CN107457168A - A kind of plank method for paint spraying - Google Patents
A kind of plank method for paint spraying Download PDFInfo
- Publication number
- CN107457168A CN107457168A CN201710730251.9A CN201710730251A CN107457168A CN 107457168 A CN107457168 A CN 107457168A CN 201710730251 A CN201710730251 A CN 201710730251A CN 107457168 A CN107457168 A CN 107457168A
- Authority
- CN
- China
- Prior art keywords
- parts
- plank
- paint
- board surface
- paint spraying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of plank method for paint spraying, it is related to plank processing technique field；Thick polishing and thin polishing are carried out to plank first, then plank is soaked in bactericidal liquid and handled, clear water is dried after cleaning, and in surface spraying layer protecting film, then spray-applied primer, recess is filled and led up with putty, then sprays layer protecting film, last spray paint, is dried；Polishing pretreatment is carried out to plank before spray painting; reach preliminary spray painting to require; plank is dipped in bactericidal liquid and handled; bactericidal action not only is played to plank; make plank not perishable, and plank surface strength can be increased, can further strengthen plank intensity in board surface coating protective film after sterilization and improve the adhesive force of plank and priming paint; diaphragm between priming paint and finish paint can strengthen the adhesive force of priming paint and finish paint, not allow finish paint easy to fall off.
Description
Technical field
The present invention relates to plank processing technique field, and in particular to a kind of plank method for paint spraying.
Background technology
Now with people's living standards continue to improve, particularly in some townie people, to the family of individual
Fill the requirement taste also more and more higher of furniture, wood furniture be also be employed it is most commonly used, but due to wood furniture in itself not
There is the color and vein of uniqueness, generally require to carry out spray painting processing to timber during processing, to reach
Unique color quality, the consumer to win vast like.
Because board surface is not very smooth in present production process, so in the last spray painting process segment, often
It is not unusual flat smooth that board surface, which can often be caused, and it is poor to touch sense, the color effects protruded show it is poor, after use usually
Occur to fall the phenomenon of paint, and the technique painted is more coarse so that Wood surface quality is uneven, influences aesthetic effect.
The content of the invention
(1) technical problem solved
In view of the shortcomings of the prior art, the invention provides a kind of plank method for paint spraying so that board surface spray painting it is smooth,
Smooth, plank intensity is high, good with PASS, it is not easy to falls paint.
(2) technical scheme
To realize object above, the present invention is achieved by the following technical programs：
A kind of plank method for paint spraying, comprises the following steps：
(1) plank of shaping is slightly polished, cleans, dry after thick polishing, then carefully polished, cleaned after polishing,
Drying；
(2) plank after step (1) processing is put into bactericidal liquid and soaks 5-8h, taken out, cleaned with clear water, place into and change
Property liquid in soak 12-15h, take out, cleaned with clear water, it be 4-6% to be dried to water content, board surface coat one layer protect
Film；
(3) board surface after step (2) processing sprays one layer of priming paint, dries, recess is filled and led up with putty；
(4) board surface after step (3) processing coats the diaphragm described in one layer of step (2) again；
(5) the board surface spray paint after step (4) processing, dries.
Preferably, step (2) bactericidal liquid is made up of the raw material of following parts by weight：Blue stone 12-15 parts, black false hellebore 15-25
Part, Cortex hibisus syriacus 15-20 parts, fruit of Rangoon creeper 8-15 parts, lemon tablet 5-15 parts, chrysanthemum 7-10 parts, urea 3-6 parts, potassium chloride 18-28
Part, water 50-65 parts；Its preparation method is：Black false hellebore, Cortex hibisus syriacus, the fruit of Rangoon creeper, chrysanthemum and lemon tablet are mixed, are put into mixture weight
2-3h is soaked in the vinegar of 8-10 times of amount, is rinsed 2-3 times, fed the mixture into water and alcohol mixture, ethanol quality with clear water
Fraction is 35%, and flow back 6-8h at 50-60 DEG C, filtering, collects filtrate, filtrate is concentrated by evaporation into 3h at 90 DEG C, to solution
In sequentially add blue stone, potassium chloride and urea, be well mixed, be made the bactericidal liquid.
