CN109629080A - A kind of antibacterial and the Graphene towel and preparation method thereof to promote blood circulation - Google Patents
A kind of antibacterial and the Graphene towel and preparation method thereof to promote blood circulation Download PDFInfo
- Publication number
- CN109629080A CN109629080A CN201910074499.3A CN201910074499A CN109629080A CN 109629080 A CN109629080 A CN 109629080A CN 201910074499 A CN201910074499 A CN 201910074499A CN 109629080 A CN109629080 A CN 109629080A
- Authority
- CN
- China
- Prior art keywords
- graphene
- towel
- fiber
- ultra
- blood circulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to household items technical fields, specially a kind of antibacterial and the Graphene towel to promote blood circulation, including (according to mass percent meter): graphene ultra-fine polyester fiber 30-45%, general fibre 10-25%, chitin fiber 5-15%, ultra-fine hollow terylene 25-35%, silica gel 3-4%, nano silver 1-2%.The invention also discloses a kind of antibacterial and the preparation methods of Graphene towel that promote blood circulation, comprising the following steps: S1: prepares cortex material;S2: composite spinning;S3: blended;S4: winder;S5: warping;S6: sizing;S7: weaving;S8: dyeing;S9: it arranges.Have the beneficial effect that antibacterial agent uses the nano-Ag particles using silica gel as carrier, graphene ultra-fine polyester fiber outer layer is distributed in by composite spinning mode, nano silver dosage can not only be reduced, and it reduces to graphene ultra-fine polyester fiber Effect on Mechanical Properties, antibiotic property is strong, elasticity is good, gas permeability is good, can industrial mass production.
Description
Technical field
The present invention relates to household items technical field, specially a kind of antibacterial and the Graphene towel to promote blood circulation and
Preparation method.
Background technique
For common cotton towel using cotton as raw material, the characteristic of pure cotton is that water suction is easy to damp, especially in plum rain season and south,
There was dampness in the air, and towel, which is constantly under humid air, is not easy drying, and such towel is easy for generating bacterium and mildew, cause using
Person's pruitus, allergy, or even skin disease must be gone up.
Summary of the invention
The purpose of the present invention is to provide a kind of antibacterial and the Graphene towel and preparation method thereof that promotes blood circulation, with
Solve the problems mentioned above in the background art.
To achieve the above object, the invention provides the following technical scheme: a kind of antibacterial and the graphene to promote blood circulation
Towel, including (according to mass percent meter): graphene ultra-fine polyester fiber 30-45%, general fibre 10-25%, chitin
Fiber 5-15%, ultra-fine hollow terylene 25-35%, silica gel 3-4%, nano silver 1-2%.
Preferably, the graphene ultra-fine polyester fiber is prepared by biomass graphene and terylene using prefabricated master batch technique
It forms, wherein biomass graphene is corncob graphene, and mass fraction 1.0%, far infrared incidence is 0.88.
Preferably, the general fibre is fine using ptt fiber, polypropylene fiber, Modal fibre, Niu Daier fiber, fibroin
One or more of dimension, cotton fiber, zein fiber, chitin fiber, bamboo charcoal fiber, wood-fibred, soybean fiber are blended
It forms.
Preferably, the diameter of the chitin fiber is 1.5D, and color is pure white.
Preferably, the Kong Rongwei 1.0-1.3cm of the silica gel3/ g, average pore size 10.0-15.0nm, specific surface area are
250.0-290.0m2/ g, water content are lower than 5%.
A kind of preparation method of antibacterial and the Graphene towel to promote blood circulation, comprising the following steps:
S1: preparing cortex material, and silica gel and nano silver investment grinder after evenly mixing, exist with chitin fiber
Under the conditions of 120-150 DEG C, cortex material is obtained through double-screw extruding pelletizing;
S2: composite spinning uses core-sheath by cortex material and graphene ultra-fine polyester fiber under inert gas protection
Spinning machine produces composite fibre silk, is cooled to room temperature, then by composite fibre silk under the conditions of 80-100 DEG C, is stretched, cut off,
Obtain functional fibre silk;
S3: it is blended, functional fibre silk pre-drawing is fed after carding machine with general fibre together, obtains scribbled;
S4: scribbled is twisted, is miscellaneous clearly, on doff bobbin by winder;
S5: warping draws the scribbled of certain radical and length from doff bobbin, forms a width yarn sheet, makes to mix
Yarn is tightly wound on warp beam in parallel to each other;
S6: then sizing is squeezed, dries, is wound by the scribbled on warp beam and at a piece of, and by slurries
Beam of a loom;
S7: weaving, using ultra-fine hollow terylene as ground warp and weft yarns, scribbled is plush yarn, is weaved, is obtained
To towel fabric;
S8: towel fabric is first bleached poststaining by dyeing;
S9: arranging, and stained towel fabric is punched, and sorts out, obtains finished product towel.
