CN105965642A - Machining process of hard veneers - Google Patents
Machining process of hard veneers Download PDFInfo
- Publication number
- CN105965642A CN105965642A CN201610569256.3A CN201610569256A CN105965642A CN 105965642 A CN105965642 A CN 105965642A CN 201610569256 A CN201610569256 A CN 201610569256A CN 105965642 A CN105965642 A CN 105965642A
- Authority
- CN
- China
- Prior art keywords
- veneer
- rigid
- hot pressing
- rigid veneer
- lagging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a machining process of hard veneers. After the hard veneers are softened and dried, wood becomes soft, so that veneer splicing machining is smoother and the splicing effect is better in veneer splicing and hotly pressing veneer laminating processes; in the hotly pressing veneer laminating process, a phenomenon that the veneers are foamed can be effectively avoided; an obtained veneer laminated product is subjected to fine machining including paint spraying, fabric process, package and the like to prepare a veneer laminated furniture product; and in a utilization period of positive and negative temperature difference, phenomena that the veneers are cracked and paint is delaminated can be effectively avoided.
Description
Technical field
The present invention relates to sheet fabrication field, particularly relate to the processing work of a kind of rigid veneer
Skill.
Background technology
The products such as existing stick-skin furniture are typically with wood and/or sheet material base as an alternative
Material, determines step routinely by replacement base material, method makes semi-finished product through preliminary working.Become half
The outer surface of product, inner surface stick natural veneer thus make lagging semi-finished product.Lagging semi-finished product
Successively through polish such as spray paint, cloth art, packagings thus make stick-skin furniture finished product.Select
The veneer of unlike material, i.e. can be made into all kinds of lagging product.Rigid veneer is (such as Flos persicae core crotch
Veneer, Caulis et Folium Hyptidis suaveolentis fruit tree tumor veneer, brazilic acid branch veneer and Huanghua Pear veneer etc.) due to wooden relatively
Hard reason, if directly carrying out lagging without processing, has been susceptible to during lagging
Bubble phenomenon, and in machining the use cycle after dispatching from the factory, affected by the temperature difference, may also can
Veneer be full of cracks and the phenomenon of paint delamination occur, and the quality of product cannot ensure.
Summary of the invention
It is an object of the invention to provide the processing technique of a kind of rigid veneer, the most only effectively keep away
Exempt to spell the generation of foaming phenomena during skin, lagging, also efficiently avoid follow-up use process
The be full of cracks of middle veneer, the generation of paint delamination.
In order to reach above-mentioned purpose, the solution of the present invention is:
A kind of processing technique of rigid veneer, including following technical process:
(1) sofening treatment: rigid veneer is soaked in the container equipped with softening liquid medicine 2-5
Min carries out sofening treatment, and the rigid veneer thin film parcel after immersion is placed on shady place and deposits
More than 24h, described thin film offers multiple air-vent；
(2) drying and processing: the rigid veneer after sofening treatment is placed on hot press and carries out
Drying, hot pressing temperature controls more than 100 DEG C, and hot pressing pressure is 6-8MPa, drying time
For 5-15min so that the moisture content of rigid veneer is below 15%；
(3) cold pressing sizing: the rigid veneer after drying is transferred to shape on cold press,
Sizing pressure is 8-12MPa, and shaping time is 12-24h；
(4) skin process is spelled: carry out cutting, splicing by the rigid veneer after sizing according to drawing,
Spell rigid veneer to be wrapped up with thin film after skin completes and deposit in shady place, or complete spelling skin
After 4h in directly carry out hot pressing lagging process；
(5) hot pressing lagging: the rigid veneer of step (4) gained is placed on sheet material and scribbles glue
In the one side of water, carrying out hot pressing in hot press, hot pressing temperature is 85-100 DEG C, hot pressing pressure
Power is 8-12MPa, and hot pressing time is 3-8min, completes hot pressing, obtains lagging product,
The moisture content of lagging product is 8-10%.
In step (1), the raw material of described softening liquid medicine includes thin slice sealing compound: water=2～4:1
Weight ratio ingredient.
In step (2), in drying course, hot press need to be carried out repeatedly blood pressure lowering in order to arrange
Discharge water point.
In step (4), when splicing rigid veneer, first spell skin machine rigid with hot melt tree lace
Tree lace is spelled at the back side of veneer, and then the edge joint position in the front of rigid veneer sticks glue paper, from
And guarantee that the piece of rigid veneer is the most firm.
In step (5), in hot pressing, for moisture content before hot pressing more than 12%
Rigid veneer and sheet material, control hot pressing temperature at 100 DEG C, and hot pressing time controls at 5-8min,
Thus ensure that the moisture content of lagging product is less than 10%.
