CN107326523A - A kind of production method of the close towel cloth of new warp knit - Google Patents
A kind of production method of the close towel cloth of new warp knit Download PDFInfo
- Publication number
- CN107326523A CN107326523A CN201710600080.8A CN201710600080A CN107326523A CN 107326523 A CN107326523 A CN 107326523A CN 201710600080 A CN201710600080 A CN 201710600080A CN 107326523 A CN107326523 A CN 107326523A
- Authority
- CN
- China
- Prior art keywords
- yarn
- warp knit
- shrinkage
- towel
- warp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of production method of the close towel cloth of new warp knit, comprises the following steps:S1. the selection of specialty yarn;S2. warp knit is weaved;S3. dyeing is arranged;Beneficial effect:The inventive method ingenious use innovation raw material, arrange in combination with special dyeing, produce towel and have the advantages that looped pile is close, good hand feeling is comfortable, looped pile will not be good by hook pull-up, resilience.
Description
Technical field
The present invention relates to a kind of production method of comfortable towel, more particularly to a kind of close towel cloth of new warp knit
Production method.
Background technology
Traditional towel cloth generally includes woven towel and knitting towel(Warp knit)Two major classes, the protrusion of two class towels is excellent
Shortcoming:Relatively close, feel is compared plentiful relax between many, towel the looped pile of woven towel pattern variety change and looped pile
It is suitable, but consumer easily trigger in use looped pile, towel resilience it is relatively poor;And the fancy of warp-knitting towel
Variety variations are few, relatively evacuation, feel are compared lax not plentiful between towel looped pile and looped pile, but consumer is using
During will not trigger completely looped pile, towel resilience it is fine.In addition to towel pattern variety, phase between looped pile and looped pile
To will not be triggered completely during the more plentiful comfortable, use of relatively close, feel looped pile, towel resilience it is again fine, this
The towel of sample is the good product that middle and high end client wants to look for always, but existing market is without such product.Therefore it provides one kind can
The method for producing this product is necessary.
The content of the invention
It can produce that looped pile is close, good hand feeling is comfortable, resilience is fine, used it is an object of the invention to provide one kind
Journey will not trigger the towel production method of looped pile again, be weaved by the selection of specialty yarn, warp knit, dyeing is arranged, by woven hair
The certain advantages of towel are dissolved into warp-knitting towel, produce the towel of middle and high end customer demand.
Technical scheme:
A kind of production method of the close towel cloth of new warp knit, comprises the following steps:
S1. the selection of specialty yarn:From specialty yarn, the specialty yarn is the yarn or high convergency that high-shrinkage fibre is spun into
Larger contraction occurs after 50 ~ 130 DEG C of liquid boiling-offs in long filament, the special yarn, and its shrinkage factor is 15 ~ 90%;
S2. warp knit is weaved:Specialty yarn described in step S1 is weaved for warp knit, before weaving during warping, special yarn needs
It is arranged in parallel as middle at least one set of yarn and bottom and surface layer lower shrinkage yarn into the specialty yarn after axle individually into axle,
And fed by warp-wise on the relevant work pin of warp knitting machine, while lopping braiding is carried out, into the specialty yarn and bottom after axle
Set is gone here and there mutually with the lower shrinkage yarn on surface layer axle weaves warp knit towel fabric;
S3. dyeing is arranged:Warp knit towel fabric described in step S2 is carried out at a temperature of 50 ~ 130 DEG C high temperature boiling-off 40 ~
60min, warp knit towel fabric cannot pass through the drying and shaping that temperature is higher than 60 DEG C before high temperature boiling-off, after high temperature boiling-off
Warp knit towel fabric enters normal dyeing and finishing process.
It is preferred that, the horizontal door width shrinkage factor of the warp knit towel fabric described in step S2 or S3 is 5 ~ 30%.
Beneficial effect:The inventive method ingenious use is innovated raw material, arranged in combination with special dyeing, produces hair
Towel has the advantages that looped pile is close, good hand feeling comfortable, looped pile will not be good by hook pull-up, resilience.
