CN108978185A - A kind of dedicated antibacterial textile fabric of baby and preparation method thereof - Google Patents

A kind of dedicated antibacterial textile fabric of baby and preparation method thereof Download PDF

Info

Publication number
CN108978185A
CN108978185A CN201810901013.4A CN201810901013A CN108978185A CN 108978185 A CN108978185 A CN 108978185A CN 201810901013 A CN201810901013 A CN 201810901013A CN 108978185 A CN108978185 A CN 108978185A
Authority
CN
China
Prior art keywords
parts
textile fabric
agent
baby
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810901013.4A
Other languages
Chinese (zh)
Inventor
傅晓鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Cherry Young Best Technology Co Ltd
Original Assignee
Fujian Cherry Young Best Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujian Cherry Young Best Technology Co Ltd filed Critical Fujian Cherry Young Best Technology Co Ltd
Priority to CN201810901013.4A priority Critical patent/CN108978185A/en
Publication of CN108978185A publication Critical patent/CN108978185A/en
Pending legal-status Critical Current

Abstract

The invention discloses dedicated antibacterial textile fabrics of a kind of baby and preparation method thereof, which includes each component of following parts by weight: 20 ~ 30 parts of Modal fibre, 5 ~ 8 parts of viscose rayon, 3 ~ 6 parts of acetate fiber, 40 ~ 50 parts of wool fiber, 15 ~ 20 parts of Zein fibers, 5 ~ 10 parts of antibacterial finishing agent, 3 ~ 5 parts of antistatic agent and 2 ~ 5 parts of anti pilling agent.Antibacterial textile fabric proposed by the present invention has good antibacterial ability, anti-static ability and anti pilling ability, can be widely used in the nursing of infant, has good market application prospect.

Description

A kind of dedicated antibacterial textile fabric of baby and preparation method thereof
Technical field
The present invention relates to textile technology field, in particular to the dedicated antibacterial textile fabric of a kind of baby and its preparation side Method.
Background technique
In people's daily life, clothing clothes play very important effect.It is on the one hand big from the point of view of the market demand It measures low-grade dress-goods and is flooded with market, the dress-goods that consumption is promoted can really be met by the other hand still lacking.Especially pair In the consumer in social intermediate strata, it is expected that being both able to satisfy the need for improving self-image in routine work and social communication It asks, and the fabric and dress ornament of daily maintenance difficulty can be reduced.
From the perspective of the consumer of clothing, the consumer of different age group is corresponding due to its special bodily trait Requirement to clothing quality is also not quite similar.Especially for baby, the characteristics of infant skin is that cutaneous immunisation ability is low, quick Sense is fragile, belongs to the cutaneous immunisation fluctuation stage.The outstanding behaviours of infant skin feature is the variation of skin bacteriostasis, parent Congenital bring immunity gradually weakens, and baby's autoimmunity still locates the budding stage, and the immunity of skin is low.If baby by Gradually start outdoor activities, then skin is easily permeated by external irritant or noxious material, causes friction impaired, i.e. this stage baby The various skin problems of youngster are easy to take advantage of a weak point.Therefore the clothing fabric that baby is worn is also required to reach by special processing Mark.
However, existing part clothes for infant fabric, does not have the effect of antibacterial substantially, change there are still biggish Kind space.
Summary of the invention
For this purpose, the purpose of the present invention is to solve existing part clothes for infant fabrics, do not have substantially anti- The problem of bacterium function.
The present invention proposes a kind of dedicated antibacterial textile fabric of baby, wherein each component including following parts by weight: not generation That 20 ~ 30 parts of fiber, 5 ~ 8 parts of viscose rayon, 3 ~ 6 parts of acetate fiber, 40 ~ 50 parts of wool fiber, Zein fibers 15 ~ 20 Part, 5 ~ 10 parts of antibacterial finishing agent, 3 ~ 5 parts of antistatic agent and 2 ~ 5 parts of anti pilling agent.
The dedicated antibacterial textile fabric of baby proposed by the present invention, due to joined antibacterial simultaneously in various fibrous materials Finishing agent, in practical applications, the antibacterial finishing agent can effectively inhibit bacterium；Further, since joined simultaneously Antistatic agent and anti pilling agent, therefore the problem of the anti-static effect of the fabric can be improved and be effectively prevented from pilling. The dedicated antibacterial textile fabric of baby proposed by the present invention has good antibacterial ability, anti-static ability and anti pilling energy Power can be widely used in the nursing of infant, have good market application prospect.
