CN107496187A - 一种贴肤性极好疏水疏油的化妆品颜料粉末及其制备方法和应用 - Google Patents
一种贴肤性极好疏水疏油的化妆品颜料粉末及其制备方法和应用 Download PDFInfo
- Publication number
- CN107496187A CN107496187A CN201710723359.5A CN201710723359A CN107496187A CN 107496187 A CN107496187 A CN 107496187A CN 201710723359 A CN201710723359 A CN 201710723359A CN 107496187 A CN107496187 A CN 107496187A
- Authority
- CN
- China
- Prior art keywords
- powder
- pigment powder
- skin
- hydrolecithin
- hydrophobic oleophobic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种疏水疏油化妆品颜料粉末，其包括颜料粉末和贴肤性处理剂，所述贴肤性处理剂对颜料粉末表面复合处理，其中贴肤性处理剂包括含氟硅烷与氢化卵磷脂，此粉末不仅具有极佳的疏水疏油性，并且具有良好的可拾取性和贴肤性，肤感弹软柔滑，本发明的全氟硅烷处理剂碳数≤8，安全友好无毒性，添加与皮肤亲和性极佳的纯植物成分，能起到滋养皮肤，易卸妆的效果。
Description
技术领域
本发明涉及化妆品领域，尤其是涉及疏水疏油的化妆品颜料粉末及其制备方法
背景技术
随着生活水平的日益提高，人们对化妆品的需求也飞速增长。以前，粉底霜/液大都具有防水功能，但很少具备防油功能。在使用过程中，皮肤分泌的油脂、汗液等容易破坏妆容。根据不同人群皮肤的差异，总是会引起不同程度的掉妆、花妆。
近年来，含氟硅烷在化妆品行业也出现少量应用。如JP2008037813，JP2008137921公布了将含氟硅烷用于化妆品颜料粉末的表面处理，从而达到疏水疏油的效果。该粉末肤感较差，使用后与皮肤的贴合性较差，且同时化妆品存在飘色问题。CN201610003469解决上述飘色问题，公开了一种疏水疏油化妆品粉末其纳米硅溶胶和全氟辛基三乙氧基硅烷处理的钛白粉。上述目前使用含氟硅烷处理得到的化妆品原料粉末虽然具有极佳的疏水疏油性，可保持较为持久的妆容，但是粉末的可拾取性和贴肤性较差，并且不易卸妆。CN201080039592.8公开一种具有紫外线屏蔽效果和皮脂固化能力的化妆品组合物，包含微粒氧化钛、氧化镁、氧化钙、氢氧化镁及氢氧化钙的一种或两种以上，组合物通过亲油化处理剂进行亲油处理。所述亲油化处理剂是由下述通式(1)表示的烷基烷氧硅烷，以下述通式(2)表示的反应性有机硅氧烷、酰基化氨基酸、聚烯烃、氢化卵磷脂、糊精脂肪酸酯、含全氟烷基或全氟聚醚基的化合物以及包括其盐的形态在内的碳数为12-22的饱和或不饱和脂肪酸的1种化合物或者两种以上化合物的混合物形成。化1,(CnH2n+1)aSi(OCmH2m+1)b,式1中，n表示1-18的整数，m表示1-3的整数，a、b表示1-3整数，a+b＝4。化2(R1 3SiO)Si(R1 2SiO)P(SiR2 3)，式2中R1全部相互独立地分别表示碳数1－4的低级烷基或氢原子，R2氨基，氢原子、羟基和碳数1－4的低级烷氧基中的任一种，P为1－300的整数。该专利中使用的全氟烷基化合物的碳数在12-22，超过8个碳的有生物毒性，CN201080039592.8得到的是疏水亲油的粉末，持妆性比较弱。主要目的是紫外屏蔽。
发明内容
为了解决上述技术问题，本发明的目的在于提供一种疏水疏油的化妆品颜料粉末。此粉末不仅具有极佳的疏水疏油性，并且具有良好的可拾取性和贴肤性，肤感弹软柔滑，本发明的全氟硅烷处理剂碳数≤8，安全友好无毒性。添加与皮肤亲和性极佳的纯植物成分，能起到滋养皮肤，易卸妆的效果。
