CN107268114A - A kind of environment-friendly antibacterial deodorization garment material - Google Patents
A kind of environment-friendly antibacterial deodorization garment material Download PDFInfo
- Publication number
- CN107268114A CN107268114A CN201710523188.1A CN201710523188A CN107268114A CN 107268114 A CN107268114 A CN 107268114A CN 201710523188 A CN201710523188 A CN 201710523188A CN 107268114 A CN107268114 A CN 107268114A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- garment material
- environment
- friendly antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of environment-friendly antibacterial deodorization garment material, and the garment material is made into fabric body by yarn of antibiotic odourproof fiber, and gained fabric body is dyed and post-processes to obtain garment material finished product, and the antibiotic odourproof fiber includes the composition of following parts by weight：Modal fibre：20 ~ 30 parts, ptt fiber：5 ~ 10 parts, nanometer silver antimicrobial master batch：20 ~ 30 parts, polyacrylonitrile carbon fiber：10 ~ 15 parts, silk fiber：15 ~ 20 parts, methylcellulose：10 ~ 20 parts, chitosan：5 ~ 10 parts, stearmide：5 ~ 10 parts, deodorant：5 ~ 10 parts, water-soluble binder：5 ~ 10 parts.The garment material uses special antibiotic odourproof fiber, assigns fabric excellent antibacterial deodourizing performance, and antibiotic odourproof fiber composition design is rationally, and preparation cost is low, good in economic efficiency.
Description
Technical field
The invention belongs to garment material technical field, in particular it relates to a kind of environment-friendly antibacterial deodorization garment material.
Background technology
Clothes are made with fabric, and fabric is exactly the material for making clothes.It is used as one of clothes three elements, fabric
Can not only annotate the style and characteristic of clothes, and directly left and right the color of clothes, the expression effect of moulding.Presentation is come from
The noble quality of body is perfect, soft.
Modern times are produced on the clothes of formal social life institute wear, many blended yarn weaved fabrics from high-quality.And it is pure cotton, pure
The natural fabric such as hair, pure silk, pure fiber crops has become general cloth because there is the easily natural fabric such as wrinkle, yielding, compared with
It is few to be used as high-grade clothing materials.Blended yarn weaved fabric has natural fabric sweat-absorbing breathable, it is soft comfortable the characteristics of, chemical fibre face is absorbed again
Material is solid to wear well, overhangs the advantages of well-pressed, good luster color is vivid, has substantial amounts of high-grade high-quality blended yarn weaved fabric to be developed every year
Come.
Intelligence is ground data research centre data and shown：Price of the cotton goes up to cause entirely to produce chain cost and increased, and produce chain one is
Row product has to appreciate, and has exactly expedited the emergence of the new opportunity of apparel industry fabric, and the upgrading scapegoat zein fiber of cotton, bamboo are fine
Dimension, novel plant flaxen fiber etc. come on stage with glittering appearance, and these bio-based fabrics more save water and agricultural chemicals, symbol in process of production than cotton
Close the demand of consumer or even the whole society to low-carbon environment-friendly.
For garment surface flitch, the current country is primarily present following patent document：
Chinese patent Authorization Notice No.：CN206264479U, discloses a kind of fabric of air permeable waterproof deodorization, including fly knitted fabric
Layer, the inner chamber of the winged surface of second order bed of material is provided with air-vent, and the inner chamber of the air-vent is provided with carbon dust layer, the winged knitted fabric
The top and bottom of layer, which are symmetrically arranged with the top of deodorization layer, the deodorization layer, is provided with waterproof comfort liner, the utility model
It is simple in construction, it is easy to use, it is ingenious in design, using reliable, with very strong practicality and novelty, fly the surface of second order bed of material for once
Shaping, so as to save cost, air-vent and the carbon dust layer being arranged in air-vent can improve permeability, and carbon dust layer can be with
Peculiar smell is absorbed, the setting of deodorization layer causes fabric to have good sterilizing and anti-foul performance, and the setting of waterproof comfort liner causes fabric
With water resistance, and also the comfortableness of fabric is greatly improved.However, the fabric that the patent is provided, passes through deodorization
Layer realizes deodorant function, and odor-resistant result is not lasting.
The content of the invention
To solve above-mentioned problem, it is an object of the invention to provide a kind of environment-friendly antibacterial deodorization garment material, institute
Garment material is stated using special antibiotic odourproof fiber, assigns fabric excellent antibacterial deodourizing performance, and antibiotic odourproof fiber into
Divide reasonable in design, preparation cost is low, good in economic efficiency.
