1%~10%、脱模剂0.2%~0.6%、固化剂1%~5%；变色材料为隐色染料壳—芯结构，其外壳为固化交联的密胺环氧树脂聚合物，内芯为隐色染料。
优选地，隐色染料为肉豆蔻醇、十六酸十二醇脂、2,2-二（4-羟基苯基）丁烷的其中的一种或几种。
优选地，脱模剂为硬脂酸钙、硬脂酸镁、硬脂酸锌其中的一种或几种。
优选地，固化剂为苯酐、三乙醇胺和苯甲酸中的一种或几种。
优选地，所述颜色粉为红、黄、蓝中的一种或几种。
本发明还公开了一种变色三聚氰胺甲醛模塑料的制备方法，包括以下步骤：
A.捏合：在反应斧中投入甲醛，加入碱液调节至合适的PH后，加入三聚氰胺，升温至90℃后保温，用20℃水测白后加入固化剂，降温至70℃，抽取入捏合机，再向捏合机中加入变色材料、纸浆、脱模剂，捏合，烘干，得到均匀的基料。
B.球磨：在球磨机投入钛白粉、颜色粉、固化剂以及步骤A制得的基料，球磨，粉筛机过筛装袋即得变色三聚氰胺甲醛塑料。
优选地，所述甲醛为质量浓度30％~50％的甲醛水溶液。
优选地，步骤A 中的pH值为8~9。
优选地，粉筛机的目数为40~80目。
优选地，捏合时间为60~80min，球磨时间为12~14h。
与现有技术相比，本发明具有以下有益效果：（1）本发明中的变色材料外壳为固化交联的蜜胺环氧树脂聚合物，内芯为肉豆蔻醇、十六酸十二醇酯、2,2-二(4羟基苯基)丁烷等隐色染料，该结构耐酸碱，耐高温，同时可使隐色染料免受其它化学物质的侵蚀，由此制得的变色三聚氰胺甲醛模塑料着色力强，在后面的塑粉阶段，有着较强的热稳定性、透明性，无变色或光泽变暗等问题出现；（2）本发明制得的变色三聚氰胺甲醛模塑料，不含重金属及其他有毒成份，且具有美观新颖的优点，可广泛应用于密胺餐具、仿瓷餐具、中低压电器等阻燃型产品；（3）本发明制得的变色三聚氰胺甲醛模塑料，本色较淡，易于制备浅色系的彩色制品；（4）本发明中加入了超量的三聚氰胺，可有效的降低树脂中的游离甲醛，同时高温干燥进一步的降低游离甲醛，使得制得的变色三聚氰胺甲醛模塑料具有较低的甲醛释放量。
具体实施方式
现在结合实施例对发明进一步详细的说明。
实施例1
一种变色三聚氰胺甲醛模塑料，包括以下质量分数的成分：三聚氰胺50%、甲醛20%、纸浆10%、变色材料1%、钛白粉5%、颜色粉9%、硬脂酸钙0.6%、苯酐4%，变色材料为隐色染料壳—芯结构，其外壳为固化交联的密胺环氧树脂聚合物，内芯为肉豆蔻醇。
该变色三聚氰胺甲醛模塑料的制备步骤如下：
A.捏合：在反应斧中投入30％的甲醛水溶液75Kg，加入NaOH碱液调节至合适的pH8后，加入70Kg三聚氰胺，升温至90℃后保温，用20℃水测白后加入苯酐5.6Kg，降温至70℃，抽取入捏合机，再向捏合机中加入变色材料1.5Kg、纸浆14Kg、硬脂酸钙0.44Kg，捏合60min后，烘干，得到均匀的基料。
B.球磨：在球磨机投入钛白粉7Kg、颜色粉12.5Kg、硬脂酸钙0.4Kg以及步骤A制得的基料，球磨12h后，40目粉筛机过筛装袋即得变色三聚氰胺甲醛塑料130Kg。
实施例2
一种变色三聚氰胺甲醛模塑料，包括以下质量分数的成分：三聚氰胺60%、甲醛25%、纸浆15%、变色材料2%、钛白粉3%、颜色粉2%、硬脂酸镁0.5%、三乙醇胺3%，变色材料为隐色染料壳—芯结构，其外壳为固化交联的密胺环氧树脂聚合物，内芯为十六酸十二醇酯。
该变色三聚氰胺甲醛模塑料的制备步骤如下：