本发明的另一目的在于一种疏水疏油化妆品颜料粉末的制备方法。
本发明是通过以下技术方案实现的：
一种疏水疏油化妆品颜料粉末，其包括颜料粉末和贴肤性处理剂，所述贴肤性处理剂对颜料粉末表面复合处理，其中贴肤性处理剂包括含氟硅烷与氢化卵磷脂。
进一步优选，本发明的贴肤性处理剂中所述的含氟硅烷与氢化卵磷脂按照重量比1：1-15：1复合使用，进一步优选1-5:1复合使用，优选3:1复合使用。
上述疏水疏油化妆品颜料粉末中，含氟硅烷的用量0.1-10.0％，氢化卵磷脂的用量0.1-10.0％，余量为颜料粉末。
上述疏水疏油化妆品颜料粉末中所述的颜料粉末包括但不限于为二氧化钛，氧化铁黄，氧化铁红，氧化铁黑，滑石、云母、群青类、氧化铬绿中的一种或者几种的混合物。
上述贴肤性处理剂中所述含氟硅烷的结构为：Rf-(CH2)2-Si-(OCmH2m+1)3，其中，Rf为CnF2n+1，1≤n≤6，n为整数，m为1或2。
进一步优选含氟硅烷为全氟辛基三乙氧基硅烷。
上述贴肤性处理剂中所述氢化卵磷脂生物学名称为磷脂酰胆碱，被誉为与蛋白质、维生素并列的“第三营养素”，通用学名称为Lecithin。在卵磷脂中发现的含磷的脂质都归为“磷脂”，磷脂与糖脂类以及(神经)鞘脂类代表了卵磷脂中的极性脂质，他们是所有细胞膜的必需成分。应用在化妆品领域的卵磷脂是从大豆中提取的，可生物降解，是生态环保产品。卵磷脂被誉为“吃的化妆品”。使用氢化卵磷脂作为化妆品粉末的表面处理剂，由于卵磷脂的存在，与皮肤生物化学性质相似，因此处理得到的化妆品粉末与皮肤相容性极佳。
一种技术方案，本发明的疏水疏油化妆品颜料粉末是由下述重量百分比物质构成：
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的滑石粉99.64％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁黄0.24％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁红0.10％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁黑0.02％。
一种技术方案，本发明的疏水疏油化妆品颜料粉末是由下述重量百分比物质构成：
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的滑石粉53.25％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的云母粉41.32％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的钛白粉2.36％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁黄0.71％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁红2.36％.
一种技术方案，本发明的疏水疏油化妆品颜料粉末是由下述重量百分比物质构成：
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的钛白粉91.8％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁黄粉末5.4％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁红粉末1.8％
6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁黑粉末1.0％。
所述贴肤性处理剂对颜料粉末表面复合处理采用常规的干法或者湿法工艺均可。
本发明所述的疏水疏油化妆品颜料粉末在化妆品中的应用。
