CN107433809A - A kind of inkstone and preparation method thereof - Google Patents
A kind of inkstone and preparation method thereof Download PDFInfo
- Publication number
- CN107433809A CN107433809A CN201710695554.1A CN201710695554A CN107433809A CN 107433809 A CN107433809 A CN 107433809A CN 201710695554 A CN201710695554 A CN 201710695554A CN 107433809 A CN107433809 A CN 107433809A
- Authority
- CN
- China
- Prior art keywords
- inkstone
- base
- lacquer
- shade
- heart
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of inkstone and preparation method thereof.A kind of inkstone, including lacquer carcass base, and the inkstone heart being embedded in the base.It can be made by the following method：Comprise the following steps：Step A：Former tire is made according to the shape of the base；Step B：In the outer surface wrap of the former tire, the slurry containing raw lacquer then is coated with its surface, is dried in the shade；Step C：Repeating said steps B is one or many, until reaching required thickness；Step D：The former tire is removed, by upper ash, polishing, obtains base；Step E：The inkstone heart is inlayed to the base with lacquer, is dried in the shade.The inkstone of the present invention is in light weight, and is stably unlikely to deform, and its preparation method flow is simple, can reinforce sizing, and operating condition is gentle, without high temperature sintering condition.
Description
Technical field
The present invention relates to office appliance field, more particularly, to a kind of inkstone and preparation method thereof.
Background technology
Inkstone is collectively referred to as the writing brush, ink stick, ink slab and paper of Chinese tradition with pen, ink, paper, is the necessary tool of Chinese calligraphy.With the epoch
Development, inkstone a great variety, it is broadly divided into traditional ecosystem inkstone, building stones inlay inkstone, clear mud formula inlays inkstone this three generation products.
Traditional ecosystem inkstone uses the production method that whole stone carving is carved, i.e., based on one block of former stone, carves out inkstone.From
Since Song Dynasty, undergone the excavation of nearly one thousand years, it is recognized that hair ink it is best, stone product highest inhales inkstone, the old hole ink-stone of Duanxi inkstone is adopted already
Pick is totally.Old hole ink-stone is to generally acknowledge best ink-stone material processed, and what is produced with the original producton location periphery district being full of on the market at present is " new
Hole " stone material is as far apart as heaven and earth in quality.Exemplified by inhaling inkstone, it is easily broken off due to the shale attribute of its stone material, during cutting, from ancient times
Since just have saying for " inhaling without big inkstone ".Thus inkstone is inhaled in real high-end old hole on the market at present, and the price of one block of former stone has been moved
Often tens of thousands of, hundreds of thousands is even up to a million, can bear far from general ink-stone fan and calligraphy fan.For livelihood and interests
Driving, ink-stone dealer generally pretend to be old hole sale newly to cheat inkstone, and the consumer not understood buys the product to fall short of the reality,
In the course of time it can influence entirely to inhale the industry reputation of inkstone.
Building stones inlay inkstone, are to imbed the more superior inkstone heart of stone matter into base with common engraved stone, and this method is from Song
In generation, rises and just has begun to use, and can also see on the market so far.Because it inside and outside all employ stone material, total quality is relatively more heavy
Weight, it is adapted to residential use, is less easy to carry.
It is that pug is moulding that base is made with boccaro, pottery mud etc. that clear mud formula, which inlays inkstone, and ink-stone is embedded in the position for needing to rub an ink stone
Put, then kiln-firing again, make ooze harden, form inkstone.This inkstone although solve the problems, such as it is overweight, but due to burning
The easy dilatation of pug during system, cause not reaching design effect, and clay inkstone body is easily damaged once colliding with.
In view of this, it is special to propose the present invention.
The content of the invention
The first object of the present invention is to provide a kind of inkstone, and described inkstone is in light weight, and is stably unlikely to deform.
The second object of the present invention is the preparation method for providing above-mentioned inkstone, and described preparation method flow is simple, energy
Enough to reinforce sizing, operating condition is gentle, without high temperature sintering.
In order to realize the above object the invention provides following technical scheme：
A kind of inkstone, including lacquer carcass base, and the inkstone heart being embedded in the base.
The inkstone heart of the present invention grinds prepared Chinese ink region.
