CN106592200A - Soft anti-wrinkle fabric processing method - Google Patents

Soft anti-wrinkle fabric processing method Download PDF

Info

Publication number
CN106592200A
CN106592200A CN201610978206.0A CN201610978206A CN106592200A CN 106592200 A CN106592200 A CN 106592200A CN 201610978206 A CN201610978206 A CN 201610978206A CN 106592200 A CN106592200 A CN 106592200A
Authority
CN
China
Prior art keywords
parts
fabric
weight portions
wrinkle
immersion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610978206.0A
Other languages
Chinese (zh)
Inventor
程素芹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui New Intelligent Technology Co Ltd
Original Assignee
Anhui New Intelligent Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui New Intelligent Technology Co Ltd filed Critical Anhui New Intelligent Technology Co Ltd
Priority to CN201610978206.0A priority Critical patent/CN106592200A/en
Publication of CN106592200A publication Critical patent/CN106592200A/en
Pending legal-status Critical Current

Abstract

The invention relates to a soft anti-wrinkle fabric processing method, which comprises: 1) blending warp yarns and weft yarns to prepare a fabric; 2) paving the fabric, and fumigating with a solution prepared from distilled water, salt and white vinegar according to a ratio of 10:1:1; 3) placing the fumigated fabric into an anti-wrinkle agent, and soaking for 20-30 min; 4) carrying out crystallization drying on the soaked fabric; 5) repeatedly fumigating, soaking and drying 2-3 times; 6) carrying out mechanical pre-shrinking treatment on the fabric obtained in the step 5); 7) spraying an aromatic antibacterial agent on both surfaces of the fabric obtained in the step 6), wherein the spraying amount is 40 g/m<2>; and 8) carrying out natural air drying on the fabric obtained in the step 7). According to the present invention, the produced fabric has characteristics of high wrinkle resistance and softness, and uses the natural aromatic antibacterial agent so as to provide the advantages of environmental protection and health.

