CN107629600A - 一种耐酸碱性涂料制备方法 - Google Patents
一种耐酸碱性涂料制备方法 Download PDFInfo
- Publication number
- CN107629600A CN107629600A CN201710920060.9A CN201710920060A CN107629600A CN 107629600 A CN107629600 A CN 107629600A CN 201710920060 A CN201710920060 A CN 201710920060A CN 107629600 A CN107629600 A CN 107629600A
- Authority
- CN
- China
- Prior art keywords
- parts
- acids
- resistance
- coating
- bases
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供的一种耐酸碱性涂料制备方法，按重量份计包括以下组分,丙烯酸树脂50‑70份,石蜡5‑15份,滑石粉3‑5份,贝壳粉2‑4份,润湿剂1‑3份,钛白粉5‑15份,增稠剂5‑15份,硅藻土10‑30份,成份简单，配置方便，成本较低，无危害，不容易产生开裂与脱落的现象，其耐候性与耐酸碱性好，有效的延长其使用寿命，更能满足厂家的需求。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及一种耐酸碱性涂料制备方法。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。然而现有的涂料在恶劣的环境下容易产生开裂与脱落的现象，其耐候性与耐酸碱性较差，满足不了使用者的需要。
发明内容
本发明的目的是提供一种耐酸碱性涂料制备方法，解决现有的涂料在恶劣的环境下容易产生开裂与脱落的现象，其耐候性与耐酸碱性较差，满足不了使用者的需要的问题。
本发明的目的可以通过以下技术方案实现；
一种耐酸碱性涂料制备方法，其制备方法如下：
（1）按重量份计称取以下组分, 丙烯酸树脂50-70份,石蜡5-15份,滑石粉3-5份,贝壳粉2-4份,润湿剂1-3份,钛白粉5-15份,增稠剂5-15份,硅藻土10-30份；
（2）将丙烯酸树脂放入反应釜中，在30℃-40℃下，均匀搅拌5-15min；
（3）当温度提升至45℃-55℃后，分别加入滑石粉、石蜡与润湿剂，继续搅拌4-12 min；
（4）当温度提升至60℃-70℃后，分别加入钛白粉、贝壳粉与增稠剂，继续搅拌12-15min；
（5）当温度提升至75℃-90℃后，加入硅藻土，继续搅拌30-50min，即可。
上述的一种耐酸碱性涂料制备方法，其中，所述的丙烯酸树脂、石蜡与硅藻土的重量分数比为6:1:2。
上述的一种耐酸碱性涂料制备方法，其中，所述的滑石粉、贝壳粉与钛白粉的重量分数比为4:3:10。
上述的一种耐酸碱性涂料制备方法，其中，所述的贝壳粉与玉石粉的重量分数比为1:2。
上述的一种耐酸碱性涂料制备方法，其中，所述的润湿剂与增稠剂的重量分数比为1:5。
本方案的有益效果：
本发明提供的一种耐酸碱性涂料制备方法，成份简单，配置方便，成本较低，无危害，不容易产生开裂与脱落的现象，其耐候性与耐酸碱性好，有效的延长其使用寿命，更能满足厂家的需求。
具体实施方式
实施例1：一种耐酸碱性涂料制备方法，其制备方法如下：
（1）按重量份计称取以下组分, 丙烯酸树脂50份,石蜡5份,滑石粉3份,贝壳粉2份,润湿剂1份,钛白粉5份,增稠剂5份,硅藻土10份；
（2）将丙烯酸树脂放入反应釜中，在30℃下，均匀搅拌5min；
（3）当温度提升至45℃后，分别加入滑石粉、石蜡与润湿剂，继续搅拌4min；
（4）当温度提升至60℃后，分别加入钛白粉、贝壳粉与增稠剂，继续搅拌12min；
（5）当温度提升至75℃后，加入硅藻土，继续搅拌30min，即可。
实施例2：一种耐酸碱性涂料制备方法，其制备方法如下：
（1）按重量份计称取以下组分, 丙烯酸树脂60份,石蜡10份,滑石粉4份,贝壳粉3份,润湿剂2份,钛白粉10份,增稠剂10份,硅藻土20份；
（2）将丙烯酸树脂放入反应釜中，在35℃下，均匀搅拌10min；
（3）当温度提升至50℃后，分别加入滑石粉、石蜡与润湿剂，继续搅拌8 min；
（4）当温度提升至65℃后，分别加入钛白粉、贝壳粉与增稠剂，继续搅拌13min；
（5）当温度提升至80℃后，加入硅藻土，继续搅拌40min，即可。
实施例3：一种耐酸碱性涂料制备方法，其制备方法如下：
（1）按重量份计称取以下组分, 丙烯酸树脂70份,石蜡15份,滑石粉5份,贝壳粉4份,润湿剂3份,钛白粉15份,增稠剂15份,硅藻土30份；
（2）将丙烯酸树脂放入反应釜中，在40℃下，均匀搅拌15min；
（3）当温度提升至55℃后，分别加入滑石粉、石蜡与润湿剂，继续搅拌12 min；
（4）当温度提升至70℃后，分别加入钛白粉、贝壳粉与增稠剂，继续搅拌15min；
（5）当温度提升至90℃后，加入硅藻土，继续搅拌50min，即可。
本发明提供的一种耐酸碱性涂料制备方法，成份简单，配置方便，成本较低，无危害，不容易产生开裂与脱落的现象，其耐候性与耐酸碱性好，有效的延长其使用寿命，更能满足厂家的需求。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围内。因此，本发明的保护范围应该以权利要求书的保护范围为准。
Claims (5)
1.一种耐酸碱性涂料制备方法，其特征为，其制备方法如下：
（1）按重量份计称取以下组分, 丙烯酸树脂50-70份,石蜡5-15份,滑石粉3-5份,贝壳粉2-4份,润湿剂1-3份,钛白粉5-15份,增稠剂5-15份,硅藻土10-30份；
（2）将丙烯酸树脂放入反应釜中，在30℃-40℃下，均匀搅拌5-15min；
（3）当温度提升至45℃-55℃后，分别加入滑石粉、石蜡与润湿剂，继续搅拌4-12 min；
（4）当温度提升至60℃-70℃后，分别加入钛白粉、贝壳粉与增稠剂，继续搅拌12-15min；
（5）当温度提升至75℃-90℃后，加入硅藻土，继续搅拌30-50min，即可。
2.如权利要求书所述的一种耐酸碱性涂料制备方法，其特征为，所述的丙烯酸树脂、石蜡与硅藻土的重量分数比为6:1:2。
3.如权利要求书所述的一种耐酸碱性涂料制备方法，其特征为，所述的滑石粉、贝壳粉与钛白粉的重量分数比为4:3:10。
4.如权利要求书所述的一种耐酸碱性涂料制备方法，其特征为，所述的贝壳粉与玉石粉的重量分数比为1:2。
5.如权利要求书所述的一种耐酸碱性涂料制备方法，其特征为，所述的润湿剂与增稠剂的重量分数比为1:5。