Embodiment
Herein below is to combine specific preferred embodiment further description made for the present invention, it is impossible to assert
The specific implementation of the present invention is confined to these explanations, it is necessary to illustrate, in the case where not conflicting, the reality in the application
Applying the feature in example and embodiment can be mutually combined.
Embodiment 1:
A kind of production method of the close towel cloth of new warp knit of the present embodiment, by taking 40s/1 high-shrinkage polyester yarns as an example, it is walked
It is rapid as follows:
The selection of S1 specialty yarns:From specialty yarn, the specialty yarn is that 40s/1 high-shrinkage polyester yarns are a kind of high receipts
Larger receipts occur after 50 ~ 130 DEG C of liquid boiling-offs in the yarn that shrinkage fibers are spun into, the 40s/1 high-shrinkage polyesters yarn
Contracting, its shrinkage factor is 15 ~ 90%;
S2. warp knit is weaved:40s/1 high-shrinkage polyesters yarn described in step S1 is weaved for warp knit, before weaving during warping,
40s/1 high-shrinkage polyesters yarn is needed individually into axle, and middle at least one set of yarn is used as into the 40s/1 high-shrinkage polyesters yarn after axle
Line and bottom(Pure cotton)And surface layer(Pure cotton)Lower shrinkage yarn is arranged in parallel, and by the relevant work of warp-wise feeding warp knitting machine
On pin, while lopping braiding is carried out, into the 40s/1 high-shrinkage polyesters yarn and bottom after axle(Pure cotton)And surface layer(Pure cotton)On
Lower shrinkage yarn goes here and there mutually set and weaves pure cotton/high-shrinkage polyester warp knit towel fabric;
S3. dyeing is arranged:Pure cotton described in step S2/high-shrinkage polyester warp knit towel fabric is carried out at a temperature of 130 DEG C
High temperature boiling-off 50min, pure cotton/high-shrinkage polyester warp knit towel fabric cannot pass through the baking that temperature is higher than 60 DEG C before high temperature boiling-off
Dry sizing, pure cotton/high-shrinkage polyester warp knit towel fabric after high temperature boiling-off enters normal dyeing and finishing process.
The horizontal door width shrinkage factor of pure cotton/high-shrinkage polyester warp knit towel fabric described in step S2 or S3 is 15%.
Embodiment 2:
A kind of production method of the close towel cloth of new warp knit of the present embodiment, by taking 100D high-shrinkage polyester yarns as an example, it is walked
It is rapid as follows:
The selection of S1 specialty yarns:From specialty yarn, the specialty yarn is that 100D high-shrinkage polyester yarns are a kind of high receipts
Larger contraction occurs after 50 ~ 130 DEG C of liquid boiling-offs in the yarn that shrinkage fibers are spun into, the 100D high-shrinkage polyesters yarn,
Its shrinkage factor is 15 ~ 90%;
S2. warp knit is weaved:100D high-shrinkage polyesters yarn described in step S1 is weaved for warp knit, before weaving during warping,
150D high-shrinkage polyesters yarn is needed individually into axle, and middle one group of yarn and bottom are used as into the 100D high-shrinkage polyesters yarn after axle
Layer(Pure cotton)And surface layer(Bamboo fiber yarn)Lower shrinkage yarn is arranged in parallel, and by the relevant work of warp-wise feeding warp knitting machine
On pin, while lopping braiding is carried out, into the 100D high-shrinkage polyesters yarn and bottom after axle(Pure cotton)And surface layer(Bamboo fiber garn
Line)On lower shrinkage yarn go here and there set mutually and weave pure cotton/high-shrinkage polyester/bamboo fiber yarn warp knit towel fabric;
S3. dyeing is arranged:By pure cotton/high-shrinkage polyester described in step S2/bamboo fiber yarn warp knit towel fabric at 100 DEG C
At a temperature of carry out high temperature boiling-off 40min, pure cotton/high-shrinkage polyester/bamboo fiber yarn warp knit towel fabric is not before high temperature boiling-off
60 DEG C of drying and shaping can be higher than through excess temperature, pure cotton/high-shrinkage polyester after high temperature boiling-off/bamboo fiber yarn warp knit hair
Towel fabric enters normal dyeing and finishing process.