The dedicated antibacterial textile fabric of baby, wherein the antibacterial finishing agent includes each component of following parts by weight: 10 ~ 15 parts of titanium dioxide nano-particle, 5 ~ 8 parts of chitosan, 6 ~ 8 parts of sodium alginate, 1 ~ 2 part of nano silver, 3 ~ 5 parts of plant extraction agent And 1 ~ 2 part of sodium iodide.
The dedicated antibacterial textile fabric of baby, wherein the chitosan is carboxymethyl chitosan or hydroxypropyl Sugar, the plant extraction agent are one of aloe extractant, tea extraction agent or cactus extractant.
The dedicated antibacterial textile fabric of baby, wherein the diameter of the Modal fibre is 41 ~ 43um, and fiber number is 397 ~ 415dtex, the diameter of the viscose rayon are 42 ~ 44um, and fiber number is 406 ~ 415dtex, the diameter of the acetate fiber For 48 ~ 49um, fiber number is 415 ~ 422dtex, and the acetate fiber is two vinegar spinning-grade cellulose acetates.
The dedicated antibacterial textile fabric of baby, wherein the diameter of the wool fiber is 30 ~ 35um, fiber number 407 ~ 425dtex, the diameter of the Zein fibers are 33 ~ 36um, and fiber number is 411 ~ 423dtex, the antibacterial textile fabric Single thread breaking strength is 10 ~ 15cN/dtex, and single thread breaking strength coefficient of variation CV value is 13% ~ 14%.
The dedicated antibacterial textile fabric of baby, wherein the antistatic agent includes each component of following parts by weight: alkane 12 ~ 15 parts of base sulfonic acid, 3 ~ 18 parts of phosphatase 11,50 ~ 65 parts of lithium ion solution, the anti pilling agent include each group of following parts by weight Point: 11 ~ 12 parts of ethyl acrylate, 13 ~ 14 parts of zinc oxide nano-particle, 12 ~ 15 parts of zinc nitrate, 10 ~ 12 parts of paraffin, sodium sulphate 5 ~ 8 parts and 1 ~ 3 part of hydrogen peroxide.
The present invention also proposes a kind of preparation method of dedicated antibacterial textile fabric of baby, wherein the method includes such as Lower step:
By Modal fibre, viscose rayon, acetate fiber, wool fiber and Zein fibers, according to corresponding default weight Amount part ratio, which is added in drawing frame, to be mixed and is handled to obtain ripe bar；
It uses fly frame that the ripe bar is carried out drawing-off attenuating to obtain rove, sprays antibiotic finish on the surface of the rove Agent continues to spray antistatic agent to the rove, stands the first preset time after air drying；
The rove is added to after impregnating the second preset time in a processing barrel equipped with anti pilling agent and is taken out, it is default first At a temperature of stand third preset time, then the 4th preset time of preliminary drying under the second preset temperature；
The rove is subjected to spun yarn processing to obtain spun yarn using spinning frame, is wound into the spun yarn in bobbin-winding machine Tubular spun yarn, by the tubular spun yarn through doubling, twist thread, obtain the dedicated antibacterial textile fabric of the baby after warping.
The preparation method of the dedicated antibacterial textile fabric of baby, wherein the antibacterial finishing agent includes following weight The each component of part: 10 ~ 15 parts of titanium dioxide nano-particle, 5 ~ 8 parts of chitosan, 6 ~ 8 parts of sodium alginate, 1 ~ 2 part of nano silver, plant 3 ~ 5 parts of extractant and 1 ~ 2 part of sodium iodide.
The preparation method of the dedicated antibacterial textile fabric of baby, wherein first preset time is 1.5 ~ 2h, institute Stating the second preset time is 4 ~ 4.5h, and the third preset time and the 4th preset time are 1 ~ 1.5h, described the One preset temperature is 30 DEG C ~ 35 DEG C, and second preset temperature is 86 DEG C ~ 95 DEG C.