Preferably, step (2) modification liquid is made up of the raw material of following parts by weight：Phenolic resin 22-30 parts, asphalt mixtures modified by epoxy resin
Fat 12-18 parts, amylalcohol 40-55 parts, shellac 20-30 parts, rosin 15-25 parts, hydrogen peroxide 6-12 parts；Its preparation method is：In 40-
Phenolic resin and epoxy resin are dissolved in amylalcohol at 55 DEG C, are well mixed, continues to be warming up to 60-70 DEG C, adds shellac and pine
Perfume (or spice), temperature is reduced to 20-25 DEG C after being well mixed, adds hydrogen peroxide and be well mixed, the modification liquid is made.
Preferably, step (2) diaphragm is glass fiber reinforcement density polyethylene film with high.
Preferably, the thickness of the diaphragm is 0.03-0.05mm.
(3) beneficial effect
The invention provides a kind of plank method for paint spraying, its advantage is：Pre- place of polishing is carried out to plank before spray painting
Reason, reach preliminary spray painting and require, plank is dipped in bactericidal liquid and handled, bactericidal action not only is played to plank, is not easy plank
To rot, and plank surface strength can be increased, potassium chloride, urea can not only kill part strain after being dissolved in water in bactericidal liquid, and
And plank top layer can be penetrated into the form of an ion, so as to strengthen plank surface strength, being advantageous to paint and extending plank uses the longevity
Life, it can further strengthen plank intensity in board surface coating protective film after sterilization and improve the adhesive force of plank and priming paint, bottom
Recess coating protective film again, last spray paint are filled and led up with putty after paint spraying, the diaphragm between priming paint and finish paint can increase
The adhesive force of strong priming paint and finish paint, does not allow finish paint easy to fall off.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not making
The every other embodiment obtained under the premise of creative work, belongs to the scope of protection of the invention.
Embodiment 1：
A kind of plank method for paint spraying, comprises the following steps：
(1) plank of shaping is slightly polished, cleans, dry after thick polishing, then carefully polished, cleaned after polishing,
Drying；
(2) plank after step (1) processing is put into bactericidal liquid and soaks 5h, taken out, cleaned with clear water, place into modification
15h is soaked in liquid, takes out, is cleaned with clear water, it is 4% to be dried to water content, and layer protecting film is coated in board surface；
(3) board surface after step (2) processing sprays one layer of priming paint, dries, recess is filled and led up with putty；
(4) board surface after step (3) processing coats the diaphragm described in one layer of step (2) again；
(5) the board surface spray paint after step (4) processing, dries.
Step (2) bactericidal liquid is made up of the raw material of following parts by weight：13 parts of blue stone, 20 parts of black false hellebore, 18 parts of Cortex hibisus syriacus,
8 parts of the fruit of Rangoon creeper, 10 parts of lemon tablet, 7 parts of chrysanthemum, 5 parts of urea, 18 parts of potassium chloride, 65 parts of water；Its preparation method is：By black false hellebore, wood
Rose of Sharon skin, the fruit of Rangoon creeper, chrysanthemum and lemon tablet mixing, are put into the vinegar of 8 times of mixture weight and soak 3h, rinsed 2 times with clear water, will be mixed
Compound is added in water and alcohol mixture, and ethanol mass fraction is 35%, and flow back 6h at 55 DEG C, filtering, is collected filtrate, will be filtered
Liquid is concentrated by evaporation 3h at 90 DEG C, and blue stone, potassium chloride and urea are sequentially added into solution, is well mixed, and the sterilization is made
Liquid.