The present invention mainly has two features：
First, material is different used by base and the inkstone heart (rub an ink stick on an inkstone area), the stone materials of a large amount of costlinesses, drop are so saved
Low cost, and the stone material that will be unable to process overall inkstone recycles.
Second, base uses the lacquer of lightweight, first, the weight of inkstone, and lacquer setting process are so not only alleviated
Without bakeing, deformation is small, easily reaches default shape；Secondly, lacquer quality is hard, pressure-resistant, corrosion-resistant, resistance to strong acid, resistance to strong
Alkali, damp proof insulation, high temperature resistant, obtained inkstone are beneficial to long-term preserve；In addition, lacquer is natural materials, it is environment-protecting and non-poisonous.
Above inkstone can also be improved further in structure, to improve other effects, such as：
Preferably, bonded between the base and the inkstone heart by lacquer.
The Stability Analysis of Structures of lacquer bonding, is unlikely to deform, and it is natural to draw materials, and cost is low, more environmentally friendly.
Preferably, the inkstone heart is patty.
The inkstone heart of patty is almost without dead angle, prepared Chinese ink of avoiding waste, or causes to grind uneven.
Preferably, the base is provided with scraping blade.
Ink is dipped in writing brush head during writing, unnecessary prepared Chinese ink scrapes off on scraping blade, and prepared Chinese ink flows into inkstone in the heart, both avoids waste,
The prepared Chinese ink for avoiding writing brush to overflow again makes desk dirty.
Preferably, the scraping blade is metal scraping blade, and is to be detachably connected with base.
So it is beneficial to storage, and reduces the manufacture difficulty of base.
Preferably, the base is provided with the groove for being used for placing pen.
It is convenient for collecting, ensure clean and tidy using process table top.
Preferably, the base, which is provided with, is used to place ink-stick groove.
Equally, also for convenient for collecting, ensure clean and tidy using process table top.
Preferably, in addition to inkstone lid.
During without using inkstone, covered with inkstone lid, prevent that dust from dropping or moisture evaporation.
Preferably, the edge of the inkstone lid is provided with gap.
It is that writing brush is placed under inkstone lid for convenience to set gap, and the shape of gap is engaged with the handle shape of writing brush.
Preferably, the inkstone lid is connected with the base by latching.
Inkstone of the present invention is positioned as lightweight, is convenient for carrying, if inkstone lid and the base are arranged into latch connection type, more
Facilitate the storage, prevent that prepared Chinese ink spills in transfer process.
Preferably, the base is provided with the bracket for being used for hanging pen.
Compared to the groove structure that setting described above prevents writing brush, damage of the structure to writing brush is small, avoids writing brush from putting down
Easy crimping hair when putting.
The core texture of the inkstone of any of the above structure is base and the inkstone heart, and it can be made by the following method：
Comprise the following steps：
Step A：Former tire is made according to the shape of the base；
Step B：In the outer surface wrap of the former tire, the slurry containing raw lacquer then is coated with its surface, is dried in the shade；
Step C：Repeating said steps B is one or many, until reaching required thickness；
Step D：The former tire is removed, by upper ash, polishing, obtains base；
Step E：The inkstone heart is inlayed to the base with lacquer, is dried in the shade.
First, this method makes raw lacquer base using the technique of bodiless lacquer, and the base color not only obtained is magnificent, light
Bright such as mirror, it is not afraid of water logging, is indeformable, be colour-fast, be firm, be heatproof, acid-alkali-corrosive-resisting, in light weight, and is grasped without high temperature sintering
Make, therefore, production cost is low, and production efficiency is high.
Secondly, this method bonds base and the inkstone heart using lacquer, because raw lacquer and the raw material similar compatibility used in base, because
This bond effect is good, and visually produces one integrated mass sense.
Preferably, the condition dried in the shade is：Humidity 50%-80%, 22-30 DEG C of temperature.
The humidity of environment of drying in the shade and temperature all have a major impact to textural shape and intensity, the embrittlement degree of base, through grinding
Study carefully discovery, the intensity of humidity 50%-80%, temperature base resulting when being 22-30 DEG C is bigger, and resistance to pressure is high, Er Qiewen
Manage regular shape.
Preferably, the wrap uses burlap.
The associativity of burlap and raw lacquer is good, and frivolous, and the moulding influence on base is smaller.
