CN107556875A - 一种防锈涂料制备方法 - Google Patents
一种防锈涂料制备方法 Download PDFInfo
- Publication number
- CN107556875A CN107556875A CN201710925313.1A CN201710925313A CN107556875A CN 107556875 A CN107556875 A CN 107556875A CN 201710925313 A CN201710925313 A CN 201710925313A CN 107556875 A CN107556875 A CN 107556875A
- Authority
- CN
- China
- Prior art keywords
- parts
- antirusting paint
- paint preparation
- stabilizer
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供的一种防锈涂料制备方法，按重量份计包括以下组分,聚氨酯改性环氧树脂10‑30份,羟基丙烯酸树脂10‑30份,乙二醇3‑5份，滑石粉1‑3份，催化剂1‑3份，钛白粉3‑9份，硅灰粉4‑12份，膨润土4‑18份，稳定剂1‑3份，成份简单，配置方便，成本较低，无危害，耐温性能好，有效的延长其使用寿命，在风雨的侵蚀下不容易尝试生锈的现象，更能满足厂家的需求。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及一种防锈涂料制备方法。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。然而现有的涂料长期受到风雨的侵蚀后，容易尝试生锈的状态，需要定期的进行维护与涂刷，成本较高，满足不了使用者的需要。
发明内容
本发明的目的是提供一种防锈涂料制备方法，解决现有的涂料长期受到风雨的侵蚀后，容易尝试生锈的状态，需要定期的进行维护与涂刷，成本较高，满足不了使用者的需要的问题。
本发明的目的可以通过以下技术方案实现；
一种防锈涂料制备方法，其制备方法如下：
（1）按重量份计称取以下组分,聚氨酯改性环氧树脂10-30份,羟基丙烯酸树脂10-30份,乙二醇3-5份，滑石粉1-3份，催化剂1-3份，钛白粉3-9份，硅灰粉4-12份，膨润土4-18份，稳定剂1-3份，
（2）将聚氨酯改性环氧树脂与羟基丙烯酸树脂放入反应釜中，在25℃-35℃下，均匀搅拌10-20min；
（3）当温度提升至40℃-50℃后，分别加入乙二醇、滑石粉与催化剂，继续搅拌5-15min；
（4）当温度提升至55℃-65℃后，分别加入钛白粉、硅灰粉与稳定剂，继续搅拌4-8min；
（5）当温度提升至70℃-85℃后，加入膨润土，继续搅拌30-45min，即可。
上述的一种防锈涂料制备方法，其中，所述的聚氨酯改性环氧树脂与羟基丙烯酸树脂的重量分数比为1:1。
上述的一种防锈涂料制备方法，其中，所述的乙二醇与膨润土的重量分数比为1:4。
上述的一种防锈涂料制备方法，其中，所述的滑石粉、钛白粉与硅灰粉的重量分数比为1:3:4。
上述的一种防锈涂料制备方法，其中，所述的催化剂与稳定剂的重量分数比为1:1。
本方案的有益效果：
本发明提供的一种防锈涂料配方，成份简单，配置方便，成本较低，无危害，耐温性能好，有效的延长其使用寿命，在风雨的侵蚀下不容易尝试生锈的现象，更能满足厂家的需求。
具体实施方式
实施例1：一种防锈涂料制备方法，其制备方法如下：
（1）按重量份计称取以下组分,聚氨酯改性环氧树脂10份,羟基丙烯酸树脂10份,乙二醇3份，滑石粉1份，催化剂1份，钛白粉3份，硅灰粉4-12份，膨润土4份，稳定剂1份，
（2）将聚氨酯改性环氧树脂与羟基丙烯酸树脂放入反应釜中，在25℃下，均匀搅拌10min；
（3）当温度提升至40℃后，分别加入乙二醇、滑石粉与催化剂，继续搅拌5min；
（4）当温度提升至55℃后，分别加入钛白粉、硅灰粉与稳定剂，继续搅拌4min；
（5）当温度提升至70℃℃后，加入膨润土，继续搅拌30min，即可。
实施例2：一种防锈涂料制备方法，其制备方法如下：
（1）按重量份计称取以下组分,聚氨酯改性环氧树脂20份,羟基丙烯酸树脂20份,乙二醇4份，滑石粉2份，催化剂2份，钛白粉6份，硅灰粉8份，膨润土16份，稳定剂2份，
（2）将聚氨酯改性环氧树脂与羟基丙烯酸树脂放入反应釜中，在30℃下，均匀搅拌15min；
（3）当温度提升至45℃后，分别加入乙二醇、滑石粉与催化剂，继续搅拌10min；
（4）当温度提升至60℃后，分别加入钛白粉、硅灰粉与稳定剂，继续搅拌6min；
（5）当温度提升至75℃后，加入膨润土，继续搅拌40min，即可。
实施例3：一种防锈涂料制备方法，其制备方法如下：
（1）按重量份计称取以下组分,聚氨酯改性环氧树脂30份,羟基丙烯酸树脂30份,乙二醇5份，滑石粉3份，催化剂3份，钛白粉9份，硅灰粉12份，膨润土18份，稳定剂3份，
（2）将聚氨酯改性环氧树脂与羟基丙烯酸树脂放入反应釜中，在35℃下，均匀搅拌20min；
（3）当温度提升至50℃后，分别加入乙二醇、滑石粉与催化剂，继续搅拌15 min；
（4）当温度提升至65℃后，分别加入钛白粉、硅灰粉与稳定剂，继续搅拌8min；
（5）当温度提升至85℃后，加入膨润土，继续搅拌45min，即可。
本发明提供的一种防锈涂料制备方法，成份简单，配置方便，成本较低，无危害，耐温性能好，有效的延长其使用寿命，避免物体表面产生融化的现象，有效的保护了整体的美观性能，更能满足厂家的需求。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围内。因此，本发明的保护范围应该以权利要求书的保护范围为准。
Claims (5)
1.一种防锈涂料制备方法，其特征为，其制备方法如下：
（1）按重量份计称取以下组分,聚氨酯改性环氧树脂10-30份,羟基丙烯酸树脂10-30份,乙二醇3-5份，滑石粉1-3份，催化剂1-3份，钛白粉3-9份，硅灰粉4-12份，膨润土4-18份，稳定剂1-3份，
（2）将聚氨酯改性环氧树脂与羟基丙烯酸树脂放入反应釜中，在25℃-35℃下，均匀搅拌10-20min；
（3）当温度提升至40℃-50℃后，分别加入乙二醇、滑石粉与催化剂，继续搅拌5-15min；
（4）当温度提升至55℃-65℃后，分别加入钛白粉、硅灰粉与稳定剂，继续搅拌4-8min；
（5）当温度提升至70℃-85℃后，加入膨润土，继续搅拌30-45min，即可。
2.如权利要求1所述的一种防锈涂料制备方法，其特征为，所述的聚氨酯改性环氧树脂与羟基丙烯酸树脂的重量分数比为1:1。
3.如权利要求1所述的一种防锈涂料制备方法，其特征为，所述的乙二醇与膨润土的重量分数比为1:4。
4.如权利要求1所述的一种防锈涂料制备方法，其特征为，所述的滑石粉、钛白粉与硅灰粉的重量分数比为1:3:4。
5.如权利要求1所述的一种防锈涂料制备方法，其特征为，所述的催化剂与稳定剂的重量分数比为1:1。