本发明所述的应用，其中，所述化妆品为具有遮盖肌肤瑕疵、修饰皮肤颜色功能的彩妆产品，例如散粉、粉饼、腮红、粉底液、粉底霜等，本发明制备的贴肤性极佳的疏水疏油的化妆品颜料粉末在这些彩妆产品中不仅起到物理遮盖的作用，能够即时修饰皮肤瑕疵，缔造完美妆容效果。并且因为纯植物来源的亲肤性极佳的氢化卵磷脂的存在，因此可滋养皮肤，打造植物护肤彩妆的概念。
所述化妆品也可以是具有美白功能的护肤品，例如，美白霜、美白乳液等，本发明制备的贴肤性极佳的疏水疏油的化妆品颜料粉末在这类护肤品中的作用是物理增白和长效滋养皮肤，能够即时美白皮肤并且滋养皮肤，有利于配合长效美白成分打造美白滋养双重效果化妆品的概念。
本发明还提供疏水疏油化妆品颜料粉末的制备方法，包括步骤如下：
步骤(1)贴肤性处理液的制备：含氟硅烷、氢化卵磷脂溶解于乙醇或多元醇中，配制成处理液；
步骤(2)高速搅拌下，将处理液喷涂颜料粉末表面，混合均匀出料，加热烘干；
步骤(3)气流粉碎成粉体。
进一步优选，一种疏水疏油化妆品颜料粉末的制备方法，包括步骤如下：
步骤(1)贴肤性处理剂的制备：含氟硅烷、氢化卵磷脂2000-20000转/min高速搅拌溶解于复合处理剂总量的(1-1.5倍)量的乙醇或多元醇中，配制成处理液；
步骤(2)2000-20000转/min高速搅拌下，将处理液喷涂颜料粉末表面，混合均匀出料，100-150℃加热烘干1-5小时；
步骤(3)气流粉碎：采用7～8MPa的高压空气对粉体进行处理，得到的粉体平均粒径0.1-5μm。
上述步骤(1)中所述的多元醇包括但不限于甘油、异丙醇乙二醇丙三醇等。
有益效果
1、本发明的疏水疏油颜料粉末使用含氟硅烷与氢化卵磷脂复合，克服了在氟化处理得到的粉末，疏水疏油性好，可是不贴肤，卸妆不易的缺陷。因为氢化卵磷脂是纯植物来源，具有极好的贴肤性，因此在保证粉末的良好疏水疏油性的前提下，能增强贴肤性和对皮肤的滋养性，并且更易卸妆，而且肤感极佳，绸缎般弹软柔滑。
2、本发明的氢化卵磷脂及与含氟硅烷的配比是经过大量筛选得到的。只有在本发明比例情况下，制备得到的疏水疏油颜料粉末才具有贴服易卸妆的效果。3、本发明用贴肤性处理剂处理颜料粉末工艺简单，易于操作，易于产业化放大生产。
4、本发明中使用氢化卵磷脂与含氟硅烷的复合处理剂不仅能够降低不同种类颜料粉末间的表面性质差异，使不同种类的颜料粉末表面包裹的含氟硅烷量趋于一致，从而有利于多种颜料粉末应用于同一化妆品配方时能够均匀分散避免飘色同时还能够使化妆品配方更贴肤性且易于卸妆。
5、CN201610003469中使用二氧化硅是通过使表面的性质趋于统一以改善飘色；本发明中添加了氢化卵磷脂的复合处理后，改善了不同种类粉体的相容性，并且得到的复合色粉与配方的配伍性更好，因此可以改善飘色。
6、CN201080039592.8使用的全氟烷基化合物的碳数在12-22个，得到的是疏水亲油的粉末，持妆性弱，主要目的是紫外屏蔽。本发明使用全氟硅烷化合物的碳数是3-8个，是安全、环境友好的全氟硅烷处理剂，得到的是疏水疏油的粉末，能够长久持妆、亲肤滋养、易卸妆。
附图说明
图1为6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的钛白粉接触角测试图片；
图2为6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁黄粉末接触角测试图片；
图3为6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁黑粉末接触角测试图片；
图4为6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁红粉末接触角测试图片。
图5为6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的滑石粉接触角测试图片。
