CN106435938B - A kind of processing method of softness heating face fabric - Google Patents

A kind of processing method of softness heating face fabric Download PDF

Info

Publication number
CN106435938B
CN106435938B CN201610978207.5A CN201610978207A CN106435938B CN 106435938 B CN106435938 B CN 106435938B CN 201610978207 A CN201610978207 A CN 201610978207A CN 106435938 B CN106435938 B CN 106435938B
Authority
CN
China
Prior art keywords
parts
weight
fabric
minutes
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610978207.5A
Other languages
Chinese (zh)
Other versions
CN106435938A (en
Inventor
程素芹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Zhenyang industry and Trade Co.,Ltd.
Original Assignee
Anhui New Intelligent Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui New Intelligent Technology Co Ltd filed Critical Anhui New Intelligent Technology Co Ltd
Priority to CN201610978207.5A priority Critical patent/CN106435938B/en
Publication of CN106435938A publication Critical patent/CN106435938A/en
Application granted granted Critical
Publication of CN106435938B publication Critical patent/CN106435938B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

A kind of processing method of softness heating face fabric, steps are as follows：1) by warp thread and weft yarn it is blended after fabric is made；2) fabric is tiled, 10 is pressed with distilled water, salt, light-coloured vinegar:1：Solution is smoked made of 2 ratio；3) fabric after smoking is put into softening agent and impregnate 20 30 minutes；4) fabric after immersion is subjected to crystallizing and drying；5) it repeats smoke, impregnate, drying steps 23 times；6) natural antibacterial agent, fountain height 40g/m are sprayed in the cloth two sides for completing step 5)2；7) cloth for completing step 6) carries out natural air drying.The fabric that the present invention makes uses the raw material with high flexibility and heat insulating ability, these principles also have spontaneous hot and hygroscopicity simultaneously, more environmentally friendly using natural antibacterial agent, and green is healthier.

