CN107009445A - The manufacture method of melamine solid wood dermatotome - Google Patents
The manufacture method of melamine solid wood dermatotome Download PDFInfo
- Publication number
- CN107009445A CN107009445A CN201710294267.XA CN201710294267A CN107009445A CN 107009445 A CN107009445 A CN 107009445A CN 201710294267 A CN201710294267 A CN 201710294267A CN 107009445 A CN107009445 A CN 107009445A
- Authority
- CN
- China
- Prior art keywords
- wood skin
- wood
- paper
- manufacture method
- finished product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of manufacture method of melamine solid wood dermatotome, it is characterised in that the step of method is included is as follows：Wood skin paper is first manufactured, wood skin paper is then heated into pressurizing attaching to base material using hot press, melamine plate solid wood dermatotome is obtained；Wherein, the technique of manufacture wood skin paper is as follows：(a) wood skin after processing is spliced into by wood skin ground paper product according to splicing instruction figure；(b) wood skin ground paper product are impregnated into melmac, make melmac uniformly penetrating into wood skin ground paper product, form the first semi-finished product；(c) by the first semi-finished product drying process, the second semi-finished product are formed；(d) the second semi-finished product are sheared, complies with required size, obtain finished product wood skin paper.The present invention can not only make sheet material keep wood surface striped, save lumber consumption, and the melamine solid wood dermatotome of finished product can be made durable in use, and wear-resisting intensity is high.
Description
Technical field
The present invention relates to a kind of manufacture method of melamine solid wood dermatotome.
Background technology
At present, the domestic production technology of solid wood decorative material has two kinds：One kind is full solid wood board；Two be that solid wood thin skin is overlayed
On medium-density plate or particieboard, painting；Wherein first method timber consumes big, and second of production technology is more multiple
It is miscellaneous, and easily have the phenomenon that wood grain is collapsed due to the native texture characteristic of wood skin after paint.
The content of the invention
The technical problems to be solved by the invention are to overcome the defect of prior art there is provided a kind of melamine solid wood dermatotome
Manufacture method, it can not only make sheet material keep wood surface striped, save lumber consumption, and can make the trimerization of finished product
Cyanamide solid wood dermatotome is durable in use, and wear-resisting intensity is high.
In order to solve the above technical problems, the technical scheme is that：A kind of manufacturer of melamine solid wood dermatotome
Method, the step of method is included is as follows：
Wood skin paper is first manufactured, wood skin paper is then heated into pressurizing attaching to base material using hot press, melamine is obtained
Plate solid wood dermatotome；Wherein, the technique of manufacture wood skin paper is as follows：
(a) wood skin after processing is spliced into by wood skin ground paper product according to splicing instruction figure；
(b) wood skin ground paper product are impregnated into resin, make resin uniformly penetrating into wood skin ground paper product, formed the first half into
Product；
(c) by the first semi-finished product drying process, the second semi-finished product are formed；
(d) the second semi-finished product are sheared, complies with required size, obtain finished product wood skin paper.
Further, the step (a) is specially：
(a1) the rigid wood skin being collected into is immersed in the container equipped with wood skin softening agent and carries out sofening treatment；Wherein,
The temperature control of sofening treatment is at 56 DEG C~65 DEG C, and keeping temperature 5~8 hours；
(a2) the rigid wood skin after sofening treatment is subjected to drying and processing；
(a3) the rigid wood skin after drying is cold-pressed and shaped；
(a4) the rigid wood skin being cold-pressed after sizing is cut and spliced according to splicing instruction figure, obtain wood skin ground paper
Product.
Further, the component and each component mass percent that the wood skin softening agent contains are as follows：70%-80% poly- second
Glycol, 10%~15% glacial acetic acid, 3%-4% anionics bleeding agent, surplus are deionized water, amount to 100%.
It it is 90 DEG C~95 DEG C further for the drying temperature realized well in drying, the step (a2), during drying
Between be 16min~20min.
Further, in the step (a3), sizing pressure is 5~7MPa, and shaping time is 8~11 hours.
Further, also there is step (ab) between the step (a) and the step (b)：Wood skin ground paper product are carried out
Then the good wood skin ground paper product of bleaching are carried out dyeing processing by bleaching.
Further, the bleaching temperature is 90 DEG C~100 DEG C, and bleaching time is 1~1.5 hour；The dyeing temperature is
105 DEG C~110 DEG C, dyeing time is 5~6 hours.
Further, in the step (c), in drying process, first under 92 DEG C~100 DEG C of environment temperature, 70 are dried
~80min；Again under 125 DEG C~130 DEG C of environment temperature, 70~80min is dried.