图6为6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的云母粉接触角测试图片。
图7为6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的钛白粉接触角测试图片；
图8为6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的氧化铁黄粉末接触角测试图片；
图9为6％全氟辛基三乙氧基硅烷处理的氧化铁黑粉末接触角测试图片；
图10为6％全氟辛基三乙氧基硅烷处理的氧化铁红粉末接触角测试图片。
图11为6％全氟辛基三乙氧基硅烷处理的滑石粉接触角测试图片。
图12为6％全氟辛基三乙氧基硅烷处理的云母粉接触角测试图片。
具体实施方式
下面结合附图，对本发明的具体实施方式进行详细描述，但应当理解本发明的保护范围并不受具体实施方式的限制。
除非另有其它明确表示，否则在整个说明书和权利要求书中，术语“包括”或其变换如“包含”或“包括有”等等将被理解为包括所陈述的元件或组成部分，而并未排除其它元件或其它组成部分。
实施例1
将60g全氟辛基三乙氧基硅烷(Dynasylan F8261，赢创德固赛)和20g氢化卵磷脂(LECIPLART-SOY·75H，日本特科诺宝)的溶解于100g乙醇中，配制成处理液。高速搅拌下，将该处理液喷入1kg钛白粉中，使处理液与粉末充分混合后出料，110℃烘3h。出料后，气流粉碎，即获得复合处理的钛白粉。
实施例2
将60g全氟辛基三乙氧基硅烷(Dynasylan F8261，赢创德固赛)和20g氢化卵磷脂(LECIPLART-SOY·75H，日本特科诺宝)的溶解于100g乙醇中，配制成处理液。高速搅拌下，将该处理液喷入1kg氧化铁黄中，使处理液与粉末充分混合后出料，110℃烘3h。出料后，气流粉碎，即获得复合处理的氧化铁黄
实施例3
将60g全氟辛基三乙氧基硅烷(Dynasylan F8261，赢创德固赛)和20g氢化卵磷脂(LECIPLART-SOY·75H，日本特科诺宝)的溶解于100g乙醇中，配制成处理液。高速搅拌下，将该处理液喷入1kg氧化铁红中，使处理液与粉末充分混合后出料，110℃烘3h。出料后，气流粉碎，即获得复合处理的氧化铁红。
实施例4
将60g全氟辛基三乙氧基硅烷(Dynasylan F8261，赢创德固赛)和20g氢化卵磷脂(LECIPLART-SOY·75H，日本特科诺宝)的溶解于100g乙醇中，配制成处理液。高速搅拌下，将该处理液喷入1kg氧化铁黑中，使处理液与粉末充分混合后出料，110℃烘3h。出料后，气流粉碎，即获得复合处理的氧化铁黑。
实施例5
将60g全氟辛基三乙氧基硅烷(Dynasylan F8261，赢创德固赛)和20g氢化卵磷脂(LECIPLART-SOY·75H，日本特科诺宝)的溶解于100g乙醇中，配制成处理液。高速搅拌下，将该处理液喷入1kg滑石粉中，使处理液与粉末充分混合后出料，110℃烘3h。出料后，气流粉碎，即获得复合处理的滑石粉。
实施例6
将60g全氟辛基三乙氧基硅烷(Dynasylan F8261，赢创德固赛)和20g氢化卵磷脂(LECIPLART-SOY·75H，日本特科诺宝)的溶解于100g乙醇中，配制成处理液。高速搅拌下，将该处理液喷入1kg绢云母中，使处理液与粉末充分混合后出料，110℃烘3h。出料后，气流粉碎，即获得复合处理的绢云母。
实施例7(散粉、粉饼)
将实施例2、3、4、5制备的粉末加入表1所示的配方中，制备散粉或者粉饼。
表1散粉配方组成
2、制备工艺
将A相原料依次加入搅拌机，高速搅拌混合1分钟，使不同粉末混合均匀；
将B、C相原料依次加入搅拌机的喷油装置，喷油的同时高速搅拌混合1分钟，使所有原料充分混匀，出料。
由此获得“散粉A”，若将此散粉称量于粉饼模具中，通过压粉机压制，即可获得一款粉饼。
实施例8(腮红制备)
将实施例1-6制备的粉末加入表2所示的配方中制备一款腮红。