Description

A kind of processing method of softness heating face fabric
Technical field：
The present invention relates to garment material technical fields, and in particular to a kind of processing method of softness heating face fabric.
Background technology：
With the raising of living standard, quality of life, people propose textile, clothes the requirement of various functions. Functional fibre and function textile are fibrous material and the spinning for representing material, chemical industry, weaving and related field technology development level Product is knitted, is one of scientific worker's focus in the fields such as fiber, weaving, dyeing and finishing, clothes, fine chemistry industry.Development functionality Textile integrates comfortable, lies fallow, health care, this has become the trend of world today's textile development.From the latter stage nineties It rises, develops and develop including fire-retardant, fragrant, anion, antibacterial, uvioresistant, warming, antistatic, accumulation of heat, intelligent air condition fiber Equal multi items functional fibre, the exploitation of functional fabric is an important content.
Invention content：
Technical problem to be solved by the present invention lies in provide a kind of adding for soft heating face fabric easy to implement the method, at low cost Work method.
The technical problems to be solved by the invention are realized using technical solution below：
A kind of processing method of softness heating face fabric, steps are as follows：
1) by warp thread and weft yarn it is blended after fabric is made；
2) fabric is tiled, 10 is pressed with distilled water, salt, light-coloured vinegar:1：Solution is smoked made of 2 ratio, can be right Fabric plays the role of softening, and pineization fabric fibre is conducive to subsequent operation；
3) fabric after smoking is put into softening agent and impregnate 20-30 minutes, make fabric to the absorption of softening agent more Fully；
4) fabric after immersion is subjected to crystallizing and drying, crystallizing and drying is more advantageous to the fiber of protection fabric；
5) it repeats smoke, impregnate, drying steps 2-3 times；
6) natural antibacterial agent, fountain height 40g/m are sprayed in the cloth two sides for completing step 5)2；
7) cloth for completing step 6) carries out natural air drying.
Further, the warp thread includes the raw material of following parts by weight：15-20 parts of Modal fibre, wool protein are fine Tie up 5-10, viscose rayon 5-10,5-10 parts of activated carbon fibre；The weft yarn includes the raw material of following parts by weight：Bamboo charcoal fiber 10-15 parts, 10-15 parts of spandex, fine jade how 2-5 parts of silk fiber, 1-3 parts of fibroin fiber.
Further, softening agent is made of the raw material of following parts by weight in the step 3)：10-15 parts of organosilicon, 1-3 parts of paraffin, 3-5 parts of vitamin E, 2-4 parts of lecithin, 3-5 parts of amino acid, 1-2 parts of Nano sol.
Further, the soaking process of the step 3) is by the way of gradually heating：30-40 ° is impregnated 5-10 minutes, 40-60 ° is impregnated 10-15 minutes, and 60-80 ° is impregnated 5-10 minutes, using the method for heat stepwise, keeps fabric immersion effect more preferable, Fabric is more preferable to the assimilation effect of softening agent.
Further, the antiseptic be by：The yellow cinnamon leaf of 20 parts by weight, the dried peppermint leaf of 10 parts by weight, 20 parts by weight Folium artemisiae argyi, the ginger of 5 parts by weight, the camphor of 2 parts by weight, the Jasmine of 5 parts by weight, the honeysuckle of 5 parts by weight, 3 parts by weight it is white The salt of vinegar, 3 parts by weight is made.
The beneficial effects of the invention are as follows：
1. the present invention is using Modal fibre, viscose fiber, bamboo charcoal fiber, the high raw material of the pliabilitys such as spandex, then adds Wool protein fiber, Lu Naisi fibers and fibroin fiber have effects that the material of spontaneous heating, not only ensure that raw material has There is good Self-heating warming, and there is flexibility and comfort, avoids the next friction of raw material heating tape, electrostatic, discomfort.
2. used in softening agent organosilicon, paraffin, Nano sol can play the role of to cloth it is soft, anlistatig, Be added to vitamin E, lecithin, amino acid plays the role of protection, nursing to cloth simultaneously, so that cloth is through more easypro on the person It is suitable, extend the usage time of cloth.
3. using the raw material of natural natural green as antiseptic, not only there is good antibacterial action, and smell Fragrant unique natural, environmentally protective nonhazardous does not injure human body.
Specific implementation mode：
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, tie below Specific embodiment is closed, the present invention is further explained.
Embodiment 1
A kind of processing method of softness heating face fabric, steps are as follows：
1) by warp thread and weft yarn it is blended after fabric is made；
2) fabric is tiled, 10 is pressed with distilled water, salt, light-coloured vinegar：1：Solution is smoked made of 2 ratio；
3) fabric after smoking is put into softening agent and impregnate 30 minutes；
4) fabric after immersion is subjected to crystallizing and drying；
5) it repeats smoke, impregnate, drying steps 2 times；
6) natural antibacterial agent, fountain height 40g/m are sprayed in the cloth two sides for completing step 5)2；
7) cloth for completing step 6) carries out natural air drying.
Above-mentioned warp thread includes the raw material of following parts by weight：15 parts of Modal fibre, 5 parts of wool protein fiber, viscose glue are fine 5 parts of dimension, 5 parts of activated carbon fibre；The weft yarn includes the raw material of following parts by weight：10 parts of bamboo charcoal fiber, 10 parts of spandex, how is fine jade 2 parts of silk, 1 part of fibroin fiber.
Above-mentioned steps 3) in softening agent be made of the raw material of following parts by weight：10 parts of organosilicon, 1 part of paraffin, dimension life It is E3 parts plain, 2 parts of lecithin, 3 parts of amino acid, 1 part of Nano sol.
Above-mentioned steps 3) soaking process by the way of gradually heating：30 ° are impregnated 10 minutes, and 40 ° are impregnated 10 minutes, 60 ° are impregnated 10 minutes.
Above-mentioned antiseptic be by：The yellow cinnamon leaf of 20 parts by weight, the dried peppermint leaf of 10 parts by weight, the folium artemisiae argyi of 20 parts by weight, 5 weight The ginger of part, the camphor of 2 parts by weight, the Jasmine of 5 parts by weight, the honeysuckle of 5 parts by weight, the light-coloured vinegar of 3 parts by weight, 3 parts by weight Salt be made.
Embodiment 2
A kind of processing method of softness heating face fabric, steps are as follows：
1) by warp thread and weft yarn it is blended after fabric is made；
2) fabric is tiled, 10 is pressed with distilled water, salt, light-coloured vinegar：1：Solution is smoked made of 2 ratio；
3) fabric after smoking is put into softening agent and impregnate 25 minutes；
4) fabric after immersion is subjected to crystallizing and drying；
5) it repeats smoke, impregnate, drying steps 3 times；
6) natural antibacterial agent, fountain height 40g/m are sprayed in the cloth two sides for completing step 5)2；
7) cloth for completing step 6) carries out natural air drying.
Above-mentioned warp thread includes the raw material of following parts by weight：20 parts of Modal fibre, wool protein fiber 10, viscose rayon 10,10 parts of activated carbon fibre；The weft yarn includes the raw material of following parts by weight：15 parts of bamboo charcoal fiber, 15 parts of spandex, fine jade how silk 5 parts, 3 parts of fibroin fiber.
Above-mentioned steps 3) in softening agent be made of the raw material of following parts by weight：15 parts of organosilicon, 3 parts of paraffin, dimension life It is E5 parts plain, 4 parts of lecithin, 5 parts of amino acid, 2 parts of Nano sol.
Above-mentioned steps 3) soaking process by the way of gradually heating：40 ° are impregnated 5 minutes, and 60 ° are impregnated 10 minutes, 80 ° It impregnates 10 minutes.
Above-mentioned antiseptic be by：The yellow cinnamon leaf of 20 parts by weight, the dried peppermint leaf of 10 parts by weight, the folium artemisiae argyi of 20 parts by weight, 5 weight The ginger of part, the camphor of 2 parts by weight, the Jasmine of 5 parts by weight, the honeysuckle of 5 parts by weight, the light-coloured vinegar of 3 parts by weight, 3 parts by weight Salt be made.
The test and appraisal such as table 1 of the present invention and soft fever under the conditions of different disposal of other samples：
Table 1
Sample 1 is a kind of soft cloth in the market, and sample 2 is a kind of fever cloth in the market.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (1)