A.捏合：在反应斧中投入40％的甲醛水溶液90Kg，加入NaOH碱液调节至合适的pH8.5后，加入90Kg三聚氰胺，升温至90℃后保温，用20℃水测白后加入三乙醇胺4Kg，降温至70℃，抽取入捏合机，再向捏合机中加入变色材料3Kg、纸浆21Kg、硬脂酸镁0.5Kg，捏合70min后，烘干，得到均匀的基料。
B.球磨：在球磨机投入钛白粉5Kg、颜色粉3Kg、硬脂酸镁0.3Kg以及步骤A制得的基料，球磨13h后，50目粉筛机过筛装袋即得变色三聚氰胺甲醛塑料150Kg。
实施例3
一种变色三聚氰胺甲醛模塑料，包括以下质量分数的成分：三聚氰胺55%、甲醛30%、纸浆15%、变色材料3%、钛白粉2%、颜色粉3%、硬脂酸锌0.2%、苯甲酸4%，变色材料为隐色染料壳—芯结构，其外壳为固化交联的密胺环氧树脂聚合物，内芯为2,2-二(4羟基苯基)丁烷。
该变色三聚氰胺甲醛模塑料的制备步骤如下：
A.捏合：在反应斧中投入50％的甲醛水溶液100Kg，加入NaOH碱液调节至合适的pH9后，加入95Kg三聚氰胺，升温至90℃后保温，用20℃水测白后加入苯甲酸7Kg，降温至70℃，抽取入捏合机，再向捏合机中加入变色材料5Kg、纸浆25Kg、硬脂酸锌0.2Kg，捏合80min后，烘干，得到均匀的基料。
B.球磨：在球磨机投入钛白粉4Kg、颜色粉5Kg、硬脂酸锌0.2Kg以及步骤A制得的基料，球磨14h后，60目粉筛机过筛装袋即得变色三聚氰胺甲醛塑料180Kg。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (10)
1.一种变色三聚氰胺甲醛模塑料，包括以下质量分数的成分：三聚氰胺50%~60%、甲醛20%~30%、纸浆10%~20%、变色材料1%~5%、钛白粉2%~5%、颜色粉1%~10%、脱模剂0.2%~0.6%、固化剂1%~5%；其特征在于：变色材料为隐色染料壳—芯结构，其外壳为固化交联的密胺环氧树脂聚合物，内芯为隐色染料。
2.根据权利要求1所述的一种变色三聚氰胺甲醛模塑料，其特征在于：隐色染料为肉豆蔻醇、十六酸十二醇脂、2,2-二（4-羟基苯基）丁烷的其中的一种或几种。
3.根据权利要求1所述的一种变色三聚氰胺甲醛模塑料，其特征在于：脱模剂为硬脂酸钙、硬脂酸镁、硬脂酸锌其中的一种或几种。
4.根据权利要求1所述的一种变色三聚氰胺甲醛模塑料，其特征在于：固化剂为苯酐、三乙醇胺、苯甲酸中的一种或几种。
5.根据权利要求1所述的一种变色三聚氰胺甲醛模塑料，其特征在于：所述颜色粉为红、黄、蓝中的一种或几种。
6.根据权利要求1所述的一种变色三聚氰胺甲醛模塑料的制备方法，其特征在于包括以下步骤：
A.捏合：在反应斧中投入甲醛，加入碱液调节至合适的pH后，加入三聚氰胺，升温至90℃后保温，用20℃水测白后加入固化剂，降温至70℃，抽取入捏合机，再向捏合机中加入变色材料、纸浆、脱模剂，捏合后，烘干，得到均匀的基料；
B.球磨：在球磨机投入钛白粉、颜色粉、固化剂以及步骤A制得的基料，球磨，粉筛机过筛装袋即得变色三聚氰胺甲醛塑料。
7.根据权利要求6所述的一种变色三聚氰胺甲醛模塑料的制备方法，其特征在于：所述甲醛为质量浓度30％~50％的甲醛水溶液。
8.根据权利要求6所述的一种变色三聚氰胺甲醛模塑料的制备方法，其特征在于：步骤A 中的pH值为8~9。
9.根据权利要求6所述的一种变色三聚氰胺甲醛模塑料的制备方法，其特征在于：粉筛机的目数为40~80目。
10.根据权利要求6所述的一种变色三聚氰胺甲醛模塑料的制备方法，其特征在于：捏合时间为60~80min，球磨时间为12~14h。