CN107573640A - 一种腹肌板用改性酚醛泡沫复合材料 - Google Patents
一种腹肌板用改性酚醛泡沫复合材料 Download PDFInfo
- Publication number
- CN107573640A CN107573640A CN201710826166.2A CN201710826166A CN107573640A CN 107573640 A CN107573640 A CN 107573640A CN 201710826166 A CN201710826166 A CN 201710826166A CN 107573640 A CN107573640 A CN 107573640A
- Authority
- CN
- China
- Prior art keywords
- parts
- foam composite
- modified phenolic
- phenolic foam
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种腹肌板用改性酚醛泡沫复合材料，所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体30‑40份、改性聚氨酯预聚体16‑20份、聚甲基硅氧烷7‑11份、羧甲基纤维素钠9‑13份、碳纳米纤维2‑6份、正戊烷2‑6份、水溶性硅油6‑10份、对甲苯磺酸6‑10份和抗氧化剂1‑5份。本发明的优点在于：本发明腹肌板用改性酚醛泡沫复合材料，能够防止材料的脆性断裂和粉化，且能够消除材料表面的静电，使值得的腹肌板更加人性化。
Description
技术领域
本发明涉及健身器材技术领域，特别涉及一种腹肌板用改性酚醛泡沫复合材料。
背景技术
腹肌板即仰卧板，是健身、瘦腹、具有仰卧起坐、收背运动、仰卧抬腿等训练功能的体育器械。现有腹肌板的材质一般为钢材，因其舒适度交叉，需在其外部包裹塑料。而酚醛泡沫塑料具有密度低、重量轻，导热系数低，使用温度范同大，尺寸稳定性好的特点，而且相比于聚氯乙烯泡沫、聚乙烯泡沫、聚氨酯泡沫，酚醛泡沫具有优异的难燃、自熄、低烟雾、耐火焰贯穿的优点。因此，近年来，酚醛泡沫塑料在船舶、航空器材、体育器材等领域得到了广泛的应用。
但由于分子结构中亚甲基连接的刚性芳环的紧密堆砌，酚羟基和亚甲基容易氧化，使得酚醛泡沫塑料本身耐氧化性不好，力学性能较差，尤其是脆性大、易粉化，这一缺陷极大地限制了其应用，特别是室外体育器材上的应用。在体育器材领域，为使酚醛泡沫塑料具有耐磨、缓冲、防震等性能，并且满足强度需求，须对其进行增强增韧改性，同时还要满足质轻、阻燃以及成本低廉等优点。
发明内容
本发明要解决的技术问题是提供一种腹肌板用改性酚醛泡沫复合材料，以解决上述技术问题。
为解决上述技术问题，本发明的技术方案为：一种腹肌板用改性酚醛泡沫复合材料，其创新点在于：所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体30-40份、改性聚氨酯预聚体16-20份、聚甲基硅氧烷7-11份、羧甲基纤维素钠9-13 份、碳纳米纤维2-6份、正戊烷2-6份、水溶性硅油6-10份、对甲苯磺酸6-10份和抗氧化剂1-5份。
进一步地，所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体34-36份、改性聚氨酯预聚体17-19份、聚甲基硅氧烷8-10份、羧甲基纤维素钠10-12份、碳纳米纤维3-5份、正戊烷3-5份、水溶性硅油7-9份、对甲苯磺酸7-9份和抗氧化剂2-4份。
进一步地，所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体35份、改性聚氨酯预聚体18份、聚甲基硅氧烷9份、羧甲基纤维素钠11 份、碳纳米纤维4份、正戊烷4份、水溶性硅油8份、对甲苯磺酸8份和抗氧化剂3份。
本发明的优点在于：本发明腹肌板用改性酚醛泡沫复合材料，能够防止材料的脆性断裂和粉化，且能够消除材料表面的静电，使值得的腹肌板更加人性化。
具体实施方式
下面的实施例可以使本专业的技术人员更全面地理解本发明，但并不因此将本发明限制在所述的实施例范围之中。
实施例1
本实施例腹肌板用改性酚醛泡沫复合材料，所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体30份、改性聚氨酯预聚体16份、聚甲基硅氧烷7份、羧甲基纤维素钠9份、碳纳米纤维2份、正戊烷2份、水溶性硅油6份、对甲苯磺酸6份和抗氧化剂1份。
实施例2
本实施例腹肌板用改性酚醛泡沫复合材料，所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体40份、改性聚氨酯预聚体20份、聚甲基硅氧烷11份、羧甲基纤维素钠13 份、碳纳米纤维6份、正戊烷6份、水溶性硅油10份、对甲苯磺酸10份和抗氧化剂5份。
实施例3
本实施例腹肌板用改性酚醛泡沫复合材料，所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体34份、改性聚氨酯预聚体17份、聚甲基硅氧烷8份、羧甲基纤维素钠10份、碳纳米纤维3份、正戊烷3份、水溶性硅油7份、对甲苯磺酸7份和抗氧化剂2份。
实施例4
本实施例腹肌板用改性酚醛泡沫复合材料，所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体36份、改性聚氨酯预聚体19份、聚甲基硅氧烷10份、羧甲基纤维素钠12份、碳纳米纤维5份、正戊烷5份、水溶性硅油9份、对甲苯磺酸9份和抗氧化剂4份。
实施例5
本实施例腹肌板用改性酚醛泡沫复合材料，所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体35份、改性聚氨酯预聚体18份、聚甲基硅氧烷9份、羧甲基纤维素钠11 份、碳纳米纤维4份、正戊烷4份、水溶性硅油8份、对甲苯磺酸8份和抗氧化剂3份。
以上显示和描述了本发明的基本原理和主要特征以及本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.一种腹肌板用改性酚醛泡沫复合材料，其特征在于：所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体30-40份、改性聚氨酯预聚体16-20份、聚甲基硅氧烷7-11份、羧甲基纤维素钠9-13 份、碳纳米纤维2-6份、正戊烷2-6份、水溶性硅油6-10份、对甲苯磺酸6-10份和抗氧化剂1-5份。
2.根据权利要求1所述的腹肌板用改性酚醛泡沫复合材料，其特征在于：所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体34-36份、改性聚氨酯预聚体17-19份、聚甲基硅氧烷8-10份、羧甲基纤维素钠10-12份、碳纳米纤维3-5份、正戊烷3-5份、水溶性硅油7-9份、对甲苯磺酸7-9份和抗氧化剂2-4份。
3.根据权利要求1所述的腹肌板用改性酚醛泡沫复合材料，其特征在于：所述改性酚醛泡沫复合材料是由以下重量份的组分组成：酚醛树脂基体35份、改性聚氨酯预聚体18份、聚甲基硅氧烷9份、羧甲基纤维素钠11 份、碳纳米纤维4份、正戊烷4份、水溶性硅油8份、对甲苯磺酸8份和抗氧化剂3份。