CN107160521A - A kind of preparation method of anti-corrosion type bamboo pen container - Google Patents
A kind of preparation method of anti-corrosion type bamboo pen container Download PDFInfo
- Publication number
- CN107160521A CN107160521A CN201710511566.4A CN201710511566A CN107160521A CN 107160521 A CN107160521 A CN 107160521A CN 201710511566 A CN201710511566 A CN 201710511566A CN 107160521 A CN107160521 A CN 107160521A
- Authority
- CN
- China
- Prior art keywords
- thick bamboo
- bamboo tube
- corrosion
- pen container
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of preparation method of anti-corrosion type bamboo pen container, it is characterised in that including following aspect：（1）Raw material is chosen：Select diameter in 7 9cm ring as raw material is made, two ends are cut flat with；（2）Bamboo skin is polished, and the inside and outside portion's epidermis polishing of thick bamboo tube is removed；（3）Engraving：To contents such as thick bamboo tube surface engraving decorative pattern, ichthyornis；（4）Maceration extract is prepared, and drug ingedient is micronized, ethanol soak extraction is used；（5）Thick bamboo tube impregnates, in pressure cooker, carries out the impregnation technology in two stages；（6）Bilayer waxing, sprays after wooden wax to thick bamboo tube, after plastic sheeting parcel, is being steamed under the conditions of 105 DEG C 110 DEG C, circulation is twice；（7）Low temperature drying, thick bamboo tube after waxing is dried at low temperature, and bamboo pen container is made.Bamboo pen container made from the inventive method, environment-protective no-smell, with very strong waterproof anti-corrosion performance.
Description
Technical field
The invention belongs to handicraft processing technique field, and in particular to a kind of preparation method of anti-corrosion type bamboo pen container.
Background technology
Mao bamboon stalk is tall and big logical straight, and material is tough and tensile light strong, and isolating property is high, and amount of contraction is small, and hardness is big, and fiber is long, and the thin bamboo strip is excellent,
Texture straight, it is smooth bright clean；With pine, plum, " three durable plants of winter: pine, bamboo and plum blossom " are described as, pen container is made using bamboo material material, it is solid durable,
Elegant taste, thick bamboo tube appearance can carve all kinds decorative pattern and embossment, and in extensive range with creating, art form is various, raw material
Source is wide, the features such as surcharge is high.But traditional bamboo pen container, waterproof to pen container and anti-corrosion measure processing be simple, by
Yu Zhuzhong contains substantial amounts of cellulose components, adsorbable Environmental Water and microorganism, easily goes mouldy, surface color becomes
Change, influence the service life and sight of bamboo pen container.In terms of water-proofing treatment, tung oil or wooden wax coating are typically adopted, is used
Tung oil coating, pollution-free, but smell weight, the short time is difficult to eliminate；Wooden wax coating, it is simple to use paint brush brush to surface,
Used after being polished, its face coat lack of homogeneity, wooden wax composition is only attached to pen container top layer, anti-corrosion and waterproof effect compared with
Difference.In terms of preservative treatment, sterilization component processing is not used, microorganism easily adheres to growth, causes to go mouldy.
The content of the invention
The problem of present invention is directed to existing：Manufacture craft, traditional bamboo pen container manufacture craft is simple, waterproof and anti-corrosion measure
Single, due to a large amount of cellulose components contained in bamboo, adsorbable Environmental Water and microorganism easily go mouldy, surface face
Color changes.In terms of water-proofing treatment, tung oil or wooden wax coating are typically adopted, it is pollution-free using tung oil coating, but smell
Weight, the short time is difficult to eliminate；Wooden wax coating, uses paint brush brush to surface, its face coat lack of homogeneity, wooden wax attachment
On pen container top layer.In terms of preservative treatment, sterilization component processing is not used, microorganism easily adheres to growth, causes to go mouldy.To solve
Above mentioned problem, the invention provides a kind of preparation method of anti-corrosion type bamboo pen container.
