KR101778981B1 - A method of manufacturing an undergarment containing an inorganic metal oxide mineral and having a high deodorization rate - Google Patents
A method of manufacturing an undergarment containing an inorganic metal oxide mineral and having a high deodorization rate Download PDFInfo
- Publication number
- KR101778981B1 KR101778981B1 KR1020170032009A KR20170032009A KR101778981B1 KR 101778981 B1 KR101778981 B1 KR 101778981B1 KR 1020170032009 A KR1020170032009 A KR 1020170032009A KR 20170032009 A KR20170032009 A KR 20170032009A KR 101778981 B1 KR101778981 B1 KR 101778981B1
- Authority
- KR
- South Korea
- Prior art keywords
- yarn
- metal oxide
- mineral
- weight
- inorganic metal
- Prior art date
Abstract
Description
본 발명은 무기계 금속산화물 성분이 함유된 광물을 사용하여 원단을 직조하여 소취율이 높은 내의류를 제공하는 방법에 관한 것으로, 좀 더 구체적으로는 무기계 금속산화물 성분을 함유한 광물을 사용하여 PET(Polyethylene), PBT(Polybutylene Terephthalate), 나일론, 레이온, PVC(Polyvinyl Chloride), PP(Polypropylene)의 스테이플 화이버(staple fiber)나 필라멘트(filament)사를 제조함으로써 소취 기능이 우수한 내의류를 직조하는 방법에 관한 것이다.The present invention relates to a method of providing an underfill having a high deodorization rate by weaving a fabric using a mineral containing an inorganic metal oxide component, and more particularly, ), Polybutylene terephthalate (PBT), nylon, rayon, polyvinyl chloride (PVC), polypropylene (PP) staple fibers or filament yarns .
생활수준의 향상으로 보다 쾌적한 생활을 추구하는 소비자들의 욕구가 증대되고 있는 요즘 사회에서 내의류는 인체의 보온과 땀 흡수, 배출 기능 그리고 겉옷의 착용상태를 보조하는 등의 목적을 더욱 효과적으로 수행하길 원하고 있다.In today's society where the desire for consumers to pursue a more comfortable life is increasing due to the improvement of the living standard, the undergarment wants to carry out the purpose such as supporting the warming of the human body, sweat absorption, discharge function and wearing of the outer garment more effectively have.
또한, 겉옷이 얇아지고 또는 밀착되거나 비치는 옷을 입을 때 내의류도 패션과 함께 외부에 보여지는 기능성까지 함께 고려해야 하는 추세이다. In addition, when the outerwear is thinned, or when the clothes are put on tightly or closely, it is also a trend that the underwear should be considered together with fashion as well as the functionality shown on the outside.
상기와 같은 현상과 함께 섬유제품에 본래 필요한 기능에서 부가적인 기능을 부여하여 생산하는 기능성 섬유가 처음에는 합성섬유에 흡수, 흡습성을 부여하는 것과 같이 천연섬유와 유사한 제품을 만드는 것이 목적이었다. 하지만, 현재 천연섬유의 성능을 지니게 하여 합성의 독자적 성능을 추구하는 방향으로 나아가 소비자들의 건강까지 고려하여 보온성, 항균, 소취 효과, 정전기 방지, 원적외선 방출, 자외선차단 등 특수한 기능을 가진 섬유를 선호하게 되었다. In addition to the above-mentioned phenomenon, the objective of the present invention is to produce a product similar to natural fibers, such as a functional fiber that imparts additional functions in the originally required function to the fiber product and then absorbs and absorbs the synthetic fiber. However, in order to pursue the unique performance of the synthetic fiber with the performance of the natural fiber, the fiber with special function such as warmth, antibacterial, deodorizing effect, antistatic, far infrared ray emission, .
상기와 같은 기능성 섬유는 의류뿐만 아니라 현재와 미래에 자동차, 전자, 우주항공, 의료 및 군수 등의 산업에 필요한 초경량, 고강도, 고 기능성을 갖추어 그 활용도가 높고 시장성이 확대되어 가면서 특수 기능을 가진 옷은 더 이상 영화속만의 일이 아니게 되었다.The above-mentioned functional fibers are used not only for clothes but also for current and future industries such as automobile, electronics, aerospace, medical and military industries, and have high utilization and high marketability. Was no longer the only thing in the film.
한편, 건강에 대한 관심이 매우 높아지면서 광물질의 특성을 이용하여 여러 가지 방법으로 건강에 도움을 받도록 이용이 되고 있다. 그 예로 황토, 게르마늄, 맥반석, 운모, 옥, 은 등의 광물질을 추출하거나 화학적인 결함을 하여 원적외선 효과, 공기정화, 음이온 발산, 항균, 탈취 등 다양하면서도 건강에 매우 도움이 되는 효과를 얻고 있다.On the other hand, as interest in health becomes very high, it is used to help health by using various characteristics of minerals. For example, various minerals such as yellow loam, germanium, elvan, mica, jade and silver are extracted or chemically defected to obtain various effects such as far-infrared rays effect, air purification, anion dissipation, antibacterial and deodorization.
섬유, 패션 사업은 웰빙 문화에서 건강뿐만 아니라 환경까지 중요시하는 로하스(LOHAS) 문화가 주류를 이루면서 섬유소재 및 패션 분야에서 고기능 친환경 소재를 원료로 한 다양한 건강 기능성 섬유 소재들이 속속 등장하였다. 식물의 천연 추출물질들에는 많은 기능성 물질이 존재하고 있다. 이들 기능성 물질 중 특유의 약리작용을 가지는 성분들은 분리, 정제 과정 등을 거처 식품, 향장품, 제약이나 의약 분야뿐만 아니라 섬유 염색, 가공분야에서도 합성화학제품의 부작용 등을 최소화 할 수 있다는 점에서 그 이용이 크게 증가하고 있다. In the textile and fashion business, LOHAS culture, which is important not only for health but also for environment, has become a mainstream in the wellbeing culture, and a variety of health functional fiber materials, which are made of high-performance and eco- There are many functional substances in natural extracts of plants. Among these functional substances, the specific pharmacological action components are separated and refined, and the use of such substances in the fields of foods, cosmetics, pharmaceuticals and medicines as well as in the textile dyeing and processing fields can be minimized .
