CN107237044A - A kind of facial mask non-woven fabrics of pro-skin excellent performance and preparation method thereof - Google Patents
A kind of facial mask non-woven fabrics of pro-skin excellent performance and preparation method thereof Download PDFInfo
- Publication number
- CN107237044A CN107237044A CN201710438041.2A CN201710438041A CN107237044A CN 107237044 A CN107237044 A CN 107237044A CN 201710438041 A CN201710438041 A CN 201710438041A CN 107237044 A CN107237044 A CN 107237044A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- parts
- facial mask
- pro
- sepiolite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of facial mask non-woven fabrics of pro-skin excellent performance, it is made up of the raw material below according to parts by weight：70 75 parts of terylene, 32 37 parts of Modal fibers, 25 29 parts of maleic anhydride grafted ethene acetate copolymer, 7 10 parts of modified meerschaum powder.The invention also discloses the preparation method of the facial mask non-woven fabrics of the pro-skin excellent performance.Facial mask non-woven fabrics prepared by the present invention has excellent pro-skin performance and water retention property, not alice, not bubbling, and skin feel is good, does not stimulate, skin is preferably absorbed facial mask nutrient solution, with wide market prospects.
Description
Technical field
The present invention relates to field of nonwoven fabric technology, the facial mask non-woven fabrics of specifically a kind of pro-skin excellent performance and its preparation
Method.
Background technology
Facial mask is a kind of carrier of face beautifying health keeping product, and it is also that most important purpose is to make up makeup removing and wash one's face still that its is most basic
So not enough cleaning, coordinates other essential ingredients to realize maintenance function on this basis, for example replenishing water and preserving moisture, whitening, anti-
Aging, Sage Extract etc..The action principle of facial mask, exactly using the of short duration time for being covered in face, is temporarily isolating the external world
Air and pollution, improve skin temperature, expand the pore of skin, promote sweat gland secretion and metabolism, make the oxygen-containing of skin
Amount rises, and the moisture for being conducive to skin to discharge in the product of epidermal cell metabolism and the oil substances of accumulation, facial mask oozes
Enter the cuticula of epidermis, skin is become soft, light is flexible naturally for skin.
At present, the most widely used facial mask base-material of in the market is non-woven fabrics, non-woven fabrics be it is a kind of using high polymer section,
Chopped fiber or long filament have soft, ventilative and planar structure non-woven fibre by what various web formations and concretion technology were formed
Fiber products.But existing facial mask is performed poor with the pro-skin performance and water retention property of non-woven fabrics, it is impossible to skin is preferably inhaled
Receive nutrient solution.
The content of the invention
It is an object of the invention to provide a kind of facial mask non-woven fabrics of pro-skin excellent performance and preparation method thereof, to solve
The problem of being proposed in above-mentioned background technology.
To achieve the above object, the present invention provides following technical scheme：
A kind of facial mask non-woven fabrics of pro-skin excellent performance, is made up of the raw material below according to parts by weight：70-75 parts of terylene,
32-37 parts of Modal fibers, maleic anhydride grafted ethene -25-29 parts of acetate copolymer, 7-10 parts of modified meerschaum powder.
It is used as further scheme of the invention：It is made up of the raw material below according to parts by weight：71-74 parts of terylene, Modal are fine
33-36 parts of dimension, maleic anhydride grafted ethene -26-28 parts of acetate copolymer, 8-9 parts of modified meerschaum powder.
It is used as further scheme of the invention：It is made up of the raw material below according to parts by weight：73 parts of terylene, Modal are fine
35 parts of dimension, 27 parts of maleic anhydride grafted ethene-acetate copolymer, 8 parts of modified meerschaum powder.
