CN107009446A - The manufacture method of wood skin paper - Google Patents

The manufacture method of wood skin paper Download PDF

Info

Publication number
CN107009446A
CN107009446A CN201710295096.2A CN201710295096A CN107009446A CN 107009446 A CN107009446 A CN 107009446A CN 201710295096 A CN201710295096 A CN 201710295096A CN 107009446 A CN107009446 A CN 107009446A
Authority
CN
China
Prior art keywords
wood skin
manufacture method
paper
finished product
wood
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710295096.2A
Other languages
Chinese (zh)
Inventor
刘建文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGZHOU JIASHIJIA DECORATIVE NEW MATERIAL Co Ltd
Original Assignee
CHANGZHOU JIASHIJIA DECORATIVE NEW MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU JIASHIJIA DECORATIVE NEW MATERIAL Co Ltd filed Critical CHANGZHOU JIASHIJIA DECORATIVE NEW MATERIAL Co Ltd
Priority to CN201710295096.2A priority Critical patent/CN107009446A/en
Publication of CN107009446A publication Critical patent/CN107009446A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of manufacture method of wood skin paper, the step of method is included is as follows：(a) wood skin after processing is spliced into by wood skin ground paper product according to splicing instruction figure；(b) wood skin ground paper product are impregnated into resin, make resin uniformly penetrating into wood skin ground paper product, form the first semi-finished product；(c) by the first semi-finished product drying process, the second semi-finished product are formed；(d) the second semi-finished product are sheared, complies with required size, obtain finished product wood skin paper.The present invention can not only make sheet material keep wood surface striped, save lumber consumption, and the wood skin paper of finished product can be made durable in use, and wear-resisting intensity is high.