Step (2) modification liquid is made up of the raw material of following parts by weight：30 parts of phenolic resin, 14 parts of epoxy resin, penta
55 parts of alcohol, 20 parts of shellac, 20 parts of rosin, 6 parts of hydrogen peroxide；Its preparation method is：By phenolic resin and epoxy resin at 55 DEG C
It is dissolved in amylalcohol, is well mixed, continues to be warming up to 60 DEG C, add shellac and rosin, temperature is reduced to 25 DEG C after being well mixed,
Add hydrogen peroxide to be well mixed, the modification liquid is made.
Step (2) diaphragm is glass fiber reinforcement density polyethylene film with high.
The thickness of the diaphragm is 0.03mm.
Embodiment 2：
A kind of plank method for paint spraying, comprises the following steps：
(1) plank of shaping is slightly polished, cleans, dry after thick polishing, then carefully polished, cleaned after polishing,
Drying；
(2) plank after step (1) processing is put into bactericidal liquid and soaks 6h, taken out, cleaned with clear water, place into modification
14h is soaked in liquid, takes out, is cleaned with clear water, it is 5% to be dried to water content, and layer protecting film is coated in board surface；
(3) board surface after step (2) processing sprays one layer of priming paint, dries, recess is filled and led up with putty；
(4) board surface after step (3) processing coats the diaphragm described in one layer of step (2) again；
(5) the board surface spray paint after step (4) processing, dries.
Step (2) bactericidal liquid is made up of the raw material of following parts by weight：15 parts of blue stone, 15 parts of black false hellebore, 20 parts of Cortex hibisus syriacus,
10 parts of the fruit of Rangoon creeper, 15 parts of lemon tablet, 8 parts of chrysanthemum, 6 parts of urea, 21 parts of potassium chloride, 60 parts of water；Its preparation method is：By black false hellebore,
Cortex hibisus syriacus, the fruit of Rangoon creeper, chrysanthemum and lemon tablet mixing, are put into the vinegar of 9 times of mixture weight and soak 3h, rinsed 3 times with clear water, will
Mixture is added in water and alcohol mixture, and ethanol mass fraction is 35%, and flow back 7h at 60 DEG C, filtering, collects filtrate, will
Filtrate is concentrated by evaporation 3h at 90 DEG C, and blue stone, potassium chloride and urea are sequentially added into solution, is well mixed, and is made described and kills
Bacterium solution.
Step (2) modification liquid is made up of the raw material of following parts by weight：28 parts of phenolic resin, 12 parts of epoxy resin, penta
50 parts of alcohol, 25 parts of shellac, 25 parts of rosin, 8 parts of hydrogen peroxide；Its preparation method is：By phenolic resin and epoxy resin at 50 DEG C
It is dissolved in amylalcohol, is well mixed, continues to be warming up to 70 DEG C, add shellac and rosin, temperature is reduced to 25 DEG C after being well mixed,
Add hydrogen peroxide to be well mixed, the modification liquid is made.
Step (2) diaphragm is glass fiber reinforcement density polyethylene film with high.
The thickness of the diaphragm is 0.04mm.
Embodiment 3：
A kind of plank method for paint spraying, comprises the following steps：
(1) plank of shaping is slightly polished, cleans, dry after thick polishing, then carefully polished, cleaned after polishing,
Drying；
(2) plank after step (1) processing is put into bactericidal liquid and soaks 7h, taken out, cleaned with clear water, place into modification
13h is soaked in liquid, takes out, is cleaned with clear water, it is 6% to be dried to water content, and layer protecting film is coated in board surface；
(3) board surface after step (2) processing sprays one layer of priming paint, dries, recess is filled and led up with putty；
(4) board surface after step (3) processing coats the diaphragm described in one layer of step (2) again；
(5) the board surface spray paint after step (4) processing, dries.