Description

A kind of processing method of soft anti-wrinkle fabric
Technical field：
The present invention relates to garment material technical field, and in particular to a kind of processing method of soft anti-wrinkle fabric.
Background technology：
With living standard, the raising of quality of life, people propose the requirement of various functions to textile, clothing. Functional fibre and function textile are fibrous material and the spinnings for representing material, chemical industry, weaving and association area Sci-Tech Level Product is knitted, is one of scientific worker's focus in the fields such as fiber, weaving, dyeing and finishing, clothing, fine chemistry industry.Development functionality Textile, integrates comfortable, leisure, health care, and this has become the trend of world today's textile development.From the latter stage nineties Rise, develop and develop including fire-retardant, fragrant, anion, antibacterial, uvioresistant, warming, antistatic, accumulation of heat, intelligent air condition fiber Deng multi items functional fibre, the exploitation of functional fabric is an important content.
The content of the invention：
The technical problem to be solved is to provide a kind of adding for soft anti-wrinkle fabric of easy to implement the method, low cost Work method.
The technical problem to be solved is realized using following technical scheme：
A kind of processing method of soft anti-wrinkle fabric, step are as follows：
1) warp thread and weft yarn are intersected into 45 °, by fabric being made after oblique " well " font blending；
2) fabric is tiled, 10 are pressed with distilled water, salt, white vinegar：1：Solution made by 1 ratio is smoked, and softens clothing Thing, makes the inorganic agent of follow-up medicated clothing be more easy to absorb；
3) fabric after smoking is put in anti-wrinkle agent carries out soaking 20-30 minutes；
4) fabric after immersion is carried out into crystallizing and drying；
5) repetition is smoked, is soaked, drying steps 2-3 time；
6) by step 5) cloth that completes carries out machine shrunk process；
7) by step 6) the sprinkling fragrant antimicrobial agent of the cloth two sides that completes, fountain height is 40g/m2；
8) by step 7) cloth that completes carries out natural air drying.
Further, the warp thread includes the raw material of following parts by weight：Absorbent cotton 15-20 parts, terylene 3-6, activated carbon Fiber 1-3 parts；The weft yarn includes the raw material of following parts by weight：Modal fibre 5-10 parts, spandex 4-8 parts, polyester fiber 2-5。
Further, the step 3) in anti-wrinkle agent be made up of the raw material of following parts by weight：Liquid nitrogen 15-20 parts, lemon Lemon acid 5-10 parts, Oxytarch slurry 5-10 parts, Nano chitosan 3-6 parts, organosilicon 2-5 parts, lecithin 1-3 parts, Nano sol 1-2 parts.
Further, the step 3) immersion process by the way of progressively heating：30-40 ° of immersion 5-10 minute, 40-60 ° of immersion 10-15 minute, 60-80 ° of immersion 5-10 minute, it is more stable that the mode for progressively heating up plays anti-wrinkle agent, is difficult It is rotten, and make absorption of the medicated clothing to anti-wrinkle agent more thoroughly abundant.
Further, the fragrant antimicrobial agent be by：The Folium Cinnamomi porrecti of 10 weight portions, the mentha leave of 10 weight portions, 15 weight The Flos Rosae Rugosae quintessence oil of part, the Flos Albiziae of 10 weight portions, the Rhizoma Zingiberis Recenss of 5 weight portions, the Flos Jasmini Sambac of 5 weight portions, the Flos Lonicerae of 5 weight portions, 2 The Fructus Piperiss of weight portion, the white vinegar of 1 weight portion.
The invention has the beneficial effects as follows：
1. the raw materials such as terylene, Modal fibre, spandex, polyester fiber are present invention employs, flexibility and crease-resistant has been had concurrently Property, the NACF of addition can not only make follow-up cloth dyeing more convenient, Color more preferably, while NACF Harmful substance can be adsorbed, it is more environmentally friendly more healthy.
2. warp is pressed into 45 ° of oblique " well " word weaving methods with parallel, medicated clothing small range is stretched up and down, more preferably It is crease-resistant.
3. add liquid nitrogen in adopting anti-wrinkle agent, then carry out the process that crystallizing and drying is denitrogenated, carry out effectively cloth Crease-resistant smoothing wrinkle, while coordinate the not only crease-resistant effect of smoothing wrinkle such as citric acid, Oxytarch slurry, organosilicon, soft phospholipid, Nano sol, And there is softness to clothes fiber, destatic, nursing role, it is to avoid cloth friction produces electrostatic, discomfort is caused to human body.
4. using the raw material of natural green, not only with good antibacterial action, and abnormal smells from the patient is fragrant for fragrant antimicrobial agent Fragrant unique natural, also environmental protection nonhazardouss are not injured to human body.
Specific embodiment：
In order that technological means, creation characteristic, reached purpose and effect that the present invention is realized are easy to understand, tie below Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of processing method of soft anti-wrinkle fabric, step are as follows：
1) fabric will be made after warp thread and weft yarn blending；
2) fabric is tiled, 10 are pressed with distilled water, salt, white vinegar:1：Solution made by 1 ratio is smoked；
3) fabric after smoking is put in anti-wrinkle agent carries out immersion 30 minutes；
4) fabric after immersion is carried out into crystallizing and drying；
5) repetition is smoked, is soaked, drying steps 2 times；
6) by step 5) cloth that completes carries out machine shrunk process；
7) by step 6) the sprinkling fragrant antimicrobial agent of the cloth two sides that completes, fountain height is 40g/m2；
8) by step 7) cloth that completes carries out natural air drying.
Above-mentioned warp thread includes the raw material of following parts by weight：15 parts of absorbent cotton, terylene 3,1 part of NACF；The latitude Yarn includes the raw material of following parts by weight：5 parts of Modal fibre, 4 parts of spandex, polyester fiber 2.
Above-mentioned steps 3) in anti-wrinkle agent be made up of the raw material of following parts by weight：15 parts of liquid nitrogen, 5 parts of citric acid, oxidation 5 parts of starch slurry, 3 parts of Nano chitosan, 2 parts of organosilicon, 1 part of lecithin, 1 part of Nano sol.
Above-mentioned steps immersion process 3) is by the way of progressively heating：30 ° are soaked 5 minutes, and 40 ° are soaked 15 minutes, 60 ° Immersion 10 minutes.
Above-mentioned fragrant antimicrobial agent be by：The Folium Cinnamomi porrecti of 10 weight portions, the mentha leave of 10 weight portions, the rhodamine toner of 15 weight portions Oil, the Flos Albiziae of 10 weight portions, the Rhizoma Zingiberis Recenss of 5 weight portions, the Flos Jasmini Sambac of 5 weight portions, the Flos Lonicerae of 5 weight portions, the Hu of 2 weight portions Green pepper, the white vinegar of 1 weight portion.
Embodiment 2
A kind of processing method of soft anti-wrinkle fabric, step are as follows：
1) fabric will be made after warp thread and weft yarn blending；
2) fabric is tiled, 10 are pressed with distilled water, salt, white vinegar:1：Solution made by 1 ratio is smoked；
3) fabric after smoking is put in anti-wrinkle agent carries out immersion 20 minutes；
4) fabric after immersion is carried out into crystallizing and drying；
5) repetition is smoked, is soaked, drying steps 3 times；
6) by step 5) cloth that completes carries out machine shrunk process；
7) by step 6) the sprinkling fragrant antimicrobial agent of the cloth two sides that completes, fountain height is 40g/m2；
8) by step 7) cloth that completes carries out natural air drying.
Above-mentioned warp thread includes the raw material of following parts by weight：20 parts of absorbent cotton, terylene 6,3 parts of NACF；The latitude Yarn includes the raw material of following parts by weight：10 parts of Modal fibre, 8 parts of spandex, polyester fiber 5.
Above-mentioned steps 3) in anti-wrinkle agent be made up of the raw material of following parts by weight：20 parts of liquid nitrogen, 10 parts of citric acid, oxidation 10 parts of starch slurry, 6 parts of Nano chitosan, 5 parts of organosilicon, 3 parts of lecithin, 2 parts of Nano sol.
Above-mentioned steps immersion process 3) is by the way of progressively heating：40 ° are soaked 5 minutes, and 60 ° are soaked 10 minutes, 80 ° Immersion 5 minutes.
Above-mentioned fragrant antimicrobial agent be by：The Folium Cinnamomi porrecti of 10 weight portions, the mentha leave of 10 weight portions, the rhodamine toner of 15 weight portions Oil, the Flos Albiziae of 10 weight portions, the Rhizoma Zingiberis Recenss of 5 weight portions, the Flos Jasmini Sambac of 5 weight portions, the Flos Lonicerae of 5 weight portions, the Hu of 2 weight portions Green pepper, the white vinegar of 1 weight portion.
The present invention soft crease-resistant test and appraisal such as table 1 under different disposal with sample：
Table 1
Sample 1 is a kind of soft cloth on market, and sample 2 is a kind of crease-resistant cloth on market.
The ultimate principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry Personnel it should be appreciated that the present invention is not restricted to the described embodiments, the simply explanation described in above-described embodiment and description this The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes Change and improvement is both fallen within scope of the claimed invention.The claimed scope of the invention by appending claims and its Equivalent thereof.

