CN107641986A - A kind of colouring method of thermal fabric - Google Patents
A kind of colouring method of thermal fabric Download PDFInfo
- Publication number
- CN107641986A CN107641986A CN201711103626.5A CN201711103626A CN107641986A CN 107641986 A CN107641986 A CN 107641986A CN 201711103626 A CN201711103626 A CN 201711103626A CN 107641986 A CN107641986 A CN 107641986A
- Authority
- CN
- China
- Prior art keywords
- parts
- warming
- raw material
- coloring agent
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of colouring method of thermal fabric, comprise the following steps：Step 1：Coloring agent pre-processes；Step 2：Warming ingrain；Step 3：Drying；Step 4：Rinsing；Step 5：Dry.The coloring agent is made up of the raw material of following parts by weight：8 10 parts of oxydiphthalic, 25 parts of polypropylene glycol, 18 20 parts of mica powder, 25 parts of zinc stearate, 47 parts of propyl acetate, 9 12 parts of oxygen iron oxide red, 7 10 parts of ethyl triethoxysilane, 6 12 parts of sodium hydroxide, 47 parts of sodium carbonate, 35 parts of ethanol, 40 45 parts of water, 58 parts of polyvinylpyrrolidone.The thermal fabric, it is the mixed yarn that line density forms in 8tex cotton thread with natural fiber by warp thread；Weft yarn is that the fiber-synthesizing filament of Woolen yarn and line density in 18tex is formed；The total tightness degree of fabric is 75%~85%；Described cotton thread content is 35%.Present invention dyeing is soft, improves the richness and color fastness of fabric.
Description
Technical field
The present invention relates to a kind of field of printing and dyeing, particularly a kind of colouring method of thermal fabric.
Background technology
As the improvement of people's living standards, requirement more and more higher of the people to textile.In the market emerge largely by
The fabric that fiber blend of different nature forms, make fabric while have the characteristic of different fibers concurrently.Polyester cotton blending is common are to knit
Thing, it is made into by terylene and cotton by the way of blending, on the one hand with the characteristic that polyester fiber strength is high, wrinkle resistance is good, meanwhile,
Again with cotton good hygroscopicity, it is comfortable and easy to wear the advantages of.But when handling the dyeing of such fabric, because the limitation of technique makes
It is not ideal enough to obtain the printing and dyeing effect of fabric, influences the richness and color fastness of article.
The content of the invention
It is an object of the present invention to provide a kind of colouring method of thermal fabric.Present invention dyeing is soft, improves face
The richness and color fastness of material.
Technical scheme：A kind of colouring method of thermal fabric, comprises the following steps：
Step 1：Coloring agent and water are added in staining jar, uniform stirring, 55- is warming up to by 3-4 DEG C of heating rate
60 DEG C, 1.5h is kept, adds carbonic acid by the pH regulations of dye liquor to 5；
Step 2：Warming raw material soaking is soaked into 1.5-3.5 hours in staining jar, then with 2-3 DEG C/min speed
Heating, is warming up to 93-96 DEG C and keeps 2.5h；The bath raio of warming raw material is 1:18；
Step 3：Drying, the warming raw material after immersion is dried in the environment of 85-90 DEG C；
Step 4：Rinsing, take out the warming raw material after drying and immerse rinsing 35-55 minutes in clear water, and add purificant；
Step 5：Dry, take out the warming raw material naturally dry after rinsing；
The coloring agent is made up of the raw material of following parts by weight：Oxydiphthalic 8-10 parts, polypropylene glycol 2-5 parts,
Mica powder 18-20 parts, zinc stearate 2-5 parts, propyl acetate 4-7 parts, oxygen iron oxide red 9-12 parts, ethyl triethoxysilane 7-10
Part, sodium hydroxide 6-12 parts, sodium carbonate 4-7 parts, ethanol 3-5 parts, water 40-45 parts, polyvinylpyrrolidone 5-8 parts；
The thermal fabric, by the warp thread mixed yarn that to be line density form in 8tex cotton thread and natural fiber with；Weft yarn
Formed for the fiber-synthesizing filament of Woolen yarn and line density in 18tex；The total tightness degree of fabric is 75%~85%；Described cotton thread content
For 35%.