The present invention is achieved by the following technical solutions：
A kind of preparation method of anti-corrosion type bamboo pen container, comprises the following steps：
（1）Raw material is chosen：Select diameter in 7-9cm ring as raw material is made, it is smooth to cut upper and lower ends；
（2）Bamboo skin is polished：With sander, the inside and outside portion's epidermis polishing of thick bamboo tube is removed, cortical layer is removed, be easy to engraving creation and
Post processing；And cleaned up with clear water；
（3）Engraving：To contents such as thick bamboo tube surface engraving decorative pattern, ichthyornis；
（4）Maceration extract is prepared：By compositions such as the coptis, the capsule of weeping forsythia, hop, the tubers of stemona, be micronized using pulverizing mill, after micro mist composition with
Solvent contact area increases, and increases extracts active ingredients effect；The ethanol that purity is 95% is added according to mass ratio, at 20 DEG C -23
Under DEG C microwave temperature, closing immersion 5-6h improves ethanol to active ingredient extraction rate；Then, in 1.3-1.5Pa high pressure distillations pot
In, ethanol distillation is gone out, and collection is condensed, obtain anti-corrosion maceration extract；
（5）Thick bamboo tube impregnates：Thick bamboo tube and anti-corrosion maceration extract after carving, are placed in pressure cooker, thick bamboo tube is completely immersed in anti-corrosion maceration extract,
Closing opening, carries out impregnation technology：First, 20 DEG C -23 DEG C of dipping temperature, pressure 1.5-1.8Pa impregnates 7-9h, improves temperature
And pressure, level of interpenetration of the maceration extract to thick bamboo tube can be increased, anti-corrosive properties are improved；Then, in 36 DEG C -40 DEG C of dipping temperature, pressure
2.0-2.3 Pa, impregnate 3-4h, and as active ingredient is reduced in ethanol, dipping effect declines, and improves temperature and pressure, can increase
Active ingredient penetration under low concentration；
（6）Bilayer waxing：It is fitted into using wooden wax in sprayer, the whole inner and outer surfaces of thick bamboo tube is sprayed using sprayer；
And wrapped up using plastic sheeting, film parcel can reduce wooden wax when steaming and overflow, and be positioned over 105 DEG C of -110 DEG C of steamers
In, 1-2h is steamed, promotes wooden wax composition to thick bamboo tube internal penetration；Then, cooling removes plastic sheeting, after drying naturally, enters
Second of spraying wood wax oil of row, is placed in steamer, steams 1-2h, increase the wooden wax thickness in thick bamboo tube surface, improve its anti-corrosion and anti-
Aqueous energy；
（7）Low temperature drying：Thick bamboo tube after waxing is dried at low temperature, bamboo pen container is made.
Anti-corrosion maceration extract described in step (4), it is respectively configured to sub-prime gauge part and is：
7-9 parts of the coptis, 3-6 parts of the capsule of weeping forsythia, 4-6 parts of hop, 3-4 parts of the tuber of stemona, windproof 3-5 parts, 1-3 parts of the fruit of summer cypress.
Anti-corrosion maceration extract described in step (4), wherein 95% ethanol：It is 12-14 to be micronized composition quality proportioning:1.
The present invention has advantages below compared with prior art：Maceration extract prepare composition, wherein the coptis, capsule of weeping forsythia part, hop,
Stronger antibacterial and antiseptic power are respectively provided with the tuber of stemona, windproof, fruit of summer cypress active ingredient, raw material is natural, pollution-free.Moving party
Method, conventional method is used after drug ingedient is carried out into boiling, and active ingredient easily fails, using water as solvent medium, leaching
The moisture of thick bamboo tube is added in stain, subsequent treatment is not utilized；Drug ingedient carry out micronization processes, increase drug ingedient with
The contact area of Extraction solvent, and in 20 DEG C of -23 DEG C of immersions, distilled by increasing pressure, active ingredient in medicine can be improved and carried
Take rate.Impregnation technology, improves temperature and pressure, increases level of interpenetration of the maceration extract to thick bamboo tube, and improving temperature using latter stage
And pressure, in the case of low active constituent content, promote active ingredient to permeate thick bamboo tube.Bilayer waxing, is sprayed after wooden wax,
Wrapped up, and steamed in high temperature using plastic sheeting, improve wooden wax composition to thick bamboo tube internal penetration, circulation twice, carry
High wax coat thickness.The bamboo pen container made by the inventive method, the holding time is long, not easy to change, environment friendly and pollution-free, waterproof
It is improved with antiseptic property.