The preparation method of the dedicated antibacterial textile fabric of baby, wherein it is corresponding that the ripe bar is subjected to drawing-off attenuating Drafting multiple be 20 ~ 25 times, when the rove being spun into the spun yarn using the spinning frame corresponding ingot speed be 7200 ~ 7800r/min。
Additional aspect and advantage of the invention will be set forth in part in the description, and will partially become from the following description Obviously, or practice through the invention is recognized.
Specific embodiment
In order to make the foregoing objectives, features and advantages of the present invention clearer and more comprehensible, the present invention can be with many differences Form realize, however it is not limited to embodiment described herein.On the contrary, purpose of providing these embodiments is makes to this hair Bright disclosure is more thorough and comprehensive.
It should be noted that it can directly on the other element when element is referred to as " being fixedly arranged on " another element Or there may also be elements placed in the middle.When an element is considered as " connection " another element, it, which can be, is directly connected to To another element or it may be simultaneously present centering elements.Term as used herein " vertical ", " horizontal ", " left side ", " right side ", "upper", "lower" and similar statement for illustrative purposes only, rather than the device or member of indication or suggestion meaning Part must have a particular orientation, be constructed and operated in a specific orientation, therefore be not considered as limiting the invention.
In the present invention unless specifically defined or limited otherwise, term " installation ", " connected ", " connection ", " fixation " etc. Term shall be understood in a broad sense, for example, it may be being fixedly connected, may be a detachable connection, or be integrally connected；It can be machine Tool connection, is also possible to be electrically connected；It can be directly connected, two members can also be can be indirectly connected through an intermediary Connection inside part.For the ordinary skill in the art, above-mentioned term can be understood in this hair as the case may be Concrete meaning in bright.Term " and or " used herein include the arbitrary of one or more relevant listed items and All combinations.
Existing part clothes for infant fabric, does not have the effect of antibacterial substantially, and it is empty that there are still biggish improvement Between.
In order to solve the above-mentioned technical problem, the present invention proposes a kind of dedicated antibacterial textile fabric of baby, wherein the weaving Fabric includes each component of following parts by weight: 20 ~ 30 parts of Modal fibre, 5 ~ 8 parts of viscose rayon, 3 ~ 6 parts of acetate fiber, wool 40 ~ 50 parts of fiber, 15 ~ 20 parts of Zein fibers, 5 ~ 10 parts of antibacterial finishing agent, 3 ~ 5 parts of antistatic agent and anti pilling agent 2 ~ 5 Part.
For above-mentioned antibacterial finishing agent, which includes each component of following parts by weight: titanium dioxide is received 10 ~ 15 parts of rice corpuscles, 5 ~ 8 parts of chitosan, 6 ~ 8 parts of sodium alginate, 1 ~ 2 part of nano silver, 3 ~ 5 parts of plant extraction agent and sodium iodide 1 ~ 2 part.Wherein, above-mentioned chitosan can be carboxymethyl chitosan or hydroxypropyl chitosan.Above-mentioned plant extraction agent can be with For one of aloe extractant, tea extraction agent or cactus extractant.
For above-mentioned Modal fibre, the diameter of the Modal fibre is 41 ~ 43um, and fiber number is 397 ~ 415dtex. The diameter of viscose rayon is 42 ~ 44um, and fiber number is 406 ~ 415dtex, and the diameter of acetate fiber is 48 ~ 49um, fiber number is 415 ~ 422dtex.Wherein, acetate fiber is two vinegar spinning-grade cellulose acetates.
For above-mentioned wool fiber, the diameter of the wool fiber is 30 ~ 35um, and fiber number is 407 ~ 425dtex.The jade The diameter of rice gluten fiber is 33 ~ 36um, and fiber number is 411 ~ 423dtex, the single thread breaking strength of antibacterial textile fabric is 10 ~ 15cN/dtex, single thread breaking strength coefficient of variation CV value are 13% ~ 14%.
For above-mentioned antistatic agent, which includes each component of following parts by weight: alkyl sulfonic acid 12 ~ 15 Part, 3 ~ 18 parts of phosphatase 11,50 ~ 65 parts of lithium ion solution.The anti pilling agent includes each component of following parts by weight: ethyl acrylate 11 ~ 12 parts, 13 ~ 14 parts of zinc oxide nano-particle, 12 ~ 15 parts of zinc nitrate, 10 ~ 12 parts of paraffin, 5 ~ 8 parts of sodium sulphate and hydrogen peroxide 1 ~ 3 part.
