CN102400246A - Method for manufacturing polyester fibers with health-care function - Google Patents

Method for manufacturing polyester fibers with health-care function Download PDF

Info

Publication number
CN102400246A
CN102400246A CN2011103899218A CN201110389921A CN102400246A CN 102400246 A CN102400246 A CN 102400246A CN 2011103899218 A CN2011103899218 A CN 2011103899218A CN 201110389921 A CN201110389921 A CN 201110389921A CN 102400246 A CN102400246 A CN 102400246A
Authority
CN
China
Prior art keywords
powder
sepiolite
obtains
acid solution
interpolation material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103899218A
Other languages
Chinese (zh)
Inventor
韩文秀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HANGZHOU FANLIN TECHNOLOGY Co Ltd
Original Assignee
HANGZHOU FANLIN TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANGZHOU FANLIN TECHNOLOGY Co Ltd filed Critical HANGZHOU FANLIN TECHNOLOGY Co Ltd
Priority to CN2011103899218A priority Critical patent/CN102400246A/en
Publication of CN102400246A publication Critical patent/CN102400246A/en
Pending legal-status Critical Current

Abstract

The invention discloses a method for manufacturing polyester fibers with a health-care function. The method comprises the following steps of: A) adding tourmaline powder into a 5 to 10 mass percent stearic acid solution in a mass ratio of 1: (8-12), stirring for 1 to 3 hours, drying, and thus obtaining modified tourmaline powder; B) adding sepiolite into a 3 to 10 mass percent hydrochloric acid solution in a mass ratio of 1: (5-10), stirring for 1 to 3 hours, dehydrating and drying, and thus obtaining activated sepiolite; C) mixing the modified tourmaline powder, the activated sepiolite and pearl powder uniformly in a mass ratio of (1-3): (0.5-1.5): 1, grinding, and thus obtaining an additive material, the grain diameter of which is not more than 15 microns; and D) adding the additive material obtained in the step C) into a polyester melt, stirring uniformly, spinning, and thus obtaining the modified polyester fibers, wherein the adding amount of the additive material prepared in the step C) is 1 to 15 percent of the weight of the polyester melt.

