CN108972815A - A kind of Wear-resistant corrosion-resistant WPC floor producing technology - Google Patents
A kind of Wear-resistant corrosion-resistant WPC floor producing technology Download PDFInfo
- Publication number
- CN108972815A CN108972815A CN201810880941.7A CN201810880941A CN108972815A CN 108972815 A CN108972815 A CN 108972815A CN 201810880941 A CN201810880941 A CN 201810880941A CN 108972815 A CN108972815 A CN 108972815A
- Authority
- CN
- China
- Prior art keywords
- bagasse
- resistant
- parts
- floor
- wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Wear-resistant corrosion-resistant WPC floor producing technologies, with litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, bagasse, pine bark, modified urea-formaldehyde resin, defoaming agent and fire retardant are raw material, the specific gravity of strict control each component, with changing tradition WPC plate prescription, litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, bagasse and pine bark material source are wide, it is cheap, save cost of material, the anti-wear agent of one layer of aluminum oxide composition is uniformly suppressed on Large block flooring surface layer, with good corrosion-resistant effect, long service life, by the way of heating water bath, it is easy to control water temperature, guarantee the temperature environment of preparation, before packing machine is packed, ultraviolet disinfection processing is carried out to material, mixture without sifting out passes through to be used repeatedly The mode that power rolls avoids the waste of material by sieve, and manufacture craft is simple, is suitble to promote the use of.
Description
Technical field
The present invention relates to WPC technical field of floor more particularly to a kind of Wear-resistant corrosion-resistant WPC floor producing technologies.
Background technique
WPC, that is, Wood-plastic floor is a kind of novel environment-friendly wood-plastic composite material products.Wood-plastic composite panel is a kind of main
It is basic material and thermoplastic macromolecule material and processing aid etc. by timber, heats squeeze out through die apparatus again after mixing
Molding and manufactured high-tech green material, have the performance and feature of timber and plastics concurrently, can substitute timber and plastics
Novel environment friendly hitech materials.WPC wood-plastic composite floor is generally blocky splicing and is laid with.Common WPC wood-plastic composite floor, two
Block floor splicing is generally fastening type structure, has interface in stitching portion, and during installation, interface also needs four sides locking buckle,
When large area batch splices, installation strength is larger.Common WPC wood-plastic composite floor, is mixed by timber and plastics, when
Be pressurized it is stronger when, be easy stress deformation occurs tilt.
Application No. is CN201721016602.1 to disclose a kind of WPC wood-plastic composite floor, including substrate layer thus, described
Substrate layer be PE foaming layer, be successively bonded on the substrate layer from top to bottom PVC surface layer, buffer layer, WPC wood plastic layer and
PVC bottom, the damping layer surface are evenly equipped with groove, acoustical cotton block are bonded in the groove；The substrate layer, PVC
Circumferentially bonding is pasted with WPC assembling item for bottom, buffer layer, PVC surface layer, and the WPC assembling surface of every piece of substrate layer side is wave
Shape face, other side WPC assembling surface then cooperate grafting, i.e., adjacent two pieces of WPC wood-plastic composite floor waveform cooperation with wavy surface.
The utility model structure is simple, and the Mosaic face that WPC assembles item is cooperatively connected using wavy surface, can reduce buckle dosage, mitigates peace
Dress burden, in addition floor main body uses lamination layer structure, can effectively improve the anti-skidding humidity resistance on floor, and floor pressure-bearing is good
The possibility that deformation occurs tilts can be effectively reduced, the service life on floor is effectively increased.But traditional WPC plate cost of manufacture
Height, complex process, anticorrosive and wear-resisting property are undesirable, lack a kind of Wear-resistant corrosion-resistant WPC floor producing technology now to solve
The above problem.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of Wear-resistant corrosion-resistant WPC proposed
Floor producing technology.