상기와 같은 천연물을 사용하여 기능성을 갖는 섬유로 등록특허 제10-1684764호가 있지만 그 효과는 높지 않다는 단점이 있으며, 등록특허 제10-0450530호나 제10-481358호와 같이 종래의 방법은 기능성이 부족한 원사의 제작방법이거나 광물이 원사에 착상하는 비율이 매우 저조하고 단가가 높다는 단점이 있다. 그러므로 원료 생산이 용이하고 경제적이며, 부가가치를 증진시켜 경쟁력을 확보하고 기술을 응용하여 제품화를 해야 하는 문제점이 있다.As a fiber having functional properties using the above-mentioned natural materials, there is a disadvantage in that the effect is not high. However, as in the case of Japanese Patent No. 10-0450530 or No. 10-481358, There is a drawback that the production method of the yarn or the ratio of the mineral to the yarn is very low and the unit price is high. Therefore, there is a problem that the raw material production is easy and economical, the value added is increased, the competitiveness is secured, and the technology is applied and commercialized.
상기와 같은 문제점을 해결하기 위한 본 발명의 목적은, 기존의 내의류의 기능성을 부여하는 방법과는 다른 천연물을 함유하여 직조한 원단을 사용한 내의류를 제공하는데 있다.It is an object of the present invention to solve the above-mentioned problems, and an object of the present invention is to provide an undergarment using a woven fabric containing a natural material different from a conventional method of imparting functionality of an undergarment.
상기와 같은 문제점을 해결하기 위한 본 발명의 다른 목적은, 기존에 광물질과 탈취제를 첨가하여 탈취 능력을 가진 내의류 보다 더 큰 효과와 지속성과 내구성을 가지고, 착용시 영구적으로 높은 소취 능력을 가진 내의류를 제공하는데 있다.It is another object of the present invention to overcome the above-mentioned problems, and it is an object of the present invention to provide an undergarment having a deodorizing ability, .
상기와 같은 문제점을 해결하기 위한 본 발명의 또 다른 목적은, 기존에 섬유에서는 가공시 항균제를 첨가하여 후가공에 의한 항균능력을 가진 내의류 보다 지속적이면서도 세탁 및 착용에도 내구성이 저하되지 않은 반 영구적인 기능을 갖는 항균내의를 제공하는데 있다.Another object of the present invention to solve the above problems is to provide an antimicrobial agent which is more persistent than an antimicrobial agent resistant to post-processing by adding an antimicrobial agent during processing, and has a semi-permanent function And the like.
상기와 같은 문제점을 해결하기 위한 본 발명의 또 다른 목적은, 본 발명과 같은 무기계 금속산화물을 함유한 암석류를 이용한 가공원단보다 가공방법이 용이하여 제조단가가 줄어들도록 제공하는데 있다.It is another object of the present invention to solve the above problems and provide a method of manufacturing the same, wherein the manufacturing cost is lower than that of the processed fabric using the pomegranate containing the inorganic metal oxide as in the present invention.
상기한 바와 같은 본 발명의 목적은 광물질 분말과 식물 추출물을 이용하여 제조된 항균 및 소취 능력이 증진된 내의류 직조에 의해 달성될 수 있다.As described above, the object of the present invention can be attained by an anti-bacterial and anti-deodorant woven fabric obtained by using mineral powder and plant extract.
상기한 바와 같은 본 발명의 목적은, 추가의 일면에 있어서,According to a further aspect of the present invention,
맥반석, 현무암, 운석류 및 제올라이트를 포함하는 광물질 중에서 2가지 내지 4가지의 광물을 선발하여 준비하는 단계;Selecting two or four kinds of minerals among minerals including quartz, quartz, basalt, rhyolite and zeolite;
상기 선발된 광물들을 개별적으로 1차 분쇄하는 단계;Separately first crushing the selected minerals;
상기 준비된 광물을 동량으로 혼합하여 2차 분쇄하여 평균 입도가 3㎛ 이하의 금속산화물의 분말을 얻는 단계;Mixing and mixing the prepared minerals in an equal amount to obtain a metal oxide powder having an average particle size of 3 탆 or less;
상기 2차 분쇄된 광물 분말 100중량부에 징크옥사이드(ZnO) 0.2 ~ 0.5중량부를 첨가하는 단계;Adding 0.2 to 0.5 parts by weight of zinc oxide (ZnO) to 100 parts by weight of the second pulverized mineral powder;
상기 징크옥사이드가 첨가된 2차 분쇄광물 분말 100중량부에 식물추출물 4 내지 7 중량부를 첨가하여 고르게 혼합하는 단계; Adding 4 to 7 parts by weight of the plant extract to 100 parts by weight of the powder of the secondary crushed mineral to which zinc oxide is added,
PET 수지 97 ~ 99.9 중량부에 상기 식물추출물이 혼합된 광물 분말 0.3 ~ 3 중량부를 고르게 혼합하여 압출기에 투입한 뒤 방사하는 단계;0.3 to 3 parts by weight of a mineral powder mixed with the plant extract is uniformly mixed in 97 to 99.9 parts by weight of a PET resin, and the mixture is injected into an extruder and then irradiated;
상기 방사된 필라멘트사는 면 60 ~ 85 중량%에 광물이 첨가된 폴리에스터 15 ~ 40 중량%로 혼방사로 연사(twisting)하는 단계; 및Twisting the blended filament yarn into a blended yarn with 60 to 85% by weight of the cotton and 15 to 40% by weight of the polyester to which the mineral is added; And
상기 연사단계를 거친 후 권축가공(crimping), 컷팅(cutting), 코밍(combing)을 거쳐 면과 함께 혼방사로 제조하는 단계;A step of crimping, cutting, and combing the yarn after the twisting step to produce a blended yarn together with the yarn;
를 포함하는 제조방법에 의해 달성될 수 있다.≪ / RTI >
기타 실시예들의 구체적인 사항들은 상세한 설명에 포함되어 있다.The details of other embodiments are included in the detailed description.
상기와 같은 본 발명에 따른 항균과 소취 능력이 증가된 혼방사로 직조된 내의류를 제조할 경우 무기광물이 분자구조를 개질하여 면과 같은 물성을 부여하여 내구성과 착용감이 좋으며, 천연물만으로 가공된 내의류를 제공 할 수 있다In the case of producing a woven underwear made of a blend yarn having increased antibacterial and deodorizing ability according to the present invention, the inorganic mineral modifies the molecular structure and imparts physical properties such as cotton to provide a durable and comfortable feeling, Can provide
상기와 같은 본 발명에 따른 항균과 소취 능력이 증가된 내의류를 착용할 경우, 탈취제를 첨가하지 않고도 내구성이 높고, 냄새를 탈취하여 일정 시간 이후 다시 냄새가 발생하는 탈취 효과가 아닌 지속적인 소취 능력에 의해 반 영구적인 고기능성 내의류를 제공하는데 있다.When the anti-microbial and anti-deodorizing ability according to the present invention as described above is worn, the durability is high without the addition of the deodorant, and the deodorizing effect is generated by the continuous deodorizing effect Semi-permanent and highly functional undercladding.