The processing technique of a kind of rigid veneer of the present invention, has the advantages that
(1) rigid veneer is through sofening treatment, its wooden deliquescing, is spelling skin and hot pressing lagging
During, to spell skin and process more smooth and easy, splicing effect is more preferable, can effectively shut out during hot pressing lagging
The generation of veneer foaming phenomena absolutely；
(2) the lagging product obtained through polish such as spray paint, cloth art, packagings thus is made
Become stick-skin furniture finished product, within the use cycle of the positive and negative temperature difference, veneer be full of cracks can be effectively prevented from
And the phenomenon of paint delamination.
Therefore, the processing technique of a kind of rigid veneer of the present invention, not only be effectively prevented from spell skin,
The generation of foaming phenomena during lagging, also efficiently avoid veneer Testudinis during follow-up use
Split, paint the generation of delamination.
In step (2), in drying course, rigid veneer is applied certain pressure, can
To prevent rigid veneer from veneer be full of cracks or the phenomenon of gross distortion occurring in drying course.
In step (2), in drying course, hot press need to be carried out repeatedly blood pressure lowering discharge water
Part, could preferably rigid veneer be dried, the moisture content accumulated in preventing hot press cannot
Discharge, the moisture content of rigid veneer is produced impact.
Detailed description of the invention
In order to technical scheme is explained further, come this below by specific embodiment
Invention is described in detail.
Embodiment one
A kind of processing technique of rigid veneer, including following technical process:
(1) sofening treatment:
1. by thin slice sealing compound: the weight ratio ingredient of water=2:1 joins in cell therefor,
Allotment softens liquid medicine, and thin slice sealing compound is that akzonobel company produces；
Every rigid veneer is soaked in the container equipped with softening liquid medicine 2min the most successively carry out
Sofening treatment；
3. the rigid veneer thin film parcel after soaking is placed on shady place and deposits more than 24h,
Multiple air-vent is offered so that the softening liquid medicine remaining in rigid veneer is slowly waved on thin film
Send out.
(2) drying and processing:
Rigid veneer after sofening treatment is neatly placed on hot press and dries, hot pressing temperature
Degree controls more than 100 DEG C, and hot pressing pressure is 8MPa, and drying time is 10min,
In drying course, hot press need to be carried out repeatedly blood pressure lowering discharge moisture, could be preferably to rigid
Veneer is dried so that the moisture content of rigid veneer is below 15%.
(3) cold pressing sizing: the rigid veneer after drying puts 15 lis of thick clamping plate of polylith
Between, all it is placed with the rigid veneer of equal number between clamping plate and clamping plate, between every piece of clamping plate
The rigid veneer quantity put is that 4-8 opens, and moves again to shape on cold press, sizing pressure
Power is 8MPa, and shaping time is 12h.
Rigid veneer quantity between clamping plate is identical, and the rigid veneer of guarantee is in type-approval process
Pressure identical, it is ensured that patterning process every veneer out is the most smooth without damaged.
(4) skin process is spelled: carry out cutting, splicing by the rigid veneer after sizing according to drawing,
When splicing rigid veneer, first spell skin machine with hot melt tree lace and spell tree lace at the back side of rigid veneer,
Then the artificial edge joint position in the front of rigid veneer sticks glue paper, it is ensured that the spelling of rigid veneer
Seam is tight firmly, spell with thin film rigid veneer wrapped up after skin completes deposit in shady place or
Directly carry out hot pressing lagging process in 4h after spelling skin and completing, stop the piece of rigid veneer
Cracking or occur that the surface of rigid veneer is uneven whole phenomenon.
(5) hot pressing lagging: the rigid veneer of step (4) gained is placed on sheet material and scribbles glue
In the one side of water, carrying out hot pressing in hot press, hot pressing temperature is 85-100 DEG C, hot pressing pressure
Power is 8MPa, and hot pressing time is that 3-8min, hot pressing temperature and hot pressing time are according to rigid wood
Moisture content before skin and sheet material hot pressing determines, completes hot pressing, just obtains lagging product, patch
The moisture content of skin product is 8-10%.
In hot pressing, for the moisture content rigid veneer more than 12% and sheet material, by heat
Pressure temperature controls at 100 DEG C, and hot pressing time controls at 5-8min, thus ensures lagging product
Moisture content is less than 10%.
