CN107160521B - A kind of production method of anti-corrosion type bamboo pen container - Google Patents
A kind of production method of anti-corrosion type bamboo pen container Download PDFInfo
- Publication number
- CN107160521B CN107160521B CN201710511566.4A CN201710511566A CN107160521B CN 107160521 B CN107160521 B CN 107160521B CN 201710511566 A CN201710511566 A CN 201710511566A CN 107160521 B CN107160521 B CN 107160521B
- Authority
- CN
- China
- Prior art keywords
- thick bamboo
- bamboo tube
- corrosion
- pen container
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of production methods of anti-corrosion type bamboo pen container, which is characterized in that including following aspect: (1) raw material is chosen: selecting diameter in the ring of 7-9cm as production raw material, both ends are cut flat with；(2) bamboo skin is polished, and the inside and outside portion's epidermis polishing of thick bamboo tube is removed；(3) it carves: to contents such as thick bamboo tube surface engraving decorative pattern, ichthyornis；(4) maceration extract is prepared, and drug ingedient is micronized, ethyl alcohol soak extraction is used；(5) thick bamboo tube impregnates, and in pressure cooker, carries out the impregnation technology in two stages；(6) the double-deck waxing after spraying wooden wax to thick bamboo tube, after plastic film package, is steaming, circulation is twice under the conditions of 105 DEG C -110 DEG C；(7) low temperature drying dries thick bamboo tube after waxing at low temperature, and bamboo pen container is made.Bamboo pen container made from the method for the present invention, environment-protective no-smell have very strong waterproof anti-corrosion performance.
Description
Technical field
The invention belongs to craftwork processing technique fields, and in particular to a kind of production method of anti-corrosion type bamboo pen container.
Background technique
Moso bamboo stalk is tall and big logical straight, and material is tough and tensile light strong, and isolating property is high, and shrinkage is small, and hardness is big, and fiber is long, and the thin bamboo strip is excellent,
Texture straight, it is smooth bright clean；With pine, plum, " three durable plants of winter: pine, bamboo and plum blossom " are known as, make pen container using bamboo material material, it is solid durable,
Elegant taste, thick bamboo tube appearance can carve various types decorative pattern and embossment, have and create in extensive range, art form multiplicity, raw material
The features such as source is wide, and surcharge is high.But traditional bamboo pen container, the waterproof and anti-corrosion measure processing to pen container are simple, by
Yu Zhuzhong contains a large amount of cellulose components, adsorbable Environmental Water and microorganism, easily goes mouldy, surface color becomes
Change, influences the service life and ornamental value of bamboo pen container.In terms of water-proofing treatment, tung oil or wooden wax coating are generally adopted, is used
Tung oil coating, it is pollution-free, but smell weight, short time are difficult to eliminate；Wooden wax coating, simply using paint brush brush to surface,
Used after being polished, surface covering uniformity is poor, wooden wax ingredient be only attached to pen container surface layer, anti-corrosion and waterproof effect compared with
Difference.In terms of preservative treatment, sterilization component processing is not used, microorganism growth easy to attach causes to go mouldy.
Summary of the invention
The present invention is directed to existing problem: manufacture craft, traditional bamboo pen container manufacture craft is simple, waterproof and anti-corrosion measure
Single, due to a large amount of cellulose components contained in bamboo, adsorbable Environmental Water and microorganism easily go mouldy, surface face
Color changes.In terms of water-proofing treatment, tung oil or wooden wax coating are generally adopted, it is pollution-free using tung oil coating, but smell
Weight, short time are difficult to eliminate；Wooden wax coating, using paint brush brush to surface, surface covering uniformity is poor, wooden wax attachment
On pen container surface layer.In terms of preservative treatment, sterilization component processing is not used, microorganism growth easy to attach causes to go mouldy.To solve
The above problem, the present invention provides a kind of production methods of anti-corrosion type bamboo pen container.
