CN101613890A - A kind of preparation method of anion terylene fiber and the application in spinning of being in thereof - Google Patents
A kind of preparation method of anion terylene fiber and the application in spinning of being in thereof Download PDFInfo
- Publication number
- CN101613890A CN101613890A CN200910054875A CN200910054875A CN101613890A CN 101613890 A CN101613890 A CN 101613890A CN 200910054875 A CN200910054875 A CN 200910054875A CN 200910054875 A CN200910054875 A CN 200910054875A CN 101613890 A CN101613890 A CN 101613890A
- Authority
- CN
- China
- Prior art keywords
- anion
- preparation
- terylene fiber
- anion terylene
- high polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to technical field of textile application, be specifically related to a kind of preparation method and application of anion terylene fiber, in order to solve the dispersing uniformity of inorganic matter anion generation particulate in fiber, fastness, problem that durability is all not high, the invention provides the preparation method that a kind of anion terylene fiber is provided, this anion terylene fiber can be used for preparing the negative-ion fiber core, uses the inorganic matter anion generation particulate in the anion terylene fiber of this method preparation to have good dispersing uniformity, fastness, durability.
Description
Technical field
The present invention relates to technical field of textile application, be specifically related to a kind of preparation method of anion terylene fiber and the application in spinning of being in.
Background technology
Along with the raising day by day of social industrialization degree, the pollution of air is more and more serious, and progress of science and technology and The development in society and economy have strengthened people's health care consciousness.Especially after the mechanism of action of negative aeroion was seen clearly day by day, a kind of fiber with anion function had attracted Chinese scholars that it is researched and developed as the functional fibre that truly can improve environment.
The widespread usage of back finishing technique, the Application Areas of anion textiles has been widened in continually developing of anion-generating material greatly.The anion lining of being developed has and contacts advantages such as soft, that water-wash resistance is good, anion generation effect is obvious with skin, be widely used in take, household with and medical etc.Especially added the anion bedding of infrared emission material, the anion of its generation and infrared ray can promote the blood of human body circulation, help for sleep, and have more strengthened the health-care effect of product.But, also exist incomplete place and anxious to be solved between topic, the dispersing uniformity of inorganic matter anion generation particulate in fiber, fastness, the problem that durability is all not high.
Summary of the invention
The problem that technical problem solved by the invention is the dispersing uniformity of inorganic matter anion generation particulate in fiber, fastness, durability is all not high, and a kind of preparation method of anion terylene fiber is provided, use the inorganic matter anion generation particulate in the anion terylene fiber of this method preparation to have good dispersing uniformity, fastness, durability.
The technical problem that will solve required for the present invention can be achieved through the following technical solutions:
A kind of preparation method of anion terylene fiber comprises:
A. negative ion generating body is made the nanometer grade powder that has good intermiscibility with high polymer material;
B. nanometer grade powder is carried out surface treatment, handle afterproduct and mix, obtain mixture with polymer support;
C. molten mixture is extruded and is made the anion master batch, again the anion master batch is carried out drying, obtains desciccate;
D. desciccate is mixed with the high polymer section, mix products and polyster fibre carry out blending, obtain anion terylene fiber.
Described negative ion generating body is a kind of in the rare earth ore, pottery of tourmaline, trace-level activity, and described high polymer material and polymer support are polyester, and described high polymer section is polyester slice.
The specific embodiment
Embodiment 1
In order to make technological means of the present invention, creation characteristic, to reach purpose and effect is easy to understand,, further set forth the present invention below in conjunction with specific embodiment.
A kind of preparation method of anion terylene fiber comprises:
1. tourmaline is made the nanometer grade powder that has good intermiscibility with polyester;
2. nanometer grade powder is carried out surface treatment, handle afterproduct and mix with polyester, obtain mixture, the mixed weight ratio is 10: 1;
3. molten mixture is extruded and is made the anion master batch, again the anion master batch is carried out drying, obtains desciccate;
4. desciccate is mixed with the high polymer section, mix products and polyster fibre carry out blending, obtain anion terylene fiber, and described high polymer section is polyester slice.