Description

A kind of manufacturing approach of health care polyester fiber
Technical field
The present invention relates to a kind of manufacturing approach of health care polyester fiber, belong to textile technology field.
Background technology
Polyester fiber is the fiber species that output is maximum in the synthetic fiber, purposes is the widest, and trade name is terylene, and its brute force, ABRASION RESISTANCE, resilience and DIMENSIONAL STABILITY all can better satisfy the needs of various final uses.Functional fibre and function textile are fibrous material and the textile products of representing material, chemical industry, weaving and association area development in science and technology level, are one of scientific worker's focus in fields such as fiber, weaving, dyeing and finishing, clothes, fine chemistry industry.The development functionality textiles, collecting comfortable, lying fallow, keep healthy is one, this has become world today's textiles development current.From the latter stage nineties, to develop and developed and comprise many varieties and functions fibers such as fire-retardant, fragrant, anion, antibiotic, uvioresistant, warming, antistatic, accumulation of heat, intelligent air condition fiber, the health care fiber development is an important content.Tourmaline is the crystal of unique band permanent electrode on the earth, the electric current that sustainable generation is 0.06 milliampere, and it is emission wavelength 4 at normal temperatures---14 microns efficient far infrared, mate with human body far infrared wave appearance.It is reported when human body is accepted such far infrared; Can the activation histocyte; Microcirculation improvement improves human body vis medicatrix naturae, immunity and resistance, simultaneously; Tourmaline automatically, the permanent anion that discharges is called as " air vitamin ", and anion purifies air, antibacterial anticorrosion deodorizing, effect such as calm the nerves, improve sleep-disorder, improve the respiratory apparatus function, promote cell to absorb nutrition and drain refuse, enhance metabolism.Pearl powder can have been strengthened the subcutaneous microcirculation of human body through the far infrared emission function of pearl micro-particle formation.
Summary of the invention
The objective of the invention is to overcome the deficiency that prior art exists, provide a kind of preparation method simple, the manufacturing approach of the health care polyester fiber that cost is low.
The objective of the invention is to accomplish through following technical scheme, the manufacturing approach of described health care polyester fiber, it comprises the steps:
A) mass ratio according to 1:8~12 joins tourmaline powder in the stearic acid solution of mass percent concentration 5~10%, stirs 1-3 hours, and drying makes the modified verdelite powder;
B) joining mass percent concentration according to the quality of 1:5~10 than sepiolite is in 3~10% the hydrochloric acid solution, stirs 1~3 hour, dehydrates, and makes the activation sepiolite;
C) quality according to 1~3:0.5~1.5:1 mixes modified verdelite powder, activation sepiolite, pearl powder, obtains the interpolation material that particle diameter is not more than 15 μ m after the grinding;
D) with step C) the interpolation material that obtains joins in the polyester fondant, after stirring, carries out spinning, obtains modified polyester fiber; The addition of the interpolation material that step C wherein) makes be polyester fondant weight 1~15%.
On the basis of the above, preferred version of the present invention is:
A) mass ratio according to 1:10 joins tourmaline powder in the stearic acid solution of mass percent concentration 7%, stirs 2 hours, and drying makes the modified verdelite powder;
B) joining mass percent concentration according to the quality of 1:8 than sepiolite is in 6% the hydrochloric acid solution, stirs 2 hours, dehydrates, and makes the activation sepiolite;
C) quality according to 2:1:1 mixes modified verdelite powder, activation sepiolite, pearl powder, obtains the interpolation material that particle diameter is not more than 15 μ m after the grinding;
D) with step C) the interpolation material that obtains joins in the polyester fondant, after stirring, carries out spinning, obtains modified polyester fiber; The addition of the interpolation material that step C wherein) makes be polyester fondant weight 10%.
This name mainly is through in the polyester fiber fiber, introducing materials such as modified verdelite powder, activation sepiolite, pearl powder, making polyester fiber possess health.
Compare with prior art, the present invention has the following advantages: 1) preparation method is simple, and cost is low; 2) automatic, the permanent anion that discharges of tourmaline makes fiber have health care; 3) pearl powder can be strengthened the subcutaneous microcirculation of human body.
The specific embodiment
To combine specific embodiment that the present invention is done detailed introduction below: the manufacturing approach of health care polyester fiber of the present invention, it comprises the steps:
A) mass ratio according to 1:8~12 joins tourmaline powder in the stearic acid solution of mass percent concentration 5~10%, stirs 1-3 hours, and drying makes the modified verdelite powder;
B) joining mass percent concentration according to the quality of 1:5~10 than sepiolite is in 3~10% the hydrochloric acid solution, stirs 1~3 hour, dehydrates, and makes the activation sepiolite;
C) quality according to 1~3:0.5~1.5:1 mixes modified verdelite powder, activation sepiolite, pearl powder, obtains the interpolation material that particle diameter is not more than 15 μ m after the grinding;
D) with step C) the interpolation material that obtains joins in the polyester fondant, after stirring, carries out spinning, obtains modified polyester fiber; The addition of the interpolation material that step C wherein) makes be polyester fondant weight 1~15%.
Other embodiments of the invention can be carried out obtaining after the combination in any to the correlation values scope on the basis of technique scheme, are not limited to the disclosed technical scope of following embodiment.
Embodiment 1, the manufacturing approach of health care polyester fiber of the present invention, and it comprises the steps:
A) mass ratio according to 1:10 joins tourmaline powder in the stearic acid solution of mass percent concentration 7%, stirs 2 hours, and drying makes the modified verdelite powder;
B) joining mass percent concentration according to the quality of 1:8 than sepiolite is in 6% the hydrochloric acid solution, stirs 2 hours, dehydrates, and makes the activation sepiolite;
C) quality according to 2:1:1 mixes modified verdelite powder, activation sepiolite, pearl powder, obtains the interpolation material that particle diameter is not more than 15 μ m after the grinding;
D) with step C) the interpolation material that obtains joins in the polyester fondant, after stirring, carries out spinning, obtains modified polyester fiber; The addition of the interpolation material that step C wherein) makes be polyester fondant weight 10%.
Embodiment 2
A) mass ratio according to 1:8 joins tourmaline powder in the stearic acid solution of mass percent concentration 5%, stirs 1 hour, and drying makes the modified verdelite powder;
B) joining mass percent concentration according to the quality of 1:5 than sepiolite is in 3% the hydrochloric acid solution, stirs 1 hour, dehydrates, and makes the activation sepiolite;
C) quality according to 1:0.5:1 mixes modified verdelite powder, activation sepiolite, pearl powder, obtains the interpolation material that particle diameter is not more than 15 μ m after the grinding;
D) with step C) the interpolation material that obtains joins in the polyester fondant, after stirring, carries out spinning, obtains modified polyester fiber; The addition of the interpolation material that step C wherein) makes be polyester fondant weight 1%.
Embodiment 3
A) mass ratio according to 1:12 joins tourmaline powder in the stearic acid solution of mass percent concentration 10%, stirs 3 hours, and drying makes the modified verdelite powder;
B) joining mass percent concentration according to the quality of 1:10 than sepiolite is in 10% the hydrochloric acid solution, stirs 3 hours, dehydrates, and makes the activation sepiolite;
C) quality according to 3:1.5:1 mixes modified verdelite powder, activation sepiolite, pearl powder, obtains the interpolation material that particle diameter is not more than 15 μ m after the grinding;
D) with step C) the interpolation material that obtains joins in the polyester fondant, after stirring, carries out spinning, obtains modified polyester fiber; The addition of the interpolation material that step C wherein) makes be polyester fondant weight 15%.