Claims (4)

1. a kind of processing method of soft anti-wrinkle fabric, step are as follows：
1) fabric will be made after warp thread and weft yarn blending；
2) fabric is tiled, 10 are pressed with distilled water, salt, white vinegar:1：Solution made by 1 ratio is smoked；
3) fabric after smoking is put in anti-wrinkle agent carries out soaking 20-30 minutes；
4) fabric after immersion is carried out into crystallizing and drying；
5) repetition is smoked, is soaked, drying steps 2-3 time；
6) by step 5) cloth that completes carries out machine shrunk process；
7) by step 6) the sprinkling fragrant antimicrobial agent of the cloth two sides that completes, fountain height is 40g/m2；
8) by step 7) cloth that completes carries out natural air drying.
Further, the step 3) in anti-wrinkle agent be made up of the raw material of following parts by weight：Liquid nitrogen 15-20 parts, citric acid 5-10 parts, Oxytarch slurry 5-10 parts, Nano chitosan 3-6 parts, organosilicon 2-5 parts, lecithin 1-3 parts, Nano sol 1-2 Part.
2. the processing method of soft anti-wrinkle fabric according to claim 1, it is characterised in that：The warp thread includes following heavy The raw material of amount number：Absorbent cotton 15-20 parts, terylene 3-6, NACF 1-3 parts；The weft yarn includes following parts by weight Raw material：Modal fibre 5-10 parts, spandex 4-8 parts, polyester fiber 2-5.
3. the processing method of soft anti-wrinkle fabric according to claim 2, it is characterised in that：The step 3) immersion The mode that Cheng Caiyong is progressively heated：30-40 ° of immersion 5-10 minute, 40-60 ° of immersion 10-15 minute, 60-80 ° of immersion 5-10 divide Clock.
4. the processing method of the soft anti-wrinkle fabric according to any one of claim 1-3, it is characterised in that：The fragrance is anti- Microbial inoculum be by：The Folium Cinnamomi porrecti of 10 weight portions, the mentha leave of 10 weight portions, the Flos Rosae Rugosae quintessence oil of 15 weight portions, the Herba Albiziae of 10 weight portions Flower, the Rhizoma Zingiberis Recenss of 5 weight portions, the Flos Jasmini Sambac of 5 weight portions, the Flos Lonicerae of 5 weight portions, the Fructus Piperiss of 2 weight portions, the white vinegar of 1 weight portion.
CN201610978206.0A 2016-11-08 2016-11-08 Soft anti-wrinkle fabric processing method Pending CN106592200A (en)