It is used as further scheme of the invention：The preparation method of the modified meerschaum powder is as follows：
a）Sepiolite is taken, coarse crushing crosses 20-30 mesh sieves, obtains sepiolite coarse powder；
b）In the citric acid solution that sepiolite coarse powder is put into 50%, then ultrasonication 50-55min soaks 24-30h, so
PH to 7.2-7.5 is adjusted using sodium hydroxide solution afterwards, 30-40min is stood, filtering obtains pretreatment sepiolite coarse powder；
c）Pretreatment sepiolite coarse powder is put into calcining furnace, at 580-600 DEG C after calcination processing 1-2h, natural cooling,
Obtain calcining sepiolite coarse powder；
d）Calcining sepiolite coarse powder is put into micronizer, crushes as 800-1000 targeted fine powders, produces modified Hai Pao
Stone flour.
It is used as further scheme of the invention：Step b）In, the consumption of 50% citric acid solution is sepiolite coarse powder weight
5 times.
It is used as further scheme of the invention：Step b）In, the ultrasonication temperature is 55-60 DEG C.
It is used as further scheme of the invention：Step b）In, the ultrasonication frequency is 38-40KHz.
The preparation method of the facial mask non-woven fabrics of the pro-skin excellent performance, step is as follows：
1）Modified meerschaum powder is prepared, it is standby；
2）Terylene and maleic anhydride grafted ethene-acetate copolymer are weighed, is added to the banbury that preheating is 115-120 DEG C
In, mixing process 3-4min obtains mixture A；
3）Modified meerschaum powder is weighed, adds to mixture A, continues mixing process 5-7min, obtain mixture B；
4）By mixture B it is thin it is logical 3-4 times after, send into spinning die head, obtain the first fiber；
5）First fiber and Modal fibers are uniformly mixed on feeding Web forming conveyer belt, continuous arlt's strata is formed；
6）Arlt's strata is passed through into hot-rolling mill, under the rolling of hot-rolling mill, non-woven fabrics base substrate is formed；
7）Non-woven fabrics base substrate is placed in fibroin liquid, ultrasonication 35-40min, then low temperature drying, produces skin-friendly
The excellent facial mask non-woven fabrics of energy.
It is used as further scheme of the invention：Step 7）In, the ultrasonication frequency is 28-32KHz.
It is used as further scheme of the invention：Step 7）In, the drying temperature of the low temperature drying is 55-60 DEG C.
Compared with prior art, the beneficial effects of the invention are as follows：
1st, the facial mask non-woven fabrics for preparing of the present invention has excellent pro-skin performance and water retention property, not alice, not bubbling, skin
Sense of touch is good, does not stimulate, and skin is preferably absorbed facial mask nutrient solution, with wide market prospects；
2nd, the facial mask non-woven fabrics for preparing of the present invention, component is simple, can large-scale production, with important market value and society
It can be worth.
Embodiment
Technical scheme is described in more detail with reference to embodiment.
Embodiment 1
A kind of facial mask non-woven fabrics of pro-skin excellent performance, is made up of the raw material below according to parts by weight：70 parts of terylene, Modal
32 parts of fiber, 25 parts of maleic anhydride grafted ethene-acetate copolymer, 7 parts of modified meerschaum powder；
The preparation method of the modified meerschaum powder is as follows：
a）Sepiolite is taken, coarse crushing crosses 20 mesh sieves, obtains sepiolite coarse powder；
b）In the citric acid solution that sepiolite coarse powder is put into 50%, then ultrasonication 50min soaks 24h, then uses
Sodium hydroxide solution adjusts pH to 7.2, stands 30min, and filtering obtains pretreatment sepiolite coarse powder, wherein, 50% citric acid solution
Consumption be 5 times of sepiolite coarse powder weight, the ultrasonication temperature is 55 DEG C, and ultrasonication frequency is 38KHz；
c）Pretreatment sepiolite coarse powder is put into calcining furnace, at 580 DEG C after calcination processing 1h, natural cooling, forged
Burn sepiolite coarse powder；
d）Calcining sepiolite coarse powder is put into micronizer, crushes as 800 targeted fine powders, produces modified meerschaum powder.