In the colouring method of foregoing thermal fabric, the step 1 is：Coloring agent and water are added in staining jar, uniformly
Stirring, 57 DEG C are warming up to by 3.5 DEG C of heating rate, keeps 1.5h, add carbonic acid by the pH regulations of dye liquor to 5.
In the colouring method of foregoing thermal fabric, the step 2 is：Warming raw material soaking is soaked in staining jar
2.5 hours, then heated up with 2.5 DEG C/min speed, be warming up to 95 DEG C and keep 2.5h；The bath raio of warming raw material is 1:18.
In the colouring method of foregoing thermal fabric, the coloring agent is made up of the raw material of following parts by weight：Diphenyl ether four
8 parts of acid dianhydride, 5 parts of polypropylene glycol, 18 parts of mica powder, 5 parts of zinc stearate, 4 parts of propyl acetate, 12 parts of oxygen iron oxide red, the second of ethyl three
7 parts of TMOS, 12 parts of sodium hydroxide, 4 parts of sodium carbonate, 5 parts of ethanol, 40 parts of water, 8 parts of polyvinylpyrrolidone.
In the colouring method of foregoing thermal fabric, the coloring agent is made up of the raw material of following parts by weight：Diphenyl ether four
10 parts of acid dianhydride, 2 parts of polypropylene glycol, 20 parts of mica powder, 2 parts of zinc stearate, 7 parts of propyl acetate, 9 parts of oxygen iron oxide red, the second of ethyl three
10 parts of TMOS, 6 parts of sodium hydroxide, 7 parts of sodium carbonate, 3 parts of ethanol, 45 parts of water, 5 parts of polyvinylpyrrolidone.
Compared with prior art, the present invention contacts dyeing, then dried, floated by dyestuff and processing with fabric tenderness
Wash and dry, so that dyeing is soft, improve the richness and color fastness of fabric.Present invention process flow is accurate, cost compared with
Low, the environmental protection of fabric after dyeing, harm to the human body is small, and even dyeing, does not fade, and is adapted to the textile printing and dyeing of a variety of occasions.This
Invention is reasonably matched by plurality of raw materials, of the invention so as to realize colouring simply with textile dyeing agent not easy to fade
The color fastness of fabric can be improved, color stability after dyeing, artificial adult body will not also be influenceed.The present invention is by limiting thermal surface
The making requirement of material, so that snug fit, and it is warming, there is very outstanding thermal property, be adapted to wear in winter,
Practicality is ideal.Present invention defines every layer of different material and technique, so as to relatively reasonable cooperation, in maximum
Change in the case of improving warmth retention property, while also improve comfortableness.Not only with breathing freely, nice and cool, humidity absorption and release is fast, feel by the present invention
The superperformances such as softness is elegant, cloth cover drapability is excellent, and there is the healthcare functions such as certain antistatic, radioresistance, simultaneously
Fabric shape-retaining ability, wrinkle resistance are splendid, are widely portable to high-grade fabric and household textiles.
Embodiment
With reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1.A kind of colouring method of thermal fabric, comprises the following steps：
Step 1：Coloring agent and water are added in staining jar, uniform stirring, 55 DEG C are warming up to by 3 DEG C of heating rate,
1.5h is kept, adds carbonic acid by the pH regulations of dye liquor to 5；
Step 2：Warming raw material soaking is soaked 1.5 hours in staining jar, then heated up with 2 DEG C/min speed, is risen
Temperature is to 93 DEG C and keeps 2.5h；The bath raio of warming raw material is 1:18；
Step 3：Drying, the warming raw material after immersion is dried in the environment of 85 DEG C；
Step 4：Rinsing, take out in the immersion clear water of the warming raw material after drying and rinse 35 minutes, and add purificant；
Step 5：Dry, take out the warming raw material naturally dry after rinsing；The coloring agent by following parts by weight raw material
It is made：8 parts of oxydiphthalic, 5 parts of polypropylene glycol, 18 parts of mica powder, 5 parts of zinc stearate, 4 parts of propyl acetate, oxygen iron oxide red
12 parts, 7 parts of ethyl triethoxysilane, 12 parts of sodium hydroxide, 4 parts of sodium carbonate, 5 parts of ethanol, 40 parts of water, polyvinylpyrrolidone
8 parts；
The thermal fabric, it is the mixed yarn that line density forms in 8tex cotton thread with natural fiber by warp thread；Weft yarn is
The fiber-synthesizing filament of Woolen yarn and line density in 18tex is formed；The total tightness degree of fabric is 75%~85%；Described cotton thread content is
35%.