The present invention is achieved by the following technical solutions:
A kind of production method of anti-corrosion type bamboo pen container, comprising the following steps:
(1) raw material is chosen: select diameter in the ring of 7-9cm as production raw material, it is smooth to cut upper and lower ends；
(2) bamboo skin is polished: using sander, the inside and outside portion's epidermis polishing of thick bamboo tube is removed, cortical layer is removed, convenient for engraving wound
Make and post-processes；And it is cleaned up with clear water；
(3) it carves: to contents such as thick bamboo tube surface engraving decorative pattern, ichthyornis；
(4) maceration extract prepare: the ingredients such as the coptis, Fructus Forsythiae, snake, the tuber of stemona are micronized using pulverizing mill, after micro mist at
Divide and increase with solvent contact area, increases effective component extraction effect；The ethyl alcohol that purity is 95% is added according to mass ratio, 20
Under DEG C -23 DEG C of microwave temperatures, 5-6h is impregnated in closing, improves ethyl alcohol to effective component extraction rate；Then, in 1.3-1.5Pa high pressure
In boiler, ethanol distillation is gone out, and condenses collection, obtains anti-corrosion maceration extract；
(5) thick bamboo tube impregnates: thick bamboo tube after engraving and anti-corrosion maceration extract being placed in pressure cooker, thick bamboo tube is completely immersed in anti-corrosion leaching
Stain liquid, closing opening, carries out impregnation technology: firstly, 20 DEG C -23 DEG C of dipping temperature, pressure 1.5-1.8Pa, 7-9h is impregnated, is improved
Temperature and pressure can increase maceration extract to the level of interpenetration of thick bamboo tube, improve anti-corrosive properties；Then, at 36 DEG C -40 DEG C of dipping temperature,
Pressure 2.0-2.3 Pa impregnates 3-4h, and as effective component reduces in ethyl alcohol, dipping effect decline improves temperature and pressure, can
Increase effective component penetration under low concentration；
(6) the double-deck waxing: being fitted into sprayer using wooden wax, is carried out using sprayer to thick bamboo tube whole inner and outer surfaces
Spraying；And wrapped up using plastic film, film package can reduce wooden wax when steaming and overflow, and be placed in 105 DEG C -110 DEG C
In steamer, 1-2h is steamed, promotes wooden wax ingredient to thick bamboo tube internal penetration；Then, cooling to remove plastic film, naturally dry
Afterwards, second of spraying wood wax oil is carried out, is placed in steamer, steams 1-2h, increase the wooden wax thickness in thick bamboo tube surface, improve its anti-corrosion
And waterproof performance；
(7) low temperature drying: thick bamboo tube after waxing is dried at low temperature, and bamboo pen container is made.
Anti-corrosion maceration extract described in step (4) is respectively configured to sub-prime meter part are as follows:
7-9 parts of the coptis, 3-6 parts of Fructus Forsythiae, 4-6 parts of snake, 3-4 parts of the tuber of stemona, 3-5 parts of radix saposhnikoviae, 1-3 parts of the fruit of summer cypress.
Anti-corrosion maceration extract described in step (4), wherein 95% ethyl alcohol: micronization composition quality proportion is 12-14:1.
The present invention have the advantage that compared with prior art maceration extract prepare ingredient, wherein the coptis, Fructus Forsythiae part, snake,
The tuber of stemona, radix saposhnikoviae all have stronger antibacterial and anti-corrosion ability in fruit of summer cypress effective component, and raw material is natural, pollution-free.Moving party
Method, conventional method are used after drug ingedient is carried out boiling, and effective component is easy failure, uses water as solvent medium, leaching
The moisture content that thick bamboo tube is increased in stain, does not utilize subsequent processing；Drug ingedient carry out micronization processes, increase drug ingedient with
The contact area of Extraction solvent, and effective component in drug can be improved and mention by increasing pressure distillation in 20 DEG C of -23 DEG C of immersions
Take rate.Impregnation technology improves temperature and pressure, increases maceration extract to the level of interpenetration of thick bamboo tube, and is improving temperature using latter stage
And pressure promotes effective component to permeate thick bamboo tube in the case where low active constituent content.Bilayer waxing, after spraying wooden wax,
It is wrapped up using plastic film, and is steamed in high temperature, improve wooden wax ingredient to thick bamboo tube internal penetration, circulation twice, mention
High wax coat thickness.The bamboo pen container made by the method for the invention, the holding time is long, not easy to change, environment friendly and pollution-free, waterproof
It is improved with antiseptic property.