또한, 기존의 섬유에서는 항균제를 첨가하여 항균능력을 가지도록 했던 가공방법보다 지속적이면서도 세탁 및 착용에도 내구성이 높은 항균력을 가진 내의류의 제조가 가능하다는 장점이 있다.In addition, the conventional fiber has an advantage that it is possible to manufacture an undergarment having a more durable antibacterial activity, which is more durable than washing and wearing, as compared with a processing method in which an antimicrobial agent is added to an antibacterial agent.
또한, 기존의 무기계 금속산화물을 함유한 암석류를 이용한 가공원단보다 가공방법이 용이하여 제조단가가 줄어들어 기능성 내의를 저렴하게 제공하는데 있다.In addition, it is easier to process than a processed fabric using a pomegranate containing an inorganic metal oxide, so that the manufacturing cost is reduced, thereby providing a functional interior at low cost.
도 1은 본 발명의 일 실시에에 따른 항균 소취가 가능한 내의류를 제조하는 과정을 나타낸 순서도.
도 2는 본 발명의 일 실시예에 따른 광물의 2차 분쇄 후 입도의 크기를 나타낸 그래프.
도 3은 본 발명의 일 실시예에 따른 광물의 2차 분쇄 후 고배율의 현미경을 통해 촬영된 분쇄물의 도면.
도 4는 본 발명의 일 실시예에 따라 제조된 원사의 항균력 검사결과 도면.
도 5는 본 발명의 일 실시예에 따라 제조된 원사에 함유된 무기물의 양과 크기를 확인할 수 있는 고배율의 현미경에 촬영된 원사의 도면.
도 6은 본 발명의 일 실시예에 따라 제조과정 중 원사의 용융추출에 의한 방적이 실시되는 모식도.
도7은 본 발명의 일 실시예에 따라 제조된 러닝셔츠의 예시도.
도 8은 본 발명의 일 실시예에 따라 제조된 여성팬티의 예시도.
도9는 본 발명의 일 실시예에 따라 제조된 남성 팬티의 예시도.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flow chart showing a process for producing an anti-microbial deodorization-capable underwater according to an embodiment of the present invention; FIG.
FIG. 2 is a graph showing the size of granules after secondary pulverization of a mineral according to an embodiment of the present invention. FIG.
3 is a view of a milled material taken through a high magnification microscope after secondary grinding of the mineral according to one embodiment of the present invention.
FIG. 4 is a result of checking the antibacterial activity of a yarn produced according to an embodiment of the present invention. FIG.
FIG. 5 is a drawing of a yarn photographed in a high magnification microscope capable of confirming the amount and size of the inorganic matter contained in the yarn produced according to an embodiment of the present invention. FIG.
6 is a schematic view illustrating spinning by spinning of a yarn during a manufacturing process according to an embodiment of the present invention.
Figure 7 is an illustration of an example of a running shirt made in accordance with one embodiment of the present invention.
Figure 8 is an illustration of a female panties made in accordance with an embodiment of the present invention.
Figure 9 is an illustration of a male panty made in accordance with an embodiment of the present invention.
본 발명의 실시예들을 설명함에 있어서 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다. 그리고 후술되는 용어들은 본 발명의 실시예에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 관례 등에 따라 달라질 수 있다. 그러므로, 그 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear. The following terms are defined in consideration of the functions in the embodiments of the present invention, which may vary depending on the intention of the user, the intention or the custom of the operator. Therefore, the definition should be based on the contents throughout this specification.
이하, 본 발명의 바람직한 실시예를 첨부된 도면을 참고하여 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
무기계 금속산화물이 함유된 암석을 첨가하여 제작을 하는 여러 가지 용도의 직물들은 대부분 많은 기능성을 가지고 있으나, 그 제조방법이 어렵고 제조비용이 고가이기 때문에 특수 기능직 직물로만 사용이 되어왔다. 본 발명과 같이 제조된 직물은 그 기능성을 증가시킬 수 있으며, 친환경적이며, 제조단가가 절감되도록 제조하는 방법에 관한 것이다. Fabrics for various purposes, which are made by adding rocks containing inorganic metal oxides, have many functions, but they have been used only as special functional fabrics since they are difficult to manufacture and expensive to manufacture. The fabric produced according to the present invention is capable of increasing its functionality, is environmentally friendly, and is manufactured to reduce manufacturing costs.
지표면에 존재하는 지각변동으로 형성된 암석중에서 맥반석, 현무암, 운석류, 제올라이트 계열의 광물질은 무기계 금속산화물 성분을 함유하고 있는 광물로써 기능성을 가지고 있으며 다공질의 3차원 망목구조를 가지고 있다. Minerals such as elvan, basalt, zeolite, and zeolite are minerals containing inorganic metal oxide components and have a porous three-dimensional network structure.
상기와 같은 구조에 의하여 다양한 환경에서 상기 원석 그대로를 흡착기능에 의한 공기 정화 및 물을 정수하고 탈취와 같이 다양한 용도로 활용하고 있다. 또한, 기술의 발달로 상기 암석을 섬유제조시 첨가하여 다양한 기능성을 발휘하도록 하고 있다. 하지만, 상기 기능성의 효과를 보기 위해서 암석을 첨가하는 방법은 가공비용이 높기 때문에 특수 기능을 가진 의류에 사용하는 경우가 대부분이다.By the above-described structure, the raw stone is utilized for various purposes such as purifying air by adsorption function and purifying water and deodorizing in various environments. In addition, with the development of technology, the above-mentioned rocks are added at the time of fiber production to exhibit various functions. However, the method of adding the rock to the effect of the above-mentioned function is mostly used for clothes having a special function because of high processing cost.
특히, 내의류는 신체에 가장 밀접하게 착용하는 의류이다. 사람들은 각종 분비물이 항문뿐만 아니라 땀샘에서도 분비되어 어디서나 악취를 내고 미생물에 의하여 오염 될 수 있는 문제점이있다.In particular, underwear is clothing that is worn most closely to the body. The secretion of various secretions from the anus as well as from the sweat glands is causing people to smell them everywhere and contaminate them by microorganisms.
