CN107502365A - A kind of solid root water conservation accelerator of nonirrigated farmland plantation olive and preparation method thereof - Google Patents
A kind of solid root water conservation accelerator of nonirrigated farmland plantation olive and preparation method thereof Download PDFInfo
- Publication number
- CN107502365A CN107502365A CN201710789309.7A CN201710789309A CN107502365A CN 107502365 A CN107502365 A CN 107502365A CN 201710789309 A CN201710789309 A CN 201710789309A CN 107502365 A CN107502365 A CN 107502365A
- Authority
- CN
- China
- Prior art keywords
- accelerator
- solution
- olive
- soil
- nonirrigated farmland
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses solid root water conservation accelerator of a kind of nonirrigated farmland plantation olive and preparation method thereof, by the compound such as deinked pulp, bentonite, hydroxypropyl chitosan and polyvinyl alcohol, micro-nano iron oxide, microencapsulation growth accelerator it is configured to that netted, ventilative, water conservation bonding colloid can be formed after colloidal state slurries are applied in soil, soil is prevented to be cracked, and the respiration capability of soil can be improved, promote root to nutritional ingredient absorption, and the growth accelerator of microencapsulation has slow release effect, lasting promoting root growth effect can reach；The survival rate of root system can be effectively improved when being applied to nonirrigated farmland olive with the obtained accelerator of the present invention, root system is more firm healthy and strong, nutritional ingredient in soil not easily runs off, there is certain regulation repair to soil environment, more preferable environment is provided for olive root growth, its production process is simple simultaneously, and product is nontoxic, and soil is had no adverse effects.
Description
Technical field
The present invention relates to the solid root water conservation of a kind of planting accelerator, more particularly to a kind of nonirrigated farmland plantation olive to promote
Enter agent.
Background technology
Olive is Oleaceae Olea aiphyllium, is world-renowned woody oleiferous plants and fruit seeds, cultivation product
Kind has higher edibility, is famous subtropical fruit tree and Important Economic woods containing abundant kind of high-quality edible plant oil-olive oil
Wood, mediterranean country is distributed mainly on, Greece, Italy, Tunisia, Spain are the concentration place of production.China was from 60 years 20th century
Generation, which rises, starts the introduction of olive batch and experimental cultivation, achieves preferable economic benefit and social benefit, but it introduces a fine variety cultivation
For the regionality of training it is obvious that being concentrated mainly on the ground such as Shaanxi south of Gansu Province, the Sichuan Basin, Yunnan, less, mesh is introduced a fine variety in other hinterland
It is preceding that with the progress of Cultivating techniques, Guangdong and Guangxi Provinces, Jiangsu and Zhejiang Provinces and the band of Basin of Huaihe River one also possess the weather geographical conditions of plantation olive,
New opportunity is provided for the development of local agricultural production industry.
Olive root system happiness temperature is aerobic, and the depth in soil is shallower, if plant root developmental state is low, it is impossible to from
Enough nutrients are drawn in soil, it is directly resulted in and yields poorly down, in addition it is dead, therefore the gesture during nonirrigated farmland plantation olive
Higher requirement must be proposed to the retain water and nutrients ability of soil, such as《Different Water-retaining Measures are to south of Gansu Province nonirrigated farmland olive garden mould
The influence of earth water content, shoot length and root system》The result of study of one text, which indicates that, takes film covering, improving straw mulching, depth
Soil texture will effectively be improved, promote robust plant growth by the Water-retaining Measure such as turning over, and realize increasing both production and income, but these are handled
Method is only extraneous supplementary means, without the solid root performance of water conservation for fundamentally improving plant soil itself, and is implemented
Waste time and energy.
The content of the invention
There is provided that a kind of to improve root system grabbing in soil attached present invention aims at the olive plant planted for nonirrigated farmland
Power, prevent soil loss, promote root system development, the accelerator of retain water and nutrients, realizing the effect of increasing both production and income.
The present invention is achieved by the following technical solutions：
A kind of solid root water conservation accelerator of nonirrigated farmland plantation olive, it is characterised in that described accelerator is by following parts by weight
Raw material be formulated：Deinked pulp 10-15, bentonite 20-30, hydroxypropyl chitosan 1-2, microencapsulation growth accelerator 1-2,
Polyvinyl alcohol 0.5-1, micro-nano iron oxide 0.01-0.02, water 300-500.
