CN107375999A - 一种降脂杀菌缝合线及其制备方法 - Google Patents

一种降脂杀菌缝合线及其制备方法 Download PDF

Info

Publication number
CN107375999A
CN107375999A CN201710810032.1A CN201710810032A CN107375999A CN 107375999 A CN107375999 A CN 107375999A CN 201710810032 A CN201710810032 A CN 201710810032A CN 107375999 A CN107375999 A CN 107375999A
Authority
CN
China
Prior art keywords
parts
suture
powder
silk
loweringing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710810032.1A
Other languages
English (en)
Inventor
孔维海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Royal Plaque Biotechnology Co Ltd
Original Assignee
Nanjing Royal Plaque Biotechnology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Royal Plaque Biotechnology Co Ltd filed Critical Nanjing Royal Plaque Biotechnology Co Ltd
Priority to CN201710810032.1A priority Critical patent/CN107375999A/zh
Publication of CN107375999A publication Critical patent/CN107375999A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种降脂杀菌缝合线及其制备方法。该缝合线包括以下组分：聚乳酸、醋粉、纳豆粉、香茅草提取物、纳米银、聚羟基丁酸脂、维生素E、丝蛋白、透明质酸、改性壳聚糖、碳纤维、蚕丝纤维、聚乙二醇、去离子水。将醋粉、纳豆粉、香茅草提取物、去离子水混合，搅拌均匀后，加入碳纤维，制备混合粉；再制备改性蚕丝纤维；将聚乳酸、聚羟基丁酸脂、维生素E、丝蛋白、透明质酸、聚乙二醇、混合粉和改性蚕丝纤维混合搅拌，喷丝板出丝，吹风冷却成型后，再在热板上进行拉伸即得缝合线。本发明降脂杀菌缝合线选材天然、工艺环保，安全无刺激，可完全生物降解，且降解后的成分融入机体，可降低机体内的胆固醇，提高免疫力，促进伤口的愈合。