상기와 같은 문제점을 해결하기 위한 각종 가공방법들은 대부분 섬유제조시 합성물질을 코팅하여 유지하여 제조비용이 저렴하고 강력한 효과를 가질 수 있다는 장점이 있으나, 상기와 같은 가공방법은 내구성이 결여되어 잦은 세탁을 하는 내의류는 금방 그 기능성을 상실하게 되고, 화학물질을 꺼려하는 소비성향에 의해 본 발명과 같이 강력한 기능성이 발휘되는 암석류를 첨가한 천연 원단의 개발은 경제적인 가치가 매우 높다. 다만, 기존의 방법으로는 제조비용이 높기 때문에 본 발명에서와 같이 제조비용을 절감하는 방법으로 제조가 가능하다.Various processing methods for solving the above problems are advantageous in that a manufacturing cost is low and a strong effect can be obtained by coating and maintaining a synthetic material in manufacturing most of the fibers. However, the above-mentioned processing method lacks durability, And the development of natural fabrics to which cancer pomegranate added with a strong function as shown in the present invention is added due to the consumption tendency to avoid chemical substances is very economically valuable. However, since the conventional method has a high manufacturing cost, it can be manufactured by a method of reducing manufacturing cost as in the present invention.
본 발명에서 사용되는 암석의 하나인 맥반석은 지질학적 분류로는 화강암류에 속하며 주성분은 무수규산과 산화 알루미늄이고, 산화제2철이 소량 함유되어 있다. 1㎤당 3~15만 개의 구멍으로 이루어져 있어 흡착성이 강하고, 약 2만 5000종의 무기염류를 함유하고 있다. 중금속과 이온을 교환하는 작용을 하기 때문에 유해금속 제거제로도 사용하며 이 암석에 열을 가하면 원적외선을 방출하는 것으로 알려져 있다. The elvan, one of the rocks used in the present invention, belongs to the granite type in geological classification, and its main components are anhydrous silicic acid and aluminum oxide, and contains a small amount of iron oxide. It is composed of 3 to 150 thousand holes per cm 3, and has a strong adsorption property and contains about 25,000 inorganic salts. It is also used as a harmful metal removing agent because it acts to exchange ions with heavy metals. It is known to release far-infrared rays when heat is applied to this rock.
암색 내지 흑색 미세립의 염기성 화성암의 하나인 현무암은 화산에서 분출되는 용암 중에서 가장 많은 양의 암석이다. 화학조성은 CaO(산화칼슘), MgO(산화마그네슘), FeO(산화제일철) + Fe2O3(산화제이철)의 함량이 많고 SiO2(이산화규소) 함량은 52%이하이다. Basalt, one of the basic igneous rocks of dark to black fine grains, is the most abundant rock in the volcanic lava. The chemical composition is CaO (calcium oxide), MgO (magnesium oxide), FeO (ferrous oxide) + Fe 2 O 3 (ferric oxide) and SiO 2 (silicon dioxide) content is 52% or less.
제올라이트는 비석(沸石)이라고도 하며, 굳기는 6을 넘지 않고 비중이 약 2.2이다. 결정구조적으로는 각 원자의 결합이 느슨하여, 그 사이를 채우고 있는 수분을 고열로 방출시켜도 골격은 그대로 있으므로 다른 미립물질을 흡착할 수가 있다. 이 성질을 이용해서 흡착제로 사용하며, 크기가 다른 미립물질을 분리시키는 분자체(分子篩)로 사용한다. Zeolite is also called zeolite, and its hardness is not more than 6 and its specific gravity is about 2.2. In crystal structure, the bonding of each atom is loosened, and even if the water filling the space is released as a high heat, the skeleton remains, so that other fine particles can be adsorbed. This property is used as an adsorbent, and it is used as a molecular sieve (molecular sieve) for separating fine particles of different sizes.
상기와 같이 맥반석, 현무암, 운석류, 제올라이트 계열의 광물질 암석은 금속 산화물을 많이 함유하고 있어 섬유와 혼합시 인체에 유용한 효과를 얻을 수 있다. 상기와 같은 광물을 섬유에 첨가하면 원래 보유하고 있는 원적외선의 방사성능과 다공질에 의한 흡착력 및 항균성을 나타내게 된다. 하지만, 상기와 같은 무기물을 혼합하였을 때, 광물의 균일성이 미흡하고, 방사간 재응집 및 강력한 수분 흡수 특징으로 용융방사시 방사조업성 확보가 어렵고 점도저하에 따른 섬유의 물성저하와 무기물 미립자에 의한 압력상승, 기타 색상불량 및 분산성 조절 등이 어려워 가공비용이 매우 높다는 단점이 있다. As described above, mineral rocks such as elvan rock, basalt rock, zeolite, and zeolite have a large amount of metal oxides, so that they can obtain useful effects on the human body when mixed with fibers. When the above-mentioned minerals are added to the fibers, they exhibit the radiation performance of far-infrared rays originally possessed and adsorption and antibacterial properties by the porous. However, when the above inorganic materials are mixed, the uniformity of the minerals is insufficient, and it is difficult to secure the spinning ability upon melt spinning due to the re-aggregation of spinning and strong water absorption. Also, The pressure rise caused by the pressure increase, the other color defects, and the dispersion property are difficult to control, and thus the processing cost is very high.
악취를 제거하는 기능성 섬유의 대부분은 탈취 기능이 제공되어 있다. 상기와 같은 탈취 기능은 이미 공기중에 확산한 냄새 물질이 활성탄이나 숯, 제올라이트 등의 다공성 물질의 세공에 물리적으로 흡착하는 것을 이용하여 냄새를 가두는 방법으로 모든 냄새에 효과가 있다는 장점이 있으나 일단 흡착된 뒤 일정 시간이 지난 후 냄새들은 다시 방출(탈착)되어 역으로 악취 원인이 될 수 있다는 단점 있다.Most of the odor-removing functional fibers are deodorized. Such a deodorizing function is advantageous in that odor substances already diffused in the air are physically adsorbed on the pores of a porous material such as activated carbon, char, zeolite, etc., After a certain period of time, the odors are released (desorbed) and the odor may be caused.
또한, 방취에 의하여 악취를 제거하는 방법이 있다. 상기 방취는 항균성 소재를 이용하여 미생물의 증가를 억제하는 것으로 미생물의 대사작용에 의해서 수반되는 냄새물질의 발생을 방지하는 것이다. 상기 방취는 이미 발생하여 확산된 냄새는 제거할 수 없다는 단점이 있다. There is also a method of removing odor by deodorization. The deodorization suppresses an increase of microorganisms by using an antimicrobial material and prevents the generation of odorous substances accompanied by the metabolism of microorganisms. The above-mentioned deodorization has already occurred and the diffused odor can not be removed.
본 발명에서 나타난 섬유의 기능인 소취는 이미 공기중에 확산한 냄새물질을 산화반응이나 중화 반응 등의 화학반응을 이용하여 냄새물질을 변화시켜 없애는 방법으로 화학변화를 동반하기 때문에 2차적인 악취원인이 되지 않는다. 하지만 특정종류의 냄새 물질만 반응한다는 단점이 있다. The deodorization function of the fiber of the present invention is a method of removing odor substances by using chemical reaction such as oxidation reaction or neutralization reaction to remove odor substances already diffused in the air, Do not. However, it has a drawback that it only reacts with certain kinds of odorous substances.