Described microencapsulation growth accelerator is prepared by following steps：
（1）By system heating water bath after immersion treatment 30-50min in gelatin input water to 40-50 DEG C, and stir and make it that gelatin is complete
Fully dissolved, it is configured to the gelatin solution that concentration is 8-12%；
（2）Forulic acid is allocated with 0.5mol/L sodium hydroxide solution, is configured to the solution that concentration is 0.2mol/L, and this is molten
Drop enters step（1）In the gelatin solution of preparation, asafoetide acid concentration is 0.04-0.05mol/L in control system, after being well mixed
Addition and the equimolar hydrogen peroxide of forulic acid, continue to be uniformly mixed, are subsequently added into sodium hydroxide solution regulation system pH
It is worth for 7.5-8；
（3）Horseradish peroxidase, enzyme activity 320-350U/L, then by its solution in 40-50 are added into above-mentioned solution
Concussion reaction crosslinking 15-20h under DEG C water bath condition, reaction crush after terminating rear solution freeze-drying, cross 100 mesh sieves, product is used
Absolute ethyl alcohol is dried after cleaning removing residual forulic acid repeatedly, and it is standby to obtain cross-linked gelatin wall material；
（4）Growth accelerator is put into water, stirring is completely dissolved it, and it is 100-500mg/L's to be configured to growth accelerator content
Core material solution is standby；
（5）Cross-linked gelatin wall material is put into appropriate water, after its be fully swelled it is scattered after heating water bath to 40-50 DEG C, stirring
Dissolving forms the wall material solution that concentration is 5%, is then 5 according to wall material and core weight ratio:1 proportioning adds core material solution, mixes
It is spray-dried after closing uniformly, produces described microencapsulation growth accelerator.
Described growth accelerator is the mixing of one or both of heteroauxin, Nafusaku.
1 μm of the average grain diameter ＜ of described micro-nano iron oxide.
A kind of preparation method of the solid root water conservation accelerator of described nonirrigated farmland plantation olive comprises the following steps：
（1）First polyvinyl alcohol, hydroxypropyl chitosan, bentonite, deinked pulp are put into water successively, system is heated to 70-
80 DEG C, mixed grinding adds micro-nano iron oxide after stirring 1-2h, and it is cold then to carry out sonic oscillation processing 30-50min rear slurries
But it is standby to room temperature；
（2）Microencapsulation growth accelerator is put into step（1）In the slurries of preparation, described promotion is produced after being uniformly mixed
Agent, directly apply during use.
The present invention plants characteristic from olive, and this promotion with solid root water retention is applied in planting process
Agent, pull-out capacity of the root system in soil is improved, prevents rainwater leaching loss, while olive root system development can also be promoted, be finally reached
The effect of increasing both production and income.This accelerator is by deinked pulp, bentonite, hydroxypropyl chitosan and polyvinyl alcohol compound
Colloidal state slurries, while the microencapsulation growth accelerator wherein coated containing micro-nano iron oxide and crosslinked gelatin are configured to, by it
Netted, ventilative, water conservation bonding colloid can be formed after being applied in soil, prevents soil to be cracked, and the breathing of soil can be improved
Ability, promote root to nutritional ingredient absorption, and the growth accelerator of microencapsulation has slow release effect, can reach lasting rush
Root effect；The survival rate of root system can be effectively improved when being applied to nonirrigated farmland olive with the obtained accelerator of the present invention, root system is more
Firmly healthy and strong, the nutritional ingredient in soil not easily runs off, and has certain regulation repair to soil environment, is olive root system
Growth provides more preferable environment, while its production process is simple, and product is nontoxic, and soil is had no adverse effects.
Embodiment
Embodiment 1
A kind of solid root water conservation accelerator of nonirrigated farmland plantation olive, the accelerator are formulated by the raw material of following parts by weight：
Deinked pulp 10, bentonite 20, hydroxypropyl chitosan 1, microencapsulation growth accelerator 1, polyvinyl alcohol 0.5, micro-nano iron oxide
0.01st, water 300.