1. resulting anion terylene fiber is used to prepare the anion terylene core, and its preparation technology's flow process is: and lining inspects → opens tailor's system → raw material by random samples and weigh → proportioning mixing → shredding comb washs → and wind send and fills suede/comb and wash lapping/no glue setting → can and coat → seal quilting → test package → finished product and put in storage.
The test verification result of the anion terylene core goods that obtain is as follows: bulking intensity 79cm
3/ g, compression ratio 68%, the elasticity of compression 92%, insulation rate 88.78%, air penetrability 40.5mm/s.The concentration of preserving in the core and discharging anion is at every cubic centimetre more than 2000.
Embodiment 2
A kind of preparation method of anion terylene fiber comprises:
1.. pottery is made the nanometer grade powder that has good intermiscibility with polyester;
2.. nanometer grade powder is carried out surface treatment, handle afterproduct and mix with polyester, obtain mixture, the mixed weight ratio is 15: 1;
3.. molten mixture, extrude and make the anion master batch, again the anion master batch is carried out drying, obtain desciccate;
4.. desciccate is mixed with the high polymer section, and mix products and polyster fibre carry out blending, obtain anion terylene fiber, and described high polymer section is polyester slice.
Resulting anion terylene fiber is used to prepare the anion terylene core, and its preparation technology's flow process is: and lining inspects → opens tailor's system → raw material by random samples and weigh → proportioning mixing → shredding comb washs → and wind send and fills suede/comb and wash lapping/no glue setting → can and coat → seal quilting → test package → finished product and put in storage.
Embodiment 3
(1). the rare earth ore of trace-level activity is made the nanometer grade powder that has good intermiscibility with polyester;
(2). nanometer grade powder is carried out surface treatment, handle afterproduct and mix with high polymer material, obtain mixture, the mixed weight ratio is 8: 1;
(3). molten mixture, extrude and make the anion master batch, again the anion master batch is carried out drying, obtain desciccate;
(4). desciccate is mixed with the high polymer section, and mix products and polyster fibre carry out blending, obtain anion terylene fiber, and described high polymer section is polyester slice.
Resulting anion terylene fiber is used to prepare the anion terylene core, and its preparation technology's flow process is: and lining inspects → opens tailor's system → raw material by random samples and weigh → proportioning mixing → shredding comb washs → and wind send and fills suede/comb and wash lapping/no glue setting → can and coat → seal quilting → test package → finished product and put in storage.
More than show and described basic principle of the present invention, principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; that describes in the foregoing description and the specification just illustrates principle of the present invention; the present invention also has various changes and modifications without departing from the spirit and scope of the present invention, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (5)
1. the preparation method of an anion terylene fiber comprises:
A. negative ion generating body is made the nanometer grade powder that has good intermiscibility with high polymer material;
B. nanometer grade powder is carried out surface treatment, handle afterproduct and mix with polymer support, obtain mixture, mixed proportion is 5-20: 1;
C. molten mixture is extruded and is made the anion master batch, again the anion master batch is carried out drying, obtains desciccate;
D. desciccate is mixed with the high polymer section, mix products and polyster fibre carry out blending, obtain anion terylene fiber.
2. the preparation method of a kind of anion terylene fiber according to claim 1 is characterized in that described negative ion generating body is a kind of in the rare earth ore, pottery of tourmaline, trace-level activity.
3. the preparation method of a kind of anion terylene fiber according to claim 1 is characterized in that described high polymer material and polymer support are polyester.
4. the preparation method of a kind of anion terylene fiber according to claim 1 is characterized in that described high polymer section is polyester slice.
5. the application by the anion terylene fiber of claim 1 preparation method preparation is characterized in that described anion terylene fiber is used to prepare the anion terylene core.