Description

The manufacture method of wood skin paper
Technical field
The present invention relates to a kind of manufacture method of wood skin paper.
Background technology
At present, the domestic production technology of solid wood decorative material has two kinds：One kind is full solid wood board；Two be that solid wood thin skin is overlayed On medium-density plate or particieboard, painting；Wherein first method timber consumes big, and second of production technology is more multiple It is miscellaneous, and easily have the phenomenon that wood grain is collapsed due to the native texture characteristic of wood skin after paint.
The content of the invention
The technical problems to be solved by the invention are to overcome the defect of prior art there is provided a kind of manufacturer of wood skin paper Method, it can not only make sheet material keep wood surface striped, save lumber consumption, and the wood skin paper of finished product can be made prolonged resistance to With wear-resisting intensity is high.
In order to solve the above-mentioned technical problem, the technical scheme is that：A kind of manufacture method of wood skin paper, method is included The step of it is as follows：
(a) wood skin after processing is spliced into by wood skin ground paper product according to splicing instruction figure；
(b) wood skin ground paper product are impregnated into resin, make resin uniformly penetrating into wood skin ground paper product, formed the first half into Product；
(c) by the first semi-finished product drying process, the second semi-finished product are formed；
(d) the second semi-finished product are sheared, complies with required size, obtain finished product wood skin paper.
Further, the step (a) is specially：
(a1) the rigid wood skin being collected into is immersed in the container equipped with wood skin softening agent and carries out sofening treatment；Wherein, The temperature control of sofening treatment is at 56 DEG C~65 DEG C, and keeping temperature 5~8 hours；
(a2) the rigid wood skin after sofening treatment is subjected to drying and processing；
(a3) the rigid wood skin after drying is cold-pressed and shaped；
(a4) the rigid wood skin being cold-pressed after sizing is cut and spliced according to splicing instruction figure, obtain wood skin ground paper Product.
Further, the component and each component mass percent that the wood skin softening agent contains are as follows：70%-80% poly- second Glycol, 10%~15% glacial acetic acid, 3%-4% anionics bleeding agent, surplus are deionized water, amount to 100%.
It it is 90 DEG C~95 DEG C further for the drying temperature realized well in drying, the step (a2), during drying Between be 16min~20min.
Further, in the step (a3), sizing pressure is 5~7MPa, and shaping time is 8~11 hours.
Further, also there is step (ab) between the step (a) and the step (b)：Wood skin ground paper product are carried out Then the good wood skin ground paper product of bleaching are carried out dyeing processing by bleaching.
Further, the bleaching temperature is 90 DEG C~100 DEG C, and bleaching time is 1~1.5 hour；The dyeing temperature is 105 DEG C~110 DEG C, dyeing time is 5~6 hours.
Further, in the step (b), resin is melmac.
Further, in the step (c), in drying process, first under 92 DEG C~100 DEG C of environment temperature, 70 are dried ~80min；Again under 125 DEG C~130 DEG C of environment temperature, 70~80min is dried.
Employ after above-mentioned technical proposal, the present invention has following beneficial effect：
(1) woodgrained paper that the present invention replaces printing out using natural veneer, gives pure natural and naturally pure and fresh sensation；
(2) present invention improves its scratch-resistant, corrosion-resistant and anti abrasive performance using resin dipping；
(3) present invention makes it pass through sofening treatment, its is wooden softer, spliced during splice plate mulberry paper Cheng Zhong, splicing more facilitates, and splicing effect is good, makes follow-up heat pressing process, has prevented the phenomenon that wood skin paper is cracked.
Embodiment
In order that present disclosure is easier to be clearly understood, below according to specific embodiment, the present invention is made into One step is described in detail.
Embodiment one
A kind of manufacture method of wood skin paper, the step of method is included is as follows：
(a) wood skin after processing is spliced into by wood skin ground paper product according to splicing instruction figure；
(b) wood skin ground paper product are impregnated into resin, make resin uniformly penetrating into wood skin ground paper product, formed the first half into Product；
(c) by the first semi-finished product drying process, the second semi-finished product are formed；
(d) the second semi-finished product are sheared, complies with required size, obtain finished product wood skin paper.
The step (a) is specially：
(a1) the rigid wood skin being collected into is immersed in the container equipped with wood skin softening agent and carries out sofening treatment；Wherein, The temperature control of sofening treatment is at 56 DEG C, and keeping temperature 5 hours；
(a2) the rigid wood skin after sofening treatment is subjected to drying and processing；
(a3) the rigid wood skin after drying is cold-pressed and shaped；
(a4) the rigid wood skin being cold-pressed after sizing is cut and spliced according to splicing instruction figure, obtain wood skin ground paper Product.
The component and each component mass percent that the wood skin softening agent contains are as follows：70% polyethylene glycol, 10% Glacial acetic acid, 3% anionic bleeding agent, surplus are deionized water.
Drying temperature in the step (a2) is 90 DEG C, and drying time is 16min.
In the step (a3), sizing pressure is 5MPa, and shaping time is 8 hours.
Also there is step (ab) between the step (a) and the step (b)：Wood skin ground paper product are carried out at bleaching Then the good wood skin ground paper product of bleaching are carried out dyeing processing by reason.
The bleaching temperature is 90 DEG C, and bleaching time is 1 hour；The dyeing temperature is 105 DEG C, and dyeing time is 5 small When.
In the step (b), resin is melmac.
In the step (c), in drying process, first under 92 DEG C of environment temperature, 70min is dried；Again at 125 DEG C Under environment temperature, 70min is dried.
Embodiment two
The step of the present embodiment method, is substantially identical with embodiment one, unlike：In step (a1), sofening treatment Temperature control is at 65 DEG C, and keeping temperature 8 hours；The component and each component mass percent that the wood skin softening agent contains are such as Under：80% polyethylene glycol, 15% glacial acetic acid, 4% anionic bleeding agent, surplus are deionized water.The step (a2) drying temperature in is 95 DEG C, and drying time is 20min.
In the step (a3), sizing pressure is 7MPa, and shaping time is 11 hours.
The bleaching temperature is 100 DEG C, and bleaching time is 1.5 hours；The dyeing temperature is 110 DEG C, and dyeing time is 6 Hour.
In the step (c), in drying process, first under 100 DEG C of environment temperature, 80min is dried；Again at 130 DEG C Environment temperature under, dry 80min.
Embodiment three
The step of the present embodiment method, is substantially identical with embodiment one, unlike：In step (a1), sofening treatment Temperature control is at 62 DEG C, and keeping temperature 7 hours；The component and each component mass percent that the wood skin softening agent contains are such as Under：75% polyethylene glycol, 13% glacial acetic acid, 3% anionic bleeding agent, surplus are deionized water, amount to 100%. Drying temperature in the step (a2) is 93 DEG C, and drying time is 18min.
In the step (a3), sizing pressure is 6MPa, and shaping time is 10 hours.
The bleaching temperature is 95 DEG C, and bleaching time is 1.3 hours；The dyeing temperature is 108 DEG C, and dyeing time is 5 Hour.
In the step (c), in drying process, first under 96 DEG C of environment temperature, 75min is dried；Again at 127 DEG C Under environment temperature, 75min is dried.
Wood skin paper prepared by three above embodiment is attached on sheet material, and sheet material can not only be made to keep wood surface striped, Lumber consumption is saved, and the wood skin paper of finished product can be made durable in use, wear-resisting intensity is high.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effect carry out It is further described, should be understood that the specific embodiment that the foregoing is only the present invention, is not limited to this Invention, within the spirit and principles of the invention, any modification, equivalent substitution and improvements done etc. should be included in this hair Within bright protection domain.

