CN107539280B - 带有覆盖母线的后风挡玻璃及其有覆盖母线加工工艺 - Google Patents

带有覆盖母线的后风挡玻璃及其有覆盖母线加工工艺 Download PDF

Info

Publication number
CN107539280B
CN107539280B CN201710065605.2A CN201710065605A CN107539280B CN 107539280 B CN107539280 B CN 107539280B CN 201710065605 A CN201710065605 A CN 201710065605A CN 107539280 B CN107539280 B CN 107539280B
Authority
CN
China
Prior art keywords
printing
heating
temperature
covering
drying
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710065605.2A
Other languages
English (en)
Other versions
CN107539280A (zh
Inventor
谢艳国
李鉴
宋子龙
武学明
杨亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUYAO GROUP CHANGCHUN CO LTD
Original Assignee
FUYAO GROUP CHANGCHUN CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUYAO GROUP CHANGCHUN CO LTD filed Critical FUYAO GROUP CHANGCHUN CO LTD
Priority to CN201710065605.2A priority Critical patent/CN107539280B/zh
Publication of CN107539280A publication Critical patent/CN107539280A/zh
Application granted granted Critical
Publication of CN107539280B publication Critical patent/CN107539280B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种带有覆盖母线的后风挡玻璃，后档玻璃(1)上的一对加热母线(2)上分别印刷有覆盖母线，覆盖母线的长度是253mm，覆盖母线的宽度是20‑22.5mm,厚度7‑12μm，一组加热线(3)下方的三根加热线(4)宽度是0.4MM，厚度17‑25mm。本发明优点是：本发明主要针对J5LA后风挡玻璃，J5LA后风挡玻璃规格1240mm*613mm，玻璃厚度3.2mm，SG，拱高102mm，加热线功率153～187W,母线长406、宽22、厚17‑25mm,通过二次印刷可将温度降至70℃以下，可满足客户对高品质玻璃的要求。

