CN107325790A - 一种地砖防滑剂配方及制备方法 - Google Patents

一种地砖防滑剂配方及制备方法 Download PDF

Info

Publication number
CN107325790A
CN107325790A CN201710627403.2A CN201710627403A CN107325790A CN 107325790 A CN107325790 A CN 107325790A CN 201710627403 A CN201710627403 A CN 201710627403A CN 107325790 A CN107325790 A CN 107325790A
Authority
CN
China
Prior art keywords
parts
floor tile
surfactant
agent prescription
sodium chloride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710627403.2A
Other languages
English (en)
Other versions
CN107325790B (zh
Inventor
郝福东
冯永伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hebei Chang Chang Surface Anti Slip Engineering Technology Co Ltd
Original Assignee
Hebei Chang Chang Surface Anti Slip Engineering Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hebei Chang Chang Surface Anti Slip Engineering Technology Co Ltd filed Critical Hebei Chang Chang Surface Anti Slip Engineering Technology Co Ltd
Priority to CN201710627403.2A priority Critical patent/CN107325790B/zh
Publication of CN107325790A publication Critical patent/CN107325790A/zh
Application granted granted Critical
Publication of CN107325790B publication Critical patent/CN107325790B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种地砖防滑剂配方，包括十八醇聚氧乙烯醚OP‑10、氟硅酸铵、表面活性剂A、表面活性剂B、氯化钠、果酸和水。使用本发明不会改变地砖额原貌，不破坏地砖；原有酸性较强的防滑剂，施工过后地砖的光泽度受到严重破坏，降低约20度以上，本发明施工过后地砖光泽度降低1‑5度，地砖受到零破坏；使用本发明的地砖，静摩擦系数可以达到0.936，远远超出了以往酸性液体腐蚀地砖达到的效果。