To reach above-mentioned purpose, the technical scheme is that：
A kind of environment-friendly antibacterial deodorization garment material, the garment material is made into fabric body, institute by yarn of antibiotic odourproof fiber
Fabric body is dyed and post-process to obtain garment material finished product, the antibiotic odourproof fiber include following parts by weight into
Point：Modal fibre：20 ~ 30 parts, ptt fiber：5 ~ 10 parts, nanometer silver antimicrobial master batch：20 ~ 30 parts, polyacrylonitrile carbon fiber：10
~ 15 parts, silk fiber：15 ~ 20 parts, methylcellulose：10 ~ 20 parts, chitosan：5 ~ 10 parts, stearmide：5 ~ 10 parts, deodorization
Agent：5 ~ 10 parts, water-soluble binder：5 ~ 10 parts.
Further, the antibiotic odourproof fiber includes the composition of following parts by weight：Modal fibre：25 ~ 30 parts, PTT is fine
Dimension：5 ~ 8 parts, nanometer silver antimicrobial master batch：25 ~ 30 parts, polyacrylonitrile carbon fiber：10 ~ 13 parts, silk fiber：15 ~ 18 parts, methyl
Cellulose：15 ~ 20 parts, chitosan：5 ~ 7 parts, stearmide：6 ~ 10 parts, deodorant：7 ~ 10 parts, water-soluble binder：5 ~ 8 parts.
Preferably, the antibiotic odourproof fiber includes the composition of following parts by weight：Modal fibre：25 parts, ptt fiber：7
Part, nanometer silver antimicrobial master batch：25 parts, polyacrylonitrile carbon fiber：13 parts, silk fiber：18 parts, methylcellulose：15 parts, shell gathers
Sugar：6 parts, stearmide：7 parts, deodorant：8 parts, water-soluble binder：8 parts.
Preferably, the nanometer silver antimicrobial master batch includes the composition of following parts by weight：Nano-Ag particles：20 ~ 30 parts, carry
Body：10 ~ 15 parts, polyester slice：30 ~ 40 parts, coupling agent：5 ~ 10 parts, dispersant：5 ~ 10 parts.
Preferably, the nanometer silver antimicrobial agglomerate preparation method comprises the following steps：Nano-Ag particles and carrier are reacted,
Make nano-Ag particles uniform adsorption into carrier, then with coupling agent and dispersant and being added in high-speed mixer, 180
At ~ 220 DEG C, mixer inner screw rotating speed is 200 ~ 300 revs/min, is kneaded 30 ~ 50 minutes, obtains powder, then by powder and with gathering
The extrusion of the mixed merga pass double screw extruder of ester section, shaping, pelletizing, obtain the nanometer silver antimicrobial master batch.
Preferably, the polyester slice is cut into slices for PBT.
Preferably, the carrier is particular type zeolite or SiO2。
Preferably, the dispersant is AEO, APES, aliphatic acid polyethenoxy ether
Or tristerin.
Preferably, the coupling agent is monoalkoxytitanates, monoalkoxy vinethene or many alkoxy vinyl ethers.
Preferably, the antibiotic odourproof fiber preparation method comprises the following steps：By Modal fibre, ptt fiber, poly- third
Alkene nitrile carbon fiber and silk fiber are uniformly mixed, and add nanometer silver antimicrobial master batch, methylcellulose, chitosan, stearmide, water
Soluble adhesive and deodorant, stirring, blending, are added in screw extruder and carry out melt extruded, by the melt fully melted
It is transported to by melt pipe in spinning manifold, 270 ~ 300 DEG C of manifold spinning temperature, 2500 ~ 3500m/min of spinning speed,
Extruded afterwards from the spray orifice of spinning head, tow carries out cooled and solidified in the crosswind that temperature is 18-20 DEG C, humidity is 58 ~ 60%
Into silk, it is then placed in boiling water and boils 20 ~ 25min, takes out drying, you can obtain the antibiotic odourproof fiber.
The beneficial effects of the present invention are：
The garment material uses special antibiotic odourproof fiber, assigns fabric excellent antibacterial deodourizing performance, and antibacterial deodourizing
Fibre composition is reasonable in design, and preparation cost is low, good in economic efficiency.
Embodiment
Below by specific embodiment, the present invention is described further, but embodiment is not intended to limit the protection of the present invention
Scope.