1. a kind of processing method of softness heating face fabric, steps are as follows：
1) by warp thread and weft yarn it is blended after fabric is made；
2) fabric is tiled, 10 is pressed with distilled water, salt, light-coloured vinegar:1：Solution is smoked made of 2 ratio；
3) fabric after smoking is put into softening agent and impregnate 20-30 minutes；
4) fabric after immersion is subjected to crystallizing and drying；
5) it repeats smoke, impregnate, drying steps 2-3 times；
6) natural antibacterial agent, fountain height 40g/m are sprayed in the cloth two sides for completing step 5)2；
7) cloth for completing step 6) carries out natural air drying；
Softening agent is made of the raw material of following parts by weight in the step 3)：10-15 parts of organosilicon, 1-3 parts of paraffin, dimension life It is E3-5 parts plain, 2-4 parts of lecithin, 3-5 parts of amino acid, 1-2 parts of Nano sol；
The warp thread includes the raw material of following parts by weight：15-20 parts of Modal fibre, 5-10 parts of wool protein fiber, viscose glue 5-10 parts of fiber, 5-10 parts of activated carbon fiber；The weft yarn includes the raw material of following parts by weight：10-15 parts of bamboo charcoal fiber, ammonia 10-15 parts of synthetic fibre, fine jade how 2-5 parts of silk, 1-3 parts of fibroin fiber；
The soaking process of the step 3) is by the way of gradually heating：30-40 DEG C is impregnated 5-10 minutes, 40-60 DEG C of immersion 10- 15 minutes, 60-80 DEG C was impregnated 5-10 minutes；
The antiseptic be by：The yellow cinnamon leaf of 20 parts by weight, the dried peppermint leaf of 10 parts by weight, the folium artemisiae argyi of 20 parts by weight, 5 parts by weight Ginger, the camphor of 2 parts by weight, the Jasmine of 5 parts by weight, the honeysuckle of 5 parts by weight, the light-coloured vinegar of 3 parts by weight, the salt of 3 parts by weight It is made.
CN201610978207.5A 2016-11-08 2016-11-08 A kind of processing method of softness heating face fabric Active CN106435938B (en)