Preferably, the slurry containing raw lacquer is mainly made up of raw lacquer, dark grey and binder, and the weight ratio of three is 5:1-
3:0.1-0.5。
For raw lacquer mainly as material main body and binding agent, dark grey is filler, can increase thickness, and binder can enter one
Walk the caking property of strengthening slurry.The control of slurry density is critically important, and too dry meeting stickiness is inadequate, and overly wet, epidermis easily wrinkles.
Through research, the weight ratio of three is 5:1-3:During 0.1-0.5, effect is preferable.
The binder is preferably polyvinyl alcohol and/or carboxymethyl cellulose.
Polyvinyl alcohol and carboxymethyl cellulose are more easy to solidify under the conditions of drying in the shade, and with the coordinative role of raw lacquer and dark grey
It is good.
Preferably, the time dried in the shade is more than 2 days.
Dry in the shade the time it is too short be easily deformed, be preferred within more than 2 days with drying in the shade.
Preferably, in the step C, the number that the step B is repeated is 3-4 times.
Although wrap and the number of plies of coating are more, base is more thick and heavy, intensity increase unobvious, through investigating, to repeat
It is preferred for 3-4 times, i.e. wrap pasting 4-5 times altogether.
Preferably, the raw material used in the upper ash is mainly made up of raw lacquer and dark grey.
This raw material is similar to the composition of base substrate, and compatibility and bond strength are more preferable.
Preferably, the upper grey number is 3 times, and the particle diameter of the dark grey used in upper ash successively decreases three times.
The outer surface of base requires exquisiteness attractive in appearance, and internal layer is higher to intensity requirement, and particle diameter successively decreases dark grey from the inside to the outside
The demand can be met.
Preferably, in the step E, after described inlay and it is described dry in the shade before also include coating with lacquer decorations：
Make textural effect using one or more of mixing in wood chip, eggshell, cassia seed and shell.
Wood chip, eggshell, cassia seed and shell are all drawn materials, and natural, environmentally friendly, nontoxic, cost is low, therefore, with its decorative base
Cost performance is higher.
Preferably, also include after the step E：Light is pushed away with pearl powder and oil, is dried in the shade.
Make inkstone as bright as a sixpence by pushing away light.
To sum up, compared with prior art, invention achieves following technique effect：
(1) twice laid, cost of material are low：The former stone material made of stones made base, save a large amount of costlinesses, drop are replaced with raw lacquer
Low cost of material, and the stone material that will be unable to process overall inkstone recycles.
(2) it is in light weight：Base uses the lacquer of lightweight, alleviates the weight of inkstone.
(3) it is sturdy and durable, it is unlikely to deform：Lacquer quality is hard, pressure-resistant, corrosion-resistant, resistance to strong acid, resistance to highly basic, damp proof insulation,
High temperature resistant, obtained inkstone are beneficial to long-term preserve.
(4) storage is convenient：The structure all kinds of articles for use convenient for collecting such as groove, bracket, inkstone lid are set.
(5) inkstone appearance colour is magnificent, as bright as a sixpence.
(6) preparation method flow is simple, and process conditions are gentle.
Brief description of the drawings
, below will be to specific in order to illustrate more clearly of the specific embodiment of the invention or technical scheme of the prior art
The required accompanying drawing used is briefly described in embodiment or description of the prior art, it should be apparent that, in describing below
Accompanying drawing is some embodiments of the present invention, for those of ordinary skill in the art, before creative work is not paid
Put, other accompanying drawings can also be obtained according to these accompanying drawings.
Fig. 1 is the schematic diagram for the inkstone that the embodiment of the present invention 1 and 3 provides；
Fig. 2 is the schematic diagram for the inkstone that embodiment 2 provides；
Reference：
1- bases；The 2- inkstone hearts；3- places the groove of ink-stick；
4- places the groove 4 of pen.
Embodiment
Technical scheme is clearly and completely described below in conjunction with the drawings and specific embodiments, but
Be it will be understood to those of skill in the art that following described embodiment is part of the embodiment of the present invention, it is rather than whole
Embodiment, the present invention is merely to illustrate, and is not construed as limiting the scope of the present invention.Based on the embodiment in the present invention, ability
The every other embodiment that domain those of ordinary skill is obtained under the premise of creative work is not made, belongs to guarantor of the present invention
The scope of shield.Unreceipted actual conditions person in embodiment, the condition suggested according to normal condition or manufacturer are carried out.Agents useful for same
Or the unreceipted production firm person of instrument, it is the conventional products that can be obtained by commercially available purchase.