Embodiment two
A kind of processing technique of rigid veneer, including following technical process:
(1) sofening treatment:
1. by thin slice sealing compound: the weight ratio ingredient of water=4:1 joins in cell therefor,
Allotment softens liquid medicine, and thin slice sealing compound is that akzonobel company produces；
Every rigid veneer is soaked in the container equipped with softening liquid medicine 5min the most successively carry out
Sofening treatment；
3. the rigid veneer thin film parcel after soaking is placed on shady place and deposits more than 24h,
Multiple air-vent is offered so that the softening liquid medicine remaining in rigid veneer is slowly waved on thin film
Send out.
(2) drying and processing:
Rigid veneer after sofening treatment is neatly placed on hot press and dries, hot pressing temperature
Degree controls more than 100 DEG C, and hot pressing pressure is 6MPa, and drying time is 15min,
In drying course, hot press need to be carried out repeatedly blood pressure lowering discharge moisture, could be preferably to rigid
Veneer is dried so that the moisture content of rigid veneer is below 15%.
(3) cold pressing sizing: the rigid veneer after drying puts 15 lis of thick clamping plate of polylith
Between, all it is placed with the rigid veneer of equal number between clamping plate and clamping plate, between every piece of clamping plate
The rigid veneer quantity put is that 4-8 opens, and moves again to shape on cold press, sizing pressure
Power is 10MPa, and shaping time is 24h.
Rigid veneer quantity between clamping plate is identical, and the rigid veneer of guarantee is in type-approval process
Pressure identical, it is ensured that patterning process every veneer out is the most smooth without damaged.
(4) skin process is spelled: carry out cutting, splicing by the rigid veneer after sizing according to drawing,
When splicing rigid veneer, first spell skin machine with hot melt tree lace and spell tree lace at the back side of rigid veneer,
Then the artificial edge joint position in the front of rigid veneer sticks glue paper, it is ensured that the spelling of rigid veneer
Seam is tight firmly, spell with thin film rigid veneer wrapped up after skin completes deposit in shady place or
Directly carry out hot pressing lagging process in 4h after spelling skin and completing, stop the piece of rigid veneer
Cracking or occur that the surface of rigid veneer is uneven whole phenomenon.
(5) hot pressing lagging: the rigid veneer of step (4) gained is placed on sheet material and scribbles glue
In the one side of water, carrying out hot pressing in hot press, hot pressing temperature is 85-100 DEG C, hot pressing pressure
Power is 10MPa, and hot pressing time is that 3-8min, hot pressing temperature and hot pressing time are according to rigid wood
Moisture content before skin and sheet material hot pressing determines, completes hot pressing, just obtains lagging product, patch
The moisture content of skin product is 8-10%.
In hot pressing, for the moisture content rigid veneer more than 12% and sheet material, by heat
Pressure temperature controls at 100 DEG C, and hot pressing time controls at 5-8min, thus ensures lagging product
Moisture content is less than 10%.
Embodiment three
A kind of processing technique of rigid veneer, including following technical process:
(1) sofening treatment:
1. by thin slice sealing compound: the weight ratio ingredient of water=2:1 joins in cell therefor,
Allotment softens liquid medicine, and thin slice sealing compound is that akzonobel company produces；
Every rigid veneer is soaked in the container equipped with softening liquid medicine 3min the most successively carry out
Sofening treatment；
3. the rigid veneer thin film parcel after soaking is placed on shady place and deposits more than 24h,
Multiple air-vent is offered so that the softening liquid medicine remaining in rigid veneer is slowly waved on thin film
Send out.
(2) drying and processing:
Rigid veneer after sofening treatment is neatly placed on hot press and dries, hot pressing temperature
Degree controls more than 100 DEG C, and hot pressing pressure is 8MPa, and drying time is 5min, is drying
During Gan, hot press need to be carried out repeatedly blood pressure lowering discharge moisture, could be preferably to rigid wood
Skin is dried so that the moisture content of rigid veneer is below 15%.
(3) cold pressing sizing: the rigid veneer after drying puts 15 lis of thick clamping plate of polylith
Between, all it is placed with the rigid veneer of equal number between clamping plate and clamping plate, between every piece of clamping plate
The rigid veneer quantity put is that 4-8 opens, and moves again to shape on cold press, sizing pressure
Power is 12MPa, and shaping time is 20h.
Rigid veneer quantity between clamping plate is identical, and the rigid veneer of guarantee is in type-approval process
Pressure identical, it is ensured that patterning process every veneer out is the most smooth without damaged.
