CN106280166A - A kind of bamboo gap filler manufacture method - Google Patents
A kind of bamboo gap filler manufacture method Download PDFInfo
- Publication number
- CN106280166A CN106280166A CN201610804415.3A CN201610804415A CN106280166A CN 106280166 A CN106280166 A CN 106280166A CN 201610804415 A CN201610804415 A CN 201610804415A CN 106280166 A CN106280166 A CN 106280166A
- Authority
- CN
- China
- Prior art keywords
- parts
- diameter
- calcium carbonate
- gap filler
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of bamboo gap filler manufacture method, be made up of the raw material of following parts by weight: acrylic emulsion: 100～200 parts, calcium carbonate powder: 50～100 parts, powdered coal cinder: 20～40 parts, cross-linking agent: 10～30 parts, polrvinyl chloride: 10～20 parts, extender: 10～20 parts；Water: 1000～2000 parts；Wherein, in acrylic emulsion in every 100 parts of water containing acrylic acid 20～80 parts；Calcium carbonate powder be calcium carbonate be dried to 70～90% degree grinds filter gained, diameter≤20 μm；Powdered coal cinder is that water content is less than the flyash of 20% and wears into slag gained, its diameter≤90 μm；Cross-linking agent is the one of VTES and dibutyl tin laurate, and extender is calcium sulphoaluminate powder and the one of entringite powder.Production of the present invention is convenient, the product of prepared acquisition, has more excellent gap filler function, improves using effect, conveniently uses as required, it is simple to for the use of multiple different field suitable time.
Description
Technical field
The present invention relates to bamboo filling technology field, be specifically related to a kind of bamboo gap filler manufacture method.
Background technology
Bamboo is a kind of fast-growing type herbaceous plant, and its Folium Bambusae is narrow lanceolar, long 7.5～16 centimetres, wide 1～2 centimetre, first
Hold tapering, base portion obtuse, petiole is about 5 millimeters, and the side at edge is smoother, opposite side have little sawtooth and coarse；Parallel veins, secondary
Arteries and veins 6～8 is right, and small crossvein is the most notable；Blade face bottle green, without hair, back side color is thin, base portion tool microtriche；Matter is thin and more crisp.Bamboo sprout length
10 to 30cm, between the dark green joint number of adult bamboo entire body typically saves 10 to 15.Bamboo can craft articles, musical instrument etc..By bamboo wood
With engineering method, through the bamboo fibre that physics and chemical action are made, it is used as textile, makes towel and medicated clothing etc..By bamboo
Material, by baking and banking up with earth, makes bamboo charcoal, is used in many occasions, including removing environment abnormal smells from the patient, and flavour food.Bamboo charcoal passes through
Pulverize and activate the activated carbon made, having well absorption and purification, be used in automobile and household, and sewage disposal
Deng.Bamboo is also commonly used for building frame (scaffolding), as article of everyday use such as building materials and broom, table, chairs.Bamboo can also work out large bamboo or wicker basket, the back of the body
The general rural area such as basket, food basket, mat is common.Bamboo has been widely used the field of textiles next to the skin such as home textile, socks, underwear now.
Bamboo in use, there will be some holes unavoidably, particularly in bamboo raft uses, waterproof or in order to stifled in order to realize
Live hole, it is necessary to use suitable gap filler, in order to preferably convenient use, improve using effect, therefore, it is necessary to use
Suitably bamboo gap filler, it is simple to use as required.
Summary of the invention
It is an object of the invention to provide a kind of bamboo gap filler manufacture method, in order to be preferably applied to bamboo raft or other
The joint filling gap of bamboo product uses, and improves using effect, conveniently uses as required.
To achieve these goals, technical scheme is as follows.
A kind of bamboo gap filler manufacture method, is made up of the raw material of following parts by weight: acrylic emulsion: 100～200
Part, calcium carbonate powder: 50～100 parts, powdered coal cinder: 20～40 parts, cross-linking agent: 10～30 parts, polrvinyl chloride: 10～20 parts,
Extender: 10～20 parts；Water: 1000～2000 parts；Wherein, acrylic emulsion contains acrylic acid 20～80 in every 100 parts of water
Part；Calcium carbonate powder be calcium carbonate be dried to 70～90% degree grinds filter gained, diameter≤20 μm；Powdered coal cinder is for containing
The water yield flyash less than 20% wears into slag gained, its diameter≤90 μm；Cross-linking agent is VTES and two Laurels
The one of acid dibutyl tin, extender is calcium sulphoaluminate powder and the one of entringite powder.