Embodiment 1
1st, gypsum mould：Former loose tool is made using gypsum, according to the complexity of inkstone, generally requires 1 day time.
2nd, wrap：Inkstone base substantially form is done, burlap is rolled in gypsum original loose tool surface to mould device shape.Thin dark grey,
Raw lacquer is with binder (polyvinyl alcohol) with 5:1:0.5 weight is coated on burlap than mixing and adheres to carcass surface, dry in the shade, then weigh
Multiple wrap, the step 4 time for scraping ash, drying in the shade and (being placed two days in humidity 70%-80%, the environment of 25-30 DEG C of temperature), treat carcass
Reach certain thickness and firmness degree.
3rd, gypsum is removed：Gypsum is broken into pieces.
4th, conformality is taken：Cut with knife or instrument, cut unnecessary corner.
5th, grey polishing is scraped：With raw lacquer mixing dark grey (weight 5:1) table of the manufactured pastel uniform fold in carcass
Face, make basal layer.It is respectively thick middle fine ash to scrape 3 times ashes, has scraped ash every time and has been required for polishing (2 days or so time of one layer of ash).
6th, mopping：Priming, close lightly grey (fine ash short covering gap), polishing priming again.So base shape molding.
7th, ink-stone shape is taken.
8th, inlay：The base obtained using lacquer bonding ink-stone and step 6.
9th, matched colors according to ink-stone.
10th, decorations are coated with lacquer：On carcass obtained in the previous step after brush finish paint, textural effect is done, lacquerware is a colored paint, cover paint
(outermost layer covers the colored varnish), mother-of-pearl inlay (spread mother-of-pearl inlay powder on not dry carcass surface), or pineapple paint (is existed with the varnish stain of certain denseness
Above carcass, dry in the shade).Skin texture material has wood chip, eggshell, cassia seed, shell etc..(pineapple paint general 2-3 months, usually paint
The one and a half months time)
11st, paint is wiped：Raw lacquer is stained with silk to wipe in surface, is dried in the shade.
12nd, light/matting is pushed away：After coating with lacquer decorations and completing, (raw material is pearl powder and edible to the light that pushes away for just having started again and again
Oil) and process of drying in the shade, with from carefully to superfine sand paper, until the skin with hand, lacquerware could being allowed to show finally that magnificent nothing
The gloss of the flaw.Matting then makes lacquer brightness be dumb light.
The shape of inkstone made from the embodiment is as shown in figure 1, including lacquer carcass base 1, and is embedded in the bottom
The inkstone heart 2 in seat, is bonded between the base 1 and the inkstone heart 2 by lacquer.
The inkstone heart 2 is patty.
The base, which is provided with, is used for the groove 4 for placing pen and the groove 3 for placing ink-stick.
Embodiment 2
1st, gypsum mould：Former loose tool is made using gypsum, according to the complexity of inkstone, generally requires 1 day time.
2nd, wrap：Inkstone base substantially form is done, burlap is rolled in gypsum original loose tool surface to mould device shape.Thin dark grey,
Raw lacquer is with binder (carboxymethyl cellulose) with 5:3:0.1 weight ratio mixing, is coated on burlap and adheres to carcass surface, dry in the shade,
Wrap, the step 3 time for scraping ash, drying in the shade and (being placed two days in humidity 50%-60%, the environment of 22-25 DEG C of temperature) are repeated, is treated
Carcass reaches certain thickness and firmness degree.
3rd, gypsum is removed：Gypsum is broken into pieces.
4th, conformality is taken：Cut with knife or instrument, cut unnecessary corner.
5th, grey polishing is scraped：With raw lacquer mixing dark grey (weight 5:1) table of the manufactured pastel uniform fold in carcass
Face, make basal layer.It is respectively thick middle fine ash to scrape 3 times ashes, has scraped ash every time and has been required for polishing (2 days or so time of one layer of ash).
6th, mopping：Priming, close lightly grey (fine ash short covering gap), polishing priming again.So base shape molding.
7th, ink-stone shape is taken.
8th, inlay：The base obtained using lacquer bonding ink-stone and step 6.