Description

一种地砖防滑剂配方及制备方法
技术领域
本发明属于防滑材料领域，涉及地砖防滑，具体的涉及一种地砖防滑剂配方及制备方法。
背景技术
随着人们生活水平的提高，地砖被广泛铺设在家庭、餐馆、广场等场所，可以说是无处不在。然而现有地砖在遇到水后没有防滑效果，成为了地砖行业难以攻克的难题。据中国疾控中心2013年度全国伤害监测数据，我国60岁以上老年人在家中发生跌倒比例占55.17％，跌倒造成骨折的占全部病例的30.24％，在跌倒的老年人中，大约40％-70％会发生伤害，需要进行医疗处理。跌倒卧床以后，老人的身体容易加速衰竭，引起肺栓塞、免疫力失调、抑郁等并发症，并可能因跌倒而缩短5-10年的健康期望寿命，58.8％的老年人因为跌倒而患上“跌倒恐惧症”，陷入“跌倒——丧失信心——不敢活动——衰弱——更易跌倒”的恶性循环。
传统地砖防滑剂通过勾兑一种酸性液体，涂刷在地砖表面，腐蚀地砖表面，让地砖达到防滑效果，这种防滑方式的缺点是破坏地砖完整性，静摩擦系数偏低，很容易形成污垢，时间长了失去防滑效果，且大大的破坏了地砖的光泽度。
发明内容
为解决上述技术问题，本发明提供了一种地砖防滑剂配方及制备方法，本防滑剂高效环保、施工简单、不破坏地砖表面。
本发明采用的技术方案为：一种地砖防滑剂配方，包括十八醇聚氧乙烯醚OP-10、氟硅酸铵、表面活性剂A、表面活性剂B、氯化钠、果酸和水。
进一步地，所述防滑剂配方按重量份数比为：十八醇聚氧乙烯醚OP-1018～25份、氟硅酸铵15～25份、表面活性剂A5～10份、表面活性剂B5～15份、氯化钠4～8份、果酸2～6份、纯净水40～60份。
进一步地，所述防滑剂配方按重量份数比为：十八醇聚氧乙烯醚OP-1020份、氟硅酸铵20份、表面活性剂A6份、表面活性剂B9份、氯化钠6份、果酸4份、纯净水51份
进一步地，所述一种地砖防滑剂配方的制备方法，包括如下步骤：按重量份数比在温度16～22度的室温下，将十八醇聚氧乙烯醚OP-10、氟硅酸铵、表面活性剂A、表面活性剂B搅拌均匀反应5分钟后，再加入氯化钠、果酸和水，即得本配方。
进一步地，所述表面活性剂A为快速渗透剂T、表面活性剂B为超强渗透剂JFC-E。
本发明获得的有益效果为：使用本发明不会改变地砖额原貌，不破坏地砖；原有酸性较强的防滑剂，施工过后地砖的光泽度受到严重破坏，降低约20度以上，本发明施工过后地砖光泽度降低1-5度，地砖受到零破坏；传统的技术防滑效果只能做到国家标准静摩擦系数0.5，防滑效果偏低，而使用本发明的地砖，静摩擦系数可以达到0.936(本数据由北京华安联合认证检测中心检测，报告编号为HAST-BG-2017-027)，远远超出了以往酸性液体腐蚀地砖达到的效果。
本发明具有超强的渗透力，能有效渗入并增宽地砖的毛细通道，其上层形成肉眼看不到坑凹，遇水或油渍时与脚底接触能形成物理的吸盘作用。
本发明可广泛应用于抛光砖、玻化砖、釉面砖、仿古砖、同质砖、马赛克、微晶石、大理石、花岗岩、防滑砖等的表面防滑处理。
具体实施方式
下面结合具体实施例对本发明做进一步详细说明
实施例1：所述防滑剂配方按重量份数比为：十八醇聚氧乙烯醚OP-1018份、氟硅酸铵15份、表面活性剂A5份、表面活性剂B5份、氯化钠4份、果酸2份、纯净水40份。
实施例2：所述防滑剂配方按重量份数比为：十八醇聚氧乙烯醚OP-1025份、氟硅酸铵25份、表面活性剂A10份、表面活性剂B15份、氯化钠8份、果酸6份、纯净水60份。
实施例3：所述防滑剂配方按重量份数比为：十八醇聚氧乙烯醚OP-1020份、氟硅酸铵20份、表面活性剂A6份、表面活性剂B9份、氯化钠6份、果酸4份、纯净水51份。
实施例4：所述防滑剂配方按重量份数比为：十八醇聚氧乙烯醚OP-1020份、氟硅酸铵18份、表面活性剂A7份、表面活性剂B8份、氯化钠5份、果酸4份、纯净水45份。
实施例5：所述防滑剂配方按重量份数比为：十八醇聚氧乙烯醚OP-1022份、氟硅酸铵23份、表面活性剂A8份、表面活性剂B12份、氯化钠6份、果酸5份、纯净水55份。
一种地砖防滑剂配方的制备方法，包括如下步骤：按重量份数比在温度16～22度的室温下，将十八醇聚氧乙烯醚OP-10、氟硅酸铵、表面活性剂A、表面活性剂B搅拌均匀反应5分钟后，再加入氯化钠、果酸和水，即得本配方。
采用本配方瓷砖处理前后物理指标
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (5)

1.一种地砖防滑剂配方，其特征在于：包括十八醇聚氧乙烯醚OP-10、氟硅酸铵、表面活性剂A、表面活性剂B、氯化钠、果酸和水。
2.根据权利要求1所述一种地砖防滑剂配方，其特征在于：所述防滑剂配方按重量份数比为：十八醇聚氧乙烯醚OP-10 18～25份、氟硅酸铵15～25份、表面活性剂A 5～10份、表面活性剂B 5～15份、氯化钠4～8份、果酸2～6份、纯净水40～60份。
3.根据权利要求2所述一种地砖防滑剂配方，其特征在于：所述防滑剂配方按重量份数比为：十八醇聚氧乙烯醚OP-10 20份、氟硅酸铵20份、表面活性剂A 6份、表面活性剂B 9份、氯化钠6份、果酸4份、纯净水51份。
4.如权利要求2所述一种地砖防滑剂配方的制备方法，其特征在于：包括如下步骤：按重量份数比在温度16～22度的室温下，将十八醇聚氧乙烯醚OP-10、氟硅酸铵、表面活性剂A、表面活性剂B搅拌均匀反应5分钟后，再加入氯化钠、果酸和水，即得本配方。
5.根据权利要求1-4任意一项所述一种地砖防滑剂配方，其特征在于：所述表面活性剂A为快速渗透剂T、表面活性剂B为超强渗透剂JFC-E。
CN201710627403.2A 2017-07-28 2017-07-28 一种地砖防滑剂的制备方法 Expired - Fee Related CN107325790B (zh)