Specific embodiment
Embodiment 1:
A kind of production method of anti-corrosion type bamboo pen container, comprising the following steps:
(1) raw material is chosen: select diameter in the ring of 7-9cm as production raw material, it is smooth to cut upper and lower ends；
(2) bamboo skin is polished: using sander, the inside and outside portion's epidermis polishing of thick bamboo tube is removed；And it is cleaned up with clear water；
(3) it carves: to contents such as thick bamboo tube surface engraving decorative pattern, ichthyornis；
(4) maceration extract is prepared: the ingredients such as the coptis, Fructus Forsythiae, snake, the tuber of stemona being micronized using pulverizing mill, according to quality
The ethyl alcohol for being 95% than purity is added, under 21 DEG C of microwave temperatures, closing dipping 5h；It then, will in 1.4Pa high pressure distillation pot
Ethanol distillation goes out, and condenses collection, obtains anti-corrosion maceration extract；
(5) thick bamboo tube impregnates: thick bamboo tube after engraving and anti-corrosion maceration extract being placed in pressure cooker, thick bamboo tube is completely immersed in anti-corrosion leaching
Stain liquid, closing opening, carries out impregnation technology: firstly, 21 DEG C of dipping temperature, pressure 1.6Pa, impregnate 7.5h；Then, in dipping temperature
37 DEG C, 2.1 Pa of pressure of degree impregnates 3.5h；
(6) the double-deck waxing: using paint brush by wood wax oil, being uniformly applied to thick bamboo tube surface and inside, with plastic film into
Row package, is placed in 106 DEG C of steamers, steams 1.5h；Then, cooling to remove plastic film, after natural drying, carry out second
Wood wax oil is applied, is placed in steamer, steams 1.5h；
(7) low temperature drying: thick bamboo tube after waxing is dried at low temperature, and bamboo pen container is made.
Anti-corrosion maceration extract described in step (4) is respectively configured to sub-prime meter part are as follows:
7.2 parts of the coptis, 3.6 parts of Fructus Forsythiae, 4.3 parts of snake, 3.2 parts of the tuber of stemona, 3.4 parts, 1.5 parts of the fruit of summer cypress of radix saposhnikoviae.
Anti-corrosion maceration extract described in step (4), wherein 95% ethyl alcohol: micronization composition quality proportion is 12:1.
Embodiment 2:
Compared with embodiment 1, step changes in the following areas the present embodiment 2:
Anti-corrosion maceration extract described in step (4) is respectively configured to sub-prime meter part are as follows:
8 parts of the coptis, 5 parts of Fructus Forsythiae, 5.4 parts of snake, 3.6 parts of the tuber of stemona, 4.2 parts, 2.6 parts of the fruit of summer cypress of radix saposhnikoviae.
Anti-corrosion maceration extract described in step (4), wherein 95% ethyl alcohol: micronization composition quality proportion is 13:1.
Maceration extract described in step (4) is prepared, and preparing temperature is 22 DEG C, distills 1.5 Pa of pressure.
The dipping of thick bamboo tube described in step (5), impregnation technology parameter are as follows:
Firstly, 22 DEG C of dipping temperature, pressure 1.7Pa, impregnate 8h；Then, at 38 DEG C of dipping temperature, 2.2 Pa of pressure, leaching
Stain 4h.
The waxing of bilayer described in step (6), applies ceroplastic are as follows:
Wooden wax is fitted into sprayer, thick bamboo tube whole inner and outer surfaces are sprayed using sprayer, use plastic film
It is wrapped up, is placed in 107 DEG C of steamers, steams 2h；Then, cooling to remove plastic film, after natural drying, carry out second
Wood wax oil is applied, is placed in steamer, steams 2h.
Comparison 1:
This comparison 1 does not carry out step (4) maceration extract and prepares and use compared with embodiment 1, other steps and embodiment 1
It is identical.
Comparison 2:
Compared with embodiment 1, step (4) maceration extract is prepared for this comparison 2, and it is 10:1 that wherein mass ratio, which is added, in ethyl alcohol,
His step is same as Example 1.
Comparison 3:
This comparison 3 does not carry out thick bamboo tube in step (5) and impregnates, other steps are same as Example 2 compared with embodiment 2.