9th, matched colors according to ink-stone.
10th, decorations are coated with lacquer：On carcass obtained in the previous step after brush finish paint, textural effect is done, lacquerware is a colored paint, cover paint
(outermost layer covers the colored varnish), mother-of-pearl inlay (spread mother-of-pearl inlay powder on not dry carcass surface), or pineapple paint (is existed with the varnish stain of certain denseness
Above carcass, dry in the shade).Skin texture material has wood chip, eggshell, cassia seed, shell etc..(pineapple paint general 2-3 months, usually paint
The one and a half months time)
11st, paint is wiped：Raw lacquer is stained with silk to wipe in surface, is dried in the shade.
12nd, light/matting is pushed away：After coating with lacquer decorations and completing, (raw material is pearl powder and edible to the light that pushes away for just having started again and again
Oil) and process of drying in the shade, with from carefully to superfine sand paper, until the skin with hand, lacquerware could being allowed to show finally that magnificent nothing
The gloss of the flaw.Matting then makes lacquer brightness be dumb light.
The shape of inkstone made from the embodiment is as shown in Fig. 2 including lacquer carcass base 1, and is embedded in the bottom
The inkstone heart 2 in seat 1, is bonded between the base 1 and the inkstone heart 2 by lacquer.
The inkstone heart 2 is patty.
Embodiment 3
1st, gypsum mould：Former loose tool is made using gypsum, according to the complexity of inkstone, generally requires 1 day time.
2nd, wrap：Inkstone base substantially form is done, burlap is rolled in gypsum original loose tool surface to mould device shape.Thin dark grey,
Raw lacquer is with binder (polyvinyl alcohol and carboxymethyl cellulose etc. mix) again with 5:2:0.3 weight is coated on burlap than mixing
Carcass surface is adhered to, is dried in the shade, wrap is repeated, scrapes ash, dries in the shade and (put in humidity 70%-80%, the environment of 25-30 DEG C of temperature
Put two days) step 4 time, treat that carcass reaches certain thickness and firmness degree.
3rd, gypsum is removed：Gypsum is broken into pieces.
4th, conformality is taken：Cut with knife or instrument, cut unnecessary corner.
5th, grey polishing is scraped：With raw lacquer mixing dark grey (weight 5:1) table of the manufactured pastel uniform fold in carcass
Face, make basal layer.It is respectively thick middle fine ash to scrape 3 times ashes, has scraped ash every time and has been required for polishing (2 days or so time of one layer of ash).
6th, mopping：Priming, close lightly grey (fine ash short covering gap), polishing priming again.So base shape molding.
7th, ink-stone shape is taken.
8th, inlay：The base obtained using lacquer bonding ink-stone and step 6.
9th, matched colors according to ink-stone.
10th, decorations are coated with lacquer：On carcass obtained in the previous step after brush finish paint, textural effect is done, lacquerware is a colored paint, cover paint
(outermost layer covers the colored varnish), mother-of-pearl inlay (spread mother-of-pearl inlay powder on not dry carcass surface), or pineapple paint (is existed with the varnish stain of certain denseness
Above carcass, dry in the shade).Skin texture material has wood chip, eggshell, cassia seed, shell etc..(pineapple paint general 2-3 months, usually paint
The one and a half months time)
11st, paint is wiped：Raw lacquer is stained with silk to wipe in surface, is dried in the shade.
12nd, light/matting is pushed away：After coating with lacquer decorations and completing, (raw material is pearl powder and edible to the light that pushes away for just having started again and again
Oil) and process of drying in the shade, with from carefully to superfine sand paper, until the skin with hand, lacquerware could being allowed to show finally that magnificent nothing
The gloss of the flaw.Matting then makes lacquer brightness be dumb light.
The shape of inkstone made from the embodiment is as shown in figure 1, including lacquer carcass base 1, and is embedded in the bottom
The inkstone heart 2 in seat 1, is bonded between the base 1 and the inkstone heart 2 by lacquer.
The inkstone heart is patty.
The base 1, which is provided with, is used for the groove 4 for placing pen and the groove 3 for placing ink-stick.
The shape of the gained inkstone of above-described embodiment 1 to 3 can also make following improve：
Scraping blade is set on base.