Preferably, in step 2, the dosage volume ratio 2:3 of the cortex material and graphene ultra-fine polyester fiber.
Preferably, in step 2, the composite fibre silk draw ratio is 3-4 times.
Preferably, in step 6, the slurries include (according to mass percent meter): converted starch 9%, starching smooth agent
1% and aqueous solvent 90%.
Compared with prior art, the beneficial effects of the present invention are:
1. present invention process is simple, rationally, antibacterial agent uses the nano-Ag particles using silica gel as carrier to formula, by compound
Spinning mode is distributed in graphene ultra-fine polyester fiber outer layer, can not only reduce nano silver dosage, but also reduce to graphite
Alkene ultra-fine polyester fiber Effect on Mechanical Properties, antibiotic property is strong, elasticity is good, gas permeability is good, can industrial mass production;
2. the present invention is in such a way that graphene ultra-fine polyester fiber incorporates graphene, when sticking towel, graphene hair
Far infrared not only promotes face's blood microcirculation out, but also expands face's pore, and cleaning effect is more preferably, and antibacterial anti-
Bacterium, it is environmentally protective, it is safe and secure.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1
The present invention provides a kind of technical solution: a kind of antibacterial and the Graphene towel to promote blood circulation, including (according to matter
Measure percentages): graphene ultra-fine polyester fiber 30%, general fibre 25%, chitin fiber 15%, ultra-fine hollow polyester are fine
Tie up 25%, silica gel 4%, nano silver 1%.
A kind of preparation method of antibacterial and the Graphene towel to promote blood circulation, comprising the following steps:
S1: preparing cortex material, and silica gel and nano silver investment grinder after evenly mixing, exist with chitin fiber
Under the conditions of 120 DEG C, cortex material is obtained through double-screw extruding pelletizing;
S2: composite spinning uses core-sheath by cortex material and graphene ultra-fine polyester fiber under inert gas protection
Spinning machine produces composite fibre silk, is cooled to room temperature, then composite fibre silk is stretched, cut off, obtained under the conditions of 80 DEG C
Functional fibre silk;
S3: it is blended, functional fibre silk pre-drawing is fed after carding machine with general fibre together, obtains scribbled;
S4: scribbled is twisted, is miscellaneous clearly, on doff bobbin by winder;
S5: warping draws the scribbled of certain radical and length from doff bobbin, forms a width yarn sheet, makes to mix
Yarn is tightly wound on warp beam in parallel to each other;
S6: then sizing is squeezed, dries, is wound by the scribbled on warp beam and at a piece of, and by slurries
Beam of a loom;
S7: weaving, using ultra-fine hollow terylene as ground warp and weft yarns, scribbled is plush yarn, is weaved, is obtained
To towel fabric;
S8: towel fabric is first bleached poststaining by dyeing;
S9: arranging, and stained towel fabric is punched, and sorts out, obtains finished product towel.
Wherein, graphene ultra-fine polyester fiber is prepared by biomass graphene and terylene using prefabricated master batch technique,
Wherein biomass graphene is corncob graphene, and mass fraction 1.0%, far infrared incidence is 0.88;It is common fine
Dimension uses ptt fiber;The diameter of chitin fiber is 1.5D, and color is pure white;The Kong Rongwei 1.2cm of silica gel3/ g, average hole
Diameter is 10nm, specific surface area 280.0m2/ g, water content 2%;In step 2, cortex material and graphene ultra-fine polyester fiber
Dosage volume ratio 2:3;In step 2, composite fibre silk draw ratio is 3 times;In step 6, slurries include (according to quality hundred
Divide than meter): converted starch 9%, starching smooth agent 1% and aqueous solvent 90%.