In the present embodiment, the preparation method of the facial mask non-woven fabrics of the pro-skin excellent performance, step is as follows：
1）Modified meerschaum powder is prepared, it is standby；
2）Terylene and maleic anhydride grafted ethene-acetate copolymer are weighed, adds and extremely preheats in the banbury for 115 DEG C,
Mixing process 3min, obtains mixture A；
3）Modified meerschaum powder is weighed, adds to mixture A, continues mixing process 5min, obtain mixture B；
4）After thin logical 3 times of mixture B, spinning die head is sent into, the first fiber is obtained；
5）First fiber and Modal fibers are uniformly mixed on feeding Web forming conveyer belt, continuous arlt's strata is formed；
6）Arlt's strata is passed through into hot-rolling mill, under the rolling of hot-rolling mill, non-woven fabrics base substrate is formed；
7）Non-woven fabrics base substrate is placed in fibroin liquid, ultrasonication 35min, then low temperature drying, produces pro-skin performance
Excellent facial mask non-woven fabrics, wherein, the ultrasonication frequency is 28KHz, and the drying temperature of the low temperature drying is 55
℃。
Embodiment 2
A kind of facial mask non-woven fabrics of pro-skin excellent performance, is made up of the raw material below according to parts by weight：71 parts of terylene, Modal
33 parts of fiber, 28 parts of maleic anhydride grafted ethene-acetate copolymer, 9 parts of modified meerschaum powder；
The preparation method of the modified meerschaum powder is as follows：
a）Sepiolite is taken, coarse crushing crosses 20 mesh sieves, obtains sepiolite coarse powder；
b）In the citric acid solution that sepiolite coarse powder is put into 50%, then ultrasonication 52min soaks 25h, then uses
Sodium hydroxide solution adjusts pH to 7.2, stands 32min, and filtering obtains pretreatment sepiolite coarse powder, wherein, 50% citric acid solution
Consumption be 5 times of sepiolite coarse powder weight, the ultrasonication temperature is 56 DEG C, and ultrasonication frequency is 38KHz；
c）Pretreatment sepiolite coarse powder is put into calcining furnace, at 590 DEG C after calcination processing 1.5h, natural cooling, obtained
Calcine sepiolite coarse powder；
d）Calcining sepiolite coarse powder is put into micronizer, crushes as 800 targeted fine powders, produces modified meerschaum powder.
In the present embodiment, the preparation method of the facial mask non-woven fabrics of the pro-skin excellent performance, step is as follows：
1）Modified meerschaum powder is prepared, it is standby；
2）Terylene and maleic anhydride grafted ethene-acetate copolymer are weighed, adds and extremely preheats in the banbury for 116 DEG C,
Mixing process 3min, obtains mixture A；
3）Modified meerschaum powder is weighed, adds to mixture A, continues mixing process 5.5min, obtain mixture B；
4）After thin logical 4 times of mixture B, spinning die head is sent into, the first fiber is obtained；
5）First fiber and Modal fibers are uniformly mixed on feeding Web forming conveyer belt, continuous arlt's strata is formed；
6）Arlt's strata is passed through into hot-rolling mill, under the rolling of hot-rolling mill, non-woven fabrics base substrate is formed；
7）Non-woven fabrics base substrate is placed in fibroin liquid, ultrasonication 36min, then low temperature drying, produces pro-skin performance
Excellent facial mask non-woven fabrics, wherein, the ultrasonication frequency is 29KHz, and the drying temperature of the low temperature drying is 58
℃。
Embodiment 3
A kind of facial mask non-woven fabrics of pro-skin excellent performance, is made up of the raw material below according to parts by weight：73 parts of terylene, Modal
35 parts of fiber, 27 parts of maleic anhydride grafted ethene-acetate copolymer, 8 parts of modified meerschaum powder；
The preparation method of the modified meerschaum powder is as follows：
a）Sepiolite is taken, coarse crushing crosses 25 mesh sieves, obtains sepiolite coarse powder；
b）In the citric acid solution that sepiolite coarse powder is put into 50%, then ultrasonication 53min soaks 27h, then uses
Sodium hydroxide solution adjusts pH to 7.3, stands 35min, and filtering obtains pretreatment sepiolite coarse powder, wherein, 50% citric acid solution
Consumption be 5 times of sepiolite coarse powder weight, the ultrasonication temperature is 58 DEG C, and ultrasonication frequency is 39KHz；
c）Pretreatment sepiolite coarse powder is put into calcining furnace, at 590 DEG C after calcination processing 1.5h, natural cooling, obtained
Calcine sepiolite coarse powder；
d）Calcining sepiolite coarse powder is put into micronizer, crushes as 900 targeted fine powders, produces modified meerschaum powder.