Wherein microencapsulation growth accelerator is prepared by following steps：
（1）By system heating water bath after immersion treatment 30min in gelatin input water to 40-50 DEG C, and stir and make it that gelatin is complete
Dissolving, it is configured to the gelatin solution that concentration is 8%；
（2）Forulic acid is allocated with 0.5mol/L sodium hydroxide solution, is configured to the solution that concentration is 0.2mol/L, and this is molten
Drop enters step（1）In the gelatin solution of preparation, asafoetide acid concentration is 0.04mol/L in control system, is added after well mixed
With the equimolar hydrogen peroxide of forulic acid, continue to be uniformly mixed, being subsequently added into sodium hydroxide solution regulation system pH value is
7.5；
（3）Horseradish peroxidase, enzyme activity 320U/L, then by its solution in 40-50 DEG C of water are added into above-mentioned solution
Concussion reaction is crosslinked 15h under the conditions of bath, and reaction crushes after terminating rear solution freeze-drying, crosses 100 mesh sieves, product absolute ethyl alcohol
Cleaning is dried after removing residual forulic acid repeatedly, and it is standby to obtain cross-linked gelatin wall material；
（4）Heteroauxin is put into water, stirring is completely dissolved it, is configured to the core that growth accelerator content is 100mg/L
Solution for standby；
（5）Cross-linked gelatin wall material is put into appropriate water, after its be fully swelled it is scattered after heating water bath to 40-50 DEG C, stirring
Dissolving forms the wall material solution that concentration is 5%, is then 5 according to wall material and core weight ratio:1 proportioning adds core material solution, mixes
It is spray-dried after closing uniformly, produces described microencapsulation growth accelerator.
1 μm of the average grain diameter ＜ of wherein micro-nano iron oxide.
The preparation method of the embodiment accelerator comprises the following steps：
（1）First polyvinyl alcohol, hydroxypropyl chitosan, bentonite, deinked pulp are put into water successively, system is heated to 70-
80 DEG C, mixed grinding adds micro-nano iron oxide after stirring 1h, then carries out sonic oscillation processing 30min rear slurries and is cooled to room
Warm standby is used；
（2）Microencapsulation growth accelerator is put into step（1）In the slurries of preparation, described promotion is produced after being uniformly mixed
Agent, directly apply during use.
Embodiment 2
A kind of solid root water conservation accelerator of nonirrigated farmland plantation olive, the accelerator are formulated by the raw material of following parts by weight：
Deinked pulp 15, bentonite 30, hydroxypropyl chitosan 2, microencapsulation growth accelerator 2, polyvinyl alcohol 1, micro-nano iron oxide
0.02nd, water 500.
Wherein microencapsulation growth accelerator is prepared by following steps：
（1）By system heating water bath after immersion treatment 50min in gelatin input water to 40-50 DEG C, and stir and make it that gelatin is complete
Dissolving, it is configured to the gelatin solution that concentration is 12%；
（2）Forulic acid is allocated with 0.5mol/L sodium hydroxide solution, is configured to the solution that concentration is 0.2mol/L, and this is molten
Drop enters step（1）In the gelatin solution of preparation, asafoetide acid concentration is 0.05mol/L in control system, is added after well mixed
With the equimolar hydrogen peroxide of forulic acid, continue to be uniformly mixed, being subsequently added into sodium hydroxide solution regulation system pH value is
8；
（3）Horseradish peroxidase, enzyme activity 350U/L, then by its solution in 40-50 DEG C of water are added into above-mentioned solution
Concussion reaction is crosslinked 20h under the conditions of bath, and reaction crushes after terminating rear solution freeze-drying, crosses 100 mesh sieves, product absolute ethyl alcohol
Cleaning is dried after removing residual forulic acid repeatedly, and it is standby to obtain cross-linked gelatin wall material；
（4）Nafusaku is put into water, stirring is completely dissolved it, is configured to the core that growth accelerator content is 500mg/L
Solution for standby；
（5）Cross-linked gelatin wall material is put into appropriate water, after its be fully swelled it is scattered after heating water bath to 40-50 DEG C, stirring
Dissolving forms the wall material solution that concentration is 5%, is then 5 according to wall material and core weight ratio:1 proportioning adds core material solution, mixes
It is spray-dried after closing uniformly, produces described microencapsulation growth accelerator.