Embodiment 2.A kind of colouring method of thermal fabric, comprises the following steps：
Step 1：Coloring agent and water are added in staining jar, uniform stirring, 60 DEG C are warming up to by 4 DEG C of heating rate,
1.5h is kept, adds carbonic acid by the pH regulations of dye liquor to 5；
Step 2：Warming raw material soaking is soaked 3.5 hours in staining jar, then heated up with 3 DEG C/min speed, is risen
Temperature is to 96 DEG C and keeps 2.5h；The bath raio of warming raw material is 1:18；
Step 3：Drying, the warming raw material after immersion is dried in the environment of 90 DEG C；
Step 4：Rinsing, take out in the immersion clear water of the warming raw material after drying and rinse 55 minutes, and add purificant；
Step 5：Dry, take out the warming raw material naturally dry after rinsing；The coloring agent by following parts by weight raw material
It is made：10 parts of oxydiphthalic, 2 parts of polypropylene glycol, 20 parts of mica powder, 2 parts of zinc stearate, 7 parts of propyl acetate, oxygen iron oxide red
9 parts, 10 parts of ethyl triethoxysilane, 6 parts of sodium hydroxide, 7 parts of sodium carbonate, 3 parts of ethanol, 45 parts of water, polyvinylpyrrolidone 5
Part；
The thermal fabric, it is the mixed yarn that line density forms in 8tex cotton thread with natural fiber by warp thread；Weft yarn is
The fiber-synthesizing filament of Woolen yarn and line density in 18tex is formed；The total tightness degree of fabric is 75%~85%；Described cotton thread content is
35%.
Embodiment 3.A kind of colouring method of thermal fabric, comprises the following steps：
Step 1：Coloring agent and water are added in staining jar, uniform stirring, 57 are warming up to by 3.5 DEG C of heating rate
DEG C, 1.5h is kept, adds carbonic acid by the pH regulations of dye liquor to 5；
Step 2：Warming raw material soaking is soaked 2.5 hours in staining jar, then heated up with 2.5 DEG C/min speed,
It is warming up to 95 DEG C and keeps 2.5h；The bath raio of warming raw material is 1:18；
Step 3：Drying, the warming raw material after immersion is dried in the environment of 87 DEG C；
Step 4：Rinsing, take out in the immersion clear water of the warming raw material after drying and rinse 45 minutes, and add purificant；
Step 5：Dry, take out the warming raw material naturally dry after rinsing；
The coloring agent is made up of the raw material of following parts by weight：9 parts of oxydiphthalic, 4 parts of polypropylene glycol, mica powder
19 parts, 3 parts of zinc stearate, 6 parts of propyl acetate, 10 parts of oxygen iron oxide red, 9 parts of ethyl triethoxysilane, 9 parts of sodium hydroxide, carbonic acid
6 parts of sodium, 4 parts of ethanol, 43 parts of water, 6 parts of polyvinylpyrrolidone；
The thermal fabric, it is the mixed yarn that line density forms in 8tex cotton thread with natural fiber by warp thread；Weft yarn is
The fiber-synthesizing filament of Woolen yarn and line density in 18tex is formed；The total tightness degree of fabric is 75%~85%；Described cotton thread content is
35%.
The present invention, with handling, dyeing is contacted with fabric tenderness by dyestuff, then is dried, rinsed and dried, so that
It must dye soft, improve the richness and color fastness of fabric.Present invention process flow is accurate, and cost is relatively low, the fabric after dyeing
Environmental protection, harm to the human body is small, and even dyeing, does not fade, and is adapted to the textile printing and dyeing of a variety of occasions.The present invention passes through plurality of raw materials
Reasonably matched, so as to realize that colouring simply can improve the color jail of fabric with textile dyeing agent not easy to fade, the present invention
Degree, color stability after dyeing, will not also influence on artificial adult body.Making requirement of the invention by limiting thermal fabric, from
And cause snug fit, and it is warming, there is very outstanding thermal property, be adapted to wear in winter, practicality is ideal.