The dedicated antibacterial textile fabric of baby proposed by the present invention, due to joined antibacterial simultaneously in various fibrous materials Finishing agent, in practical applications, the antibacterial finishing agent can effectively inhibit bacterium；Further, since joined simultaneously Antistatic agent and anti pilling agent, therefore the problem of the anti-static effect of the fabric can be improved and be effectively prevented from pilling. The dedicated antibacterial textile fabric of baby proposed by the present invention has good antibacterial ability, anti-static ability and anti pilling energy Power can be widely used in the nursing of infant, have good market application prospect.
The present invention also proposes a kind of preparation method of dedicated antibacterial textile fabric of baby, wherein this method includes as follows Step:
(1) by Modal fibre, viscose rayon, acetate fiber, wool fiber and Zein fibers, according to corresponding default Weight part ratio, which is added in drawing frame, to be mixed and is handled to obtain ripe bar.
Wherein, the parts by weight of the Modal fibre of addition are 20 ~ 30 parts, and the parts by weight of viscose rayon are 5 ~ 8 parts, acetic acid is fine The parts by weight of dimension are 3 ~ 6 parts, the parts by weight of wool fiber are 40 ~ 50 parts, the parts by weight of Zein fibers are 15 ~ 20 parts.
The diameter of above-mentioned Modal fibre is 41 ~ 43um, and fiber number is 397 ~ 415dtex, the diameter of viscose rayon is 42 ~ 44um, fiber number are 406 ~ 415dtex, and the diameter of acetate fiber is 48 ~ 49um, and fiber number is 415 ~ 422dtex.Wherein, acetic acid is fine Dimension is two vinegar spinning-grade cellulose acetates.The diameter of above-mentioned wool fiber is 30 ~ 35um, and fiber number is 407 ~ 425dtex.The corn The diameter of azelon is 33 ~ 36um, and fiber number is 411 ~ 423dtex.
(2) it uses fly frame that ripe bar is carried out drawing-off attenuating to obtain rove, sprays antibacterial finishing agent on the surface of rove, After air drying, continue to spray antistatic agent to rove, stand 1.5 ~ 2h.
In this step, the antibacterial finishing agent of addition includes each component of following parts by weight: titanium dioxide nano-particle 10 ~ 15 parts, 5 ~ 8 parts of chitosan, 6 ~ 8 parts of sodium alginate, 1 ~ 2 part of nano silver, 3 ~ 5 parts of plant extraction agent and 1 ~ 2 part of sodium iodide.Its In, above-mentioned chitosan can be carboxymethyl chitosan or hydroxypropyl chitosan.Above-mentioned plant extraction agent can extract for aloe Take one of agent, tea extraction agent or cactus extractant.
(3) rove is added to after impregnating 4 ~ 4.5h in a processing barrel equipped with anti pilling agent and is taken out, at 30 DEG C ~ 35 DEG C 1 ~ 1.5h is stood, then 1 ~ 1.5h of preliminary drying at 86 DEG C ~ 95 DEG C.
In this step, which includes each component of following parts by weight: 11 ~ 12 parts of ethyl acrylate, zinc oxide 13 ~ 14 parts of nanoparticle, 12 ~ 15 parts of zinc nitrate, 10 ~ 12 parts of paraffin, 5 ~ 8 parts of sodium sulphate and 1 ~ 3 part of hydrogen peroxide.
(4) rove is subjected to spun yarn processing to obtain spun yarn using spinning frame, is wound into spun yarn in bobbin-winding machine Tubular spun yarn, by tubular spun yarn through doubling, twist thread, obtain the dedicated antibacterial textile fabric of baby after warping.
It is 20 ~ 25 times that ripe bar, which is carried out the corresponding drafting multiple of drawing-off attenuating, is spun into the rove carefully using spinning frame Corresponding ingot speed is 7200 ~ 7800r/min when yarn.
It is carried out in further detail with preparation method of several specific embodiments to antibacterial textile fabric of the invention below Explanation.
Embodiment one
(1) by Modal fibre, viscose rayon, acetate fiber, wool fiber and Zein fibers, according to corresponding default Weight part ratio, which is added in drawing frame, to be mixed and is handled to obtain ripe bar.
