CN108286083A - A kind of textile material and preparation method thereof with water-proof antibiotic ability - Google Patents
A kind of textile material and preparation method thereof with water-proof antibiotic ability Download PDFInfo
- Publication number
- CN108286083A CN108286083A CN201810093771.8A CN201810093771A CN108286083A CN 108286083 A CN108286083 A CN 108286083A CN 201810093771 A CN201810093771 A CN 201810093771A CN 108286083 A CN108286083 A CN 108286083A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- textile material
- proof antibiotic
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to textile material fields, and in particular to a kind of textile material and preparation method thereof with water-proof antibiotic ability；Its ingredient is by weight：Its ingredient is by weight：25 32 parts of cotton fiber,18 22 parts of flaxen fiber,13 16 parts of vinylon,9 13 parts of Fypro,3.5 5.5 parts of fire retardant,6.8 7.6 parts of adhesive,3.3 3.8 parts of cumyl peroxide,4.2 4.7 parts of dibenzoyl peroxide,7.8 10.5 parts of dispersant,12.6 14.2 parts of antiseptic and appropriate amount of deionized water,Textile material prepared by the present invention has water resistance good,Anti-microbial property is good,The advantages that wear-resisting property is good and flame retardant property is good,Nano phase ag_2 o and nano aluminium oxide are under fire retardant effect in the raw material that wherein prepared by the present invention,So that the antibacterial ability of nano phase ag_2 o and nano aluminium oxide is significantly improved,In addition,Outdoor water-proof clothes are made in textile material prepared by the present invention,Waterproof index has reached 6000mmH2O or more, water resistance are good.
Description
Technical field
The present invention relates to textile material fields, and in particular to a kind of textile material and its preparation with water-proof antibiotic ability
Method.
Background technology
Traditional textile material is primarily referred to as fiber, and fiber is the basic unit of textile material.The source of fiber, composition,
Preparation, form, performance are extremely abundant and complicated.In simple terms, fiber is divided into natural fiber and chemical fibre two major classes.According to fibre
Natural fiber is divided into plant fiber, animal fiber and mineral fiber by the substance source attribute of dimension.By raw material, processing side
The difference of method and constituent, and regenerated fiber, synthetic fibers and inorfil three classes can be divided into.
Textile can absorb the effluents such as the sweat of human secretory, sebum, under the suitable environment of temperature and humidity, live away from home
Microorganism on the textile can mass propagation, decompose human secretion, generate the substance that ammonia etc. carries peculiar smell, or on the fabric
Bacterial plaque is generated, so that in dress or application process, uncomfortable or harmful effect is generated to human body, textile generation is made to go mouldy, is crisp
Change even rotten.With the development and the improvement of people's living standards of society, the new market demand is produced, consumer wishes to spin
Fabric has antibacterial functions, to meet the comfortable living needs of civilization.In textile, natural fiber is arranged than synthetic fibers moisture absorption
Sweat performance is good and comfortable and easy to wear, and the personal clothing overwhelming majority such as underwear, socks, towel, sheet of people uses natural fiber material
Material, so natural fiber material becomes the main product of antibiotic fabric.Antibiotic fabric refer to do not change fabric sense organ itself or
Under the premise of physical and chemical character (such as intensity, water imbibition, feel, aberration), antibacterial is carried out to fabric with various antiseptics and is added
Work not only makes fibrous material itself that can resist microorganism decomposition and goes bad, can also make the microorganism devitalization of attachment on the fabric
Or not excessive multiplication, the quality of textile and the quality of life of consumer are improved, antibiotic fabric is made also to enter household consumption
Conduct arranges.
In addition, existing textile material performance requirement is also higher and higher, such as water resistance, flame retardant property and wearability
Energy is equal.
Invention content
In view of the deficiencies of the prior art, the present invention provides a kind of textile material with water-proof antibiotic ability, not only have
Have that water resistance is good, anti-microbial property is good, also has many advantages, such as that wearability and flame retardant property are good.