Claims (9)

1. a kind of manufacture method of wood skin paper, it is characterised in that the step of method is included is as follows：
(a) wood skin after processing is spliced into by wood skin ground paper product according to splicing instruction figure；
(b) wood skin ground paper product are impregnated into resin, make resin uniformly penetrating into wood skin ground paper product, form the first semi-finished product；
(c) by the first semi-finished product drying process, the second semi-finished product are formed；
(d) the second semi-finished product are sheared, complies with required size, obtain finished product wood skin paper.
2. the manufacture method of wood skin paper according to claim 1, it is characterised in that：The step (a) is specially：
(a1) the rigid wood skin being collected into is immersed in the container equipped with wood skin softening agent and carries out sofening treatment；Wherein, soften The temperature control of processing is at 56 DEG C~65 DEG C, and keeping temperature 5~8 hours；
(a2) the rigid wood skin after sofening treatment is subjected to drying and processing；
(a3) the rigid wood skin after drying is cold-pressed and shaped；
(a4) the rigid wood skin being cold-pressed after sizing is cut and spliced according to splicing instruction figure, obtain wood skin ground paper product.
3. the manufacture method of wood skin paper according to claim 2, it is characterised in that：It is described in described step (a1) The component and each component mass percent that wood skin softening agent contains are as follows：70%-80% polyethylene glycol, 10%~15% ice Acetic acid, 3%-4% anionic bleeding agent, surplus are deionized water, amount to 100%.
4. the manufacture method of wood skin paper according to claim 2, it is characterised in that：Drying temperature in the step (a2) For 90 DEG C~95 DEG C, drying time is 16min~20min.
5. the manufacture method of wood skin paper according to claim 2, it is characterised in that：In the step (a3), sizing pressure Power is 5~7MPa, and shaping time is 8~11 hours.
6. the manufacture method of wood skin paper according to claim 1, it is characterised in that：In the step (a) and the step (b) also there is step (ab) between：Wood skin ground paper product are subjected to bleaching, then entered the good wood skin ground paper product of bleaching Row dyeing is handled.
7. the manufacture method of wood skin paper according to claim 6, it is characterised in that：The bleaching temperature is 90 DEG C~100 DEG C, bleaching time is 1~1.5 hour；The dyeing temperature is 105 DEG C~110 DEG C, and dyeing time is 5~6 hours.
8. the manufacture method of wood skin paper according to claim 1, it is characterised in that：In the step (b), resin is three Cymel.
9. the manufacture method of wood skin paper according to claim 1, it is characterised in that：In the step (c), drying process In, first under 92 DEG C~100 DEG C of environment temperature, dry 70~80min；Again under 125 DEG C~130 DEG C of environment temperature, do Dry 70~80min.
CN201710295096.2A 2017-04-28 2017-04-28 The manufacture method of wood skin paper Pending CN107009446A (en)