상기와 같은 소취 기능을 가진 섬유는 생활속의 4대 악취의 하나인 암모니아(NH3) 냄새를 소취하는 것이 가능하다. 상기와 같은 암모니아 냄새는 땀 이나 소변과 같은 몸에서 발생하는 자극적인 냄새로써 본 발명과 같이 광물을 첨가하여 제작된 섬유에서는 소취가 가능하며, 내구성을 높여 원단의 경제성이 높고 가공비율이 절감되도록 제작이 가능하다.The fiber having the deodorizing function as described above can deodorize the odor of ammonia (NH 3 ) which is one of the four odors in daily life. The ammonia odor is an irritating odor generated in the body such as sweat and urine. It is possible to deodorize the fabric produced by adding minerals as in the present invention, to increase the durability and to make the fabric economical and reduce the processing rate This is possible.
본 발명과 같이 항균·소취 섬유를 제조하기 위해서는 맥반석, 현무암, 운석류, 제올라이트 계열의 광물질 1가지 광물만을 사용하지 않고 맥반석, 현무암, 운석류, 제올라이트 계열의 광물 중 2가지 이상의 광물을 선발하여 동량으로 혼합한다. In order to produce antimicrobial and deodorizing fibers as in the present invention, at least two minerals, such as elvan, basalt, zeolite and zeolite, are selected without using only one mineral such as quartz, basalt, zeolite or zeolite, .
상기의 광물은 다공질의 3차원 망목구조를 가지고 있어 흡착이 가능하여 냄새나 수분을 제거하는 기능으로 이미 사용 되어 왔다. 상기와 같은 흡착기능은 악취를 끌어 당기는 효과가 있어 냄세 제거에 매우 효율적이다. 하지만, 상기와 같은 구조의 광물을 섬유에 이용하였을 경우 섬유에 고른 배합이 어렵고, 분쇄물이 3 ㎛ 이하의 크기로 분쇄가 안될 경우, 섬유의 지속적인 사용 및 세탁에 의하여 광물의 탈락현상이 쉽게 발생하여 상기 광물에 의한 기능성 면에서 광물의 균일성이 미흡하고, 방사간 재응집 및 강력한 수분 흡수 특징으로 용융방사시 방사조업성 확보가 어려우며 점도저하에 따른 섬유의 물성저하 및 무기물 미립자에 의한 압력상승, 기타 색상불량 및 분산성 조절 등이 어려워 제조과정에 비용이 매우 높다. The above-mentioned minerals have a porous three-dimensional network structure and can be adsorbed and have been used for removing odor and moisture. The adsorption function as described above has an effect of attracting odor and is very effective in removing the smell. However, when the mineral of the above-mentioned structure is used in the fiber, it is difficult to uniformly mix the fiber. When the crushed material is not crushed to a size of 3 μm or less, the detachment of the mineral easily occurs due to the continuous use and washing of the fiber It is difficult to secure the spinnability in the melt spinning due to the re-aggregation of spinning and strong water absorption, and it is difficult to secure the spinnability by the spinnability. Also, the lowering of the physical properties of the fiber and the pressure rise due to the inorganic fine particles , Other color defects and dispersibility are difficult to control, and the manufacturing process is very expensive.
상기와 같은 단점을 극복하기 위해서 본 발명에서는 2종류 이상의 광물을 혼합하여 분쇄과정을 수행하여 섬유를 제조하도록 하였다. 상기와 같이 2종류 이상의 광물을 사용하였을 경우 광물이 섬유에 고르게 분포하며 촉감이 부드럽게 유지가 가능한 크기의 분쇄작업이 더욱 용이해지는 장점이 있다. 즉, 상기 광물들을 섬유에 혼합하기 위해서 분쇄작업을 수행할 때 각각의 경도가 달라서 섬유에 투입이 가능한 크기인 3㎛ 이하로 분쇄가 더 쉽고 효율이 증대 되어 시간과 비용이 절감 되어 지금까지 생산비용의 증가로 공급 단가가 높으므로 시장점유율이 낮은 단점을 보완할 수 있게 된다. In order to overcome such disadvantages, in the present invention, fibers are prepared by mixing two or more kinds of minerals and pulverizing them. As described above, when two or more kinds of minerals are used, the minerals are uniformly distributed on the fibers, and the crushing operation of the size capable of keeping the soft feel is further facilitated. That is, when grinding is performed to mix the minerals into the fibers, the hardness is different and the grinding is easier and the efficiency is increased to 3 μm or less, which is a size that can be put into the fibers, , Which is expected to compensate for the low market share due to the high supply price.
선택된 두 종류의 광물은 각각 50㎛크기의 파우더가 되도록 크랏샤(Crusher:분쇄기)로 1차 분쇄하는 작업을 수행하게 된다. 상기와 같이 1차로 분쇄하는 과정에서는 광물이 섞이지 않도록 하여 분쇄를 실시하면 광물은 1차에서 50㎛크기까지의 분쇄가 가능하게 된다. The selected two types of minerals will be subjected to a primary crushing operation with a crusher to obtain a powder having a size of 50 μm each. In the primary pulverization process as described above, the minerals can be pulverized to a size of 50 탆 from the primary by performing the pulverization so that the minerals are not mixed.
상기와 같이 분쇄된 광물은 선택된 기능성에 따라 2가지 이상의 광물을 1:1로 동량을 배합하여 평균입도 1㎛크기의 파우더가 되도록 2차 분쇄를 실시하게 된다. 상기와 같이 선택된 광물은 3가지일 경우 1:1:1로 항상 무게 비율로 같은 양을 배합하도록 한다. 상기와 같이 2가지 이상의 광물을 사용하였을 경우 광물들의 경도가 서로 상이하여 분쇄가 더 빠르고 수득률이 높다. 상기와 같은 과정에 의해서 도2와 도 3에서와 같이 본 발명에서 사용되는 광물은 평균입도가 1㎛까지 재현성이 나타나도록 분쇄하는 것이 가능하였으며, 대부분 3㎛ 이하로 97%이상 분쇄되는 것이 가능하게 되었다. According to the selected functionality, the above-mentioned pulverized minerals are mixed with two or more minerals in a ratio of 1: 1, and the second milling is carried out so as to obtain a powder having an average particle size of 1 탆. In the case of three kinds of minerals selected as above, 1: 1: 1, always mix the same amount by weight ratio. When two or more minerals are used as described above, the hardness of the minerals is different from each other, so that the milling is faster and the yield is higher. As shown in FIGS. 2 and 3, the mineral used in the present invention can be pulverized to have reproducibility of an average particle size of up to 1 μm, and can be pulverized by 97% or less at most 3 μm .