A kind of environment-friendly antibacterial deodorization garment material of the present invention, the garment material is using antibiotic odourproof fiber as yarn
Fabric body is made into, gained fabric body is dyed and post-processes to obtain garment material finished product, and the antibiotic odourproof fiber includes
The composition of following parts by weight：Modal fibre：20 ~ 30 parts, ptt fiber：5 ~ 10 parts, nanometer silver antimicrobial master batch：20 ~ 30 parts, gather
Acrylic carbon fibre：10 ~ 15 parts, silk fiber：15 ~ 20 parts, methylcellulose：10 ~ 20 parts, chitosan：5 ~ 10 parts, stearoyl
Amine：5 ~ 10 parts, deodorant：5 ~ 10 parts, water-soluble binder：5 ~ 10 parts.
Further, the antibiotic odourproof fiber includes the composition of following parts by weight：Modal fibre：25 ~ 30 parts, PTT is fine
Dimension：5 ~ 8 parts, nanometer silver antimicrobial master batch：25 ~ 30 parts, polyacrylonitrile carbon fiber：10 ~ 13 parts, silk fiber：15 ~ 18 parts, methyl
Cellulose：15 ~ 20 parts, chitosan：5 ~ 7 parts, stearmide：6 ~ 10 parts, deodorant：7 ~ 10 parts, water-soluble binder：5 ~ 8 parts.
Preferably, the antibiotic odourproof fiber includes the composition of following parts by weight：Modal fibre：25 parts, ptt fiber：7
Part, nanometer silver antimicrobial master batch：25 parts, polyacrylonitrile carbon fiber：13 parts, silk fiber：18 parts, methylcellulose：15 parts, shell gathers
Sugar：6 parts, stearmide：7 parts, deodorant：8 parts, water-soluble binder：8 parts.
Preferably, the nanometer silver antimicrobial master batch includes the composition of following parts by weight：Nano-Ag particles：20 ~ 30 parts, carry
Body：10 ~ 15 parts, polyester slice：30 ~ 40 parts, coupling agent：5 ~ 10 parts, dispersant：5 ~ 10 parts.
Preferably, the nanometer silver antimicrobial agglomerate preparation method comprises the following steps：Nano-Ag particles and carrier are reacted,
Make nano-Ag particles uniform adsorption into carrier, then with coupling agent and dispersant and being added in high-speed mixer, 180
At ~ 220 DEG C, mixer inner screw rotating speed is 200 ~ 300 revs/min, is kneaded 30 ~ 50 minutes, obtains powder, then by powder and with gathering
The extrusion of the mixed merga pass double screw extruder of ester section, shaping, pelletizing, obtain the nanometer silver antimicrobial master batch.
Preferably, the polyester slice is cut into slices for PBT.
Preferably, the carrier is particular type zeolite or SiO2。
Preferably, the dispersant is AEO, APES, aliphatic acid polyethenoxy ether
Or tristerin.
Preferably, the coupling agent is monoalkoxytitanates, monoalkoxy vinethene or many alkoxy vinyl ethers.
Preferably, the antibiotic odourproof fiber preparation method comprises the following steps：By Modal fibre, ptt fiber, poly- third
Alkene nitrile carbon fiber and silk fiber are uniformly mixed, and add nanometer silver antimicrobial master batch, methylcellulose, chitosan, stearmide, water
Soluble adhesive and deodorant, stirring, blending, are added in screw extruder and carry out melt extruded, by the melt fully melted
It is transported to by melt pipe in spinning manifold, 270 ~ 300 DEG C of manifold spinning temperature, 2500 ~ 3500m/min of spinning speed,
Extruded afterwards from the spray orifice of spinning head, tow carries out cooled and solidified in the crosswind that temperature is 18-20 DEG C, humidity is 58 ~ 60%
Into silk, it is then placed in boiling water and boils 20 ~ 25min, takes out drying, you can obtain the antibiotic odourproof fiber.
It should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the technology of invention
Scheme is modified or equivalent substitution, and without departing from the scope of technical solution of the present invention, it all should cover the power in the present invention
In sharp claimed range.