To achieve the goals above, present invention employs following technical solutions:
A kind of Wear-resistant corrosion-resistant WPC floor producing technology, raw material are as follows by weight: 4~8 parts of litter decoration, sawdust 6~10
Part, 3~5 parts of rice husk, 3~5 parts of bagasse, 10~16 parts of wheat stalk, 3~5 parts of corn stover, 5~7 parts of bagasse, pine tree
10~16 parts of skin, 20~30 parts of modified urea-formaldehyde resin, 1~2 part of defoaming agent, 15~20 parts of fire retardant, which includes below
Step:
S1: the selection of raw material: by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, bagasse, pine tree
Skin, modified urea-formaldehyde resin, defoaming agent and fire retardant weigh spare in proportion；
S2: it drying and impregnates: using drying equipment by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, sweet
Bagasse and pine bark are dried, and controlling its moisture content is 6%-8%, hereafter by litter decoration, sawdust, rice husk, bagasse, wheat
Stalk, corn stover, bagasse and pine bark, which are added in milling apparatus, to be ground, and control grinding temperature is Celsius in 42-52
Between degree, milling time is controlled between 0.2h-0.3h, and the revolving speed of control grinding motor makes to grind at 1100-1200 revs/min
Mill product crosses 60-80 mesh, and unsanctioned raw material is returned in milling apparatus and regrind, and avoids waste material, then
It pours into liquid modified Lauxite, defoaming agent and fire retardant, impregnates 5-12 hours；
S3: it dries again: soaked raw material being subjected to drying sunning, make its aqueous dose rate between 6%-8%；
S4: raw material is hot-forming: the raw material dried is put into hot press die cavity, progress is hot-forming, and process is as follows:
Die cavity when first using low pressure 3.3Mpa hot pressing 55 ± 5 seconds, then use high pressure 6.3Mpa hot pressing 5 ± 0.5 minutes, and controlling hot pressing
Interior temperature is 165 ± 5 DEG C, arrives hot-forming Large block flooring after the completion of hot pressing；
S5: the anti-wear agent of one layer of aluminum oxide composition is uniformly suppressed on Large block flooring surface layer；
S6: Large block flooring is stood, and eliminates internal stress: the Large block flooring for being suppressed with anti-wear agent is placed in the position of dry ventilation,
It places 200 hours, to achieve the purpose that eliminate internal stress, to adapt to environment；
S7: it cuts: the big plate after placement being sent into and cuts workshop, the length and width of demand is cut to according to design size, is obtained
To the fritter blank of Manufacture of Floor；
S8: the blank after the completion of cutting: being placed on the place of dry ventilation, further stood by the standing and aligning of blank, quiet
Only the time is not less than 24 hours, discharges stress, is then aligned using aligning machinery to blank, controls the flatness of blank
Error；
S9: selected dash board is fitted on embryo material according to demand, obtains floor；
S10: corresponding slot and tenon are opened up in four sides on floor；
S11: cleaning and packaging are cleaned using surface of the high pressure blower to floor, then pack obtained floor.
Preferably, it is all made of the heating method of heating water bath in the step S2, guarantees the temperature environment of preparation.
Preferably, the humidity of storage environment is no more than 20% in the step S11, and environment temperature is no more than 50 degrees Celsius.
Preferably, before being packed in the step S11, ultraviolet disinfection processing is carried out to material.
A kind of Wear-resistant corrosion-resistant WPC floor producing technology provided by the invention, with litter decoration, sawdust, rice husk, bagasse,
Wheat stalk, corn stover, bagasse, pine bark, modified urea-formaldehyde resin, defoaming agent and fire retardant are raw material, and strict control is each
The specific gravity of component, with changing tradition WPC plate prescription, litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, sugarcane
Slag and pine bark material source are wide, cheap, save cost of material, one layer of three oxidation is uniformly suppressed on Large block flooring surface layer
The anti-wear agent of two aluminium composition, has good corrosion-resistant and wear-resisting effect, and long service life is held by the way of heating water bath
Easily water temperature is controlled, guarantees the temperature environment of preparation, before packing machine is packed, material is carried out at ultraviolet disinfection
Reason, the mixture without sifting out pass through sieve by way of firmly rolling repeatedly, avoid the waste of material, manufacture craft letter
It is single, it is suitble to promote the use of.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Embodiment 1
A kind of Wear-resistant corrosion-resistant WPC floor producing technology, raw material are as follows by weight: 4 parts of litter decoration, 6 parts of sawdust, and rice husk 3
Part, 3 parts of bagasse, 10 parts of wheat stalk, 3 parts of corn stover, 5 parts of bagasse, 10 parts of pine bark, 20 parts of modified urea-formaldehyde resin,
1 part of defoaming agent, 15 parts of fire retardant, which includes the following steps:
S1: the selection of raw material: by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, bagasse, pine tree
Skin, modified urea-formaldehyde resin, defoaming agent and fire retardant weigh spare in proportion；
S2: it drying and impregnates: using drying equipment by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, sweet
Bagasse and pine bark are dried, and controlling its moisture content is 6%-8%, hereafter by litter decoration, sawdust, rice husk, bagasse, wheat
Stalk, corn stover, bagasse and pine bark, which are added in milling apparatus, to be ground, and control grinding temperature is Celsius in 42-52