Further, during using hot press heating pressurization, hot pressing temperature is 210 DEG C~250 DEG C, and the weight of pressurization is
2100 tons~2200 tons, pressing time is 5~10 minutes.
Employ after above-mentioned technical proposal, the present invention has following beneficial effect：
(1) woodgrained paper that the present invention replaces printing out using natural veneer, and heat pressurizing attaching on base material, gives
Pure natural and naturally pure and fresh sensation；
(2) present invention improves its scratch-resistant, corrosion-resistant and anti abrasive performance using melmac dipping；
(3) present invention makes it pass through sofening treatment, its is wooden softer, spliced during splice plate mulberry paper
Cheng Zhong, splicing more facilitates, and splicing effect is good, makes follow-up heat pressing process, has prevented the phenomenon that wood skin paper is cracked.
Embodiment
In order that present disclosure is easier to be clearly understood, below according to specific embodiment, the present invention is made into
One step is described in detail.
Embodiment one
A kind of manufacture method of melamine solid wood dermatotome, the step of method is included is as follows：
Wood skin paper is first manufactured, wood skin paper is then heated into pressurizing attaching to base material using hot press, melamine is obtained
Plate solid wood dermatotome；Wherein, during using hot press heating pressurization, hot pressing temperature is 210 DEG C, and the weight of pressurization is 2100
Ton, pressing time is 5 minutes, and the technique for manufacturing wood skin paper is as follows：
(a) wood skin after processing is spliced into by wood skin ground paper product according to splicing instruction figure；
(b) wood skin ground paper product are impregnated into resin, make resin uniformly penetrating into wood skin ground paper product, formed the first half into
Product；
(c) by the first semi-finished product drying process, the second semi-finished product are formed；
(d) the second semi-finished product are sheared, complies with required size, obtain finished product wood skin paper.
The step (a) is specially：
(a1) the rigid wood skin being collected into is immersed in the container equipped with wood skin softening agent and carries out sofening treatment；Wherein,
The temperature control of sofening treatment is at 56 DEG C, and keeping temperature 5 hours；
(a2) the rigid wood skin after sofening treatment is subjected to drying and processing；
(a3) the rigid wood skin after drying is cold-pressed and shaped；
(a4) the rigid wood skin being cold-pressed after sizing is cut and spliced according to splicing instruction figure, obtain wood skin ground paper
Product.
The component and each component mass percent that the wood skin softening agent contains are as follows：70% polyethylene glycol, 10%
Glacial acetic acid, 3% anionic bleeding agent, surplus are deionized water.
Drying temperature in the step (a2) is 90 DEG C, and drying time is 16min.
In the step (a3), sizing pressure is 5MPa, and shaping time is 8 hours.
Also there is step (ab) between the step (a) and the step (b)：Wood skin ground paper product are carried out at bleaching
Then the good wood skin ground paper product of bleaching are carried out dyeing processing by reason.
The bleaching temperature is 90 DEG C, and bleaching time is 1 hour；The dyeing temperature is 105 DEG C, and dyeing time is 5 small
When.
In the step (c), in drying process, first under 92 DEG C of environment temperature, 70min is dried；Again at 125 DEG C
Under environment temperature, 70min is dried.
Embodiment two
The step of the present embodiment method, is substantially identical with embodiment one, unlike：The mistake of pressurization is heated using hot press
Cheng Zhong, hot pressing temperature is 250 DEG C, and the weight of pressurization is 2200 tons, and pressing time is 10 minutes；In step (a1), at softening
The temperature control of reason is at 65 DEG C, and keeping temperature 8 hours；Component and each component mass percent that the wood skin softening agent contains
It is as follows：80% polyethylene glycol, 15% glacial acetic acid, 4% anionic bleeding agent, surplus are deionized water.The step
(a2) drying temperature in is 95 DEG C, and drying time is 20min.
In the step (a3), sizing pressure is 7MPa, and shaping time is 11 hours.
The bleaching temperature is 100 DEG C, and bleaching time is 1.5 hours；The dyeing temperature is 110 DEG C, and dyeing time is 6
Hour.
In the step (c), in drying process, first under 100 DEG C of environment temperature, 80min is dried；Again at 130 DEG C
Environment temperature under, dry 80min.