Further, aforesaid propylene acid uses acrylic acid crystal grinds, its diameter≤40 μm.
Above-mentioned bamboo gap filler manufacture method, its preparation methods steps is as follows:
1) water intaking 1000～2000 parts, adds the cross-linking agent of above-mentioned mass fraction, polrvinyl chloride, extender wherein, and mixing is all
Even acquisition mixed liquor A；
2) taking acrylic acid crystal grinds, its diameter≤40 μm, according to containing acrylic acid 20～the ratio of 80 parts in every 100 parts of water
Mix homogeneously is configured to acrylic emulsion；
3) calcium carbonate is dried to 70～90% degree grinds filter gained, diameter≤20 μm, prepare Paris white；
4) take the water content flyash less than 20% and wear into slag gained, its diameter≤90 μm, it is thus achieved that powdered coal cinder；
5) acrylic emulsion, Paris white and the powdered coal cinder that are prepared by said method join according to above-mentioned mass fraction
Mixed liquor A obtains mixed liquid B；
6), after mixed liquid B being stirred, after packaging, this product is obtained.
This beneficial effect of the invention is: production of the present invention is convenient, the product of prepared acquisition, has more excellent
Gap filler function, improve using effect, convenient use as required, it is simple to for multiple different field suitable time
Use.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Bamboo gap filler manufacture method in the present embodiment, is made up of the raw material of following parts by weight: acrylic emulsion: 100 parts,
Calcium carbonate powder: 50 parts, powdered coal cinder: 20 parts, cross-linking agent: 10 parts, polrvinyl chloride: 10 parts, extender: 10 parts；Water: 1000
Part；Wherein, acrylic emulsion contains 20 parts of acrylic acid in every 100 parts of water；Calcium carbonate powder is that calcium carbonate is dried to 70% degree
Grinds filters gained, diameter 10 μm；Powdered coal cinder is that water content is less than the flyash of 20% and wears into slag gained, its diameter 40 μm；
Cross-linking agent is VTES, and extender is calcium sulphoaluminate powder.
Aforesaid propylene acid uses acrylic acid crystal grinds, its diameter 10 μm.
Above-mentioned bamboo gap filler manufacture method, its preparation methods steps is as follows:
1) water intaking 1000 parts, adds the cross-linking agent of above-mentioned mass fraction, polrvinyl chloride, extender wherein, and mix homogeneously obtains
Mixed liquor A；
2) taking acrylic acid crystal grinds, its diameter 10 μm, according to containing the ratio mixing of 20 parts of acrylic acid in every 100 parts of water all
Even it is configured to acrylic emulsion；
3) calcium carbonate is dried to 70% degree grinds and filters gained, diameter 10 μm, prepare Paris white；
4) take the water content flyash less than 20% and wear into slag gained, its diameter 40 μm, it is thus achieved that powdered coal cinder；
5) acrylic emulsion, Paris white and the powdered coal cinder that are prepared by said method join according to above-mentioned mass fraction
Mixed liquor A obtains mixed liquid B；
6), after mixed liquid B being stirred, after packaging, this product is obtained.
Embodiment 2
Bamboo gap filler manufacture method in the present embodiment, is made up of the raw material of following parts by weight: acrylic emulsion: 200
Part, calcium carbonate powder: 100 parts, powdered coal cinder: 40 parts, cross-linking agent: 30 parts, polrvinyl chloride: 20 parts, extender: 20 parts；Water:
2000 parts；Wherein, acrylic emulsion contains 80 parts of acrylic acid in every 100 parts of water；Calcium carbonate powder is that calcium carbonate is dried to 90%
Degree grinds filters gained, diameter 20 μm；Powdered coal cinder is that water content is less than the flyash of 20% and wears into slag gained, its diameter
90μm；Cross-linking agent is the one of VTES and dibutyl tin laurate, and extender is calcium sulphoaluminate powder
One with entringite powder.
Aforesaid propylene acid uses acrylic acid crystal grinds, its diameter 40 μm.