Description

一种降脂杀菌缝合线及其制备方法
技术领域
本发明涉及医疗用品领域，具体涉及一种降脂杀菌缝合线及其制备方法。
背景技术
医用缝合线是一种用于人体手术缝合线的线型材料，是常用的生物纺织品。随着生物医学和高分子材料科学的发展，生物可降解医用材料正引起人们越来越广泛的关注。
申请号201410684311.4，名称为一种医用可吸收缝合线及其制备方法，该缝合线包括如下组分：聚二恶烷酮，聚乳酸，海蜇胶原，壳聚糖，交联剂，稳定剂及抗菌剂。制备方法：按重量份称取各组分；将各组分加入反应釜中，加热，搅拌，共混，得到共混物；将共混物送入双螺杆挤出机挤出，挤出样条经水冷、风干、切粒，得到母粒；将母粒加热融化，脱泡，通过喷丝板，形成初级纤维，再将初级纤维水浴中二次拉伸，即得。虽然该发明的原料可体内生物降解，对组织无刺激，促进伤口的愈合，但该缝合线的性能单一，需要改进。
发明内容
针对现有技术的不足，本发明的目的在于提供一种降脂杀菌缝合线及其制备方法，该缝合线可溶性好，被降解的成分可有效地降低人体的血脂，增强机体免疫，促进上口愈合。
为解决现有技术问题，本发明采取的技术方案为：
一种降脂杀菌缝合线，包括以下按重量份数计的组分：聚乳酸55-78份、醋粉12-35份、纳豆粉1-8份、香茅草提取物1-4份、纳米银0.2-0.8份、聚羟基丁酸脂14-27份、维生素E2-9份、丝蛋白24-48份、透明质酸12-18份、改性壳聚糖1-5份、碳纤维34-48份、蚕丝纤维14-24份、聚乙二醇35-48份、去离子水24-58份。
作为改进的是，上述降脂杀菌缝合线，包括以下按重量份数计的组分：聚乳酸65份、醋粉30份、纳豆粉5份、香茅草提取物3份、纳米银0.4份、聚羟基丁酸脂22份、维生素E6份、丝蛋白30份、透明质酸15份、改性壳聚糖3份、碳纤维45份、蚕丝纤维20份、聚乙二醇40份、去离子水45份。
作为改进的是，所述纳米银的粒径为10-25μｍ。
作为改进的是，所述碳纤维和蚕丝纤维的长度为10-15mm。
作为改进的是，所述改性壳聚糖的制备方法，包括以下步骤：步骤1，将壳聚糖清洗干净后，置于-80℃冰箱中冻干，研磨成细粉；步骤2，向细粉中加入二氧化钛混合搅拌，喷雾干燥得改性壳聚糖。
上述降脂杀菌缝合线的制备方法，包括以下步骤：第一步，称取各组分；第二步，将醋粉、纳豆粉、香茅草提取物、去离子水混合，搅拌均匀后，加入碳纤维，惰性环境下，文火煮12-20分钟后，喷雾干燥得混合粉；第三步，将纳米银、改性壳聚糖和蚕丝纤维混合，微波处理1-3分钟得改性蚕丝纤维；第四步，将聚乳酸、聚羟基丁酸脂、维生素E、丝蛋白、透明质酸、聚乙二醇、混合粉和改性蚕丝纤维混合搅拌，喷丝板出丝，吹风冷却成型后，再100-120℃热板上进行拉伸即得缝合线。
与现有技术相比，本发明降脂杀菌缝合线选材天然、工艺环保，安全无刺激，可完全生物降解，且降解后的成分融入机体，可降低机体内的胆固醇，提高免疫力，促进伤口的愈合。另外，本发明缝合线机械性能好，抗张能力强，摩擦性强，不易打结。
具体实施方式
下面通过具体实施例对本发明作进一步详细介绍。
实施例1
一种降脂杀菌缝合线，包括以下按重量份数计的组分：聚乳酸55份、醋粉12份、纳豆粉1份、香茅草提取物1份、纳米银0.2份、聚羟基丁酸脂14份、维生素E2份、丝蛋白24份、透明质酸12份、改性壳聚糖1份、碳纤维34份、蚕丝纤维14份、聚乙二醇35份、去离子水24份。
其中，所述纳米银的粒径为10μｍ。
所述碳纤维和蚕丝纤维的长度为10mm。
所述改性壳聚糖的制备方法，包括以下步骤：步骤1，将壳聚糖清洗干净后，置于-80℃冰箱中冻干，研磨成细粉；步骤2，向细粉中加入二氧化钛混合搅拌，喷雾干燥得改性壳聚糖。
上述降脂杀菌缝合线的制备方法，包括以下步骤：第一步，称取各组分；第二步，将醋粉、纳豆粉、香茅草提取物、去离子水混合，搅拌均匀后，加入碳纤维，惰性环境下，文火煮12分钟后，喷雾干燥得混合粉；第三步，将纳米银、改性壳聚糖和蚕丝纤维混合，微波处理1分钟得改性蚕丝纤维；第四步，将聚乳酸、聚羟基丁酸脂、维生素E、丝蛋白、透明质酸、聚乙二醇、混合粉和改性蚕丝纤维混合搅拌，喷丝板出丝，吹风冷却成型后，再100℃热板上进行拉伸即得缝合线。
实施例2
一种降脂杀菌缝合线，包括以下按重量份数计的组分：聚乳酸65份、醋粉30份、纳豆粉5份、香茅草提取物3份、纳米银0.4份、聚羟基丁酸脂22份、维生素E6份、丝蛋白30份、透明质酸15份、改性壳聚糖3份、碳纤维45份、蚕丝纤维20份、聚乙二醇40份、去离子水45份。
其中，所述纳米银的粒径为18μｍ。
所述碳纤维和蚕丝纤维的长度为12mm。
所述改性壳聚糖的制备方法，包括以下步骤：步骤1，将壳聚糖清洗干净后，置于-80℃冰箱中冻干，研磨成细粉；步骤2，向细粉中加入二氧化钛混合搅拌，喷雾干燥得改性壳聚糖。
上述降脂杀菌缝合线的制备方法，包括以下步骤：第一步，称取各组分；第二步，将醋粉、纳豆粉、香茅草提取物、去离子水混合，搅拌均匀后，加入碳纤维，惰性环境下，文火煮18分钟后，喷雾干燥得混合粉；第三步，将纳米银、改性壳聚糖和蚕丝纤维混合，微波处理1-3分钟得改性蚕丝纤维；第四步，将聚乳酸、聚羟基丁酸脂、维生素E、丝蛋白、透明质酸、聚乙二醇、混合粉和改性蚕丝纤维混合搅拌，喷丝板出丝，吹风冷却成型后，再110℃热板上进行拉伸即得缝合线。
实施例3
一种降脂杀菌缝合线，包括以下按重量份数计的组分：聚乳酸78份、醋粉35份、纳豆粉8份、香茅草提取物4份、纳米银0.8份、聚羟基丁酸脂27份、维生素E9份、丝蛋白48份、透明质酸18份、改性壳聚糖5份、碳纤维48份、蚕丝纤维24份、聚乙二醇48份、去离子水58份。
其中，所述纳米银的粒径为25μｍ。
所述碳纤维和蚕丝纤维的长度为15mm。
所述改性壳聚糖的制备方法，包括以下步骤：步骤1，将壳聚糖清洗干净后，置于-80℃冰箱中冻干，研磨成细粉；步骤2，向细粉中加入二氧化钛混合搅拌，喷雾干燥得改性壳聚糖。
上述降脂杀菌缝合线的制备方法，包括以下步骤：第一步，称取各组分；第二步，将醋粉、纳豆粉、香茅草提取物、去离子水混合，搅拌均匀后，加入碳纤维，惰性环境下，文火煮20分钟后，喷雾干燥得混合粉；第三步，将纳米银、改性壳聚糖和蚕丝纤维混合，微波处理1-3分钟得改性蚕丝纤维；第四步，将聚乳酸、聚羟基丁酸脂、维生素E、丝蛋白、透明质酸、聚乙二醇、混合粉和改性蚕丝纤维混合搅拌，喷丝板出丝，吹风冷却成型后，再120℃热板上进行拉伸即得缝合线。
对比例1
除不含纳豆粉外，其他同实施例2。
对比例2
除不含醋粉外，其他同实施例2。
对实施例1-3和对比例1-2的缝合线进行测试，所得数据如下表所示。
典型案例：
张某某，女，20岁，剖宫产后，采用实施例2的缝合线缝合，一周后切口愈合，疤痕不明显，未出现感染排异症状，术后25天，缝合线开始降解，术后30天，缝合线完全被吸收，并一直未出现并发症。
赵某，男，65岁，胆囊炎手术后用实施例2的缝合线缝合，8天后切口愈合，术后28天，缝合线开始降解，术后35天缝合线完全被吸收，且未出现并发症，另外该患者的血脂含量有所降低。
王某某，女，50岁，子宫肌瘤手术后采用对比例1的缝合线缝合，10天后切口愈合，术后30天缝合线开始降解，术后40天缝合线完全被吸收，切口微痒，但胆固醇含量为出现降低。
李某，男，45岁，车祸手术后采用对比例2的缝合线缝合，9后切口愈合，疤痕不明显，未出现感染排异症状，术后27天，缝合线开始降解，术后32天，缝合线完全被吸收，并一直未出现并发症。
从上述结果可以看出，本发明缝合线能促进伤口愈合，且能全部降解，不引起排异现象，尤其是患高血脂患者使用后，能明显降低血脂含量，具有良好的市场前景
另外，本发明不限于上述实施方式，只要在不超出本发明的范围内，可以采取各种方式实施本发明。