Claims (10)
1. a kind of environment-friendly antibacterial deodorization garment material, it is characterised in that the garment material is knitted by yarn of antibiotic odourproof fiber
Into fabric body, gained fabric body is dyed and post-processes to obtain garment material finished product, and the antibiotic odourproof fiber is included such as
The composition of lower parts by weight：Modal fibre：20 ~ 30 parts, ptt fiber：5 ~ 10 parts, nanometer silver antimicrobial master batch：20 ~ 30 parts, poly- third
Alkene nitrile carbon fiber：10 ~ 15 parts, silk fiber：15 ~ 20 parts, methylcellulose：10 ~ 20 parts, chitosan：5 ~ 10 parts, stearoyl
Amine：5 ~ 10 parts, deodorant：5 ~ 10 parts, water-soluble binder：5 ~ 10 parts.
2. a kind of environment-friendly antibacterial deodorization garment material according to claim 1, it is characterised in that the antibiotic odourproof fiber
Include the composition of following parts by weight：Modal fibre：25 ~ 30 parts, ptt fiber：5 ~ 8 parts, nanometer silver antimicrobial master batch：25 ~ 30 parts,
Polyacrylonitrile carbon fiber：10 ~ 13 parts, silk fiber：15 ~ 18 parts, methylcellulose：15 ~ 20 parts, chitosan：It is 5 ~ 7 parts, stearic
Acid amides：6 ~ 10 parts, deodorant：7 ~ 10 parts, water-soluble binder：5 ~ 8 parts.
3. a kind of environment-friendly antibacterial deodorization garment material according to claim 1, it is characterised in that the antibiotic odourproof fiber
Include the composition of following parts by weight：Modal fibre：25 parts, ptt fiber：7 parts, nanometer silver antimicrobial master batch：25 parts, polyacrylonitrile
Carbon fiber：13 parts, silk fiber：18 parts, methylcellulose：15 parts, chitosan：6 parts, stearmide：7 parts, deodorant：8 parts,
Water-soluble binder：8 parts.
4. a kind of environment-friendly antibacterial deodorization garment material according to any one of claim 1 ~ 3, it is characterised in that described to receive
The silver-colored antibacterial matrices of rice include the composition of following parts by weight：Nano-Ag particles：20 ~ 30 parts, carrier：10 ~ 15 parts, polyester slice：30~
40 parts, coupling agent：5 ~ 10 parts, dispersant：5 ~ 10 parts.
5. a kind of environment-friendly antibacterial deodorization garment material according to claim 4, it is characterised in that the nanometer silver antimicrobial is female
Grain preparation method comprises the following steps：Nano-Ag particles and carrier are reacted, make nano-Ag particles uniform adsorption into carrier, then
With coupling agent and dispersant and being added in high-speed mixer, at 180 ~ 220 DEG C, mixer inner screw rotating speed is 200 ~
300 revs/min, knead 30 ~ 50 minutes, obtain powder, then merga pass double screw extruder is mixed by powder and with polyester slice
Extrusion, shaping, pelletizing, obtain the nanometer silver antimicrobial master batch.
6. a kind of environment-friendly antibacterial deodorization garment material according to claim 4, it is characterised in that the polyester slice is
PBT cuts into slices.
7. a kind of environment-friendly antibacterial deodorization garment material according to claim 4, it is characterised in that the carrier boils to be extraordinary
Stone or SiO2。
8. a kind of environment-friendly antibacterial deodorization garment material according to claim 4, it is characterised in that the dispersant is fat
Alcohol APEO, APES, aliphatic acid polyethenoxy ether or tristerin.
9. a kind of environment-friendly antibacterial deodorization garment material according to claim 4, it is characterised in that the coupling agent is single alkane
Epoxide titanate esters, monoalkoxy vinethene or many alkoxy vinyl ethers.
10. a kind of environment-friendly antibacterial deodorization garment material according to claim 1, it is characterised in that the antibacterial deodourizing is fine
Dimension preparation method comprises the following steps：Modal fibre, ptt fiber, polyacrylonitrile carbon fiber and silk fiber are uniformly mixed,
Nanometer silver antimicrobial master batch, methylcellulose, chitosan, stearmide, water-soluble binder and deodorant are added, stirs, be blended,
It is added in screw extruder and carries out melt extruded, the melt fully melted is transported in spinning manifold by melt pipe,
270 ~ 300 DEG C of manifold spinning temperature, 2500 ~ 3500m/min of spinning speed is extruded, tow from the spray orifice of spinning head afterwards
Cooled and solidified is carried out in the crosswind that temperature is 18-20 DEG C, humidity is 58 ~ 60% into silk, be then placed in boiling water and boil 20 ~
25min, takes out drying, you can obtain the antibiotic odourproof fiber.