In order to achieve the above object, the present invention is achieved by the following technical programs：
A kind of textile material with water-proof antibiotic ability, ingredient is by weight：25-32 parts of cotton fiber, flaxen fiber 18-22
Part, 13-16 parts of vinylon, 9-13 parts of Fypro, 3.5-5.5 parts of fire retardant, adhesive 6.8-7.6
Part, 3.3-3.8 parts of cumyl peroxide, 4.2-4.7 parts of dibenzoyl peroxide, 7.8-10.5 parts of dispersant, antiseptic
12.6-14.2 parts and appropriate amount of deionized water.
Preferably, a kind of textile material with water-proof antibiotic ability, preparation method includes the following steps：
A, cotton fiber, flaxen fiber, vinylon and Fypro bubble are disappeared in the hydrogen peroxide of 4.2-4.8%
Poison activation, after impregnating 110-160min, in 60-65 DEG C of drying, Ultrasonic Pulverization 30min, ultrasonic power 200-250KW are obtained
Mixture, it is spare；
B, fire retardant, adhesive, cumyl peroxide, dibenzoyl peroxide, dispersant and antiseptic high temperature is placed in stir
It mixes in kettle, 33-39 parts of deionized waters is added into high-temperature stirring kettle, when 220-260 DEG C of temperature, mixing time 65-
76min, mixing speed 550-650r/min obtain water-proof antibiotic intermixture；
C, the water-proof antibiotic intermixture in mixture and step b in step a is added in high pressure homogenizer, is mixed equal
It is even, 230 DEG C are heated to, vapor is filled with, heat preservation stands 40min, device is depressurized to external atmosphere pressure, continues to be heated to
265-290 DEG C, keep the temperature 12-16min；
D, reactant spinning under closed environment in step c, is handled by drawing, deaerate drying, be cooled to room temperature up at
Product.
Preferably, described adhesive selects polyurethane, polystyrene, polyacrylate and ethylene-acetate ethylene copolymer
One of which is a variety of.
Preferably, the dispersant selects the mixture of lauryl sodium sulfate and neopelex, dodecane
Base sodium sulphate and neopelex component ratio are 1:3.
Preferably, the fire retardant selects tricresyl phosphate-diphenyl ester, tricresyl phosphate, triphenyl phosphate and phosphoric acid (2-
Ethylhexyl)-diphenyl ester.
Preferably, the antiseptic selects nano phase ag_2 o and nano aluminium oxide.
Preferably, the high pressure homogenizer pressure in the step c is 8.2-9.6MPa.
Preferably, the spinning speed in the step d is 1600-1800m/min.
Advantageous effect：
The present invention is with cotton fiber, flaxen fiber vinylon, Fypro, fire retardant, adhesive, peroxidating two
Isopropylbenzene, dibenzoyl peroxide, dispersant and antiseptic are as the raw material for preparing textile material, prepared textile material tool
Have the advantages that water resistance is good, anti-microbial property is good, wear-resisting property is good and flame retardant property is good.In the raw material that wherein prepared by the present invention
Nano phase ag_2 o and nano aluminium oxide are under fire retardant effect so that the antibacterial ability of nano phase ag_2 o and nano aluminium oxide obtains
It significantly improves.In addition, outdoor water-proof clothes are made in textile material prepared by the present invention, waterproof index has reached 6000mmH2O with
On, water resistance is good.
Specific implementation mode
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
The every other embodiment obtained under the premise of creative work, shall fall within the protection scope of the present invention.
Embodiment 1：
A kind of textile material with water-proof antibiotic ability, ingredient is by weight：25 parts of cotton fiber, gathers 22 parts of flaxen fiber
13 parts of vinyl formal fiber, 11 parts of Fypro, 3.5 parts of fire retardant, 6.8 parts of adhesive, cumyl peroxide 3.3
Part, 4.6 parts of dibenzoyl peroxide, 7.8 parts of dispersant, 14.2 parts of antiseptic and appropriate amount of deionized water.
