CN107587137A - 一种用于金属表面的长效型防锈转锈剂 - Google Patents
一种用于金属表面的长效型防锈转锈剂 Download PDFInfo
- Publication number
- CN107587137A CN107587137A CN201710795426.4A CN201710795426A CN107587137A CN 107587137 A CN107587137 A CN 107587137A CN 201710795426 A CN201710795426 A CN 201710795426A CN 107587137 A CN107587137 A CN 107587137A
- Authority
- CN
- China
- Prior art keywords
- agent
- long
- metal surface
- acting type
- type antirust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种用于金属表面的长效型防锈转锈剂，属于防腐材料技术领域，其组分按重量百分比计为，载体油30～50％、渗透稳定剂1～4％、缓释载体6～10％、灭菌剂3～5％、抗氧剂1～2％、触变剂2～6％、植酸10～20％、没食子酸9～15％、聚苯胺6～20％，上述组分配成100％。本发明产品环保无毒、施工工艺灵活简便、表面处理要求等级低，用于港口码头设施、海上平台、电厂钢架、储罐及管道阀门等，能够提供长效持久地防腐蚀保护功能，防腐层附着力强，致密隔绝性好，协同保护作用突出，渗透性且螯合转锈抑锈能力强；可有效消除或抑制微生物腐蚀，从而确保在各种苛刻恶劣的环境下达到对金属结构的永久性防腐蚀保护。
Description
本专利申请案主张申请号为“201710006582.8”、名称为“一种用于金属表面的长效型防锈转锈剂”、申请日为“2017.01.06”的中国发明专利申请的优先权。
技术领域
本发明涉及一种用于金属表面的长效型防锈转锈剂，属于防腐材料技术领域。
背景技术
金属材料受周围环境的作用很容易发生腐蚀，在其界面上发生化学或是电化学等相反应，使金属转为氧化态或是离子态，显著降低金属材料的力学性能。据相关报道，每年我国因金属腐蚀而造成的经济损失达上千亿元，因此研究金属的腐蚀防护方法具有重要意义。目前，最常用的方法就是在金属表面涂覆有机防腐涂层。常用的涂层多为含铬、钼化合物的有机涂层，但铬、钼属于严重污染环境的重金属，同时也严重威胁人体健康；另外涂层材料的涂覆前金属表面需要达到较高的表面处理要求，劳动强度大，经济成本高，也对环境造成粉尘污染及噪音污染，同时对施工人员身体也造成损害。针对涂层防腐的不足，近几年也有相应的解决方案，并且取得了较广泛应用。随着社会和科学的进步，人类越来越注重环境保护，因此，研究开发具备施工经济性好、渗透性好且防锈转锈效率高等特点的绿色环保型防锈转锈剂具有重要意义。
专利CN101037636公布了一种防锈组成物，其防锈有效期短，主要用于工序间防锈；专利CN102816523公布了一种环保型金属防锈剂，其防锈效果可达三年，但渗透性一般，同时难以阻止微生物腐蚀。
发明内容
本发明的技术任务是针对现有防锈转锈剂毒性大，施工经济性差，渗透性不佳及对微生物腐蚀防护效果一般等不足，提供一种用于金属表面的长效型防锈转锈剂，本发明提供的长效型防锈转锈剂可用于钢结构，特别是钢结构连接部位，渗透性好，可有效杀灭铁细菌、硫杆菌、硫酸盐还原菌等微生物，防止微生物腐蚀，采用缓释技术，保证了杀菌抑菌性能的持久性，防腐蚀效果可达20年以上，免去了较频繁的维护，节约资源及人力物力，具有显著的经济效益。
本发明具体采用的技术方案是：