Wherein, the parts by weight of the Modal fibre of addition are 20 parts, and the parts by weight of viscose rayon are 3 parts, acetate fiber Parts by weight are 3 parts, the parts by weight of wool fiber are 40 parts, the parts by weight of Zein fibers are 20 parts.
The diameter of above-mentioned Modal fibre is 41um, and the diameter of fiber number 397dtex, viscose rayon are 42um, and fiber number is 406dtex, the diameter of acetate fiber are 48um, fiber number 415dtex.Wherein, acetate fiber is two vinegar spinning-grade acetate fibers Element.The diameter of above-mentioned wool fiber is 30um, fiber number 407dtex.The diameter of the Zein fibers is 33um, and fiber number is 411dtex。
(2) it uses fly frame that ripe bar is carried out drawing-off attenuating to obtain rove, sprays antibacterial finishing agent on the surface of rove, After air drying, continue to spray antistatic agent to rove, stand 1.5 ~ 2h.
In this step, the antibacterial finishing agent of addition includes each component of following parts by weight: titanium dioxide nano-particle 10 Part, 5 parts of chitosan, 6 parts of sodium alginate, 1 part of nano silver, 3 parts of plant extraction agent and 2 parts of sodium iodide.Wherein, above-mentioned shell is poly- Sugar is carboxymethyl chitosan.Above-mentioned plant extraction agent is aloe extractant.
(3) rove is added to after impregnating 4h in a processing barrel equipped with anti pilling agent and is taken out, 1h is stood at 30 DEG C, so The preliminary drying 1h at 86 DEG C afterwards.
In this step, which includes each component of following parts by weight: 11 parts of ethyl acrylate, zinc-oxide nano 13 parts of particle, 12 parts of zinc nitrate, 10 parts of paraffin, 5 parts of sodium sulphate and 1 part of hydrogen peroxide.
(4) rove is subjected to spun yarn processing to obtain spun yarn using spinning frame, is wound into spun yarn in bobbin-winding machine Tubular spun yarn, by tubular spun yarn through doubling, twist thread, obtain the dedicated antibacterial textile fabric of baby after warping.
In this step, ripe bar is carried out the corresponding drafting multiple of drawing-off attenuating is 20 times, will be described thick using spinning frame It is 7200r/min that yarn, which is spun into corresponding ingot speed when spun yarn,.
The single thread breaking strength of the antibacterial textile fabric prepared using the present embodiment is 10cN/dtex, single thread fracture Strength variable coefficient CV value is 13%.
Embodiment two
(1) by Modal fibre, viscose rayon, acetate fiber, wool fiber and Zein fibers, according to corresponding default Weight part ratio, which is added in drawing frame, to be mixed and is handled to obtain ripe bar.
Wherein, the parts by weight of the Modal fibre of addition are 30 parts, and the parts by weight of viscose rayon are 8 parts, acetate fiber Parts by weight are 6 parts, the parts by weight of wool fiber are 50 parts, the parts by weight of Zein fibers are 20 parts.
The diameter of above-mentioned Modal fibre is 43um, and the diameter of fiber number 415dtex, viscose rayon are 44um, and fiber number is 415dtex, the diameter of acetate fiber are 49um, fiber number 422dtex.Wherein, acetate fiber is two vinegar spinning-grade acetate fibers Element.The diameter of above-mentioned wool fiber is 35um, fiber number 425dtex.The diameter of the Zein fibers is 36um, and fiber number is 423dtex。
(2) it uses fly frame that ripe bar is carried out drawing-off attenuating to obtain rove, sprays antibacterial finishing agent on the surface of rove, After air drying, continue to spray antistatic agent to rove, stand 2h.
In this step, the antibacterial finishing agent of addition includes each component of following parts by weight: titanium dioxide nano-particle 15 Part, 8 parts of chitosan, 8 parts of sodium alginate, 2 parts of nano silver, 5 parts of plant extraction agent and 1 part of sodium iodide.Wherein, above-mentioned shell is poly- Sugar is hydroxypropyl chitosan.Above-mentioned plant extraction agent is tea extraction agent.
(3) rove is added to after impregnating 4.5h in a processing barrel equipped with anti pilling agent and is taken out, stood at 35 DEG C 1.5h, then the preliminary drying 1.5h at 95 DEG C.