Between degree, using the heating method of heating water bath, guarantee the temperature environment of preparation, control milling time between 0.2h-0.3h,
The revolving speed of control grinding motor makes grinding product cross 60-80 mesh, unsanctioned raw material returns at 1100-1200 revs/min
It is regrind in milling apparatus, avoids waste material, be subsequently poured into liquid modified Lauxite, defoaming agent and fire retardant
It is interior, it impregnates 5-12 hours；
S3: it dries again: soaked raw material being subjected to drying sunning, make its aqueous dose rate between 6%-8%；
S4: raw material is hot-forming: the raw material dried is put into hot press die cavity, progress is hot-forming, and process is as follows:
Die cavity when first using low pressure 3.3Mpa hot pressing 55 ± 5 seconds, then use high pressure 6.3Mpa hot pressing 5 ± 0.5 minutes, and controlling hot pressing
Interior temperature is 165 ± 5 DEG C, arrives hot-forming Large block flooring after the completion of hot pressing；
S5: the anti-wear agent of one layer of aluminum oxide composition is uniformly suppressed on Large block flooring surface layer；
S6: Large block flooring is stood, and eliminates internal stress: the Large block flooring for being suppressed with anti-wear agent is placed in the position of dry ventilation,
It places 200 hours, to achieve the purpose that eliminate internal stress, to adapt to environment；
S7: it cuts: the big plate after placement being sent into and cuts workshop, the length and width of demand is cut to according to design size, is obtained
To the fritter blank of Manufacture of Floor；
S8: the blank after the completion of cutting: being placed on the place of dry ventilation, further stood by the standing and aligning of blank, quiet
Only the time is not less than 24 hours, discharges stress, is then aligned using aligning machinery to blank, controls the flatness of blank
Error；
S9: selected dash board is fitted on embryo material according to demand, obtains floor；
S10: corresponding slot and tenon are opened up in four sides on floor；
S11: cleaning and packaging are cleaned using surface of the high pressure blower to floor, then pack obtained floor,
The humidity of storage environment is no more than 20%, and environment temperature is no more than 50 degrees Celsius, before being packed, and carries out ultraviolet light to material
Sterilization treatment.
Embodiment 2
A kind of Wear-resistant corrosion-resistant WPC floor producing technology, raw material are as follows by weight: 6 parts of litter decoration, 8 parts of sawdust, and rice husk 4
Part, 4 parts of bagasse, 13 parts of wheat stalk, 4 parts of corn stover, 6 parts of bagasse, 8 parts of pine bark, 25 parts of modified urea-formaldehyde resin, disappear
1.5 parts of infusion, 17.5 parts of fire retardant, which includes the following steps:
S1: the selection of raw material: by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, bagasse, pine tree
Skin, modified urea-formaldehyde resin, defoaming agent and fire retardant weigh spare in proportion；
S2: it drying and impregnates: using drying equipment by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, sweet
Bagasse and pine bark are dried, and controlling its moisture content is 6%-8%, hereafter by litter decoration, sawdust, rice husk, bagasse, wheat
Stalk, corn stover, bagasse and pine bark, which are added in milling apparatus, to be ground, and control grinding temperature is Celsius in 42-52
Between degree, using the heating method of heating water bath, guarantee the temperature environment of preparation, control milling time between 0.2h-0.3h,
The revolving speed of control grinding motor makes grinding product cross 60-80 mesh, unsanctioned raw material returns at 1100-1200 revs/min
It is regrind in milling apparatus, avoids waste material, be subsequently poured into liquid modified Lauxite, defoaming agent and fire retardant
It is interior, it impregnates 5-12 hours；
S3: it dries again: soaked raw material being subjected to drying sunning, make its aqueous dose rate between 6%-8%；
S4: raw material is hot-forming: the raw material dried is put into hot press die cavity, progress is hot-forming, and process is as follows:
Die cavity when first using low pressure 3.3Mpa hot pressing 55 ± 5 seconds, then use high pressure 6.3Mpa hot pressing 5 ± 0.5 minutes, and controlling hot pressing
Interior temperature is 165 ± 5 DEG C, arrives hot-forming Large block flooring after the completion of hot pressing；
S5: the anti-wear agent of one layer of aluminum oxide composition is uniformly suppressed on Large block flooring surface layer；
S6: Large block flooring is stood, and eliminates internal stress: the Large block flooring for being suppressed with anti-wear agent is placed in the position of dry ventilation,
It places 200 hours, to achieve the purpose that eliminate internal stress, to adapt to environment；
S7: it cuts: the big plate after placement being sent into and cuts workshop, the length and width of demand is cut to according to design size, is obtained
To the fritter blank of Manufacture of Floor；
S8: the blank after the completion of cutting: being placed on the place of dry ventilation, further stood by the standing and aligning of blank, quiet
Only the time is not less than 24 hours, discharges stress, is then aligned using aligning machinery to blank, controls the flatness of blank
Error；
S9: selected dash board is fitted on embryo material according to demand, obtains floor；
S10: corresponding slot and tenon are opened up in four sides on floor；
S11: cleaning and packaging are cleaned using surface of the high pressure blower to floor, then pack obtained floor,
The humidity of storage environment is no more than 20%, and environment temperature is no more than 50 degrees Celsius, before being packed, and carries out ultraviolet light to material
Sterilization treatment.