상기와 같은 분쇄 결과는 2가지 이상의 광물이 합하여 질 때 항상 재현성이 있도록 분쇄가 되어, 기존에 여러 번 실시하여 3㎛ 이하로 분쇄하여 시간과 비용이 증가되거나, 3㎛ 이하로 분쇄되는 비율이 적어 섬유에 점착률이 낮은 것과는 다르게, 본 발명에 의한 분쇄방법은 생산비용과 시간이 절감되는 효과를 얻을 수 있다. The above-mentioned pulverization result is pulverized so as to be reproducible at all times when two or more minerals are combined, and it has been conventionally carried out several times to pulverize to 3 탆 or less to increase time and cost, Unlike the case where the adhesive ratio to fibers is low, the grinding method according to the present invention can achieve the effect of reducing production cost and time.
2차 분쇄된 광물 파우더 100중량부에 0.2 ~ 0.5중량부에 해당하는 징크옥사이드(ZnO)를 첨가하여 고르게 혼합한다. 0.2 to 0.5 part by weight of zinc oxide (ZnO) is added to 100 parts by weight of the secondary pulverized mineral powder and mixed evenly.
본 발명과 같이 투입되는 ZnO는 무기계 금속산화물 성분을 가지고 있는 광물에 미미하게 포함되어 있는 물질로 항균효과를 발휘하는 기능을 한다. 하지만, 항균효과가 충분하지 않기 때문에 ZnO를 더 첨가하면, 항균효과가 증대되는 현상을 확인할 수 있다. 상기와 같은 항균효과는 도4와 같이 나타났다. ZnO added as in the present invention is a substance slightly contained in minerals having an inorganic metal oxide component and exhibits an antimicrobial effect. However, since the antimicrobial effect is not sufficient, it is confirmed that the addition of ZnO further increases the antimicrobial effect. The antimicrobial effect was as shown in Fig.
ZnO(징크옥사이드; 산화아연)는 분말화 형태로 베이비 파우더에 들어가는 주요성분으로 사용되어온 안전한 성분이며, 높은 자외선 차단력을 가지고 있고, 열과 충격에 내성이 있으며, 인체에도 필수 영양성분이기 때문에 영양제나 가축 사료에도 사용되는 특징이 있다. 상기와 같은 특징을 가진 산화 아연을 첨가하여 제작된 원사는 소취 능력과 함께 항균능력이 증가될 수 있는 기능성 원사의 제작이 가능하게 되었다.ZnO (zinc oxide) is a safe ingredient that has been used as a main ingredient in baby powder in powder form, has a high ultraviolet blocking power, is resistant to heat and shock, and is an essential nutrient in the human body. It is also used for feed. The yarn produced by adding zinc oxide having the above characteristics has become capable of producing a functional yarn capable of increasing antimicrobial activity along with deodorizing ability.
상기 2차 분쇄가 된 광물파우더의 조성은 표1과 같이 확인되었다.The composition of the mineral pulverized secondary powder was confirmed as shown in Table 1.
상기와 같이 2차 분쇄가 된 광물파우더의 평균 입도가 1㎛가 되는 분쇄물에 ZnO를 투입하여 고르게 혼합하여 방사를 실시하기 위해서 스크류 익스트루더(압출기)(30)에 그대로 투입할 경우 방사된 원사에 고르게 첨가되지 않는 문제 점이 발생하게 된다. 고르게 첨가되지 않은 원사는 기능과 촉감 및 내구성에 저하되게 된다. When ZnO is added to the pulverized material having an average particle size of 1 탆 of the second-order pulverized mineral powder, and the powder is mixed into the pulverized material to be uniformly mixed and injected into the screw extruder (30) Problems that are not evenly added to the yarn are caused. A yarn which is not evenly added is deteriorated in function, texture and durability.
상기와 같은 문제점 때문에 대부분의 광물을 사용한 원사는 광물파우더를 마스터배치 칩으로 제조하여 합성수지와 함께 익스트루더에 혼합하여 방사를 실시한다. 하지만 상기와 같은 방법은 제조비용이 증가하게 되는 문제가 발생하여 본 발명에서는 마스터 배치 칩을 사용하지 않고 익스트루더에 광물 파우더와 합성수지, 식물추출물을 함께 첨가하여 방사하였다. In order to solve the above problems, the raw material using most of the minerals is produced by mixing the mineral powder with the master batch chip, and then mixing with the synthetic resin to mix the mixture with the extruder. However, in the above method, there is a problem that the manufacturing cost is increased. In the present invention, the mineral powder, the synthetic resin and the plant extract are added to the extruder together without using the master batch chip.
상기와 같은 방사물을 얻기 위해서 내의류의 용도에 따라 전체 방사물의 100중량 부에 대하여 0.3 ~ 1중량부에 해당하는 광물파우더를 첨가하게 된다. In order to obtain the above-mentioned radiation, the mineral powder corresponding to 0.3 to 1 part by weight with respect to 100 parts by weight of the total radiation is added depending on the use of the undergarment.
상기 첨가되는 광물파우더의 분량은 직조되어 사용되는 용도에 따라서 그 첨가량이 다양하게 된다. 광물파우더는 1중량부만 포함되어도 영구적인 소취 능력이 증가하지만 제작비용을 감소시키기 위해서 내의류중에서도 겨드랑이 쪽이나 팬티의 덧대어 있는 부분에는 1중량부가 포함된 방사물을 첨가하여 강력한 소취효과를 나타내고, 강한 악취가 나지 않는 그 외의 부분에는 광물파우더의 분량을 감소시켜 직조함으로써 제조비용을 감소하면서도 강한 기능성을 가진 내의류의 제조가 가능하다. 또한, 광물파우더의 특징 중 하나인 흡착능력은 접촉한 부분과 함께 더 광범위 하게 소취가 가능하여 더욱 효과적이면서도 제조단가가 낮은 내의류의 제조가 가능하게 된다.The amount of the mineral powder to be added may vary depending on the application in which the mineral powder is used. In order to reduce the manufacturing cost, the mineral powder has permanent deodorizing ability even though it contains only 1 part by weight. In order to reduce the manufacturing cost, however, a strong deodorizing effect is exhibited by adding a radiation containing 1 part by weight to the underarm portion of the underarms or panties, In the other parts where odor is not generated, the amount of mineral powder is reduced to weave, thereby making it possible to manufacture the undergarment having a high functionality while reducing the manufacturing cost. In addition, the adsorption ability, which is one of the characteristics of the mineral powder, can be deodorized more extensively together with the contacted portion, thereby making it possible to manufacture the undergarment which is more effective and has a low manufacturing cost.