In this step, which includes each component of following parts by weight: 12 parts of ethyl acrylate, zinc-oxide nano 14 parts of particle, 15 parts of zinc nitrate, 12 parts of paraffin, 8 parts of sodium sulphate and 3 parts of hydrogen peroxide.
(4) rove is subjected to spun yarn processing to obtain spun yarn using spinning frame, is wound into spun yarn in bobbin-winding machine Tubular spun yarn, by tubular spun yarn through doubling, twist thread, obtain the dedicated antibacterial textile fabric of baby after warping.
In this step, ripe bar is carried out the corresponding drafting multiple of drawing-off attenuating is 25 times, will be described thick using spinning frame It is 7800r/min that yarn, which is spun into corresponding ingot speed when spun yarn,.
The single thread breaking strength of the antibacterial textile fabric prepared using the present embodiment is 12cN/dtex, single thread fracture Strength variable coefficient CV value is 13%.
Embodiment three
(1) by Modal fibre, viscose rayon, acetate fiber, wool fiber and Zein fibers, according to corresponding default Weight part ratio, which is added in drawing frame, to be mixed and is handled to obtain ripe bar.
Wherein, the parts by weight of the Modal fibre of addition are 25 parts, and the parts by weight of viscose rayon are 6 parts, acetate fiber Parts by weight are 5 parts, the parts by weight of wool fiber are 45 parts, the parts by weight of Zein fibers are 17 parts.
The diameter of above-mentioned Modal fibre is 42um, and the diameter of fiber number 406dtex, viscose rayon are 43um, and fiber number is 410dtex, the diameter of acetate fiber are 48.5um, fiber number 417dtex.Wherein, acetate fiber is that two vinegar spinning-grade acetic acid are fine Dimension element.The diameter of above-mentioned wool fiber is 33um, fiber number 417dtex.The diameter of the Zein fibers is 34um, and fiber number is 416dtex。
(2) it uses fly frame that ripe bar is carried out drawing-off attenuating to obtain rove, sprays antibacterial finishing agent on the surface of rove, After air drying, continue to spray antistatic agent to rove, stand 1.5h.
In this step, the antibacterial finishing agent of addition includes each component of following parts by weight: titanium dioxide nano-particle 12 Part, 6 parts of chitosan, 7 parts of sodium alginate, 1 part of nano silver, 4 parts of plant extraction agent and 1 part of sodium iodide.Wherein, above-mentioned shell is poly- Sugar is carboxymethyl chitosan.Above-mentioned plant extraction agent is cactus extractant.
(3) rove is added to after impregnating 4h in a processing barrel equipped with anti pilling agent and is taken out, stand 1.5h at 32 DEG C, Then the preliminary drying 1h at 90 DEG C.
In this step, which includes each component of following parts by weight: 11 parts of ethyl acrylate, zinc-oxide nano 13 parts of particle, 14 parts of zinc nitrate, 11 parts of paraffin, 6 parts of sodium sulphate and 2 parts of hydrogen peroxide.
(4) rove is subjected to spun yarn processing to obtain spun yarn using spinning frame, is wound into spun yarn in bobbin-winding machine Tubular spun yarn, by tubular spun yarn through doubling, twist thread, obtain the dedicated antibacterial textile fabric of baby after warping.
In this step, ripe bar is carried out the corresponding drafting multiple of drawing-off attenuating is 24 times, will be described thick using spinning frame It is 7600r/min that yarn, which is spun into corresponding ingot speed when spun yarn,.
The single thread breaking strength of the antibacterial textile fabric prepared using the present embodiment is 13cN/dtex, single thread fracture Strength variable coefficient CV value is 14%.
Example IV
(1) by Modal fibre, viscose rayon, acetate fiber, wool fiber and Zein fibers, according to corresponding default Weight part ratio, which is added in drawing frame, to be mixed and is handled to obtain ripe bar.
Wherein, the parts by weight of the Modal fibre of addition are 25 parts, and the parts by weight of viscose rayon are 7 parts, acetate fiber Parts by weight are 5 parts, the parts by weight of wool fiber are 46 parts, the parts by weight of Zein fibers are 18 parts.