Embodiment 2
The present invention provides a kind of technical solution: a kind of antibacterial and the Graphene towel to promote blood circulation, including (according to matter
Measure percentages): graphene ultra-fine polyester fiber 35%, general fibre 20%, chitin fiber 15%, ultra-fine hollow polyester are fine
Tie up 25%, silica gel 4%, nano silver 1%.
A kind of preparation method of antibacterial and the Graphene towel to promote blood circulation, comprising the following steps:
S1: preparing cortex material, and silica gel and nano silver investment grinder after evenly mixing, exist with chitin fiber
Under the conditions of 130 DEG C, cortex material is obtained through double-screw extruding pelletizing;
S2: composite spinning uses core-sheath by cortex material and graphene ultra-fine polyester fiber under inert gas protection
Spinning machine produces composite fibre silk, is cooled to room temperature, then composite fibre silk is stretched, cut off, obtained under the conditions of 85 DEG C
Functional fibre silk;
S3: it is blended, functional fibre silk pre-drawing is fed after carding machine with general fibre together, obtains scribbled;
S4: scribbled is twisted, is miscellaneous clearly, on doff bobbin by winder;
S5: warping draws the scribbled of certain radical and length from doff bobbin, forms a width yarn sheet, makes to mix
Yarn is tightly wound on warp beam in parallel to each other;
S6: then sizing is squeezed, dries, is wound by the scribbled on warp beam and at a piece of, and by slurries
Beam of a loom;
S7: weaving, using ultra-fine hollow terylene as ground warp and weft yarns, scribbled is plush yarn, is weaved, is obtained
To towel fabric;
S8: towel fabric is first bleached poststaining by dyeing;
S9: arranging, and stained towel fabric is punched, and sorts out, obtains finished product towel.
Wherein, graphene ultra-fine polyester fiber is prepared by biomass graphene and terylene using prefabricated master batch technique,
Wherein biomass graphene is corncob graphene, and mass fraction 1.0%, far infrared incidence is 0.88;It is common fine
Dimension is using bamboo charcoal fiber and wood-fibred is blended forms;The diameter of chitin fiber is 1.5D, and color is pure white;The Kong Rong of silica gel
For 1.2cm3/ g, average pore size 10.0nm, specific surface area 280.0m2/ g, water content 2%;In step 2, cortex material and
The dosage volume ratio 2:3 of graphene ultra-fine polyester fiber;In step 2, composite fibre silk draw ratio is 3 times;In step 6,
Slurries include (according to mass percent meter): converted starch 9%, starching smooth agent 1% and aqueous solvent 90%.
Embodiment 3
The present invention provides a kind of technical solution: a kind of antibacterial and the Graphene towel to promote blood circulation, including (according to matter
Measure percentages): graphene ultra-fine polyester fiber 40%, general fibre 15%, chitin fiber 10%, ultra-fine hollow polyester are fine
Tie up 30%, silica gel 3%, nano silver 2%.
A kind of preparation method of antibacterial and the Graphene towel to promote blood circulation, comprising the following steps:
S1: preparing cortex material, and silica gel and nano silver investment grinder after evenly mixing, exist with chitin fiber
Under the conditions of 140 DEG C, cortex material is obtained through double-screw extruding pelletizing;
S2: composite spinning uses core-sheath by cortex material and graphene ultra-fine polyester fiber under inert gas protection
Spinning machine produces composite fibre silk, is cooled to room temperature, then composite fibre silk is stretched, cut off, obtained under the conditions of 90 DEG C
Functional fibre silk;
S3: it is blended, functional fibre silk pre-drawing is fed after carding machine with general fibre together, obtains scribbled;
S4: scribbled is twisted, is miscellaneous clearly, on doff bobbin by winder;
S5: warping draws the scribbled of certain radical and length from doff bobbin, forms a width yarn sheet, makes to mix
Yarn is tightly wound on warp beam in parallel to each other;
S6: then sizing is squeezed, dries, is wound by the scribbled on warp beam and at a piece of, and by slurries
Beam of a loom;
S7: weaving, using ultra-fine hollow terylene as ground warp and weft yarns, scribbled is plush yarn, is weaved, is obtained
To towel fabric;
S8: towel fabric is first bleached poststaining by dyeing;
S9: arranging, and stained towel fabric is punched, and sorts out, obtains finished product towel.
