CN107631928A - 一种手提硬度计校验试块的制作方法 - Google Patents

一种手提硬度计校验试块的制作方法 Download PDF

Info

Publication number
CN107631928A
CN107631928A CN201710811284.6A CN201710811284A CN107631928A CN 107631928 A CN107631928 A CN 107631928A CN 201710811284 A CN201710811284 A CN 201710811284A CN 107631928 A CN107631928 A CN 107631928A
Authority
CN
China
Prior art keywords
hardometer
hardness
test block
verification test
sample
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710811284.6A
Other languages
English (en)
Inventor
邓中涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Iron and Steel Co Ltd
Original Assignee
Nanjing Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Iron and Steel Co Ltd filed Critical Nanjing Iron and Steel Co Ltd
Priority to CN201710811284.6A priority Critical patent/CN107631928A/zh
Publication of CN107631928A publication Critical patent/CN107631928A/zh
Pending legal-status Critical Current

Abstract

本发明一种手提硬度计校验试块的制作方法，包括以下步骤：㈠选取一定厚度的模具钢钢板，在模具钢热处理后，在模具钢钢板的头部取样，取样位置为钢板宽度方向1/2处或1/4处，得试样；㈡待试样冷却后，将试样进行铣样和制样，制成所需要的试样尺寸，并采用砂纸和抛光纸将试样表面光滑处理，得硬度计校验试块；㈢将制作好的硬度计校验试块采用台式硬度计测量同一截面硬度，分为布什硬度或洛氏硬度，记下四个角及中心的硬度；㈣现场手提硬度计按照标准试块校验后，再测定硬度计校验试块的四个角和中心的硬度。本发明能够根据硬度计测试材料特点，确保待使用手提硬度计使用前的准确，同时制作的硬度计校验试块能够节约费用。

Description

一种手提硬度计校验试块的制作方法
技术领域
本发明涉及冶金领域的验试块的制作方法，具体的说是一种手提硬度计校验试块的制作方法。
背景技术
手提硬度计在使用前，都会要求采用标准试块进行校验以确保待使用硬度计的正常，但是由于经常校验，造成购买的标准试块校验表面测试点太多后而造成破坏，无法进行正常校验。如何利用现场的材料制作硬度计校验试块，以达到减少购买标准试块的费用，充分利用现场的边角材料的目的，是本领域技术人员有待解决的技术问题。
发明内容
本发明所要解决的技术问题是，针对以上现有技术存在的缺点，提出一种手提硬度计校验试块的制作方法，可以根据现场待测的硬度，制作对应的硬度计校验试块，能够根据硬度计测试材料特点，确保待使用手提硬度计使用前的准确，同时制作的硬度计校验试块能够节约费用。
本发明解决以上技术问题的技术方案是：
一种手提硬度计校验试块的制作方法，包括以下步骤：
㈠选取一定厚度的模具钢钢板，在模具钢热处理后，在模具钢钢板的头部取样，取样位置为钢板宽度方向1/2处或1/4处，得试样；
㈡待试样冷却后，将试样进行铣样和制样，制成所需要的试样尺寸，并采用砂纸和抛光纸将试样表面光滑处理，并将制作的试样棱角圆弧平滑过渡，得硬度计校验试块；
㈢将制作好的硬度计校验试块采用台式硬度计测量同一截面硬度，分为布什硬度（HBW）或洛氏硬度（HRC），记下四个角及中心的硬度，四个角和中心的硬度之间的差值布什硬度小于等于5 HBW，或洛氏硬度小于等于1HRC；
㈣现场手提硬度计按照标准试块校验后，再测定硬度计校验试块的四个角和中心的硬度，四个角和中心之间的差值小于等于布什硬度5HBW或洛氏硬度1HRC，并以现场测试的5个值加权求平均值作为硬度计校验试块的校验硬度值，校验值分为布什硬度（HBW）或洛氏硬度（HRC）；
㈤在制作好的硬度计校验试块上涂上防锈油，并采用布包裹即可。
本发明进一步限定的技术方案是：
前述的手提硬度计校验试块的制作方法，其中步骤㈠中，选取厚度为90mm的模具钢钢板。
前述的手提硬度计校验试块的制作方法，其中步骤㈠中，取样尺寸为：长*宽=110*110mm。
前述的手提硬度计校验试块的制作方法，其中步骤㈡中，试样尺寸为：厚*长*宽=80*100*100 mm。
前述的手提硬度计校验试块的制作方法，其中步骤㈢中，截面硬度为硬度计校验试块的上表面或下表面。
本发明的有益效果是：本发明能够根据硬度计测试材料特点，确保待使用手提硬度计使用前的准确，同时制作的硬度计校验试块能够节约费用。本发明可以根据现场待测的硬度，制作对应的硬度计校验试块，这样更加贴近生产现场，避免硬度计测试出现较大的偏差，影响材料性能的正确判定。
具体实施方式
实施例1
一种手提硬度计校验试块的制作方法，包括以下步骤：
㈠选取厚度为90mm的模具钢钢板718H，在模具钢热处理后，在模具钢钢板的头部取样，取样位置为钢板宽度方向1/2处或1/4处，取样尺寸为：长*宽=110*110mm，得试样；
㈡待试样冷却后，将试样进行铣样和制样，制成的试样尺寸为：厚*长*宽=80*100*100mm，并采用砂纸和抛光纸将试样表面光滑处理，并将制作的试样棱角圆弧平滑过渡，得硬度计校验试块；
㈢将制作好的硬度计校验试块采用台式硬度计测量同一截面硬度，分为布什硬度（HBW）或洛氏硬度（HRC），记下四个角及中心的硬度，四个角和中心的硬度之间的差值布什硬度小于等于5 HBW，或洛氏硬度小于等于1HRC；
㈣现场手提硬度计按照标准试块校验后，再测定硬度计校验试块的四个角和中心的硬度，四个角和中心之间的差值小于等于布什硬度5HBW或洛氏硬度1HRC，并以现场测试的5个值加权求平均值作为硬度计校验试块的校验硬度值，校验值分为布什硬度（HBW）或洛氏硬度（HRC）；
㈤在制作好的硬度计校验试块上涂上防锈油，并采用布包裹即可。
根据待测钢板的硬度是布什硬度（HBW）或洛氏硬度（HRC），采用对应的校验试块进行校验，校验完成后即可进行正常的现场操作。
除上述实施例外，本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案，均落在本发明要求的保护范围。