1 μm of the average grain diameter ＜ of wherein micro-nano iron oxide.
The preparation method of the solid root water conservation accelerator of the embodiment comprises the following steps：
（1）First polyvinyl alcohol, hydroxypropyl chitosan, bentonite, deinked pulp are put into water successively, system is heated to 70-
80 DEG C, mixed grinding adds micro-nano iron oxide after stirring 2h, then carries out sonic oscillation processing 50min rear slurries and is cooled to room
Warm standby is used；
（2）Microencapsulation growth accelerator is put into step（1）In the slurries of preparation, described promotion is produced after being uniformly mixed
Agent, directly apply during use.
Claims (5)
1. a kind of solid root water conservation accelerator of nonirrigated farmland plantation olive, it is characterised in that described accelerator is by following weight
The raw material of part is formulated：Deinked pulp 10-15, bentonite 20-30, hydroxypropyl chitosan 1-2, microencapsulation growth accelerator 1-
2nd, polyvinyl alcohol 0.5-1, micro-nano iron oxide 0.01-0.02, water 300-500.
2. the solid root water conservation accelerator of a kind of nonirrigated farmland plantation olive as claimed in claim 1, it is characterised in that described
Microencapsulation growth accelerator is prepared by following steps：
（1）By system heating water bath after immersion treatment 30-50min in gelatin input water to 40-50 DEG C, and stir and make it that gelatin is complete
Fully dissolved, it is configured to the gelatin solution that concentration is 8-12%；
（2）Forulic acid is allocated with 0.5mol/L sodium hydroxide solution, is configured to the solution that concentration is 0.2mol/L, and this is molten
Drop enters step（1）In the gelatin solution of preparation, asafoetide acid concentration is 0.04-0.05mol/L in control system, after being well mixed
Addition and the equimolar hydrogen peroxide of forulic acid, continue to be uniformly mixed, are subsequently added into sodium hydroxide solution regulation system pH
It is worth for 7.5-8；
（3）Horseradish peroxidase, enzyme activity 320-350U/L, then by its solution in 40-50 are added into above-mentioned solution
Concussion reaction crosslinking 15-20h under DEG C water bath condition, reaction crush after terminating rear solution freeze-drying, cross 100 mesh sieves, product is used
Absolute ethyl alcohol is dried after cleaning removing residual forulic acid repeatedly, and it is standby to obtain cross-linked gelatin wall material；
（4）Growth accelerator is put into water, stirring is completely dissolved it, and it is 100-500mg/L's to be configured to growth accelerator content
Core material solution is standby；
（5）Cross-linked gelatin wall material is put into appropriate water, after its be fully swelled it is scattered after heating water bath to 40-50 DEG C, stirring
Dissolving forms the wall material solution that concentration is 5%, is then 5 according to wall material and core weight ratio:1 proportioning adds core material solution, mixes
It is spray-dried after closing uniformly, produces described microencapsulation growth accelerator.
3. the solid root water conservation accelerator of a kind of nonirrigated farmland plantation olive as claimed in claim 2, it is characterised in that described
Growth accelerator is the mixing of one or both of heteroauxin, Nafusaku.
4. the solid root water conservation accelerator of a kind of nonirrigated farmland plantation olive as claimed in claim 1, it is characterised in that described
1 μm of the average grain diameter ＜ of micro-nano iron oxide.
5. a kind of preparation method of the solid root water conservation accelerator of nonirrigated farmland plantation olive as described in claim 1-4 is any,
Characterized in that, described preparation method comprises the following steps：
（1）First polyvinyl alcohol, hydroxypropyl chitosan, bentonite, deinked pulp are put into water successively, system is heated to 70-
80 DEG C, mixed grinding adds micro-nano iron oxide after stirring 1-2h, and it is cold then to carry out sonic oscillation processing 30-50min rear slurries
But it is standby to room temperature；
（2）Microencapsulation growth accelerator is put into step（1）In the slurries of preparation, described promotion is produced after being uniformly mixed
Agent, directly apply during use.