CN107572811A - 一种呈红色的钧瓷釉料 - Google Patents
一种呈红色的钧瓷釉料 Download PDFInfo
- Publication number
- CN107572811A CN107572811A CN201711058308.1A CN201711058308A CN107572811A CN 107572811 A CN107572811 A CN 107572811A CN 201711058308 A CN201711058308 A CN 201711058308A CN 107572811 A CN107572811 A CN 107572811A
- Authority
- CN
- China
- Prior art keywords
- parts
- red
- glaze
- pottery
- feldspar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种呈红色的钧瓷釉料，它是由下列原料制成的：钾长石、红长石、草木灰、铁红粉和萤石；本发明制作的钧瓷釉料，有立体感，流动性好，光泽度好，且用本发明的釉料烧制的钧瓷釉色莹润、裂纹少、呈色稳定。
Description
技术领域
本发明属于钧瓷技术领域，具体涉及一种呈红色的钧瓷釉料。
背景技术
钧瓷以釉厚为本，其色或沉釉底、或悬釉中、或浮釉表，釉厚浑活，釉层乳光莹润，层次繁多透活欲滴，立体感极强。钧瓷以窑变为神，自然窑变是钧瓷艺术的精华所在，也是钧瓷赖以扬名四海，蜚声瓷林的珍奇之处。烧制中同施一种釉，一经烧成则呈五光十色即“入窑一色，出窑万彩”。千变万化的窑变效果，形成了色彩变幻无穷的神奇，红里透紫、紫中藏青、青中寓白、白中泛红，五彩渗化，相映生辉，且有“钧瓷无对，窑变无双”之称。
钧瓷的关键在于瓷釉，瓷釉在进行烧制后的窑变色彩决定了钧瓷的价值，白色的钧瓷有月白、鱼肚白、牙白、玉白等，蓝色的钧瓷有天蓝、湖蓝、粉蓝、宝石蓝、孔雀蓝。釉质配方的不同，烧制出来的颜色也有差异，且传统烧制钧瓷时，是在素胎表面施一层釉，根据窑内的烧制环境钧釉发生窑变，会出现一些不可控制的花纹或者色块，烧制出的成品较难配对或者配置成套，所以才会有“入窑一色，出窑万彩”的说法。
发明内容
为了使钧瓷有更多的颜色变化，需要有不同的釉料配方，本发明提供一种呈红色的钧瓷釉料，使烧出来的钧瓷呈现红色色彩。
本发明采用的技术方案为：
一种呈红色的钧瓷釉料，它是由下列原料制成的：钾长石、红长石、草木灰、铁红粉和萤石。
一种呈红色的钧瓷釉料，它是由下列重量范围的原料制成的：钾长石35-45份、红长石20-30份、草木灰5-9份、铁红粉4-8份和萤石7-11份。
一种呈红色的钧瓷釉料，它是由下列重量范围的原料制成的：钾长石40份、红长石25份、草木灰7份、铁红粉6份和萤石9份。
钾长石属于硅酸盐矿物盐，其内部含量为钾元素、钠元素和钙元素等，分为黄色、白色和红色等，是釉料的主要成分，主要对于釉料的形成起到重要作用。禹州分布有众多矿藏。
草木灰主要引入钙磷等元素，是良好的助溶剂，对釉浆有一定的悬浮性，可降低釉的熔融温度和釉的高温粘度，同时具有乳浊性和对钧釉分相的促进作用，用量应当控制。
红长石属于硅酸盐矿物盐，其内部含量为钾元素、钠元素和钙元素等，分为黄色、白色和红色等，是釉料的主要成分，主要对于釉料的形成起到重要作用。禹州分布有众多矿藏。
铁红粉，是一种化工原料，用于油漆,橡胶,塑料,建筑等的着色。用于油漆,橡胶,塑料,建筑等的着色，有天然的和人造的两种。由于生产方法和操作条件的不同，它们的晶体结构和物理性状都有很大的差别，色泽变动于橙光到蓝光至紫光之间。遮盖力和着色力都很大。有优越的耐光、耐高温性能，并耐大气影响、耐污浊气体、耐一切碱类。在浓酸中只有在加热情况下才逐渐被溶解。用途很广泛，普遍使用于建筑、橡胶、塑料、涂料等工业，特别是铁红底漆具有防锈功能，可以代替高价的红丹漆，节约有色金属。又是高级精磨材料，使用于精密的五金仪器、光学玻璃等的抛光。
萤石是一种矿物，等轴晶系，其主要成分是氟化钙，能降低釉的熔融温度，增加釉的流动性，同时具有乳浊作用，可提高钧釉的光泽度，提高釉浆的悬浮性。
本发明的有益效果是：本发明制作的钧瓷釉料，有立体感，流动性好，光泽度好，且用本发明的釉料烧制的钧瓷釉色莹润、裂纹少、呈色稳定。
具体实施方式
一种呈红色的钧瓷釉料，它是由下列原料制成的：钾长石、红长石、草木灰、铁红粉和萤石。
一种呈红色的钧瓷釉料，它是由下列重量范围的原料制成的：钾长石35-45份、红长石20-30份、草木灰5-9份、铁红粉4-8份和萤石7-11份。
一种呈红色的钧瓷釉料，它是由下列重量范围的原料制成的：钾长石40份、红长石25份、草木灰7份、铁红粉6份和萤石9份。
实施例1
一种呈红色的钧瓷釉料，它是由下列重量范围的原料制成的：钾长石40份、红长石25份、草木灰7份、铁红粉6份和萤石9份。
实施例2
一种呈红色的钧瓷釉料，它是由下列重量范围的原料制成的：钾长石45份、红长石30份、草木灰9份、铁红粉8份和萤石11份。
实施例3
一种呈红色的钧瓷釉料，它是由下列重量范围的原料制成的：钾长石35份、红长石20份、草木灰5份、铁红粉4份和萤石7份。
Claims (3)
1.一种呈红色的钧瓷釉料，其特征在于：它是由下列原料制成的：钾长石、红长石、草木灰、铁红粉和萤石。
2.根据权利要求1所述的一种呈红色的钧瓷釉料，其特征在于：它是由下列重量范围的原料制成的：钾长石35-45份、红长石20-30份、草木灰5-9份、铁红粉4-8份和萤石7-11份。
3.根据权利要求1所述的一种呈红色的钧瓷釉料，其特征在于：它是由下列重量范围的原料制成的：钾长石40份、红长石25份、草木灰7份、铁红粉6份和萤石9份。