Step (2) bactericidal liquid is made up of the raw material of following parts by weight：12 parts of blue stone, 20 parts of black false hellebore, 18 parts of Cortex hibisus syriacus,
12 parts of the fruit of Rangoon creeper, 5 parts of lemon tablet, 9 parts of chrysanthemum, 4 parts of urea, 25 parts of potassium chloride, 55 parts of water；Its preparation method is：By black false hellebore, wood
Rose of Sharon skin, the fruit of Rangoon creeper, chrysanthemum and lemon tablet mixing, are put into the vinegar of 10 times of mixture weight and soak 2h, rinsed 3 times with clear water, will
Mixture is added in water and alcohol mixture, and ethanol mass fraction is 35%, and flow back 8h at 55 DEG C, filtering, collects filtrate, will
Filtrate is concentrated by evaporation 3h at 90 DEG C, and blue stone, potassium chloride and urea are sequentially added into solution, is well mixed, and is made described and kills
Bacterium solution.
Step (2) modification liquid is made up of the raw material of following parts by weight：28 parts of phenolic resin, 16 parts of epoxy resin, penta
45 parts of alcohol, 30 parts of shellac, 20 parts of rosin, 10 parts of hydrogen peroxide；Its preparation method is：By phenolic resin and epoxy resin at 45 DEG C
It is dissolved in amylalcohol, is well mixed, continues to be warming up to 65 DEG C, add shellac and rosin, temperature is reduced to 20 DEG C after being well mixed,
Add hydrogen peroxide to be well mixed, the modification liquid is made.
Step (2) diaphragm is glass fiber reinforcement density polyethylene film with high.
The thickness of the diaphragm is 0.05mm.
Embodiment 4：
A kind of plank method for paint spraying, comprises the following steps：
(1) plank of shaping is slightly polished, cleans, dry after thick polishing, then carefully polished, cleaned after polishing,
Drying；
(2) plank after step (1) processing is put into bactericidal liquid and soaks 8h, taken out, cleaned with clear water, place into modification
12h is soaked in liquid, takes out, is cleaned with clear water, it is 5% to be dried to water content, and layer protecting film is coated in board surface；
(3) board surface after step (2) processing sprays one layer of priming paint, dries, recess is filled and led up with putty；
(4) board surface after step (3) processing coats the diaphragm described in one layer of step (2) again；
(5) the board surface spray paint after step (4) processing, dries.
Step (2) bactericidal liquid is made up of the raw material of following parts by weight：14 parts of blue stone, 25 parts of black false hellebore, 15 parts of Cortex hibisus syriacus,
15 parts of the fruit of Rangoon creeper, 10 parts of lemon tablet, 10 parts of chrysanthemum, 3 parts of urea, 28 parts of potassium chloride, 50 parts of water；Its preparation method is：By black false hellebore,
Cortex hibisus syriacus, the fruit of Rangoon creeper, chrysanthemum and lemon tablet mixing, are put into the vinegar of 8 times of mixture weight and soak 2h, rinsed 2 times with clear water, will
Mixture is added in water and alcohol mixture, and ethanol mass fraction is 35%, and flow back 6h at 50 DEG C, filtering, collects filtrate, will
Filtrate is concentrated by evaporation 3h at 90 DEG C, and blue stone, potassium chloride and urea are sequentially added into solution, is well mixed, and is made described and kills
Bacterium solution.
Step (2) modification liquid is made up of the raw material of following parts by weight：22 parts of phenolic resin, 18 parts of epoxy resin, penta
40 parts of alcohol, 25 parts of shellac, 15 parts of rosin, 12 parts of hydrogen peroxide；Its preparation method is：By phenolic resin and epoxy resin at 40 DEG C
It is dissolved in amylalcohol, is well mixed, continues to be warming up to 65 DEG C, add shellac and rosin, temperature is reduced to 20 DEG C after being well mixed,
Add hydrogen peroxide to be well mixed, the modification liquid is made.
Step (2) diaphragm is glass fiber reinforcement density polyethylene film with high.
The thickness of the diaphragm is 0.04mm.