表2腮红配方
2、制备工艺
将A相原料和E相原料依次加入搅拌机，高速搅拌混合1分钟；
再将B相原料加入搅拌机中，高速搅拌3分钟混合均匀，得到A相和E相和B相的混合物；
将D相预先溶解搅拌均匀，然后将其加入搅拌机的喷油装置，喷油的同时高速搅拌混合1分钟，使所有原料充分混匀，出料；
将其压制到铝盘或者塑料壳中，即获得一款腮红。
实施例9
将实施例1,2,3,4制备的粉末加入下列粉底液(霜)如表3所示配方中。
表3粉底液(霜)配方组成
2、制备工艺
配制38V Gel：20％Bentone 38V(海明斯)+75％PMX-0345Fluid+5％95°酒精，快速搅拌均匀后，均质5分钟；
将A相搅拌加热至70℃左右，待组分完全溶解，均质(10000转/分钟)30秒；
加入C相粉料，均质(10000转/分钟)1分钟，使粉末分散均匀；
将B相加入AC相中，快速搅拌(400转/分钟)ABC相；同时D相加热至75-80度左右溶解完全；
维持温度，加快ABC相搅拌速度(400-500转/分钟)，将D相缓慢加入ABC相中，使乳化完全。均质(10000转/分钟)1分钟；
搅拌(380-400转/分钟)降温至45度以下，加入E相，搅匀出料。
试验例一
对比例1：将60g全氟辛基三乙氧基硅烷(Dynasylan F8261，赢创德固赛)溶解于100g乙醇中，配制成处理液。高速搅拌下，将该处理液喷入1kg钛白粉中，使处理液与粉末充分混合后出料，110℃烘3h。出料后，气流粉碎，即获得氟化处理的钛白粉。
对比例2：将对比例1中的钛白粉换成氧化铁黄。
对比例3：将对比例1中的钛白粉换成氧化铁红。
对比例4：将对比例1中的钛白粉换成氧化铁黑。
对比例5：将对比例1中的钛白粉换成滑石粉。
对比例6：将对比例1中的钛白粉换成绢云母。
对实施例1，2，3，4，5，6及对比例1，2，3，4，5,6制备的粉进行接触角测试，测试液体分别为去离子水、液体石蜡。测试结果如图1-图12(左侧为水，右侧为液体石蜡)及表4所示。
表4实施例1，2，3，4及对比例1，2，3，4制备的粉进行接触角测试
结论：复合氢化卵磷脂处理后粉末的疏水疏油性并没有降低，因此持妆性很好。
试验例二
用对比例2、3、4制备的6％全氟辛基三乙氧基硅烷处理的粉末替换实施例2、3、4制备的6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的粉末加入表2所示粉饼(散粉)配方中，按照相同工艺打样，获得“散粉B”。
粉底评价方法：寻找若干志愿者，“将粉底A”与“粉底B”分别涂抹于左、右侧脸颊，在涂抹的时候评价两种粉底的弹性、滑感及涂抹性，涂抹后评价粉底的亲肤性及持妆效果。对比结果如表5所示。
表5散粉A、B的肤感对比结果
附：以10分为满分。
结论：本发明6％全氟辛基三乙氧基硅烷+2％氢化卵磷脂处理的粉末在亲肤性、弹性、滑感、涂抹性、卸妆容易程度都优于没有填加氢化卵磷脂处理的粉末。
试验例三，与全氟辛基三乙氧基硅烷复合使用的处理剂种类筛选试验
氨基酸、卵磷脂和氢化卵磷脂均属于与皮肤具有生物相容性的物质。因此从这三种类型的亲肤性处理剂筛选合适的处理剂。
高纯度的卵磷脂氧化性能强，极易被氧化，因此未经过氢化处理的卵磷脂，一般要求在充氮的密封容器中，使用极不方便。
氨基酸一般使用湿法工艺进行处理，处理成本高，会产生大量污水排放。
将50g卵磷脂的溶解于100g乙醇中，配制成处理液。高速搅拌下，将该处理液喷入1kg钛白粉中，使处理液与粉末充分混合后出料，110℃烘3h。出料后，气流粉碎，即获得5％卵磷脂处理的钛白粉。
将上述卵磷脂改为氢化卵磷脂，进行同样的过程，得到5％氢化卵磷脂处理的钛白粉。
将1kg钛白粉预分散成16％～20％的水溶液，用氢氧化钠调节溶液pH至11左右，加入50g月桂基赖氨酸粉末；溶液升温至80℃搅拌混合40分钟，用盐酸调节pH至6，保持温度搅拌反应4分钟，洗涤干燥粉碎，即获得5％氨基酸处理的钛白粉。