Present invention defines every layer of different material and technique, and so as to relatively reasonable cooperation, warmth retention property is improved maximizing
In the case of, while also improve comfortableness.Not only with breathing freely, nice and cool, humidity absorption and release is fast, soft elegant, cloth cover hangs by the present invention
Hang down the superperformances such as property is excellent, and with healthcare functions such as certain antistatic, radioresistances, at the same it is fabric shape-retaining ability, crease-resistant
Property is splendid, is widely portable to high-grade fabric and household textiles.
Claims (5)
1. a kind of colouring method of thermal fabric, it is characterised in that comprise the following steps：
Step 1：Coloring agent and water are added in staining jar, uniform stirring, 55-60 DEG C is warming up to by 3-4 DEG C of heating rate,
1.5h is kept, adds carbonic acid by the pH regulations of dye liquor to 5；
Step 2：Warming raw material soaking is soaked into 1.5-3.5 hours in staining jar, then heated up with 2-3 DEG C/min speed,
It is warming up to 93-96 DEG C and keeps 2.5h；The bath raio of warming raw material is 1:18；
Step 3：Drying, the warming raw material after immersion is dried in the environment of 85-90 DEG C；
Step 4：Rinsing, take out the warming raw material after drying and immerse rinsing 35-55 minutes in clear water, and add purificant；
Step 5：Dry, take out the warming raw material naturally dry after rinsing；
The coloring agent is made up of the raw material of following parts by weight：Oxydiphthalic 8-10 parts, polypropylene glycol 2-5 parts, mica
Powder 18-20 parts, zinc stearate 2-5 parts, propyl acetate 4-7 parts, oxygen iron oxide red 9-12 parts, ethyl triethoxysilane 7-10 parts, hydrogen
Sodium oxide molybdena 6-12 parts, sodium carbonate 4-7 parts, ethanol 3-5 parts, water 40-45 parts, polyvinylpyrrolidone 5-8 parts；
The thermal fabric, it is the mixed yarn that line density forms in 8tex cotton thread with natural fiber by warp thread；Weft yarn is wool
The fiber-synthesizing filament of line and line density in 18tex is formed；The total tightness degree of fabric is 75%~85%；Described cotton thread content is
35%.
2. the colouring method of thermal fabric according to claim 1, it is characterised in that：The step 1 is：In staining jar
Coloring agent and water are added, uniform stirring, 57 DEG C is warming up to by 3.5 DEG C of heating rate, keeps 1.5h, adds carbonic acid by dye liquor
PH regulations to 5.
3. the colouring method of thermal fabric according to claim 1, it is characterised in that：The step 2 is：By warming raw material
It is immersed in staining jar and soaks 2.5 hours, is then heated up with 2.5 DEG C/min speed, be warming up to 95 DEG C and keep 2.5h；It is warming
The bath raio of raw material is 1:18.
4. the colouring method of thermal fabric according to claim 1, it is characterised in that the coloring agent is by following parts by weight
Raw material be made：8 parts of oxydiphthalic, 5 parts of polypropylene glycol, 18 parts of mica powder, 5 parts of zinc stearate, 4 parts of propyl acetate,
12 parts of oxygen iron oxide red, 7 parts of ethyl triethoxysilane, 12 parts of sodium hydroxide, 4 parts of sodium carbonate, 5 parts of ethanol, 40 parts of water, polyethylene pyrrole
8 parts of pyrrolidone.
5. the colouring method of thermal fabric according to claim 1, it is characterised in that the coloring agent is by following parts by weight
Raw material be made：10 parts of oxydiphthalic, 2 parts of polypropylene glycol, 20 parts of mica powder, 2 parts of zinc stearate, 7 parts of propyl acetate,
9 parts of oxygen iron oxide red, 10 parts of ethyl triethoxysilane, 6 parts of sodium hydroxide, 7 parts of sodium carbonate, 3 parts of ethanol, 45 parts of water, polyethylene pyrrole
5 parts of pyrrolidone.