Embodiment 3
A kind of Wear-resistant corrosion-resistant WPC floor producing technology, raw material are as follows by weight: 8 parts of litter decoration, 10 parts of sawdust, and rice husk 5
Part, 5 parts of bagasse, 16 parts of wheat stalk, 5 parts of corn stover, 7 parts of bagasse, 16 parts of pine bark, 30 parts of modified urea-formaldehyde resin,
2 parts of defoaming agent, 20 parts of fire retardant, which includes the following steps:
S1: the selection of raw material: by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, bagasse, pine tree
Skin, modified urea-formaldehyde resin, defoaming agent and fire retardant weigh spare in proportion；
S2: it drying and impregnates: using drying equipment by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, sweet
Bagasse and pine bark are dried, and controlling its moisture content is 6%-8%, hereafter by litter decoration, sawdust, rice husk, bagasse, wheat
Stalk, corn stover, bagasse and pine bark, which are added in milling apparatus, to be ground, and control grinding temperature is Celsius in 42-52
Between degree, using the heating method of heating water bath, it is easy to open water temperature, guarantees the temperature environment of preparation, when control is ground
Between between 0.2h-0.3h, control grinding motor revolving speed at 1100-1200 revs/min, so that grinding product is crossed 60-80 mesh,
Unsanctioned raw material is returned in milling apparatus and is regrind, and is avoided waste material, is subsequently poured into liquid modified ureaformaldehyde tree
In rouge, defoaming agent and fire retardant, impregnate 5-12 hours；
S3: it dries again: soaked raw material being subjected to drying sunning, make its aqueous dose rate between 6%-8%；
S4: raw material is hot-forming: the raw material dried is put into hot press die cavity, progress is hot-forming, and process is as follows:
Die cavity when first using low pressure 3.3Mpa hot pressing 55 ± 5 seconds, then use high pressure 6.3Mpa hot pressing 5 ± 0.5 minutes, and controlling hot pressing
Interior temperature is 165 ± 5 DEG C, arrives hot-forming Large block flooring after the completion of hot pressing；
S5: uniformly suppressing the anti-wear agent of one layer of aluminum oxide composition on Large block flooring surface layer, has good corrosion-resistant work
With；
S6: Large block flooring is stood, and eliminates internal stress: the Large block flooring for being suppressed with anti-wear agent is placed in the position of dry ventilation,
It places 200 hours, to achieve the purpose that eliminate internal stress, to adapt to environment；
S7: it cuts: the big plate after placement being sent into and cuts workshop, the length and width of demand is cut to according to design size, is obtained
To the fritter blank of Manufacture of Floor；
S8: the blank after the completion of cutting: being placed on the place of dry ventilation, further stood by the standing and aligning of blank, quiet
Only the time is not less than 24 hours, discharges stress, is then aligned using aligning machinery to blank, controls the flatness of blank
Error；
S9: selected dash board is fitted on embryo material according to demand, obtains floor；
S10: corresponding slot and tenon are opened up in four sides on floor；
S11: cleaning and packaging are cleaned using surface of the high pressure blower to floor, then pack obtained floor,
The humidity of storage environment is no more than 20%, and environment temperature is no more than 50 degrees Celsius, before being packed, and carries out ultraviolet light to material
Sterilization treatment.