Embodiment
Embodiment 1：
A kind of preparation method of anti-corrosion type bamboo pen container, comprises the following steps：
（1）Raw material is chosen：Select diameter in 7-9cm ring as raw material is made, it is smooth to cut upper and lower ends；
（2）Bamboo skin is polished：With sander, the inside and outside portion's epidermis polishing of thick bamboo tube is removed；And cleaned up with clear water；
（3）Engraving：To contents such as thick bamboo tube surface engraving decorative pattern, ichthyornis；
（4）Maceration extract is prepared：By compositions such as the coptis, the capsule of weeping forsythia, hop, the tubers of stemona, be micronized using pulverizing mill, according to mass ratio plus
Enter the ethanol that purity is 95%, under 21 DEG C of microwave temperatures, closing dipping 5h；Then, in 1.4Pa high pressure distillations pot, by ethanol
Distill out, and condense collection, obtain anti-corrosion maceration extract；
（5）Thick bamboo tube impregnates：Thick bamboo tube and anti-corrosion maceration extract after carving, are placed in pressure cooker, thick bamboo tube is completely immersed in anti-corrosion maceration extract,
Closing opening, carries out impregnation technology：First, 21 DEG C of dipping temperature, pressure 1.6Pa impregnates 7.5h；Then, in dipping temperature 37
DEG C, the Pa of pressure 2.1 impregnates 3.5h；
（6）Bilayer waxing：Using paint brush by wood wax oil, thick bamboo tube surface and inside are uniformly applied to, is wrapped with plastic sheeting
Wrap up in, be positioned in 106 DEG C of steamers, steam 1.5h；Then, cooling removes plastic sheeting, after drying naturally, carries out second and applies wood
Wax oil, is placed in steamer, steams 1.5h；
（7）Low temperature drying：Thick bamboo tube after waxing is dried at low temperature, bamboo pen container is made.
Anti-corrosion maceration extract described in step (4), it is respectively configured to sub-prime gauge part and is：
7.2 parts of the coptis, 3.6 parts of the capsule of weeping forsythia, 4.3 parts of hop, 3.2 parts of the tuber of stemona, windproof 3.4 parts, 1.5 parts of the fruit of summer cypress.
Anti-corrosion maceration extract described in step (4), wherein 95% ethanol：It is 12 to be micronized composition quality proportioning:1.
Embodiment 2：
The present embodiment 2 is compared with embodiment 1, and step changes in the following areas：
Step（4）Described anti-corrosion maceration extract, it is respectively configured to sub-prime gauge part and is：
8 parts of the coptis, 5 parts of the capsule of weeping forsythia, 5.4 parts of hop, 3.6 parts of the tuber of stemona, windproof 4.2 parts, 2.6 parts of the fruit of summer cypress.
Step（4）Described anti-corrosion maceration extract, wherein 95% ethanol：It is 13 to be micronized composition quality proportioning:1.
Step（4）Described maceration extract is prepared, and it is 22 DEG C that it, which prepares temperature, distillation pressure 1.5 Pa.
Step（5）Described thick bamboo tube impregnates, and its impregnation technology parameter is：
First, 22 DEG C of dipping temperature, pressure 1.7Pa impregnates 8h；Then, in 38 DEG C of dipping temperature, the Pa of pressure 2.2 impregnates 4h.
Step（6）Described bilayer is waxed, and its painting ceroplastic is：
Wooden wax is fitted into sprayer, the whole inner and outer surfaces of thick bamboo tube are sprayed using sprayer, carried out with plastic sheeting
Parcel, is positioned in 107 DEG C of steamers, steams 2h；Then, cooling removes plastic sheeting, after drying naturally, carries out second and applies wood
Wax oil, is placed in steamer, steams 2h.
Contrast 1：
This contrast 1 is compared with embodiment 1, and step is not carried out（4）Maceration extract is prepared and used, and other steps are same as Example 1.
Contrast 2：
This contrast 2 is compared with embodiment 1, step（4）Maceration extract is prepared, and it is 10 that wherein ethanol, which adds mass ratio,:1, other steps
It is rapid same as Example 1.
Contrast 3：
This contrast 3 is compared with embodiment 2, and step is not carried out（5）Middle thick bamboo tube dipping, other steps are same as Example 2.