Wherein, graphene ultra-fine polyester fiber is prepared by biomass graphene and terylene using prefabricated master batch technique,
Wherein biomass graphene is corncob graphene, and mass fraction 1.0%, far infrared incidence is 0.88;It is common fine
Dimension uses Modal fibre;The diameter of chitin fiber is 1.5D, and color is pure white;The Kong Rongwei 1.0cm of silica gel3/ g is put down
Equal aperture is 12.0nm, specific surface area 250.0m2/ g, water content 2%;In step 2, cortex material and graphene is ultra-fine washs
The dosage volume ratio 2:3 of synthetic fibre fiber;In step 2, composite fibre silk draw ratio is 4 times;In step 6, slurries include (according to
Mass percent meter): converted starch 9%, starching smooth agent 1% and aqueous solvent 90%.
Embodiment 4
The present invention provides a kind of technical solution: a kind of antibacterial and the Graphene towel to promote blood circulation, including (according to matter
Measure percentages): graphene ultra-fine polyester fiber 45%, general fibre 10%, chitin fiber 5%, ultra-fine hollow polyester are fine
Tie up 35%, silica gel 3%, nano silver 2%.
A kind of preparation method of antibacterial and the Graphene towel to promote blood circulation, comprising the following steps:
S1: preparing cortex material, and silica gel and nano silver investment grinder after evenly mixing, exist with chitin fiber
Under the conditions of 150 DEG C, cortex material is obtained through double-screw extruding pelletizing;
S2: composite spinning uses core-sheath by cortex material and graphene ultra-fine polyester fiber under inert gas protection
Spinning machine produces composite fibre silk, is cooled to room temperature, then composite fibre silk is stretched, cut off, obtained under the conditions of 100 DEG C
To functional fibre silk;
S3: it is blended, functional fibre silk pre-drawing is fed after carding machine with general fibre together, obtains scribbled;
S4: scribbled is twisted, is miscellaneous clearly, on doff bobbin by winder;
S5: warping draws the scribbled of certain radical and length from doff bobbin, forms a width yarn sheet, makes to mix
Yarn is tightly wound on warp beam in parallel to each other;
S6: then sizing is squeezed, dries, is wound by the scribbled on warp beam and at a piece of, and by slurries
Beam of a loom;
S7: weaving, using ultra-fine hollow terylene as ground warp and weft yarns, scribbled is plush yarn, is weaved, is obtained
To towel fabric;
S8: towel fabric is first bleached poststaining by dyeing;
S9: arranging, and stained towel fabric is punched, and sorts out, obtains finished product towel.
Wherein, graphene ultra-fine polyester fiber is prepared by biomass graphene and terylene using prefabricated master batch technique,
Wherein biomass graphene is corncob graphene, and mass fraction 1.0%, far infrared incidence is 0.88;It is common fine
Dimension uses zein fiber;The diameter of chitin fiber is 1.5D, and color is pure white;The Kong Rongwei 1.3cm of silica gel3/ g, it is average
Aperture is 15.0nm, specific surface area 290.0m2/ g, water content 2%;In step 2, cortex material and graphene super fine polyester
The dosage volume ratio 2:3 of fiber;In step 2, composite fibre silk draw ratio is 4 times;In step 6, slurries include (according to matter
Measure percentages): converted starch 9%, starching smooth agent 1% and aqueous solvent 90%.
Using common cotton knop cloth as reference, four groups of above-mentioned embodiments are lain in a horizontal plane in the environment of same humidity
In, after standing 24 hours, the mean concentration (CFU/mL) of Escherichia coli and staphylococcus aureus is counted respectively, such as 1 institute of table
Show:
Table 1
Strain bacteriostasis rate calculating formula are as follows: (the strain mean concentration of common cotton knop cloth-embodiment strain concentration is flat
Mean value)/common cotton knop cloth strain mean concentration × 100%.
The Graphene towel they four groups of above-mentioned embodiments available antibacterial of the invention and promoted blood circulation, wherein
The towel bacteriostasis rate highest that embodiment 2 obtains, is worth of widely use.