A kind of Wear-resistant corrosion-resistant WPC floor producing technology provided by the invention, with litter decoration, sawdust, rice husk, bagasse,
Wheat stalk, corn stover, bagasse, pine bark, modified urea-formaldehyde resin, defoaming agent and fire retardant are raw material, and strict control is each
The specific gravity of component, with changing tradition WPC plate prescription, litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, sugarcane
Slag and pine bark material source are wide, cheap, save cost of material, one layer of three oxidation is uniformly suppressed on Large block flooring surface layer
The anti-wear agent of two aluminium composition, has good corrosion-resistant and wear-resisting effect, and long service life is held by the way of heating water bath
Easily water temperature is controlled, guarantees the temperature environment of preparation, before packing machine is packed, material is carried out at ultraviolet disinfection
Reason, the mixture without sifting out pass through sieve by way of firmly rolling repeatedly, avoid the waste of material, manufacture craft letter
It is single, it is suitble to promote the use of.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of Wear-resistant corrosion-resistant WPC floor producing technology, it is characterised in that: its raw material is as follows by weight: litter decoration 4~8
Part, 6~10 parts of sawdust, 3~5 parts of rice husk, 3~5 parts of bagasse, 10~16 parts of wheat stalk, 3~5 parts of corn stover, bagasse
5~7 parts, 10~16 parts of pine bark, 20~30 parts of modified urea-formaldehyde resin, 1~2 part of defoaming agent, 15~20 parts of fire retardant, the technique
Include the following steps:
S1: the selection of raw material: by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, bagasse, pine tree
Skin, modified urea-formaldehyde resin, defoaming agent and fire retardant weigh spare in proportion；
S2: it drying and impregnates: using drying equipment by litter decoration, sawdust, rice husk, bagasse, wheat stalk, corn stover, sweet
Bagasse and pine bark are dried, and controlling its moisture content is 6%-8%, hereafter by litter decoration, sawdust, rice husk, bagasse, wheat
Stalk, corn stover, bagasse and pine bark, which are added in milling apparatus, to be ground, and control grinding temperature is Celsius in 42-52
Between degree, milling time is controlled between 0.2h-0.3h, and the revolving speed of control grinding motor makes to grind at 1100-1200 revs/min
Mill product crosses 60-80 mesh, and unsanctioned raw material is returned in milling apparatus and regrind, and avoids waste material, then
It pours into liquid modified Lauxite, defoaming agent and fire retardant, impregnates 5-12 hours；
S3: it dries again: soaked raw material being subjected to drying sunning, make its aqueous dose rate between 6%-8%；
S4: raw material is hot-forming: the raw material dried is put into hot press die cavity, progress is hot-forming, and process is as follows:
Die cavity when first using low pressure 3.3Mpa hot pressing 55 ± 5 seconds, then use high pressure 6.3Mpa hot pressing 5 ± 0.5 minutes, and controlling hot pressing
Interior temperature is 165 ± 5 DEG C, arrives hot-forming Large block flooring after the completion of hot pressing；
S5: the anti-wear agent of one layer of aluminum oxide composition is uniformly suppressed on Large block flooring surface layer；
S6: Large block flooring is stood, and eliminates internal stress: the Large block flooring for being suppressed with anti-wear agent is placed in the position of dry ventilation,
It places 200 hours, to achieve the purpose that eliminate internal stress, to adapt to environment；
S7: it cuts: the big plate after placement being sent into and cuts workshop, the length and width of demand is cut to according to design size, is obtained
To the fritter blank of Manufacture of Floor；
S8: the blank after the completion of cutting: being placed on the place of dry ventilation, further stood by the standing and aligning of blank, quiet
Only the time is not less than 24 hours, discharges stress, is then aligned using aligning machinery to blank, controls the flatness of blank
Error；
S9: selected dash board is fitted on embryo material according to demand, obtains floor；
S10: corresponding slot and tenon are opened up in four sides on floor；
S11: cleaning and packaging are cleaned using surface of the high pressure blower to floor, then pack obtained floor.
2. a kind of Wear-resistant corrosion-resistant WPC floor producing technology according to claim 1, it is characterised in that: the step S2
In be all made of the heating method of heating water bath, guarantee the temperature environment of preparation.
3. a kind of Wear-resistant corrosion-resistant WPC floor producing technology according to claim 1, it is characterised in that: the step S11
The humidity of middle storage environment is no more than 20%, and environment temperature is no more than 50 degrees Celsius.
4. a kind of Wear-resistant corrosion-resistant WPC floor producing technology according to claim 1, it is characterised in that: the step S11
In packed before, to material carry out ultraviolet disinfection processing.