상기와 같이 광물파우더를 마스터배치칩으로 생성하여 원사를 제조하게 되면 고르게 원사에 투입하는 것은 가능하지만 제작비용이 증가하는 문제점이 발생한다.As described above, when the mineral powder is produced as a master batch chip and the yarn is produced, it is possible to uniformly input the same into the yarn, but the manufacturing cost increases.
그러므로, 본 발명에서는 마스터 배치 칩이 아닌 ZnO가 혼합된 광물파우더를 100중량부로 할 때 4~7 중량부에 해당하는 식물성 추출물을 첨가하여 1차 혼합을 실시하였다. 상기 식물성 추출물은 소취성분이 있는 식물들로 동백나무, 소나무, 감귤, 장미, 노송나무 등 35종 이상의 식물류에서 잎, 열매, 줄기 뿌리 등을 이용하여 추출할 수 있으며, 그 중에서도 소취율이 높은 동백나무의 잎, 줄기, 뿌리, 열매 등을 추출 한 뒤 수득한 추출물로 다량의 소취성분이 함유되어 있는 식물추출물이다. 상기와 같은 식물성 추출물은 소취율과 항균력이 있으며 상기와 같이 식물추출물에 광물파우더를 고르게 혼합한 뒤 원사를 제조할 경우 광물파우더가 익스트루더에 부착된 주입장치에 의해 고르게 원사에 투입 된다는 장점이 있다. Therefore, in the present invention, when 100 parts by weight of the mineral powder mixed with ZnO, not the master batch chip, is added with 4 to 7 parts by weight of the plant extract, primary mixing is carried out. The plant extracts can be extracted from leaves of more than 35 kinds of plants such as camellia, pine, citrus, rose, cypress and the like using leaves, fruits, stem roots, etc. Among them, It is a plant extract obtained by extracting leaves, stems, roots, and fruits of trees, and containing a large amount of deodorant components. The vegetable extract has a deodorization rate and an antibacterial activity. When the mineral powder is uniformly mixed in the plant extract as described above, the mineral powder is uniformly injected into the yarn by the injection device attached to the extruder have.
상기와 같이 고르게 투입된 원사의 모습은 도5와 같이 현미경으로 확인하였다. The shape of the yarn thus injected evenly was confirmed by a microscope as shown in FIG.
본 발명에 바람직한 실시예로 사용이 가능한 식물추출물의 성분 중 하나인 동백나무과는 식물체와 꽃은 관상용으로 많이 사용하며, 종자에서는 기름을짜서 사용한다. 잿물을 내어 매염제로 쓰이기도 하지만 동백나무과 추출물은 항균효과와 소취능력은 여러 논문에서 증명되어 있으며, 특히 항균효과는 인체에 무해한 천연 항균 소재로써 의약품이나 화장품 원료로 많이 활용되고 있다. 상기 동백나무과의 조직을 분쇄하여 40% 에탄올에 72시간 침전하였다가 에탄올 층을 분리한 후 다시 40% EtOAc(Ethyl acetate;에틸 아세테이트)에 2차 24시간 침전하였다가 추출물만을 분리한 뒤 용매층을 제거하여 사용하였다. 상기와 같이 추출된 식물추출물은 오일층이 대량으로 함유되어 있으며 항균력과 소취능을 포함하고 있다.One of the components of the plant extract that can be used as a preferred embodiment of the present invention is Camelliaceae, which is widely used for ornamental plants and flowers, and oil is used for seeds. Although it is used as a mordant for making lye, the antimicrobial effect and deodorizing ability of Camellia sinensis extract have been proved in various papers. In particular, the antibacterial effect is a natural antibacterial material harmless to human body and is widely used as a medicine and cosmetic raw material. The tissues of the camellia were crushed and precipitated in 40% ethanol for 72 hours. The ethanol layer was separated and further precipitated in 40% EtOAc (ethyl acetate) for 24 hours. After extracting only the extract, . The plant extract thus extracted contains a large amount of oil layer and contains antibacterial activity and deodorizing ability.
ZnO가 함유된 광물파우더를 식물추출물과 혼합하여 원사를 제작할 경우, 마스터 배치 칩을 제작하는 단계를 생략할 수 있기 때문에 원사의 제조 비용이 절감되는 효과를 얻을 수 있다. 광물이 첨가되어 제작되는 원사는 그 기능이 매우 우수함에도 불구하고 동일한 지역에서 채취되는 광물도 성분이 조금씩 상이하여 순수한 성분을 얻기위한 선별작없이 난이성과 생산비용이 높아 활용이 적으며, 이와 같은 이유로 내구성이 떨어지는 탈취제나 향균제와 같은 유기화학물질을 원사에 코팅하여 제조하는 기능성 원사가 시장의 점유율이 높은 실정에 있다. 하지만, 본 발명과 같이 제작비용에 단가를 절감함으로써 경쟁령이 높은 원사의 생산이 가능하게 된다.When the mineral powder containing ZnO is mixed with the plant extract to produce the yarn, the step of producing the master batch chip can be omitted, and the manufacturing cost of the yarn can be reduced. Despite its excellent function, the raw materials produced by adding minerals are slightly different from the minerals extracted from the same region, so there is little utilization due to the difficulty and production cost without selecting to obtain pure components. For this reason Functional yarn, which is produced by coating an organic chemical substance such as a deodorant or an antibacterial agent having low durability, on a yarn, has a high market share. However, as in the present invention, production costs can be reduced, thereby enabling the production of yarn of high competition.
상기와 같이 ZnO가 첨가되고 식물성추출물에 혼합된 광물파우더는 PET Chip또는 합성수지와 함께 스크류 익스트루더에 투입되어 혼합하여 290℃에서 원사에 따라 속도를 조정하여 방사를 실시하여 스테이플 화이버(Staple fiber)를 도 6과 같이 제작하게 된다. 상기와 같이 분쇄된 광물질과 오일이 혼합되어 방사 과정에서 더 고르게 혼합이 가능하였으며 압출기(익스투루더: extruder)에 의하여 용융방사되는 과정에서 오일은 50℃ 이하에서 수분제거가 됨으로써 품질이 더욱 안정적이어서 내구성이 높은 원사의 생성이 가능하였다.As described above, the mineral powder added with ZnO and mixed with the vegetable extract is put into a screw extruder together with a PET chip or a synthetic resin, mixed and adjusted by spinning at 290 ° C according to a yarn, and staple fibers As shown in FIG. The pulverized minerals and oil are mixed to allow more uniform mixing in the spinning process. In the process of melt spinning by an extruder, the oil is more stable in quality by removing water at 50 ° C or less It was possible to produce a durable yarn.