In order to verify the effect of method for paint spraying of the present invention, China fir plank is chosen, spray painting plank prepared by the present invention is carried out
Properties detect, as a comparison, spray painting plank prepared by lacquer spraying technique disclosed in Chinese patent CN201510800354.9
As a control group, same test is done with present invention spray painting plank, it is as a result as follows：
From above table, plank prepared by method for paint spraying of the present invention has a more smooth flatness, higher intensity,
Paint is not easy to peel off from board surface, so as to which the plank service life after painting extends.
It should be noted that herein, such as first and second or the like relational terms are used merely to a reality
Body or operation make a distinction with another entity or operation, and not necessarily require or imply and deposited between these entities or operation
In any this actual relation or order.Moreover, term " comprising ", "comprising" or its any other variant are intended to
Nonexcludability includes, so that process, method, article or equipment including a series of elements not only will including those
Element, but also the other element including being not expressly set out, or it is this process, method, article or equipment also to include
Intrinsic key element.In the absence of more restrictions, the key element limited by sentence "including a ...", it is not excluded that
Other identical element also be present in process, method, article or equipment including the key element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those within the art that：It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic；And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (5)
1. a kind of plank method for paint spraying, it is characterised in that comprise the following steps：
(1) plank of shaping is slightly polished, cleans, dry after thick polishing, then carefully polished, cleaned, dry after polishing；
(2) plank after step (1) processing is put into bactericidal liquid and soaks 5-8h, taken out, cleaned with clear water, place into modification liquid
Middle immersion 12-15h, take out, cleaned with clear water, it is 4-6% to be dried to water content, and layer protecting film is coated in board surface；
(3) board surface after step (2) processing sprays one layer of priming paint, dries, recess is filled and led up with putty；
(4) board surface after step (3) processing coats the diaphragm described in one layer of step (2) again；
(5) the board surface spray paint after step (4) processing, dries.
2. plank method for paint spraying as claimed in claim 1, it is characterised in that step (2) bactericidal liquid is by following parts by weight
Raw material composition：Blue stone 12-15 parts, black false hellebore 15-25 parts, Cortex hibisus syriacus 15-20 parts, fruit of Rangoon creeper 8-15 parts, lemon tablet 5-15 parts, chrysanthemum
Flower 7-10 parts, urea 3-6 parts, potassium chloride 18-28 parts, water 50-65 parts；Its preparation method is：By black false hellebore, Cortex hibisus syriacus, the fruit of Rangoon creeper,
Chrysanthemum and lemon tablet mixing, are put into the vinegar of 8-10 times of mixture weight and soak 2-3h, rinsed 2-3 times with clear water, by mixture
Add in water and alcohol mixture, ethanol mass fraction is 35%, and flow back 6-8h at 50-60 DEG C, filtering, collects filtrate, will
Filtrate is concentrated by evaporation 3h at 90 DEG C, and blue stone, potassium chloride and urea are sequentially added into solution, is well mixed, and is made described and kills
Bacterium solution.
3. plank method for paint spraying as claimed in claim 1, it is characterised in that step (2) modification liquid is by following parts by weight
Raw material composition：Phenolic resin 22-30 parts, epoxy resin 12-18 parts, amylalcohol 40-55 parts, shellac 20-30 parts, rosin 15-25
Part, hydrogen peroxide 6-12 parts；Its preparation method is：Phenolic resin and epoxy resin are dissolved in amylalcohol at 40-55 DEG C, mixing is equal
It is even, continue to be warming up to 60-70 DEG C, add shellac and rosin, temperature is reduced to 20-25 DEG C after being well mixed, add hydrogen peroxide
It is well mixed, the modification liquid is made.
4. plank method for paint spraying as claimed in claim 1, it is characterised in that step (2) diaphragm increases for glass fibre
Strong density polyethylene film with high.
5. the plank method for paint spraying described in claim 4, it is characterised in that the thickness of the diaphragm is 0.03-0.05mm.