一种用于金属表面的长效型防锈转锈剂，其特征在于：按其组分重量百分比计为，载体油30～50％、渗透稳定剂1～4％、缓释载体6～10％、灭菌剂3～5％、抗氧剂1～2％、触变剂2～6％、植酸10～20％、没食子酸9～15％、聚苯胺6～20％，上述组分配成100％。
其中，所述的载体油为聚α-烯烃油、聚丁烯、合成环烷烃、植物油基多元醇酯、聚醚中的一种。
其中，所述的渗透稳定剂为大豆卵磷脂、吐温-60按照重量比2:1组成的混合物；
其中，所述的缓释载体为海泡石粉、硅藻土按照重量比2:1组成的混合物；
其中，所述的灭菌剂为氟唑菌酰胺、吡唑醚菌酯和三唑类灭菌剂按照重量比1:1:1组成的混合物；
其中，所述的抗氧剂为抗氧剂1010、抗氧剂BHT按照重量比3:1组成的混合物。
本发明的制备方法，包括如下步骤：
先将载体油加入反应釜中，加热至温度95℃～120℃，保温30min～40min，再降温，保持温度50℃～70℃，依次加入渗透稳定剂、缓释载体、灭菌剂，搅拌20min～30min后再加入抗氧剂、触变剂、植酸、没食子酸、聚苯胺，常压下搅拌1h～1.5h后出料，即得本发明产品。
本发明中，所采用的所有原料均为本领域常用原料或者市售商品，普通技术人员很容易获取。
与现有技术相比，本发明的有益效果在于：
1、环保无毒，对环境无污染，无挥发性有机物，不含危险品，施工人员接触本发明产品无任何危害。本发明采用的植酸、没食子酸、聚苯胺等均为对环境无副作用材料，采用的灭菌剂均为环境友好型新品种灭菌剂，另外其他组分也是对人体和环境没有危害的，即使发生泄露对环境不会造成污染或者其导致的结果也是可预见的或者可控的。
2、表面处理要求等级低，适用于港口码头设施、海上平台、电厂钢架、储罐罐底边缘板及管道阀门等。通常在工程现场由于受作业条件等的限制，表面处理很难达到要求的级别，而采用本发明所提供的一种用于金属表面的长效型防锈转锈剂时，表面处理达到St2.0即可。
3、施工工艺灵活简便，施工包容性好。针对金属结构的特点，可采用多种施工方法，手工抹涂、刮涂、刷涂、胶枪挤出施涂、喷涂均可；另外本发明可带水带锈施工，涂覆后形成的防腐蚀保护膜可轻松覆盖到待保护物表面。
4、本发明具有长效持久地防腐蚀保护功能，防腐层附着力强且致密隔绝性好，协同保护作用突出，渗透性好且螯合转锈抑锈能力强。首先，该发明产品采用了植酸、没食子酸、聚苯胺，前两种可与已经形成的金属氧化物或者金属本身通过螯合作用形成牢固的络合物层，而聚苯胺也可在金属表面形成钝化膜，阻止氧分等对金属的进一步腐蚀，三种缓蚀剂的协同作用，增强了协同迁移保护作用的发挥；其次，该发明采用了两种抗氧剂协同作用，可长期有效地防止防腐层酸化及氧化变质，确保防腐层防腐作用的长效性；第三，通过采用不同HLB值的渗透稳定剂优化配合，渗透性强，可将被保护物表面的水、锈等置换出，而缓蚀剂可与其通过螯合反应在被保护金属表面形成络合物层，即单分子层防腐蚀保护膜，可抑制锈层再生，起到对金属表面的防腐蚀保护作用。
5、可有效消除和抑制微生物腐蚀。本发明配方中采用了氟唑菌酰胺、吡唑醚菌酯和三唑类等三种灭菌剂的组合，可有效抑制或杀灭易滋生微生物如硫酸盐还原菌、硫氧化菌、腐生菌、铁细菌和真菌等，从而防止了微生物细胞新陈代谢的中间产物和/或最终产物的分泌物以及外酵素等引起的防腐材料失效而导致的腐蚀破坏；另外本发明中采用了缓释技术，灭菌剂被吸附于缓释载体中，其有效成分的释放稳定而缓慢，保证了杀菌抑菌性能的长效性。这也是本发明的目的之一。
具体实施方式
实施例1
一种用于金属表面的长效型防锈转锈剂，其组成按重量百分比计成分为载体油30％、渗透稳定剂4％、缓释载体10％、抗氧剂2％、灭菌剂3％、触变剂2％、植酸20％、没食子酸9％、聚苯胺20％。
实施例2