A kind of textile material with water-proof antibiotic ability, preparation method includes the following steps：
A, cotton fiber, flaxen fiber, vinylon and Fypro bubble are sterilized in 4.2% hydrogen peroxide and is lived
Change, after impregnating 125min, in 60 DEG C of drying, Ultrasonic Pulverization 30min, ultrasonic power 250KW obtain mixture, spare；
B, fire retardant, adhesive, cumyl peroxide, dibenzoyl peroxide, dispersant and antiseptic high temperature is placed in stir
It mixes in kettle, 33 parts of deionized waters is added into high-temperature stirring kettle, when 240 DEG C of temperature, mixing time 65min, mixing speed
For 620r/min, water-proof antibiotic intermixture is obtained；
C, the water-proof antibiotic intermixture in mixture and step b in step a is added in high pressure homogenizer, is mixed equal
It is even, 230 DEG C are heated to, vapor is filled with, heat preservation stands 40min, device is depressurized to external atmosphere pressure, continues to be heated to 265
DEG C, keep the temperature 12min；
D, reactant spinning under closed environment in step c, is handled by drawing, deaerate drying, be cooled to room temperature up at
Product.
Adhesive selects polyurethane.
Dispersant selects the mixture of lauryl sodium sulfate and neopelex, lauryl sodium sulfate and ten
Dialkyl benzene sulfonic acids sodium component ratio is 1:3.
Fire retardant selects tricresyl phosphate-diphenyl ester, tricresyl phosphate, triphenyl phosphate and phosphoric acid (2- ethylhexyls)-
Diphenyl ester.
Antiseptic selects nano phase ag_2 o and nano aluminium oxide.
High pressure homogenizer pressure in step c is 8.2MPa.
Spinning speed in step d is 1730m/min.
Embodiment 2：
A kind of textile material with water-proof antibiotic ability, ingredient is by weight：27 parts of cotton fiber, gathers 18 parts of flaxen fiber
14 parts of vinyl formal fiber, 9 parts of Fypro, 4.2 parts of fire retardant, 7.4 parts of adhesive, cumyl peroxide 3.5
Part, 4.4 parts of dibenzoyl peroxide, 8.4 parts of dispersant, 13.5 parts of antiseptic and appropriate amount of deionized water.
A kind of textile material with water-proof antibiotic ability, preparation method includes the following steps：
A, cotton fiber, flaxen fiber, vinylon and Fypro bubble are sterilized in 4.4% hydrogen peroxide and is lived
Change, after impregnating 110min, in 62 DEG C of drying, Ultrasonic Pulverization 30min, ultrasonic power 200KW obtain mixture, spare；
B, fire retardant, adhesive, cumyl peroxide, dibenzoyl peroxide, dispersant and antiseptic high temperature is placed in stir
It mixes in kettle, 35 parts of deionized waters is added into high-temperature stirring kettle, when 220 DEG C of temperature, mixing time 69min, mixing speed
For 580r/min, water-proof antibiotic intermixture is obtained；
C, the water-proof antibiotic intermixture in mixture and step b in step a is added in high pressure homogenizer, is mixed equal
It is even, 230 DEG C are heated to, vapor is filled with, heat preservation stands 40min, device is depressurized to external atmosphere pressure, continues to be heated to 275
DEG C, keep the temperature 12min；
D, reactant spinning under closed environment in step c, is handled by drawing, deaerate drying, be cooled to room temperature up at
Product.
Adhesive select polyurethane, polystyrene, polyacrylate and ethylene-acetate ethylene copolymer one of which or
Person is a variety of.
Dispersant selects the mixture of lauryl sodium sulfate and neopelex, lauryl sodium sulfate and ten
Dialkyl benzene sulfonic acids sodium component ratio is 1:3.
Fire retardant selects tricresyl phosphate-diphenyl ester, tricresyl phosphate and phosphoric acid (2- ethylhexyls)-diphenyl ester.
Antiseptic selects nano phase ag_2 o and nano aluminium oxide.
High pressure homogenizer pressure in step c is 8.6MPa.
Spinning speed in step d is 1680m/min.
