CN106592056B - A kind of processing method of waterproof insulating fabric - Google Patents
A kind of processing method of waterproof insulating fabric Download PDFInfo
- Publication number
- CN106592056B CN106592056B CN201610978210.7A CN201610978210A CN106592056B CN 106592056 B CN106592056 B CN 106592056B CN 201610978210 A CN201610978210 A CN 201610978210A CN 106592056 B CN106592056 B CN 106592056B
- Authority
- CN
- China
- Prior art keywords
- fabric
- weight
- parts
- minutes
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of processing method of waterproof insulating fabric, steps are as follows：1) by warp thread and weft yarn it is blended after fabric is made；2) fabric is tiled, 10 is pressed with distilled water and light-coloured vinegar:Solution is smoked made of 2 ratio；3) fabric after smoking is put into macromolecule solvent and impregnate 20 30 minutes；4) fabric after immersion is subjected to high temperature drying；5) it repeats smoke, impregnate, baking step 23 times；6) natural antibacterial agent, fountain height 60g/m are sprayed in the cloth two sides for completing step 5)2；7) cloth for completing step 6) carries out naturally dry.The beneficial effects of the invention are as follows：The fabric that the present invention makes has heat preservation and water proofing property well, while having antibiotic property, more robust, more natural more environmentally friendly, pollution-free.
Description
Technical field：
The present invention relates to garment material technical fields, and in particular to a kind of processing method of waterproof insulating fabric.
Background technology：
With the raising of living standard, quality of life, people propose textile, clothes the requirement of various functions.
Functional fibre and function textile are fibrous material and the spinning for representing material, chemical industry, weaving and related field technology development level
Product is knitted, is one of scientific worker's focus in the fields such as fiber, weaving, dyeing and finishing, clothes, fine chemistry industry.Development functionality
Textile integrates comfortable, lies fallow, health care, this has become the trend of world today's textile development.From the latter stage nineties
It rises, develops and develop including fire-retardant, fragrant, anion, antibacterial, uvioresistant, warming, antistatic, accumulation of heat, intelligent air condition fiber
Equal multi items functional fibre, the exploitation of functional fabric is an important content.
Invention content：
Technical problem to be solved by the present invention lies in provide a kind of adding for waterproof insulating fabric easy to implement the method, at low cost
Work method.
The technical problems to be solved by the invention are realized using technical solution below：
A kind of processing method of waterproof insulating fabric, steps are as follows：
1) by warp thread and weft yarn it is blended after fabric is made；
2) fabric is tiled, 10 is pressed with distilled water and light-coloured vinegar:Solution is smoked made of 2 ratio, can be to fabric
Play the role of softening, pineization fabric fibre is conducive to subsequent operation；
3) fabric after smoking is put into macromolecule solvent and impregnate 20-30 minutes, make suction of the fabric to softening agent
It receives more abundant；
4) fabric after immersion is carried out to 130-150 ° of high temperature to dry, so that Polymer Solution is adhered to rapidly and is wrapped in cloth
On fiber, attachment degree higher is closer；
5) it repeats smoke, impregnate, baking step 2-3 times；
6) natural antibacterial agent, fountain height 60g/m are sprayed in the cloth two sides for completing step 5)2；
7) cloth for completing step 6) carries out naturally dry.
Further, the warp thread and weft yarn by deoxidation cotton, polyester fiber, viscose fiber, spandex, press 3：2:1:1 ratio
Example is blended to be made into.
Further, the macromolecule solvent is by polyacrylate, polysiloxanes, polyvinyl chloride, rubber according to 1.2:
0.8:1:0.6 ratio is made.
It is further that the step 3) soaking process is carried out by way of gradually heating up, 60-70 ° is impregnated 5 minutes,
70-90 ° is impregnated 5-10 minutes, and 90-120 ° is impregnated 10-15 minutes, using the method for heat stepwise, fabric is made to impregnate effect more
Good, fabric is more preferable to the assimilation effect of Polymer Solution.
Further, the antiseptic be by：The yellow cinnamon leaf of 20 parts by weight, the dried peppermint leaf of 10 parts by weight, 20 parts by weight
Folium artemisiae argyi, the ginger of 5 parts by weight, the camphor of 2 parts by weight, the Jasmine of 5 parts by weight, the honeysuckle of 5 parts by weight, 3 parts by weight it is white
The salt of vinegar, 3 parts by weight is made.
The beneficial effects of the invention are as follows：
1. the present invention high, raw material extremely efficient in preserving heat using pliabilitys such as deoxidation cotton, viscose fiber, spandexs, then it is added to tool
There is the polyester fiber of water proofing property, wrinkle resistance, the blended cloth being made into of these raw materials has flexibility, heat insulating ability, while these are former
Material has high-absorbable, can fully absorb the Polymer Solution with water resistance.
2. using polyacrylate, polysiloxanes, polyvinyl chloride, rubber in Polymer Solution, these raw materials have height
Water proofing property, high viscosity and film forming, can fully wrap clothes fiber, and filling cloth gap is formed anti-on fabric fibre
Moisture film.
3. using the raw material of natural natural green as antiseptic, not only there is good antibacterial action, and smell
Fragrant unique natural, environmentally protective nonhazardous does not injure human body.