In the present embodiment, the preparation method of the facial mask non-woven fabrics of the pro-skin excellent performance, step is as follows：
1）Modified meerschaum powder is prepared, it is standby；
2）Terylene and maleic anhydride grafted ethene-acetate copolymer are weighed, adds and extremely preheats in the banbury for 118 DEG C,
Mixing process 3.5min, obtains mixture A；
3）Modified meerschaum powder is weighed, adds to mixture A, continues mixing process 6min, obtain mixture B；
4）After thin logical 4 times of mixture B, spinning die head is sent into, the first fiber is obtained；
5）First fiber and Modal fibers are uniformly mixed on feeding Web forming conveyer belt, continuous arlt's strata is formed；
6）Arlt's strata is passed through into hot-rolling mill, under the rolling of hot-rolling mill, non-woven fabrics base substrate is formed；
7）Non-woven fabrics base substrate is placed in fibroin liquid, ultrasonication 37min, then low temperature drying, produces pro-skin performance
Excellent facial mask non-woven fabrics, wherein, the ultrasonication frequency is 30KHz, and the drying temperature of the low temperature drying is 57
℃。
Embodiment 4
A kind of facial mask non-woven fabrics of pro-skin excellent performance, is made up of the raw material below according to parts by weight：74 parts of terylene, Modal
36 parts of fiber, 26 parts of maleic anhydride grafted ethene-acetate copolymer, 8 parts of modified meerschaum powder；
The preparation method of the modified meerschaum powder is as follows：
a）Sepiolite is taken, coarse crushing crosses 30 mesh sieves, obtains sepiolite coarse powder；
b）In the citric acid solution that sepiolite coarse powder is put into 50%, then ultrasonication 54min soaks 28h, then uses
Sodium hydroxide solution adjusts pH to 7.5, stands 38min, and filtering obtains pretreatment sepiolite coarse powder, wherein, 50% citric acid solution
Consumption be 5 times of sepiolite coarse powder weight, the ultrasonication temperature is 60 DEG C, and ultrasonication frequency is 40KHz；
c）Pretreatment sepiolite coarse powder is put into calcining furnace, at 590 DEG C after calcination processing 2h, natural cooling, forged
Burn sepiolite coarse powder；
d）Calcining sepiolite coarse powder is put into micronizer, crushes as 1000 targeted fine powders, produces modified meerschaum powder.