Claims (5)

1.一种手提硬度计校验试块的制作方法，其特征在于：包括以下步骤：
㈠选取一定厚度的模具钢钢板，在模具钢热处理后，在模具钢钢板的头部取样，取样位置为钢板宽度方向1/2处或1/4处，得试样；
㈡待试样冷却后，将试样进行铣样和制样，制成所需要的试样尺寸，并采用砂纸和抛光纸将试样表面光滑处理，并将制作的试样棱角圆弧平滑过渡，得硬度计校验试块；
㈢将制作好的硬度计校验试块采用台式硬度计测量同一截面硬度，分为布什硬度或洛氏硬度，记下四个角及中心的硬度，四个角和中心的硬度之间的差值布什硬度小于等于5HBW，或洛氏硬度小于等于1HRC；
㈣现场手提硬度计按照标准试块校验后，再测定硬度计校验试块的四个角和中心的硬度，四个角和中心之间的差值小于等于布什硬度5HBW或洛氏硬度1HRC，并以现场测试的5个值加权求平均值作为硬度计校验试块的校验硬度值，校验值分为布什硬度或洛氏硬度；
㈤在制作好的硬度计校验试块上涂上防锈油，并采用布包裹即可。
2.如权利要求1所述的手提硬度计校验试块的制作方法，其特征在于：所述步骤㈠中，选取厚度为90mm的模具钢钢板。
3.如权利要求1所述的手提硬度计校验试块的制作方法，其特征在于：所述步骤㈠中，取样尺寸为：长*宽=110*110mm。
4.如权利要求1所述的手提硬度计校验试块的制作方法，其特征在于：所述步骤㈡中，试样尺寸为：厚*长*宽=80*100*100 mm。
5.如权利要求1所述的手提硬度计校验试块的制作方法，其特征在于：所述步骤㈢中，截面硬度为硬度计校验试块的上表面或下表面。
CN201710811284.6A 2017-09-11 2017-09-11 一种手提硬度计校验试块的制作方法 Pending CN107631928A (zh)