Comparison 4:
This comparison 4 does not carry out the double-deck waxing in step (6), only carries out wooden wax brushing compared with embodiment 1, other steps
It is rapid same as Example 1.
Control group:
Maceration extract preparation, thick bamboo tube dipping and double-coating is not used only with wooden wax coating to thick bamboo tube processing in this control group
Wax.
To embodiment 1, embodiment 2, comparison 1, comparison 2, comparison 3, comparison 4 and control group experimental program, statistics is used 1 year
It the water content of bamboo pen container, mildew rate and is compared afterwards using the time.
Experimental data:
| Project | Water content % | Mildew rate % | It uses time (year) |
| Embodiment 1 | 2.52% | 0.21% | It is used for a long time |
| Embodiment 2 | 2.35% | 0.18% | It is used for a long time |
| Comparison 1 | 4.62% | 1.64% | 8-10 |
| Comparison 2 | 3.47% | 0.80% | 8-10 |
| Comparison 3 | 5.02% | 2.23% | 5-7 |
| Comparison 4 | 18.71% | 3.38% | 3-5 |
| Control group | 23.14% | 7.43% | 1-2 |
Synthesis result: by bamboo pen container using the double-deck waxing, using water content 16.2%, mildew rate can be reduced after 1 year
Decline 3.17%, improves the service life of bamboo pen container；Using maceration extract and impregnation technology, water content in bamboo pen container can be reduced
Respectively 2.10%, 2.7%, the decline of mildew rate are respectively 2.05%, 1.43%, improve the service life of bamboo pen container, improve bamboo
The waterproof and anticorrosion ability of pen container.
Claims (3)
1. a kind of production method of anti-corrosion type bamboo pen container, which comprises the following steps:
(1) raw material is chosen: select diameter in the ring of 7-9cm as production raw material, it is smooth to cut upper and lower ends；
(2) bamboo skin is polished: using sander, the inside and outside portion's epidermis polishing of thick bamboo tube is removed；And it is cleaned up with clear water；
(3) it carves: to thick bamboo tube surface engraving；
(4) maceration extract is prepared: the coptis, Fructus Forsythiae, snake, the tuber of stemona, radix saposhnikoviae, the fruit of summer cypress being micronized using pulverizing mill, according to matter
The ethyl alcohol for being 95% than purity is added is measured, under 20 DEG C of -23 DEG C of microwave temperatures, closing dipping 5-6h；Then, in 1.3-1.5Pa high
It presses in boiler, ethanol distillation is gone out, and condense collection, obtain anti-corrosion maceration extract；
(5) thick bamboo tube impregnates: thick bamboo tube after engraving and anti-corrosion maceration extract are placed in pressure cooker, thick bamboo tube is completely immersed in anti-corrosion maceration extract,
Closing opening, carries out impregnation technology: firstly, 20 DEG C -23 DEG C of dipping temperature, pressure 1.5-1.8Pa, impregnate 7-9h；Then, it is soaking
36 DEG C -40 DEG C of stain temperature, pressure 2.0-2.3 Pa, impregnate 3-4h；
(6) the double-deck waxing: wooden wax is fitted into sprayer, thick bamboo tube whole inner and outer surfaces are sprayed using sprayer, is used
Plastic film is wrapped up, and is placed in 105 DEG C of -110 DEG C of steamers, is steamed 1-2h；Then, cooling to remove plastic film, nature
After drying, carries out second and apply wood wax oil, be placed in steamer, steam 1-2h；
(7) low temperature drying: thick bamboo tube after waxing is dried at low temperature, and bamboo pen container is made.
2. the production method of anti-corrosion type bamboo pen container as described in claim 1, which is characterized in that the leaching of anti-corrosion described in step (4)
Stain liquid is respectively configured to sub-prime meter part are as follows:
7-9 parts of the coptis, 3-6 parts of Fructus Forsythiae, 4-6 parts of snake, 3-4 parts of the tuber of stemona, 3-5 parts of radix saposhnikoviae, 1-3 parts of the fruit of summer cypress.
3. the production method of anti-corrosion type bamboo pen container as described in claim 1, which is characterized in that the leaching of anti-corrosion described in step (4)
Stain liquid, wherein 95% ethyl alcohol: micronization composition quality proportion is 12-14:1.