The horizontal door width of pure cotton/high-shrinkage polyester/bamboo fiber yarn warp knit towel fabric described in step S2 or S3 shrinks
Rate is 30%.
Embodiment 3:
A kind of production method of the close towel cloth of new warp knit of the present embodiment, by taking 60s/1 high-shrinkage polyester yarns as an example, it is walked
It is rapid as follows:
The selection of S1 specialty yarns:From specialty yarn, the specialty yarn is that 60s/1 high-shrinkage polyester yarns are a kind of high receipts
Larger receipts occur after 50 ~ 130 DEG C of liquid boiling-offs in the yarn that shrinkage fibers are spun into, the 60s/1 high-shrinkage polyesters yarn
Contracting, its shrinkage factor is 15 ~ 90%;
S2. warp knit is weaved:60s/1 high-shrinkage polyesters yarn described in step S1 is weaved for warp knit, before weaving during warping,
60s/1 high-shrinkage polyesters yarn is needed individually into axle, and middle at least one set of yarn is used as into the 60s/1 high-shrinkage polyesters yarn after axle
Line and bottom(Pure cotton)And surface layer(Pure cotton)Lower shrinkage yarn is arranged in parallel, and by the relevant work of warp-wise feeding warp knitting machine
On pin, while lopping braiding is carried out, into the 60s/1 high-shrinkage polyesters yarn and bottom after axle(Pure cotton)And surface layer(Pure cotton)On
Lower shrinkage yarn goes here and there mutually set and weaves pure cotton/high-shrinkage polyester warp knit towel fabric;
S3. dyeing is arranged:Pure cotton described in step S2/high-shrinkage polyester warp knit towel fabric is subjected to height at a temperature of 50 DEG C
Warm boiling-off 60min, pure cotton/high-shrinkage polyester warp knit towel fabric cannot pass through the drying that temperature is higher than 60 DEG C before high temperature boiling-off
Sizing, pure cotton/high-shrinkage polyester warp knit towel fabric after high temperature boiling-off enters normal dyeing and finishing process.
The horizontal door width shrinkage factor of pure cotton/high-shrinkage polyester warp knit towel fabric described in step S2 or S3 is 5%.
For general technical staff of the technical field of the invention, without departing from the inventive concept of the premise,
Some simple deduction or replace can also be made, protection scope of the present invention should be all considered as belonging to.
Claims (2)
1. a kind of production method of the close towel cloth of new warp knit, comprises the following steps:
S1. the selection of specialty yarn:From specialty yarn, the specialty yarn is the yarn or high convergency that high-shrinkage fibre is spun into
Larger contraction occurs after 50 ~ 130 DEG C of liquid boiling-offs in long filament, the special yarn, and its shrinkage factor is 15 ~ 90%;
S2. warp knit is weaved:Specialty yarn described in step S1 is weaved for warp knit, before weaving during warping, special yarn needs
It is arranged in parallel as middle at least one set of yarn and bottom and surface layer lower shrinkage yarn into the specialty yarn after axle individually into axle,
And fed by warp-wise on the relevant work pin of warp knitting machine, while lopping braiding is carried out, into the specialty yarn and bottom after axle
Set is gone here and there mutually with the lower shrinkage yarn on surface layer axle weaves warp knit towel fabric;
S3. dyeing is arranged:Warp knit towel fabric described in step S2 is carried out at a temperature of 50 ~ 130 DEG C high temperature boiling-off 40 ~
60min, warp knit towel fabric cannot pass through the drying and shaping that temperature is higher than 60 DEG C before high temperature boiling-off, after high temperature boiling-off
Warp knit towel fabric enters normal dyeing and finishing process.
2. a kind of production method of the close towel cloth of new warp knit, the warp described in step S2 or S3 according to claim 1
The horizontal door width shrinkage factor for compiling towel fabric is 5 ~ 30%.