Contrast 4：
This contrast 4 is compared with embodiment 1, and step is not carried out（6）Middle double-deck waxing, only carries out wooden wax brushing, other steps with
Embodiment 1 is identical.
Control group：
This control group is to thick bamboo tube processing, only with wooden wax coating, and maceration extract preparation, thick bamboo tube dipping and double-deck waxing is not used.
To embodiment 1, embodiment 2, contrast 1, contrast 2, contrast 3, contrast 4 and control group experimental program, statistics is used 1 year
The water content of bamboo pen container, rate of going mouldy and use time are compared afterwards.
Experimental data：
| Project | Water content % | Rate of going mouldy % | Use time（Year） |
| Embodiment 1 | 2.52% | 0.21% | Use for a long time |
| Embodiment 2 | 2.35% | 0.18% | Use for a long time |
| Contrast 1 | 4.62% | 1.64% | 8-10 |
| Contrast 2 | 3.47% | 0.80% | 8-10 |
| Contrast 3 | 5.02% | 2.23% | 5-7 |
| Contrast 4 | 18.71% | 3.38% | 3-5 |
| Control group | 23.14% | 7.43% | 1-2 |
Synthesis result：By being waxed to bamboo pen container using double-deck, using that can reduce water content 16.2% after 1 year, rate of going mouldy declines
3.17%, improve the service life of bamboo pen container；Use maceration extract and impregnation technology, it is possible to decrease water content is distinguished in bamboo pen container
For 2.10%, 2.7%, rate of going mouldy decline respectively 2.05%, 1.43%, the service life of raising bamboo pen container, raising bamboo pen container
Water-tight corrosion-proof ability.
Claims (3)
1. a kind of preparation method of anti-corrosion type bamboo pen container, it is characterised in that comprise the following steps：
（1）Raw material is chosen：Select diameter in 7-9cm ring as raw material is made, it is smooth to cut upper and lower ends；
（2）Bamboo skin is polished：With sander, the inside and outside portion's epidermis polishing of thick bamboo tube is removed；And cleaned up with clear water；
（3）Engraving：To thick bamboo tube surface engraving；
（4）Maceration extract is prepared：It is micronized, the coptis, the capsule of weeping forsythia, hop, the tuber of stemona, the windproof, fruit of summer cypress according to matter using pulverizing mill
Measure than adding the ethanol that purity is 95%, under 20 DEG C of -23 DEG C of microwave temperatures, closing dipping 5-6h；Then, it is high in 1.3-1.5Pa
Press in boiler, ethanol distillation is gone out, and condense collection, obtain anti-corrosion maceration extract；
（5）Thick bamboo tube impregnates：Thick bamboo tube and anti-corrosion maceration extract after carving, are placed in pressure cooker, thick bamboo tube is completely immersed in anti-corrosion maceration extract,
Closing opening, carries out impregnation technology：First, 20 DEG C -23 DEG C of dipping temperature, pressure 1.5-1.8Pa impregnates 7-9h；Then, in leaching
36 DEG C -40 DEG C of stain temperature, pressure 2.0-2.3 Pa impregnate 3-4h；
（6）Bilayer waxing：Wooden wax is fitted into sprayer, the whole inner and outer surfaces of thick bamboo tube are sprayed using sprayer, used
Plastic sheeting is wrapped up, and is positioned in 105 DEG C of -110 DEG C of steamers, is steamed 1-2h；Then, cooling removes plastic sheeting, natural
After drying, carry out second and apply wood wax oil, be placed in steamer, steam 1-2h；
（7）Low temperature drying：Thick bamboo tube after waxing is dried at low temperature, bamboo pen container is made.
2. the preparation method of anti-corrosion type bamboo pen container as claimed in claim 1, it is characterised in that the anti-corrosion leaching described in step (4)
Stain liquid, it is respectively configured to sub-prime gauge part and is：
7-9 parts of the coptis, 3-6 parts of the capsule of weeping forsythia, 4-6 parts of hop, 3-4 parts of the tuber of stemona, windproof 3-5 parts, 1-3 parts of the fruit of summer cypress.
3. the preparation method of anti-corrosion type bamboo pen container as claimed in claim 1, it is characterised in that the anti-corrosion leaching described in step (4)
Stain liquid, wherein 95% ethanol：It is 12-14 to be micronized composition quality proportioning:1.