Embodiment 3：
A kind of textile material with water-proof antibiotic ability, ingredient is by weight：29 parts of cotton fiber, gathers 19 parts of flaxen fiber
15 parts of vinyl formal fiber, 10 parts of Fypro, 4.8 parts of fire retardant, 7.1 parts of adhesive, cumyl peroxide 3.6
Part, 4.3 parts of dibenzoyl peroxide, 9.3 parts of dispersant, 12.6 parts of antiseptic and appropriate amount of deionized water.
A kind of textile material with water-proof antibiotic ability, preparation method includes the following steps：
A, cotton fiber, flaxen fiber, vinylon and Fypro bubble are sterilized in 4.6% hydrogen peroxide and is lived
Change, after impregnating 160min, in 63 DEG C of drying, Ultrasonic Pulverization 30min, ultrasonic power 220KW obtain mixture, spare；
B, fire retardant, adhesive, cumyl peroxide, dibenzoyl peroxide, dispersant and antiseptic high temperature is placed in stir
It mixes in kettle, 37 parts of deionized waters is added into high-temperature stirring kettle, when 260 DEG C of temperature, mixing time 72min, mixing speed
For 550r/min, water-proof antibiotic intermixture is obtained；
C, the water-proof antibiotic intermixture in mixture and step b in step a is added in high pressure homogenizer, is mixed equal
It is even, 230 DEG C are heated to, vapor is filled with, heat preservation stands 40min, device is depressurized to external atmosphere pressure, continues to be heated to 283
DEG C, keep the temperature 13min；
D, reactant spinning under closed environment in step c, is handled by drawing, deaerate drying, be cooled to room temperature up at
Product.
Adhesive select polyurethane, polyacrylate and ethylene-acetate ethylene copolymer.
Dispersant selects the mixture of lauryl sodium sulfate and neopelex, lauryl sodium sulfate and ten
Dialkyl benzene sulfonic acids sodium component ratio is 1:3.
Fire retardant selects tricresyl phosphate-diphenyl ester, tricresyl phosphate, triphenyl phosphate and phosphoric acid (2- ethylhexyls)-
Diphenyl ester.
Antiseptic selects nano phase ag_2 o and nano aluminium oxide.
High pressure homogenizer pressure in step c is 9.1MPa.
Spinning speed in step d is 1600m/min.
Embodiment 4：
A kind of textile material with water-proof antibiotic ability, ingredient is by weight：32 parts of cotton fiber, gathers 21 parts of flaxen fiber
16 parts of vinyl formal fiber, 13 parts of Fypro, 5.5 parts of fire retardant, 7.6 parts of adhesive, cumyl peroxide 3.8
Part, 4.7 parts of dibenzoyl peroxide, 10.5 parts of dispersant, 13.1 parts of antiseptic and appropriate amount of deionized water.
A kind of textile material with water-proof antibiotic ability, preparation method includes the following steps：
A, cotton fiber, flaxen fiber, vinylon and Fypro bubble are sterilized in 4.8% hydrogen peroxide and is lived
Change, after impregnating 145min, in 65 DEG C of drying, Ultrasonic Pulverization 30min, ultrasonic power 230KW obtain mixture, spare；
B, fire retardant, adhesive, cumyl peroxide, dibenzoyl peroxide, dispersant and antiseptic high temperature is placed in stir
It mixes in kettle, 39 parts of deionized waters is added into high-temperature stirring kettle, when 235 DEG C of temperature, mixing time 76min, mixing speed
For 650r/min, water-proof antibiotic intermixture is obtained；
C, the water-proof antibiotic intermixture in mixture and step b in step a is added in high pressure homogenizer, is mixed equal
It is even, 230 DEG C are heated to, vapor is filled with, heat preservation stands 40min, device is depressurized to external atmosphere pressure, continues to be heated to 290
DEG C, keep the temperature 13min；
D, reactant spinning under closed environment in step c, is handled by drawing, deaerate drying, be cooled to room temperature up at
Product.
Adhesive selects polyacrylate.