The diameter of above-mentioned Modal fibre is 42um, and the diameter of fiber number 410dtex, viscose rayon are 43um, and fiber number is 411dtex, the diameter of acetate fiber are 48um, fiber number 420dtex.Wherein, acetate fiber is two vinegar spinning-grade acetate fibers Element.The diameter of above-mentioned wool fiber is 33um, fiber number 416dtex.The diameter of the Zein fibers is 34um, and fiber number is 418dtex。
(2) it uses fly frame that ripe bar is carried out drawing-off attenuating to obtain rove, sprays antibacterial finishing agent on the surface of rove, After air drying, continue to spray antistatic agent to rove, stand 1.5h.
In this step, the antibacterial finishing agent of addition includes each component of following parts by weight: titanium dioxide nano-particle 10 Part, 5 parts of chitosan, 6 parts of sodium alginate, 1 part of nano silver, 4 parts of plant extraction agent and 2 parts of sodium iodide.Wherein, above-mentioned shell is poly- Sugar is carboxymethyl chitosan.Above-mentioned plant extraction agent is aloe extractant.
(3) rove is added to after impregnating 4.5h in a processing barrel equipped with anti pilling agent and is taken out, stand 1h at 30 DEG C, Then the preliminary drying 1h at 86 DEG C.
In this step, which includes each component of following parts by weight: 11 parts of ethyl acrylate, zinc-oxide nano 13 parts of particle, 12 parts of zinc nitrate, 12 parts of paraffin, 8 parts of sodium sulphate and 3 parts of hydrogen peroxide.
(4) rove is subjected to spun yarn processing to obtain spun yarn using spinning frame, is wound into spun yarn in bobbin-winding machine Tubular spun yarn, by tubular spun yarn through doubling, twist thread, obtain the dedicated antibacterial textile fabric of baby after warping.
In this step, ripe bar is carried out the corresponding drafting multiple of drawing-off attenuating is 25 times, will be described thick using spinning frame It is 7200r/min that yarn, which is spun into corresponding ingot speed when spun yarn,.
In the present invention, by antibacterial textile fabric preparation-obtained in above-described embodiment one to four, to different bacterium colonies Rejection ability is tested, and the result of test is as shown in Table 1:
As can be seen from Table I, in above-described embodiment one to four, the preparation side of antibacterial textile fabric proposed by the present invention is utilized The preparation-obtained antibacterial textile fabric of method, to the inhibiting rate of Escherichia coli, staphylococcus aureus and Candida albicans It is significantly larger than existing textile fabric, therefore there is good antibacterial inhibitory effect.Baby proposed by the present invention is dedicated anti- Bacterium textile fabric has good antibacterial ability, anti-static ability and anti pilling ability, can be widely used in infant's In nursing, there is good market application prospect.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show The description of example " or " some examples " etc. means specific features, structure, material or spy described in conjunction with this embodiment or example Point is included at least one embodiment or example of the invention.In the present specification, schematic expression of the above terms are not Centainly refer to identical embodiment or example.Moreover, particular features, structures, materials, or characteristics described can be any One or more embodiment or examples in can be combined in any suitable manner.
The embodiments described above only express several embodiments of the present invention, and the description thereof is more specific and detailed, but simultaneously Limitations on the scope of the patent of the present invention therefore cannot be interpreted as.It should be pointed out that for those of ordinary skill in the art For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to guarantor of the invention Protect range.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.

Claims (10)

1. a kind of dedicated antibacterial textile fabric of baby, which is characterized in that each component including following parts by weight: Modal fibre 20 ~ 30 parts, 5 ~ 8 parts of viscose rayon, 3 ~ 6 parts of acetate fiber, 40 ~ 50 parts of wool fiber, 15 ~ 20 parts of Zein fibers, antibacterial 5 ~ 10 parts of finishing agent, 3 ~ 5 parts of antistatic agent and 2 ~ 5 parts of anti pilling agent.
2. the dedicated antibacterial textile fabric of baby according to claim 1, which is characterized in that the antibacterial finishing agent includes The each component of following parts by weight: 10 ~ 15 parts of titanium dioxide nano-particle, 5 ~ 8 parts of chitosan, 6 ~ 8 parts of sodium alginate, nano silver 1 ~ 2 parts, 3 ~ 5 parts of plant extraction agent and 1 ~ 2 part of sodium iodide.