一种用于金属表面的长效型防锈转锈剂，其组成重量按百分比计成分为载体油34.5％、渗透稳定剂3.2％、缓释载体9％、抗氧剂1.8％、灭菌剂3.5％、触变剂3％、植酸17.5％、没食子酸10.5％、聚苯胺17％。
实施例3
一种用于金属表面的长效型防锈转锈剂，其组成按重量百分比计成分为载体油40％、缓释载体8％、抗氧剂1.5％、灭菌剂4％、触变剂4％、渗透稳定剂2.5％、植酸15％、没食子酸12％、聚苯胺13％、。
实施例4
一种用于金属表面的长效型防锈转锈剂，其组成按重量百分比计成分为载体油45.5％、渗透稳定剂1.8％、缓释载体7％、抗氧剂1.2％、灭菌剂4.5％、触变剂5％、植酸12.5％、没食子酸13.5％、聚苯胺9％。
实施例5
一种用于金属表面的长效型防锈转锈剂，其组成按重量百分比计成分为载体油50％、缓释载体6％、渗透稳定剂1％、抗氧剂1％、灭菌剂5％、触变剂6％、植酸10％、没食子酸15％、聚苯胺6％。
实施例6
取实施例1-5任一配方，先将载体油加入反应釜中，加热至温度95℃～120℃，保温30min～40min，再降温，保持温度50℃～70℃，依次加入渗透稳定剂、缓释载体、灭菌剂，搅拌20min～30min后再加入抗氧剂、触变剂、植酸、没食子酸、聚苯胺，常压下搅拌1h～1.5h后出料，即得本发明产品。
该发明产品环保无毒；施工工艺灵活简便，表面处理要求等级低，可用于港口码头设施、海上平台、电厂钢架、储罐及管道阀门等；能够提供长效持久地防腐蚀保护功能，防腐层附着力强，致密隔绝性好，协同保护作用突出，优异的渗透性且螯合转锈抑锈能力强；可有效消除或抑制微生物腐蚀，从而确保在各种苛刻恶劣的环境下达到对金属结构的永久性防腐蚀保护之目的。
以下附表1是本发明一种用于金属表面的长效型防锈转锈剂的实施例1-5所的产品的相关技术指标测试结果，结果证明具备良好的防腐蚀性能；附表2是本发明一种用于金属表面的长效型防锈转锈剂的实施例1-5所的产品针对常见腐蚀微生物硫酸盐还原菌、铁细菌、硫氧化菌等杀灭性能试验的相关数据，结果表明可有效杀灭该系列微生物。
附表1产品技术指标测试结果
Claims (7)
1.一种用于金属表面的长效型防锈转锈剂，其特征在于：其组分按重量百分比计为，载体油30～50％、渗透稳定剂1～4％、缓释载体6～10％、灭菌剂3～5％、抗氧剂1～2％、触变剂2～6％、植酸10～20％、没食子酸9～15％、聚苯胺6～20％，上述组分配成100％。
2.根据权利要求1所述的用于金属表面的长效型防锈转锈剂，其特征在于，所述的载体油为聚α-烯烃油、聚丁烯、合成环烷烃、植物油基多元醇酯、聚醚中的一种。
3.根据权利要求1所述的用于金属表面的长效型防锈转锈剂，其特征在于，所述的渗透稳定剂为大豆卵磷脂、吐温-60按照重量比2:1组成的混合物。
4.根据权利要求1所述的用于金属表面的长效型防锈转锈剂，其特征在于，所述的缓释载体为海泡石粉、硅藻土按照重量比2:1组成的混合物。
5.根据权利要求1所述的用于金属表面的长效型防锈转锈剂，其特征在于，所述的灭菌剂为氟唑菌酰胺、吡唑醚菌酯和三唑类灭菌剂按照重量比1:1:1组成的混合物。
6.根据权利要求1所述的用于金属表面的长效型防锈转锈剂，其特征在于，所述的抗氧剂为抗氧剂1010、抗氧剂BHT按照重量比3:1组成的混合物。
7.根据权利要求1至6任一项所述的用于金属表面的长效型防锈转锈剂，其特征在于，所述防锈转锈剂的制法，包括如下步骤：
先将载体油加入反应釜中，加热至温度95℃～120℃，保温30min～40min，再降温，保持温度50℃～70℃，依次加入渗透稳定剂、缓释载体、灭菌剂，搅拌20min～30min后再加入抗氧剂、触变剂、植酸、没食子酸、聚苯胺，常压下搅拌1h～1.5h后出料，即得本发明产品。