Dispersant selects the mixture of lauryl sodium sulfate and neopelex, lauryl sodium sulfate and ten
Dialkyl benzene sulfonic acids sodium component ratio is 1:3.
Fire retardant selects tricresyl phosphate-diphenyl ester, tricresyl phosphate, triphenyl phosphate and phosphoric acid (2- ethylhexyls)-
Diphenyl ester.
Antiseptic selects nano phase ag_2 o and nano aluminium oxide.
High pressure homogenizer pressure in step c is 9.6MPa.
Spinning speed in step d is 1800m/min.
It should be noted that herein, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also include other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in process, method, article or equipment including the element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
Invention is explained in detail, it will be understood by those of ordinary skill in the art that：It still can be to aforementioned each implementation
Technical solution recorded in example is modified or equivalent replacement of some of the technical features；And these modification or
It replaces, the spirit and scope for various embodiments of the present invention technical solution that it does not separate the essence of the corresponding technical solution.
Claims (8)
1. a kind of textile material with water-proof antibiotic ability, which is characterized in that its ingredient is by weight：Cotton fiber 25-32
Part, 18-22 parts of flaxen fiber, 13-16 parts of vinylon, 9-13 parts of Fypro, 3.5-5.5 parts of fire retardant,
6.8-7.6 parts of adhesive, 3.3-3.8 parts of cumyl peroxide, 4.2-4.7 parts of dibenzoyl peroxide, dispersant 7.8-
10.5 parts, 12.6-14.2 parts of antiseptic and appropriate amount of deionized water.
2. a kind of textile material with water-proof antibiotic ability according to claim 1, which is characterized in that preparation method
Include the following steps：
A, cotton fiber, flaxen fiber, vinylon and Fypro bubble are disappeared in the hydrogen peroxide of 4.2-4.8%
Poison activation, after impregnating 110-160min, in 60-65 DEG C of drying, Ultrasonic Pulverization 30min, ultrasonic power 200-250KW are obtained
Mixture, it is spare；
B, fire retardant, adhesive, cumyl peroxide, dibenzoyl peroxide, dispersant and antiseptic high temperature is placed in stir
It mixes in kettle, 33-39 parts of deionized waters is added into high-temperature stirring kettle, when 220-260 DEG C of temperature, mixing time 65-
76min, mixing speed 550-650r/min obtain water-proof antibiotic intermixture；
C, the water-proof antibiotic intermixture in mixture and step b in step a is added in high pressure homogenizer, is mixed equal
It is even, 230 DEG C are heated to, vapor is filled with, heat preservation stands 40min, device is depressurized to external atmosphere pressure, continues to be heated to
265-290 DEG C, keep the temperature 12-16min；
D, reactant spinning under closed environment in step c, is handled by drawing, deaerate drying, be cooled to room temperature up at
Product.
3. according to a kind of textile material with water-proof antibiotic ability described in claim 1 is weighed, it is characterised in that：Described adhesive
Select polyurethane, polystyrene, polyacrylate and ethylene-acetate ethylene copolymer one of which or a variety of.
4. a kind of textile material with water-proof antibiotic ability according to claim 1, it is characterised in that：The dispersant
Select the mixture of lauryl sodium sulfate and neopelex, lauryl sodium sulfate and neopelex
Component ratio is 1:3.
5. a kind of textile material with water-proof antibiotic ability according to claim 1, it is characterised in that：The fire retardant
Select tricresyl phosphate-diphenyl ester, tricresyl phosphate, triphenyl phosphate and phosphoric acid (2- ethylhexyls)-diphenyl ester.
6. a kind of textile material with water-proof antibiotic ability according to claim 1, it is characterised in that：The antiseptic
Select nano phase ag_2 o and nano aluminium oxide.
7. a kind of textile material preparation method with water-proof antibiotic ability according to claim 1, it is characterised in that：Institute
It is 8.2-9.6MPa to state the high pressure homogenizer pressure in step c.
8. a kind of textile material preparation method with water-proof antibiotic ability according to claim 1, it is characterised in that：Institute
It is 1600-1800m/min to state the spinning speed in step d.