(4) skin process is spelled: carry out cutting, splicing by the rigid veneer after sizing according to drawing,
When splicing rigid veneer, first spell skin machine with hot melt tree lace and spell tree lace at the back side of rigid veneer,
Then the artificial edge joint position in the front of rigid veneer sticks glue paper, it is ensured that the spelling of rigid veneer
Seam is tight firmly, spell with thin film rigid veneer wrapped up after skin completes deposit in shady place or
Directly carry out hot pressing lagging process in 4h after spelling skin and completing, stop the piece of rigid veneer
Cracking or occur that the surface of rigid veneer is uneven whole phenomenon.
(5) hot pressing lagging: the rigid veneer of step (4) gained is placed on sheet material and scribbles glue
In the one side of water, carrying out hot pressing in hot press, hot pressing temperature is 85-100 DEG C, hot pressing pressure
Power is 12MPa, and hot pressing time is that 3-8min, hot pressing temperature and hot pressing time are according to rigid wood
Moisture content before skin and sheet material hot pressing determines, completes hot pressing, just obtains lagging product, patch
The moisture content of skin product is 8-10%.
In hot pressing, for the moisture content rigid veneer more than 12% and sheet material, by heat
Pressure temperature controls at 100 DEG C, and hot pressing time controls at 5-8min, thus ensures lagging product
Moisture content is less than 10%.
The processing technique of a kind of rigid veneer of the present invention, has the advantages that
(1) rigid veneer is through sofening treatment, its wooden deliquescing, is spelling skin and hot pressing lagging
During, to spell skin and process more smooth and easy, splicing effect is more preferable, can effectively shut out during hot pressing lagging
The generation of veneer foaming phenomena absolutely；
(2) the lagging product obtained through polish such as spray paint, cloth art, packagings thus is made
Become stick-skin furniture finished product, within the use cycle of the positive and negative temperature difference, veneer be full of cracks can be effectively prevented from
And the phenomenon of paint delamination.
Therefore, the processing technique of a kind of rigid veneer of the present invention, not only be effectively prevented from spell skin,
The generation of foaming phenomena during lagging, also efficiently avoid veneer Testudinis during follow-up use
Split, paint the generation of delamination.
Above-described embodiment the product form of the non-limiting present invention and style, any belonging to technology neck
The those of ordinary skill in territory is suitably changed what it did or modifies, and all should be regarded as without departing from this
Bright patent category.
Claims (5)
1. the processing technique of a rigid veneer, it is characterised in that: include following technical process:
(1) sofening treatment: rigid veneer is soaked in the container equipped with softening liquid medicine 2-5
Min carries out sofening treatment, and the rigid veneer thin film parcel after immersion is placed on shady place and deposits
More than 24h, described thin film offers multiple air-vent；
(2) drying and processing: the rigid veneer after sofening treatment is placed on hot press and carries out
Drying, hot pressing temperature controls more than 100 DEG C, and hot pressing pressure is 6-8MPa, drying time
For 5-15min so that the moisture content of rigid veneer is below 15%；
(3) cold pressing sizing: the rigid veneer after drying is transferred to shape on cold press,
Sizing pressure is 8-12MPa, and shaping time is 12-24h；
(4) skin process is spelled: carry out cutting, splicing by the rigid veneer after sizing according to drawing,
Spell rigid veneer to be wrapped up with thin film after skin completes and deposit in shady place or complete spelling skin
After 4h in directly carry out hot pressing lagging process；
(5) hot pressing lagging: the rigid veneer of step (4) gained is placed on sheet material and scribbles glue
In the one side of water, carrying out hot pressing in hot press, hot pressing temperature is 85-100 DEG C, hot pressing pressure
Power is 8-12MPa, and hot pressing time is 3-8min, completes hot pressing, obtains lagging product,
The moisture content of lagging product is 8-10%.
The processing technique of a kind of rigid veneer the most according to claim 1, its feature exists
In: in step (1), the raw material of described softening liquid medicine includes thin slice sealing compound: water=2～4:1
Weight ratio ingredient.
The processing technique of a kind of rigid veneer the most according to claim 1, its feature exists
In: in step (2), in drying course, hot press need to be carried out repeatedly blood pressure lowering in order to arrange
Discharge water point.
The processing technique of a kind of rigid veneer the most according to claim 1, its feature exists
In: in step (4), when splicing rigid veneer, first spell skin machine rigid with hot melt tree lace
Tree lace is spelled at the back side of veneer, and then the edge joint position in the front of rigid veneer sticks glue paper, from
And guarantee that the piece of rigid veneer is the most firm.
The processing technique of a kind of rigid veneer the most according to claim 1, its feature exists
In: in step (5), in hot pressing, for moisture content before hot pressing more than 12%
Rigid veneer and sheet material, control hot pressing temperature at 100 DEG C, and hot pressing time controls at 5-8min,
Thus ensure that the moisture content of lagging product is less than 10%.