Specific implementation mode：
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1
A kind of processing method of waterproof insulating fabric, steps are as follows：
1) by warp thread and weft yarn it is blended after fabric is made；
2) fabric is tiled, 10 is pressed with distilled water and light-coloured vinegar:Solution is smoked made of 2 ratio；
3) fabric after smoking is put into macromolecule solvent and impregnate 20 minutes；
4) fabric after immersion is carried out to 130 ° of high temperature to dry；
5) it repeats smoke, impregnate, baking step 2 times；
6) natural antibacterial agent, fountain height 60g/m are sprayed in the cloth two sides for completing step 5)2；
7) cloth for completing step 6) carries out naturally dry.
Above-mentioned warp thread and weft yarn by deoxidation cotton, polyester fiber, viscose fiber, spandex, press 3：2:1:1 ratio is blended to knit
At.
Above-mentioned macromolecule solvent is by polyacrylate, polysiloxanes, polyvinyl chloride, rubber according to 1.2:0.8:1:0.6
Ratio be made.
Above-mentioned steps 3) soaking process carried out by way of gradually heating up, 60 ° are impregnated 5 minutes, and 70 ° are impregnated 10 points
Clock, 90 ° are impregnated 15 minutes.
Above-mentioned antiseptic be by：The yellow cinnamon leaf of 20 parts by weight, the dried peppermint leaf of 10 parts by weight, the folium artemisiae argyi of 20 parts by weight, 5 weight
The ginger of part, the camphor of 2 parts by weight, the Jasmine of 5 parts by weight, the honeysuckle of 5 parts by weight, the light-coloured vinegar of 3 parts by weight, 3 parts by weight
Salt be made.
Embodiment 2
A kind of processing method of waterproof insulating fabric, steps are as follows：
1) by warp thread and weft yarn it is blended after fabric is made；
2) fabric is tiled, 10 is pressed with distilled water and light-coloured vinegar:Solution is smoked made of 2 ratio；
3) fabric after smoking is put into macromolecule solvent and impregnate 30 minutes；
4) fabric after immersion is carried out to 150 ° of high temperature to dry；
5) it repeats smoke, impregnate, baking step 3 times；
6) natural antibacterial agent, fountain height 60g/m are sprayed in the cloth two sides for completing step 5)2；
7) cloth for completing step 6) carries out naturally dry.
Above-mentioned warp thread and weft yarn by deoxidation cotton, polyester fiber, viscose fiber, spandex, press 3：2:1:1 ratio is blended to knit
At.
Above-mentioned macromolecule solvent is by polyacrylate, polysiloxanes, polyvinyl chloride, rubber according to 1.2:0.8:1:0.6
Ratio be made.
Above-mentioned steps 3) soaking process carried out by way of gradually heating up, 60 ° are impregnated 5 minutes, and 90 ° are impregnated 10 points
Clock, 120 ° are impregnated 15 minutes.
Above-mentioned antiseptic be by：The yellow cinnamon leaf of 20 parts by weight, the dried peppermint leaf of 10 parts by weight, the folium artemisiae argyi of 20 parts by weight, 5 weight
The ginger of part, the camphor of 2 parts by weight, the Jasmine of 5 parts by weight, the honeysuckle of 5 parts by weight, the light-coloured vinegar of 3 parts by weight, 3 parts by weight
Salt be made.
The present invention and sample test and appraisal waterproof thermal-insulated under different disposal such as table 1：
Table 1
Sample 1 is a kind of waterproof cloth in the market, and sample 2 is a kind of Heat-insulation cloth in the market.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (1)
1. a kind of processing method of waterproof insulating fabric, which is characterized in that steps are as follows：
1) by warp thread and weft yarn it is blended after fabric is made；
2) fabric is tiled, 10 is pressed with distilled water and light-coloured vinegar:Solution is smoked made of 2 ratio；
3) fabric after smoking is put into macromolecule solvent and impregnate 20-30 minutes；
4) fabric after immersion is carried out to 130-150 DEG C of high temperature to dry；
5) it repeats smoke, impregnate, baking step 2-3 times；
6) natural antibacterial agent, fountain height 60g/m are sprayed in the cloth two sides for completing step 5)2；
7) cloth for completing step 6) carries out naturally dry；
The macromolecule solvent is by polyacrylate, polysiloxanes, polyvinyl chloride, rubber according to 1.2:0.8:1:0.6 ratio
Example is made；
The warp thread and weft yarn by deoxidation cotton, polyester fiber, viscose fiber, spandex, press 3:2:1:1 ratio is blended to be made into；
Step 3) the soaking process is carried out by way of gradually heating up, and 60-70 DEG C is impregnated 5 minutes, 70-90 DEG C of immersion 5-
10 minutes, 90-120 DEG C was impregnated 10-15 minutes；
The antiseptic be by：The yellow cinnamon leaf of 20 parts by weight, the dried peppermint leaf of 10 parts by weight, the folium artemisiae argyi of 20 parts by weight, 5 parts by weight
Ginger, the camphor of 2 parts by weight, the Jasmine of 5 parts by weight, the honeysuckle of 5 parts by weight, the light-coloured vinegar of 3 parts by weight, the salt of 3 parts by weight
It is made.