In the present embodiment, the preparation method of the facial mask non-woven fabrics of the pro-skin excellent performance, step is as follows：
1）Modified meerschaum powder is prepared, it is standby；
2）Terylene and maleic anhydride grafted ethene-acetate copolymer are weighed, adds and extremely preheats in the banbury for 120 DEG C,
Mixing process 3.5min, obtains mixture A；
3）Modified meerschaum powder is weighed, adds to mixture A, continues mixing process 6.5min, obtain mixture B；
4）After thin logical 3 times of mixture B, spinning die head is sent into, the first fiber is obtained；
5）First fiber and Modal fibers are uniformly mixed on feeding Web forming conveyer belt, continuous arlt's strata is formed；
6）Arlt's strata is passed through into hot-rolling mill, under the rolling of hot-rolling mill, non-woven fabrics base substrate is formed；
7）Non-woven fabrics base substrate is placed in fibroin liquid, ultrasonication 40min, then low temperature drying, produces pro-skin performance
Excellent facial mask non-woven fabrics, wherein, the ultrasonication frequency is 31KHz, and the drying temperature of the low temperature drying is 60
℃。
Embodiment 5
A kind of facial mask non-woven fabrics of pro-skin excellent performance, is made up of the raw material below according to parts by weight：75 parts of terylene, Modal
37 parts of fiber, 29 parts of maleic anhydride grafted ethene-acetate copolymer, 10 parts of modified meerschaum powder；
The preparation method of the modified meerschaum powder is as follows：
a）Sepiolite is taken, coarse crushing crosses 30 mesh sieves, obtains sepiolite coarse powder；
b）In the citric acid solution that sepiolite coarse powder is put into 50%, then ultrasonication 55min soaks 30h, then uses
Sodium hydroxide solution adjusts pH to 7.5, stands 40min, and filtering obtains pretreatment sepiolite coarse powder, wherein, 50% citric acid solution
Consumption be 5 times of sepiolite coarse powder weight, the ultrasonication temperature is 60 DEG C, and ultrasonication frequency is 40KHz；
c）Pretreatment sepiolite coarse powder is put into calcining furnace, at 600 DEG C after calcination processing 2h, natural cooling, forged
Burn sepiolite coarse powder；
d）Calcining sepiolite coarse powder is put into micronizer, crushes as 1000 targeted fine powders, produces modified meerschaum powder.
In the present embodiment, the preparation method of the facial mask non-woven fabrics of the pro-skin excellent performance, step is as follows：
1）Modified meerschaum powder is prepared, it is standby；
2）Terylene and maleic anhydride grafted ethene-acetate copolymer are weighed, adds and extremely preheats in the banbury for 120 DEG C,
Mixing process 4min, obtains mixture A；
3）Modified meerschaum powder is weighed, adds to mixture A, continues mixing process 7min, obtain mixture B；
4）After thin logical 4 times of mixture B, spinning die head is sent into, the first fiber is obtained；
5）First fiber and Modal fibers are uniformly mixed on feeding Web forming conveyer belt, continuous arlt's strata is formed；
6）Arlt's strata is passed through into hot-rolling mill, under the rolling of hot-rolling mill, non-woven fabrics base substrate is formed；
7）Non-woven fabrics base substrate is placed in fibroin liquid, ultrasonication 40min, then low temperature drying, produces pro-skin performance
Excellent facial mask non-woven fabrics, wherein, the ultrasonication frequency is 32KHz, and the drying temperature of the low temperature drying is 60
℃。
Comparative example 1
Compared with Example 3, without modified meerschaum powder, other are same as Example 3.
Comparative example 2
Compared with Example 3, without maleic anhydride grafted ethene-acetate copolymer, other are same as Example 3.
Comparative example 3
Compared with Example 3, without modified meerschaum powder and maleic anhydride grafted ethene-acetate copolymer, other and reality
Apply example 3 identical.
Facial mask is made to the embodiment 1-5 and comparative example 1-3 non-woven fabrics prepared, using effect experiment is carried out.
Test method is：By above-mentioned facial mask with 10min in same condition immersion distilled water, using effect is then notified.
Result of the test is as shown in the table.
The pro-skin performance and water retention property of embodiment 3 are superior to comparative example 1-3, and comparative example 1-2 pro-skin performance and guarantor
It is aqueous to be superior to comparative example 3.It can therefore be seen that facial mask non-woven fabrics of the present invention is by adding modified meerschaum powder and Malaysia
Anhydride grafted ethylene-acetate copolymer, is conducive to improving the pro-skin performance and water retention property of facial mask non-woven fabrics.
Facial mask non-woven fabrics prepared by the present invention has excellent pro-skin performance and water retention property, not alice, not bubbling, skin
Skin sense of touch is good, does not stimulate, and skin is preferably absorbed facial mask nutrient solution, with wide market prospects；Face prepared by the present invention
Film non-woven fabrics, component is simple, can large-scale production, with important market value and social value.
The better embodiment to the present invention is explained in detail above, but the present invention is not limited to above-mentioned embodiment party
, can also be on the premise of present inventive concept not be departed from formula, the knowledge that one skilled in the relevant art possesses
Various changes can be made.