Claims (2)

1. the manufacturing approach of a health care polyester fiber is characterized in that this manufacturing approach comprises the steps:
A) mass ratio according to 1:8~12 joins tourmaline powder in the stearic acid solution of mass percent concentration 5~10%, stirs 1-3 hours, and drying makes the modified verdelite powder;
B) joining mass percent concentration according to the quality of 1:5~10 than sepiolite is in 3~10% the hydrochloric acid solution, stirs 1~3 hour, dehydrates, and makes the activation sepiolite;
C) quality according to 1~3:0.5~1.5:1 mixes modified verdelite powder, activation sepiolite, pearl powder, obtains the interpolation material that particle diameter is not more than 15 μ m after the grinding;
D) with step C) the interpolation material that obtains joins in the polyester fondant, after stirring, carries out spinning, obtains modified polyester fiber; The addition of the interpolation material that step C wherein) makes be polyester fondant weight 1~15%.
2. the manufacturing approach of health care polyester fiber according to claim 1 is characterized in that in the described step:
A) mass ratio according to 1:10 joins tourmaline powder in the stearic acid solution of mass percent concentration 7%, stirs 2 hours, and drying makes the modified verdelite powder;
B) joining mass percent concentration according to the quality of 1:8 than sepiolite is in 6% the hydrochloric acid solution, stirs 2 hours, dehydrates, and makes the activation sepiolite;
C) quality according to 2:1:1 mixes modified verdelite powder, activation sepiolite, pearl powder, obtains the interpolation material that particle diameter is not more than 15 μ m after the grinding;
D) with step C) the interpolation material that obtains joins in the polyester fondant, after stirring, carries out spinning, obtains modified polyester fiber; The addition of the interpolation material that step C wherein) makes be polyester fondant weight 10%.
CN2011103899218A 2011-08-24 2011-11-30 Method for manufacturing polyester fibers with health-care function Pending CN102400246A (en)