Claims (6)

1.一种降脂杀菌缝合线，其特征在于，包括以下按重量份数计的组分：聚乳酸55-78份、醋粉12-35份、纳豆粉1-8份、香茅草提取物1-4份、纳米银0.2-0.8份、聚羟基丁酸脂14-27份、维生素E2-9份、丝蛋白24-48份、透明质酸12-18份、改性壳聚糖1-5份、碳纤维34-48份、蚕丝纤维14-24份、聚乙二醇35-48份、去离子水24-58份。
2.根据权利要求1所述的一种降脂杀菌缝合线，其特征在于，聚乳酸65份、醋粉30份、纳豆粉5份、香茅草提取物3份、纳米银0.4份、聚羟基丁酸脂22份、维生素E6份、丝蛋白30份、透明质酸15份、改性壳聚糖3份、碳纤维45份、蚕丝纤维20份、聚乙二醇40份、去离子水45份。
3.根据权利要求1所述的一种降脂杀菌缝合线，其特征在于，所述纳米银的粒径为10-25μｍ。
4.根据权利要求1所述的一种降脂杀菌缝合线，其特征在于，所述碳纤维和蚕丝纤维的长度为10-15mm。
5.根据权利要求1所述的一种降脂杀菌缝合线，其特征在于，所述改性壳聚糖的制备方法，包括以下步骤：步骤1，将壳聚糖清洗干净后，置于-80℃冰箱中冻干，研磨成细粉；步骤2，向细粉中加入二氧化钛混合搅拌，喷雾干燥得改性壳聚糖。
6.基于权利要求1所述的一种降脂杀菌缝合线的制备方法，其特征在于，包括以下步骤：第一步，称取各组分；第二步，将醋粉、纳豆粉、香茅草提取物、去离子水混合，搅拌均匀后，加入碳纤维，惰性环境下，文火煮12-20分钟后，喷雾干燥得混合粉；第三步，将纳米银、改性壳聚糖和蚕丝纤维混合，微波处理1-3分钟得改性蚕丝纤维；第四步，将聚乳酸、聚羟基丁酸脂、维生素E、丝蛋白、透明质酸、聚乙二醇、混合粉和改性蚕丝纤维混合搅拌，喷丝板出丝，吹风冷却成型后，再100-120℃热板上进行拉伸即得缝合线。
CN201710810032.1A 2017-09-11 2017-09-11 一种降脂杀菌缝合线及其制备方法 Pending CN107375999A (zh)