3. the dedicated antibacterial textile fabric of baby according to claim 2, which is characterized in that the chitosan is carboxymethyl Chitosan or hydroxypropyl chitosan, the plant extraction agent are in aloe extractant, tea extraction agent or cactus extractant It is a kind of.
4. the dedicated antibacterial textile fabric of baby according to claim 2, which is characterized in that the Modal fibre it is straight Diameter is 41 ~ 43um, and fiber number is 397 ~ 415dtex, and the diameter of the viscose rayon is 42 ~ 44um, and fiber number is 406 ~ 415dtex, The diameter of the acetate fiber is 48 ~ 49um, and fiber number is 415 ~ 422dtex, and the acetate fiber is that two vinegar spinning-grade acetic acid are fine Dimension element.
5. the dedicated antibacterial textile fabric of baby according to claim 4, which is characterized in that the diameter of the wool fiber For 30 ~ 35um, fiber number is 407 ~ 425dtex, and the diameter of the Zein fibers is 33 ~ 36um, fiber number is 411 ~ 423dtex, the single thread breaking strength of the antibacterial textile fabric are 10 ~ 15cN/dtex, single thread breaking strength coefficient of variation CV value It is 13% ~ 14%.
6. the dedicated antibacterial textile fabric of baby according to claim 1, which is characterized in that the antistatic agent includes such as The each component of lower parts by weight: 12 ~ 15 parts of alkyl sulfonic acid, 3 ~ 18 parts of phosphatase 11,50 ~ 65 parts of lithium ion solution, the anti pilling agent packet Include each component of following parts by weight: 11 ~ 12 parts of ethyl acrylate, 13 ~ 14 parts of zinc oxide nano-particle, 12 ~ 15 parts of zinc nitrate, stone 10 ~ 12 parts of wax, 5 ~ 8 parts of sodium sulphate and 1 ~ 3 part of hydrogen peroxide.
7. a kind of preparation method of the dedicated antibacterial textile fabric of baby, which is characterized in that described method includes following steps:
By Modal fibre, viscose rayon, acetate fiber, wool fiber and Zein fibers, according to corresponding default weight Amount part ratio, which is added in drawing frame, to be mixed and is handled to obtain ripe bar；
It uses fly frame that the ripe bar is carried out drawing-off attenuating to obtain rove, sprays antibiotic finish on the surface of the rove Agent continues to spray antistatic agent to the rove, stands the first preset time after air drying；
The rove is added to after impregnating the second preset time in a processing barrel equipped with anti pilling agent and is taken out, it is default first At a temperature of stand third preset time, then the 4th preset time of preliminary drying under the second preset temperature；
The rove is subjected to spun yarn processing to obtain spun yarn using spinning frame, is wound into the spun yarn in bobbin-winding machine Tubular spun yarn, by the tubular spun yarn through doubling, twist thread, obtain the dedicated antibacterial textile fabric of the baby after warping.
8. the preparation method of the dedicated antibacterial textile fabric of baby according to claim 7, which is characterized in that the antibacterial Finishing agent includes each component of following parts by weight: 10 ~ 15 parts of titanium dioxide nano-particle, 5 ~ 8 parts of chitosan, sodium alginate 6 ~ 8 Part, 1 ~ 2 part of nano silver, 3 ~ 5 parts of plant extraction agent and 1 ~ 2 part of sodium iodide.
9. the preparation method of the dedicated antibacterial textile fabric of baby according to claim 7, which is characterized in that described first Preset time be 1.5 ~ 2h, second preset time be 4 ~ 4.5h, the third preset time and it is described 4th it is default when Between be 1 ~ 1.5h, first preset temperature be 30 DEG C ~ 35 DEG C, second preset temperature be 86 DEG C ~ 95 DEG C.
10. the preparation method of the dedicated antibacterial textile fabric of baby according to claim 7, which is characterized in that will be described It is 20 ~ 25 times that ripe bar, which carries out the corresponding drafting multiple of drawing-off attenuating, and the rove is spun into the spun yarn using the spinning frame When corresponding ingot speed be 7200 ~ 7800r/min.
CN201810901013.4A 2018-08-09 2018-08-09 A kind of dedicated antibacterial textile fabric of baby and preparation method thereof Pending CN108978185A (en)