Description

带有覆盖母线的后风挡玻璃及其有覆盖母线加工工艺
技术领域
本发明涉及机械设备领域，具体涉及一种带有覆盖母线的后风挡玻璃。
背景技术
目前，现有对后风挡玻璃加热的要求越来越高，需要加热线及母线温度不超过70℃，现在还不能达到不超过70℃的加热线及母线温度的要求。
发明内容
本发明的目的就是针对目前现有对后风挡玻璃加热的要求越来越高，需要加热线及母线温度不超过70℃，现在还不能达到不超过70℃的加热线及母线温度的要求之不足，而提供一种带有覆盖母线的后风挡玻璃。
本发明包括后档玻璃，后档玻璃上印刷有一对加热母线和与一对加热母线电连接的一组加热线，后档玻璃上的一对加热母线上分别印刷有覆盖母线，覆盖母线的长度是253mm，覆盖母线的宽度是20-22.5mm,厚度7-12μm，一组加热线下方的三根加热线宽度是0.4MM，厚度17-25mm。
具体步骤如下：
A、将需要印刷加热线的后档玻璃洗涤烘干；
B、上片：将洗涤烘干完成后的后档玻璃放入预定位工作台内；
C、黑边印刷：将后档玻璃上指定印刷黑边位置处印刷黑边，印刷温度18-25℃，印刷湿度40%-70%；
D、烘干：烘干温度180±20℃；
E、冷却：冷却至常温；
F、加热线印刷：将一对加热母线和一组加热线印刷在后档玻璃表面；印刷温度18-25℃，印刷湿度40%-70%；一组加热线下方的三根加热线宽度是0.4MM,厚度是17-25mm；
G、二次加热线印刷：在一对加热母线的基础上分别印刷覆盖母线，覆盖母线的长253mm，宽20-22.5mm，厚度7-12μm，印刷温度18-25℃，印刷湿度40%-70%；
H、烘干：烘干温度：180±20℃;
I、冷却：冷却至常温；
K、下片。
冷却完成后，覆盖层印刷：将覆盖层印刷在后档玻璃上，并覆盖在加热线和二次加热线上，温度18-25℃，2、湿度40%-70%，然后下片。
本发明优点是：本发明主要针对J5LA后风挡玻璃，J5LA后风挡玻璃规格1240mm*613mm，玻璃厚度3.2mm，SG，拱高102mm，加热线功率153～187W,母线长406、宽22、厚17-25mm,通过二次印刷可将温度降至70℃以下，可满足客户对高品质玻璃的要求。
附图说明
图1是本发明结构示意图。
具体实施方式
如图1所示，本发明包括后档玻璃1，后档玻璃1上印刷有一对加热母线2和与一对加热母线2电连接的一组加热线3，后档玻璃1上的一对加热母线2上分别印刷有覆盖母线，覆盖母线的长度是253mm，覆盖母线的宽度是20-22.5mm,厚度7-12μm，一组加热线3下方的三根加热线4宽度是0.4MM，厚度17-25mm。
具体步骤如下：
A、将需要印刷加热线的后档玻璃1洗涤烘干；
B、上片：将洗涤烘干完成后的后档玻璃1放入预定位工作台内；
C、黑边印刷：将后档玻璃1上指定印刷黑边位置处印刷黑边，印刷温度18-25℃，印刷湿度40%-70%；
D、烘干：烘干温度180±20℃；
E、冷却：冷却至常温；
F、加热线印刷：将一对加热母线2和一组加热线3印刷在后档玻璃1表面；印刷温度18-25℃，印刷湿度40%-70%；一组加热线3下方的三根加热线4宽度是0.4MM,厚度是17-25mm；其余加热线宽度是0.35MM，厚度17-25mm；
G、二次加热线印刷：在一对加热母线的基础上分别印刷覆盖母线，覆盖母线的长253mm，宽20-22.5mm，厚度7-12μm，印刷温度18-25℃，印刷湿度40%-70%；
H、烘干：烘干温度：180±20℃;
I、冷却：冷却至常温；
K、下片。
步骤I冷却完成后，覆盖层印刷：将覆盖层印刷在后档玻璃1上，并覆盖在加热线和二次加热线上，温度18-25℃，2、湿度40%-70%，然后下片。
Figure DEST_PATH_IMAGE001
Figure 210079DEST_PATH_IMAGE002

Claims (2)

1.一种后档玻璃的覆盖母线加工工艺，其特征在于具体步骤如下：
A、将需要印刷加热线的后档玻璃(1)洗涤烘干；
B、上片：将洗涤烘干完成后的后档玻璃(1)放入预定位工作台内；
C、黑边印刷：将后档玻璃(1)上指定印刷黑边位置处印刷黑边，印刷温度18-25℃，印刷湿度40%-70%；
D、烘干：烘干温度180±20℃；
E、冷却：冷却至常温；
F、加热线印刷：将一对加热母线(2)和一组加热线(3)印刷在后档玻璃(1)表面；印刷温度18-25℃，印刷湿度40%-70%；一组加热线(3)下方的三根加热线(4)宽度是0.4MM,厚度是17-25mm；
G、二次加热线印刷：在一对加热母线的基础上分别印刷覆盖母线，覆盖母线的长253mm，宽20-22.5mm，厚度7-12μm，印刷温度18-25℃，印刷湿度40%-70%；
H、烘干：烘干温度：180±20℃;
I、冷却：冷却至常温；
K、下片。
2.根据权利要求1的一种后档玻璃的覆盖母线加工工艺：其特征在于冷却完成后，覆盖层印刷：将覆盖层印刷在后档玻璃(1)上，并覆盖在加热线和二次加热线上，温度18-25℃，湿度40%-70%，然后下片。
CN201710065605.2A 2017-02-06 2017-02-06 带有覆盖母线的后风挡玻璃及其有覆盖母线加工工艺 Active CN107539280B (zh)