Claims (10)
1. a kind of facial mask non-woven fabrics of pro-skin excellent performance, it is characterised in that be made up of the raw material below according to parts by weight：Wash
70-75 parts of synthetic fibre, 32-37 parts of Modal fibers, maleic anhydride grafted ethene -25-29 parts of acetate copolymer, modified meerschaum
7-10 parts of powder.
2. the facial mask non-woven fabrics of pro-skin excellent performance according to claim 1, it is characterised in that by below according to weight
The raw material of part is made：71-74 parts of terylene, 33-36 parts of Modal fibers, maleic anhydride grafted ethene-acetate copolymer 26-
28 parts, 8-9 parts of modified meerschaum powder.
3. the facial mask non-woven fabrics of pro-skin excellent performance according to claim 2, it is characterised in that by below according to weight
The raw material of part is made：73 parts of terylene, 35 parts of Modal fibers, 27 parts of maleic anhydride grafted ethene-acetate copolymer, modification
8 parts of sepiolite powder.
4. the facial mask non-woven fabrics of pro-skin excellent performance according to claim 1, it is characterised in that the modified meerschaum
The preparation method of powder is as follows：
a）Sepiolite is taken, coarse crushing crosses 20-30 mesh sieves, obtains sepiolite coarse powder；
b）In the citric acid solution that sepiolite coarse powder is put into 50%, then ultrasonication 50-55min soaks 24-30h, so
PH to 7.2-7.5 is adjusted using sodium hydroxide solution afterwards, 30-40min is stood, filtering obtains pretreatment sepiolite coarse powder；
c）Pretreatment sepiolite coarse powder is put into calcining furnace, at 580-600 DEG C after calcination processing 1-2h, natural cooling,
Obtain calcining sepiolite coarse powder；
d）Calcining sepiolite coarse powder is put into micronizer, crushes as 800-1000 targeted fine powders, produces modified Hai Pao
Stone flour.
5. the facial mask non-woven fabrics of pro-skin excellent performance according to claim 4, it is characterised in that step b）In, 50% lemon
The consumption of lemon acid solution is 5 times of sepiolite coarse powder weight.
6. the facial mask non-woven fabrics of pro-skin excellent performance according to claim 4, it is characterised in that step b）In, it is described
Ultrasonication temperature is 55-60 DEG C.
7. the facial mask non-woven fabrics of pro-skin excellent performance according to claim 4, it is characterised in that step b）In, it is described
Ultrasonication frequency is 38-40KHz.
8. a kind of preparation method of the facial mask non-woven fabrics of pro-skin excellent performance as described in claim 1-7 is any, its feature
It is, step is as follows：
1）Modified meerschaum powder is prepared, it is standby；
2）Terylene and maleic anhydride grafted ethene-acetate copolymer are weighed, is added to the banbury that preheating is 115-120 DEG C
In, mixing process 3-4min obtains mixture A；
3）Modified meerschaum powder is weighed, adds to mixture A, continues mixing process 5-7min, obtain mixture B；
4）By mixture B it is thin it is logical 3-4 times after, send into spinning die head, obtain the first fiber；
5）First fiber and Modal fibers are uniformly mixed on feeding Web forming conveyer belt, continuous arlt's strata is formed；
6）Arlt's strata is passed through into hot-rolling mill, under the rolling of hot-rolling mill, non-woven fabrics base substrate is formed；
7）Non-woven fabrics base substrate is placed in fibroin liquid, ultrasonication 35-40min, then low temperature drying, produces skin-friendly
The excellent facial mask non-woven fabrics of energy.
9. the preparation method of the facial mask non-woven fabrics of pro-skin excellent performance according to claim 8, it is characterised in that step
7）In, the ultrasonication frequency is 28-32KHz.
10. the preparation method of the facial mask non-woven fabrics of pro-skin excellent performance according to claim 8, it is characterised in that step
Rapid 7）In, the drying temperature of the low temperature drying is 55-60 DEG C.