CN107556874A - 一种防锈涂料配方 - Google Patents
一种防锈涂料配方 Download PDFInfo
- Publication number
- CN107556874A CN107556874A CN201710925309.5A CN201710925309A CN107556874A CN 107556874 A CN107556874 A CN 107556874A CN 201710925309 A CN201710925309 A CN 201710925309A CN 107556874 A CN107556874 A CN 107556874A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint formula
- antirusting paint
- weight
- stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供的一种防锈涂料配方，按重量份计包括以下组分,聚氨酯改性环氧树脂10‑30份,羟基丙烯酸树脂10‑30份,乙二醇3‑5份，滑石粉1‑3份，催化剂1‑3份，钛白粉3‑9份，硅灰粉4‑12份，膨润土4‑18份，稳定剂1‑3份，成份简单，配置方便，成本较低，无危害，耐温性能好，有效的延长其使用寿命，在风雨的侵蚀下不容易尝试生锈的现象，更能满足厂家的需求。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及一种防锈涂料配方。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。然而现有的涂料长期受到风雨的侵蚀后，容易尝试生锈的状态，需要定期的进行维护与涂刷，成本较高，满足不了使用者的需要。
发明内容
本发明的目的是提供一种防锈涂料配方，解决现有的涂料长期受到风雨的侵蚀后，容易尝试生锈的状态，需要定期的进行维护与涂刷，成本较高，满足不了使用者的需要的问题。
本发明的目的可以通过以下技术方案实现；
一种防锈涂料配方，按重量份计包括以下组分；
聚氨酯改性环氧树脂 10-30份
羟基丙烯酸树脂 10-30份
乙二醇 3-5份
滑石粉 1-3份
催化剂 1-3份
钛白粉 3-9份
硅灰粉 4-12份
膨润土 14-18份
稳定剂 1-3份。
上述的一种防锈涂料配方，其中，优选的，其组成成份按重量份数计如下：
聚氨酯改性环氧树脂 20份
羟基丙烯酸树脂 20份
乙二醇 4份
滑石粉 2份
催化剂 2份
钛白粉 6份
硅灰粉 8份
膨润土 16份
稳定剂 2份。
上述的一种防锈涂料配方，其中，所述的聚氨酯改性环氧树脂与羟基丙烯酸树脂的重量分数比为1:1。
上述的一种防锈涂料配方，其中，所述的乙二醇与膨润土的重量分数比为1:4。
上述的一种防锈涂料配方，其中，所述的滑石粉、钛白粉与硅灰粉的重量分数比为1:3:4。
上述的一种防锈涂料配方，其中，所述的催化剂与稳定剂的重量分数比为1:1。
本方案的有益效果：
本发明提供的一种防锈涂料配方，成份简单，配置方便，成本较低，无危害，耐温性能好，有效的延长其使用寿命，在风雨的侵蚀下不容易尝试生锈的现象，更能满足厂家的需求。
具体实施方式
实施例1：一种防锈涂料配方，其组成成份按重量份数计如下：
聚氨酯改性环氧树脂 10份
羟基丙烯酸树脂 10份
乙二醇 3份
滑石粉 1份
催化剂 1份
钛白粉 3份
硅灰粉 4份
膨润土 14份
稳定剂 1份。
实施例2：一种防锈涂料配方，其组成成份按重量份数计如下：
聚氨酯改性环氧树脂 20份
羟基丙烯酸树脂 20份
乙二醇 4份
滑石粉 2份
催化剂 2份
钛白粉 6份
硅灰粉 8份
膨润土 16份
稳定剂 2份。
实施例3：一种防锈涂料配方，其组成成份按重量份数计如下：
聚氨酯改性环氧树脂 30份
羟基丙烯酸树脂 30份
乙二醇 5份
滑石粉 3份
催化剂 3份
钛白粉 9份
硅灰粉 12份
膨润土 18份
稳定剂 3份。
本发明提供的一种防锈涂料配方，成份简单，配置方便，成本较低，无危害，耐温性能好，有效的延长其使用寿命，在风雨的侵蚀下不容易尝试生锈的现象，更能满足厂家的需求。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围内。因此，本发明的保护范围应该以权利要求书的保护范围为准。
Claims (6)
1.一种防锈涂料配方，其特征为，按重量份计包括以下组分；
聚氨酯改性环氧树脂 10-30份
羟基丙烯酸树脂 10-30份
乙二醇 3-5份
滑石粉 1-3份
催化剂 1-3份
钛白粉 3-9份
硅灰粉 4-12份
膨润土 14-18份
稳定剂 1-3份。
2.如权利要求1所述的一种防锈涂料配方，其特征为，优选的，其组成成份按重量份数计如下：
聚氨酯改性环氧树脂 20份
羟基丙烯酸树脂 20份
乙二醇 4份
滑石粉 2份
催化剂 2份
钛白粉 6份
硅灰粉 8份
膨润土 16份
稳定剂 2份。
3.如权利要求1所述的一种防锈涂料配方，其特征为，所述的聚氨酯改性环氧树脂与羟基丙烯酸树脂的重量分数比为1:1。
4.如权利要求1所述的一种防锈涂料配方，其特征为，所述的乙二醇与膨润土的重量分数比为1:4。
5.如权利要求1所述的一种防锈涂料配方，其特征为，所述的滑石粉、钛白粉与硅灰粉的重量分数比为1:3:4。
6.如权利要求1所述的一种防锈涂料配方，其特征为，所述的催化剂与稳定剂的重量分数比为1:1。