The invention has the following advantages that present invention process is simple, rationally, antibacterial agent uses receiving using silica gel as carrier to formula
Rice Argent grain, is distributed in graphene ultra-fine polyester fiber outer layer by composite spinning mode, can not only reduce nano silver dosage,
And reduce to graphene ultra-fine polyester fiber Effect on Mechanical Properties, antibiotic property is strong, elasticity is good, gas permeability is good, can be industrial big
Large-scale production;The present invention is in such a way that graphene ultra-fine polyester fiber incorporates graphene, and when sticking towel, graphene is issued
Far infrared not only promotes face's blood microcirculation, but also expands face's pore, cleaning effect more preferably, and bacteriostasis antibiosis,
It is environmentally protective, it is safe and secure.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (9)
1. a kind of antibacterial and the Graphene towel to promote blood circulation, which is characterized in that including (according to mass percent meter): stone
Black alkene ultra-fine polyester fiber 30-45%, general fibre 10-25%, chitin fiber 5-15%, ultra-fine hollow terylene 25-
35%, silica gel 3-4%, nano silver 1-2%.
2. a kind of antibacterial according to claim 1 and the Graphene towel to promote blood circulation, it is characterised in that: the stone
Black alkene ultra-fine polyester fiber is prepared by biomass graphene and terylene using prefabricated master batch technique, wherein biomass graphene
For corncob graphene, mass fraction 1.0%, far infrared incidence is 0.88.
3. a kind of antibacterial according to claim 1 and the Graphene towel to promote blood circulation, it is characterised in that: described general
Perforating fiber uses ptt fiber, polypropylene fiber, Modal fibre, Niu Daier fiber, fibroin fiber, cotton fiber, zein fiber, first
One or more of shell cellulose fiber, bamboo charcoal fiber, wood-fibred, soybean fiber are blended to be formed.
4. a kind of antibacterial according to claim 1 and the Graphene towel to promote blood circulation, it is characterised in that: the first
The diameter of shell cellulose fiber is 1.5D, and color is pure white.
5. a kind of antibacterial according to claim 1 and the Graphene towel to promote blood circulation, it is characterised in that: the silicon
The Kong Rongwei 1.0-1.3cm of glue3/ g, average pore size 10.0-15.0nm, specific surface area 250.0-290.0m2/ g, water content
Lower than 5%.
6. the preparation method of a kind of antibacterial as described in any one in claim 1-5 and the Graphene towel to promote blood circulation,
Characterized by comprising the following steps:
S1: preparing cortex material, and silica gel and nano silver investment grinder are carried out after evenly mixing, with chitin fiber in 120-
Under the conditions of 150 DEG C, cortex material is obtained through double-screw extruding pelletizing;
S2: composite spinning, by cortex material and graphene ultra-fine polyester fiber under inert gas protection, with core-sheath spinning
Mechanism goes out composite fibre silk, is cooled to room temperature, then by composite fibre silk under the conditions of 80-100 DEG C, is stretched, cut off, and obtains
Functional fibre silk;
S3: it is blended, functional fibre silk pre-drawing is fed after carding machine with general fibre together, obtains scribbled;
S4: scribbled is twisted, is miscellaneous clearly, on doff bobbin by winder;
S5: warping draws the scribbled of certain radical and length from doff bobbin, forms a width yarn sheet, makes mixed yarn
Line is tightly wound on warp beam in parallel to each other;
S6: then sizing squeezes, dries, is wound into beam of a loom by the scribbled on warp beam and at a piece of, and by slurries;
S7: weaving, using ultra-fine hollow terylene as ground warp and weft yarns, scribbled is plush yarn, is weaved, obtains hair
Towel fabric;
S8: towel fabric is first bleached poststaining by dyeing;
S9: arranging, and stained towel fabric is punched, and sorts out, obtains finished product towel.
7. the preparation method of a kind of antibacterial according to claim 6 and the Graphene towel to promote blood circulation, feature
It is: in step 2, the dosage volume ratio 2:3 of the cortex material and graphene ultra-fine polyester fiber.
8. the preparation method of a kind of antibacterial according to claim 6 and the Graphene towel to promote blood circulation, feature
Be: in step 2, the composite fibre silk draw ratio is 3-4 times.
9. the preparation method of a kind of antibacterial according to claim 6 and the Graphene towel to promote blood circulation, feature
Be: in step 6, the slurries include (according to mass percent meter): converted starch 9%, starching smooth agent 1% and solvent
Water 90%.