Ink is dipped in writing brush head during writing, unnecessary prepared Chinese ink scrapes off on scraping blade, and prepared Chinese ink flows into inkstone in the heart, both avoids waste,
The prepared Chinese ink for avoiding writing brush to overflow again makes desk dirty.
The scraping blade can use metal scraping blade, and be to be detachably connected with base.So it is beneficial to storage, and reduces base
Manufacture difficulty.
Or increase inkstone lid, during without using inkstone, covered with inkstone lid, prevent that dust from dropping or moisture evaporation.
In order that inkstone lid and above-mentioned inkstone respective outer side edges, can also set gap at the edge of inkstone lid, it is convenient to put writing brush
Under inkstone lid, the shape of gap is engaged with the handle shape of writing brush.
Or design inkstone lid is connected with base by latching.
Inkstone of the present invention is positioned as lightweight, is convenient for carrying, if inkstone lid and the base are arranged into latch connection type, more
Facilitate the storage, prevent that prepared Chinese ink spills in transfer process.
Either increase bracket or groove is replaced with into bracket, i.e., be provided for hanging the bracket of pen on base.
Compared to groove structure, damage of the bracket to writing brush is small, avoids writing brush easy crimping hair when keeping flat.
The quality test results of different inkstones such as table 1.
The quality of 1 different inkstones of table
Finally it should be noted that：Various embodiments above is merely illustrative of the technical solution of the present invention, rather than its limitations；To the greatest extent
The present invention is described in detail with reference to foregoing embodiments for pipe, it will be understood by those within the art that：Its according to
The technical scheme described in foregoing embodiments can so be modified, either which part or all technical characteristic are entered
Row equivalent substitution；And these modifications or replacement, the essence of appropriate technical solution is departed from various embodiments of the present invention technology
The scope of scheme.
Claims (10)
- A kind of 1. inkstone, it is characterised in that including lacquer carcass base, and the inkstone heart being embedded in the base.
- 2. inkstone according to claim 1, it is characterised in that bonded between the base and the inkstone heart by lacquer；Preferably, the inkstone heart is patty；Preferably, the base is provided with dismountable scraping blade.
- 3. inkstone according to claim 1, it is characterised in that the base is provided with the groove for being used for placing pen；Preferably, the base, which is provided with, is used to place ink-stick groove.
- 4. inkstone according to claim 1, it is characterised in that also including inkstone lid；Preferably, the edge of the inkstone lid is provided with gap；Preferably, the inkstone lid is connected with the base by latching.
- 5. inkstone according to claim 1, it is characterised in that the base is provided with the bracket for being used for hanging pen.
- 6. the preparation method of the inkstone described in claim any one of 1-5, it is characterised in that comprise the following steps：Step A：Former tire is made according to the shape of the base；Step B：In the outer surface wrap of the former tire, the slurry containing raw lacquer then is coated with its surface, is dried in the shade；Step C：Repeating said steps B is one or many, until reaching required thickness；Step D：The former tire is removed, by upper ash, polishing, obtains base；Step E：The inkstone heart is inlayed to the base with lacquer, is dried in the shade.
- 7. the preparation method of inkstone according to claim 6, it is characterised in that the condition dried in the shade is：Humidity 50%- 80%, 22-30 DEG C of temperature.
- 8. the preparation method of inkstone according to claim 6, it is characterised in that the wrap uses burlap；Preferably, the slurry containing raw lacquer is mainly made up of raw lacquer, dark grey and binder, and the weight ratio of three is 5:1-3: 0.1-0.5；The binder is preferably polyvinyl alcohol and/or carboxymethyl cellulose；Preferably, the time dried in the shade is more than 2 days；Preferably, in the step C, the number that the step B is repeated is 3-4 times.
- 9. the preparation method of inkstone according to claim 6, it is characterised in that the raw material used in the upper ash is mainly by giving birth to Paint and dark grey composition；Preferably, the upper grey number is 3 times, and the particle diameter of the dark grey used in upper ash successively decreases three times.
- 10. the preparation method of inkstone according to claim 6, it is characterised in that in the step E, inlayed described Also include coating with lacquer decorations before with described dry in the shade afterwards：Make textural effect using one or more of mixing in wood chip, eggshell, cassia seed and shell；Preferably, also include after the step E：Light is pushed away with pearl powder and oil, is dried in the shade.