比较三种处理得到的粉末的贴肤性，发现使用卵磷脂和氢化卵磷脂处理得到的粉末的贴肤性优于氨基酸处理得到的粉末。但因为卵磷脂极易氧化，使用不便，因此选用氢化卵磷脂作为贴肤处理剂。
试验例四，与全氟辛基三乙氧基硅烷复合使用的处理剂的用量筛选试验
本专利前面所述的全氟辛基三乙氧基硅烷与氢化卵磷脂的处理比例在1:1到15:1，进一步优选为3:1。筛选实验如下：
按照实施例1的实验过程，固定全氟辛基三乙氧基硅烷的用量，改变氢化卵磷脂的量以改变两种处理剂的比例关系。氢化卵磷脂分别添加70g、60g、20g、4g、3g，相应改变乙醇的用量为150g、130g、100g、80g、80g。得到全氟辛基三乙氧基硅烷与氢化卵磷脂复合处理比例分别为6:7、1:1、3:1、5:1、20:1的钛白粉。
后发现当氢化卵磷脂用量多于全氟辛基三乙氧基硅烷时，即处理比例为6:7时，处理得到的粉末的疏油性不佳(液体石蜡接触角小于90°)。当氢化卵磷脂用量过于少时，即全氟辛基三乙氧基硅烷与氢化卵磷脂的复合处理达到15:1以上时，粉体失去弹滑感和极佳的贴肤性。因此选定全氟辛基三乙氧基硅烷与氢化卵磷脂的处理比例在1:1到15:1之间，在此区间内，即可保证双疏性、又可保证弹滑性和贴肤性。而当全氟辛基三乙氧基硅烷与氢化卵磷脂的处理比例在3:1时，双疏性和弹滑感均最佳。
前述对本发明的具体示例性实施方案的描述是为了说明和例证的目的。这些描述并非想将本发明限定为所公开的精确形式，并且很显然，根据上述教导，可以进行很多改变和变化。对示例性实施例进行选择和描述的目的在于解释本发明的特定原理及其实际应用，从而使得本领域的技术人员能够实现并利用本发明的各种不同的示例性实施方案以及各种不同的选择和改变。本发明的范围意在由权利要求书及其等同形式所限定。
Claims (10)
1.一种疏水疏油化妆品颜料粉末，其包括颜料粉末和贴肤性处理剂，所述贴肤性处理剂对颜料粉末表面复合处理，其中贴肤性处理剂包括含氟硅烷与氢化卵磷脂。
2.如权利要求1所述的一种疏水疏油化妆品颜料粉末，其特征在于：所述的贴肤性处理剂中含氟硅烷与氢化卵磷脂按照重量比1：1-15：1复合使用。
3.如权利要求1所述的一种疏水疏油化妆品颜料粉末，其包括重量百分比含氟硅烷0.1-10.0％，氢化卵磷脂0.1-10.0％，余量为颜料粉末。
4.如权利要求1所述的一种疏水疏油化妆品颜料粉末，其特征在于：所述的颜料粉末包括为二氧化钛，氧化铁黄，氧化铁红，氧化铁黑，滑石、云母、群青类、氧化铬绿中的一种或者几种的混合物。
5.如权利要求1所述的一种疏水疏油化妆品颜料粉末，其特征在于：所述含氟硅烷的结构为：Rf-(CH2)2-Si-(OCmH2m+1)3，其中，Rf为CnF2n+1，1≤n≤6，n为整数，m为1或2。
6.如权利要求1所述的一种疏水疏油化妆品颜料粉末，其特征在于：所述含氟硅烷为全氟辛基三乙氧基硅烷。
7.如权利要求1所述的一种疏水疏油化妆品颜料粉末，其特征在于：是由下述重量百分比物质构成：
或
或
8.如权利要求1-7任意一项所述的一种疏水疏油化妆品颜料粉末在化妆品中的应用。
9.如权利要求1所述的一种疏水疏油化妆品颜料粉末的制备方法，其特征在于包括如下步骤：
步骤(1)贴肤性处理液的制备：含氟硅烷、氢化卵磷脂溶解于乙醇或多元醇中，配制成处理液；
步骤(2)高速搅拌下，将处理液喷涂颜料粉末表面，混合均匀出料，加热烘干；
步骤(3)气流粉碎成粉体。
10.如权利要求9所述的一种疏水疏油化妆品颜料粉末的制备方法，其特征在于包括如下步骤：
步骤(1)贴肤性处理液的制备：含氟硅烷、氢化卵磷脂2000-20000转/min高速搅拌溶解于1-1.5倍量的乙醇或多元醇中，配制成处理液；
步骤(2)2000-20000转/min高速搅拌下，将处理液喷涂颜料粉末表面，混合均匀出料，100-150℃加热烘干1-5小时；
步骤(3)气流粉碎：采用7～8MPa的高压空气对粉体进行处理，得到的粉体平均粒径0.1-5μm。