Embodiment three
The step of the present embodiment method, is substantially identical with embodiment one, unlike：Wherein, heated and pressurizeed using hot press
During, hot pressing temperature is 230 DEG C, and the weight of pressurization is 2150 tons, and pressing time is 8 minutes；In step (a1), softening
The temperature control of processing is at 62 DEG C, and keeping temperature 7 hours；Component and each component quality percentage that the wood skin softening agent contains
Than as follows：75% polyethylene glycol, 13% glacial acetic acid, 3% anionic bleeding agent, surplus are deionized water, are amounted to
100%.Drying temperature in the step (a2) is 93 DEG C, and drying time is 18min.
In the step (a3), sizing pressure is 6MPa, and shaping time is 10 hours.
The bleaching temperature is 95 DEG C, and bleaching time is 1.3 hours；The dyeing temperature is 108 DEG C, and dyeing time is 5
Hour.
In the step (c), in drying process, first under 96 DEG C of environment temperature, 75min is dried；Again at 127 DEG C
Under environment temperature, 75min is dried.
Melamine solid wood dermatotome prepared by three above embodiment, can not only make sheet material keep wood surface striped,
Lumber consumption is saved, and the wood skin paper of finished product can be made durable in use, wear-resisting intensity is high.
Particular embodiments described above, has been carried out further in detail to the purpose of the present invention, technical scheme and beneficial effect
Describe in detail it is bright, should be understood that the foregoing is only the present invention specific embodiment, be not intended to limit the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvements done etc., should be included in the guarantor of the present invention
Within the scope of shield.
Claims (9)
1. a kind of manufacture method of melamine solid wood dermatotome, it is characterised in that the step of method is included is as follows：
Wood skin paper is first manufactured, wood skin paper is then heated into pressurizing attaching to base material using hot press, melamine plate is obtained real
Wood skin plate；Wherein, the technique of manufacture wood skin paper is as follows：
(a) wood skin after processing is spliced into by wood skin ground paper product according to splicing instruction figure；
(b) wood skin ground paper product are impregnated into melmac, make melmac uniformly penetrating into wood skin ground paper product,
Form the first semi-finished product；
(c) by the first semi-finished product drying process, the second semi-finished product are formed；
(d) the second semi-finished product are sheared, complies with required size, obtain finished product wood skin paper.
2. the manufacture method of melamine solid wood dermatotome according to claim 1, it is characterised in that：Step (a) tool
Body is：
(a1) the rigid wood skin being collected into is immersed in the container equipped with wood skin softening agent and carries out sofening treatment；Wherein, soften
The temperature control of processing is at 56 DEG C~65 DEG C, and keeping temperature 5~8 hours；
(a2) the rigid wood skin after sofening treatment is subjected to drying and processing；
(a3) the rigid wood skin after drying is cold-pressed and shaped；
(a4) the rigid wood skin being cold-pressed after sizing is cut and spliced according to splicing instruction figure, obtain wood skin ground paper product.
3. the manufacture method of melamine solid wood dermatotome according to claim 2, it is characterised in that：In described step
(a1) in, the component and each component mass percent that the wood skin softening agent contains are as follows：70%-80% polyethylene glycol,
10%~15% glacial acetic acid, 3%-4% anionics bleeding agent, surplus are deionized water, amount to 100%.
4. the manufacture method of wood skin paper according to claim 2, it is characterised in that：Drying temperature in the step (a2)
For 90 DEG C~95 DEG C, drying time is 16min~20min.
5. the manufacture method of melamine solid wood dermatotome according to claim 2, it is characterised in that：At the step (a3)
In, sizing pressure is 5~7MPa, and shaping time is 8~11 hours.
6. the manufacture method of melamine solid wood dermatotome according to claim 1, it is characterised in that：In the step (a)
Also there is step (ab) between the step (b)：Wood skin ground paper product are subjected to bleaching, then by the good wood of bleaching
Mulberry paper made-up article carries out dyeing processing.
7. the manufacture method of melamine solid wood dermatotome according to claim 6, it is characterised in that：The bleaching temperature is
90 DEG C~100 DEG C, bleaching time is 1~1.5 hour；The dyeing temperature is 105 DEG C~110 DEG C, and dyeing time is 5~6 small
When.
8. the manufacture method of melamine solid wood dermatotome according to claim 1, it is characterised in that：In the step (c)
In, in drying process, first under 92 DEG C~100 DEG C of environment temperature, dry 70~80min；Again in 125 DEG C~130 DEG C of ring
At a temperature of border, 70~80min is dried.
9. the manufacture method of melamine solid wood dermatotome according to claim 6, it is characterised in that：Heated using hot press
During pressurization, hot pressing temperature is 210 DEG C~250 DEG C, and the weight of pressurization is 2100 tons~2200 tons, pressing time is 5~
10 minutes.