Above-mentioned bamboo gap filler manufacture method, its preparation methods steps is as follows:
1) water intaking 2000 parts, adds the cross-linking agent of above-mentioned mass fraction, polrvinyl chloride, extender wherein, and mix homogeneously obtains
Mixed liquor A；
2) taking acrylic acid crystal grinds, its diameter 40 μm, according to containing the ratio mixing of 80 parts of acrylic acid in every 100 parts of water all
Even it is configured to acrylic emulsion；
3) calcium carbonate is dried to 90% degree grinds and filters gained, diameter 20 μm, prepare Paris white；
4) take the water content flyash less than 20% and wear into slag gained, its diameter 90 μm, it is thus achieved that powdered coal cinder；
5) acrylic emulsion, Paris white and the powdered coal cinder that are prepared by said method join according to above-mentioned mass fraction
Mixed liquor A obtains mixed liquid B；
6), after mixed liquid B being stirred, after packaging, this product is obtained.
Embodiment 3
Bamboo gap filler manufacture method in the present embodiment, is made up of the raw material of following parts by weight: acrylic emulsion: 150 parts,
Calcium carbonate powder: 75 parts, powdered coal cinder: 30 parts, cross-linking agent: 20 parts, polrvinyl chloride: 15 parts, extender: 15 parts；Water: 1500
Part；Wherein, acrylic emulsion contains 50 parts of acrylic acid in every 100 parts of water；Calcium carbonate powder is that calcium carbonate is dried to 80% degree
Grinds filters gained, diameter 10 μm；Powdered coal cinder is that water content is less than the flyash of 20% and wears into slag gained, its diameter 50 μm；
Cross-linking agent is the one of VTES and dibutyl tin laurate, and extender is calcium sulphoaluminate powder and calcium vitriol
The one of stone powder.
Further, aforesaid propylene acid uses acrylic acid crystal grinds, its diameter 30 μm.
Above-mentioned bamboo gap filler manufacture method, its preparation methods steps is as follows:
1) water intaking 1500 parts, adds the cross-linking agent of above-mentioned mass fraction, polrvinyl chloride, extender wherein, and mix homogeneously obtains
Mixed liquor A；
2) taking acrylic acid crystal grinds, its diameter 30 μm, according to containing the ratio mixing of 50 parts of acrylic acid in every 100 parts of water all
Even it is configured to acrylic emulsion；
3) calcium carbonate is dried to 80% degree grinds and filters gained, diameter 10 μm, prepare Paris white；
4) take the water content flyash less than 20% and wear into slag gained, its diameter 50 μm, it is thus achieved that powdered coal cinder；
5) acrylic emulsion, Paris white and the powdered coal cinder that are prepared by said method join according to above-mentioned mass fraction
Mixed liquor A obtains mixed liquid B；
6), after mixed liquid B being stirred, after packaging, this product is obtained.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (3)
1. a bamboo gap filler manufacture method, it is characterised in that: it is made up of the raw material of following parts by weight: acrylic emulsion:
100～200 parts, calcium carbonate powder: 50～100 parts, powdered coal cinder: 20～40 parts, cross-linking agent: 10～30 parts, polrvinyl chloride: 10
～20 parts, extender: 10～20 parts；Water: 1000～2000 parts；Wherein, acrylic emulsion contains acrylic acid in every 100 parts of water
20～80 parts；Calcium carbonate powder be calcium carbonate be dried to 70～90% degree grinds filter gained, diameter≤20 μm；Flyash
Slag is that water content is less than the flyash of 20% and wears into slag gained, its diameter≤90 μm；Cross-linking agent be VTES and
The one of dibutyl tin laurate, extender is calcium sulphoaluminate powder and the one of entringite powder.
Bamboo gap filler manufacture method the most according to claim 1, it is characterised in that: described acrylic acid uses propylene acid crystals
Body grinds, its diameter≤40 μm.
Bamboo gap filler manufacture method the most according to claim 1, it is characterised in that: described bamboo gap filler making side
Method, its preparation methods steps is as follows:
1) water intaking 1000～2000 parts, adds the cross-linking agent of above-mentioned mass fraction, polrvinyl chloride, extender wherein, and mixing is all
Even acquisition mixed liquor A；
2) taking acrylic acid crystal grinds, its diameter≤40 μm, according to containing acrylic acid 20～the ratio of 80 parts in every 100 parts of water
Mix homogeneously is configured to acrylic emulsion；
3) calcium carbonate is dried to 70～90% degree grinds filter gained, diameter≤20 μm, prepare Paris white；
4) take the water content flyash less than 20% and wear into slag gained, its diameter≤90 μm, it is thus achieved that powdered coal cinder；
5) acrylic emulsion, Paris white and the powdered coal cinder that are prepared by said method join according to above-mentioned mass fraction
Mixed liquor A obtains mixed liquid B；
6), after mixed liquid B being stirred, after packaging, this product is obtained.