상기와 같은 방사에 의해서 스테이플 화이버는 인조 섬유를 짧게 잘라 양털이나 솜처럼 자아낸 섬유로 만들은 실로써 방적하기에 알맞으며 그 활용도가 높다. 스테이플 화이버에 무기계 금속산화물 성분을 가지고 있는 광물을 고르게PET Chip과 고르게 섞이도록 하기 위해서 본 발명에서는 소취성능을 가진 식물성 추출물을 방사시 주입하여 무기광물이 고르게 첨가되어 품질의 불량률이 줄어들고 기능성이 항상 우수하며 내구성이 높은 원사의 생산이 가능하다. The staple fiber is a thread made of short fibers and made of fibers such as wool or cotton, which is suitable for spinning and is highly utilized. In order to uniformly mix minerals having an inorganic metal oxide component in a staple fiber evenly with a PET chip, the present invention uses a vegetable extract having a deodorizing ability to be injected during spinning to uniformly add inorganic minerals, resulting in a reduction in defective quality, It is possible to produce highly durable yarn.
도 6과 같이 익스투루터에 의하여 마스터배치 칩과 PET칩은 기능성에 따라 일정량을 투입하게 되고 상기와 같이 투입된 칩들의 290℃에서 원사에 따라 속도를 조정하여 방사를 실시하게 된다. As shown in FIG. 6, the master batch chip and the PET chip are injected by the expander according to their functionality, and spinning is performed by adjusting the speed according to the yarn at 290 ° C of the chips as described above.
상기와 같이 방사된 원사는 섬유의 배향성을 향상시키고 섬유를 가늘게 하는 연신(drawing)과정을 수행하게 된다. 상기 과정에 의해서 상기 섬유의 강도나 탄성률이 향상시킬 수 있다. The yarn thus spun is subjected to a drawing process for improving the orientation of the fibers and for reducing the size of the fibers. The strength and elastic modulus of the fiber can be improved by the above process.
상기와 같이 연신 과정을 거친 섬유는 권축가공(crimping), 컷팅(cutting), 코밍(combing)을 거쳐 면과 함께 혼방사로 제조한다. The fibers thus stretched are crimped, cut, and combed to form blended yarn together with the cotton.
본 발명과 같이 제조된 면 혼방사는 면의 특성인 감촉이 좋으면서도, 면제품의 특유의 저조한 내구성과 신축성이 더욱 보강이 되어 더욱 편안한 착용감을 나타낼 수 있다. The cotton blend yarn produced according to the present invention has a good texture, which is a characteristic of the cotton fabric, but also the unique low durability and stretchability of the cotton fabric can be further reinforced and a more comfortable fit can be exhibited.
또한, 상기와 같이 제조된 원단은 후가공 없이 기능성을 나타내어 착용시기 동안은 영구정으로 소취와 항균의 기능성을 나타낼 수있다.In addition, the fabric prepared as described above exhibits functionality without post-processing, and can exhibit deodorization and antibacterial functions with permanent tablets during the wearing period.
본 발명과 같은 가고엥 의하여 첨가된 폴리에스터는 많은 단점이 무기계 금속산화물 성분을 가지고 있는 광물질을 첨가하여 분자 구조를 개질하여 면과 같은 물성을 부여시켜 폴리에스터 섬유의 단점을 개선함과 동시에 항균, 소취, 등과 같이 천연 섬유인 면에서는 볼 수 없는 위생적인 기능을 부여하여 피부 친화성 섬유로 제조가 가능하게 되었다. The gogophyte-added polyester according to the present invention has many disadvantages in that it is modified with molecular structure by adding a mineral having an inorganic metal oxide component so as to improve the disadvantages of the polyester fiber by imparting physical properties such as cotton, Deodorant, and the like, it is possible to manufacture a skin-friendly fiber by imparting a hygienic function that can not be seen in the case of natural fibers.
상기 혼방사는 면 60 ~ 85 중량%에 광물이 첨가된 폴리에스터 15 ~ 40 중량%로 하여 내의를 직조하게된다.The blend yarn is made from 60 to 85% by weight of cotton and 15 to 40% by weight of polyester having mineral added thereto.
상기와 같은 방법에 의해서 기능성으로 직조되는 내의류는 방사물은 연사(twisting)를 하여 원사를 직조한다. The undergarment, which is woven in a functional manner by the above-mentioned method, twists the yarn by weaving the yarn.
상기의 원사로 직조된 원단은 무기계 금속산화 광물을 함유하여 소취율이 높은 내의류의 원단이 된다. 상기의 원단을 내의류 전체에 적용하여 내의류를 생산할 경우 그 소취율은 매우 높으나 제조 단가가 증가하여 소비자가 쉽게 사용이 불가능할 수 있으므로 본 발명에서는 도 7, 도 8, 도 9와 같이 완성된 내의류에 일부의 원단으로 사용함으로써 제조비용을 절감하도록 할 수 있다.The fabric woven with the above yarn is a fabric of an undergarment containing an inorganic metal oxide mineral and having a high deodorization rate. When the fabric is applied to the entire underwear to produce an undergarment, the deodorization rate is very high. However, since the manufacturing cost is increased and the product can not be easily used by the consumer, in the present invention, The manufacturing cost can be reduced.
상기 원단은 악취를 흡착하여 소취하기 때문에 내의에 적용이 국부적이어도 소취 성능이 높게 나타낼 수 있다.Since the fabric absorbs odor and deodorizes it, the deodorizing performance can be high even if the application is locally applied.
일실시예로 소취율이 높은 원단으로 팬티를 제조하는 방법으로는 남·녀 착용자의 국부가 접하는 내저부(100)로 재단된 일부의 원단을 소취율이 높은 내의 원단으로 구성함으로써 제조비용이 저렴하면서도 소취율이 높은 팬티로 제작할 수 있다.In one embodiment, the method of manufacturing the panty with a high deodorization rate includes a method of fabricating a portion of the fabric cut into the
또한, 소취율이 높은 러닝셔츠를 제조하는 방법으로는 착용자의 겨드랑이가 접하는 소매부(110)로 재단된 일부의 원단을 소취율이 높은 내의 원단으로 구성하여 제조비용이 저렴하면서도 소취율이 높은 러닝셔츠로 제작할 수 있다.As a method of manufacturing a running shirt having a high deodorization rate, there is a method of manufacturing a running shirt in which a part of the fabric cut by the
상기와 같은 제조방법에 의해서 무기물이 함유된 원사는 원사속에 함유된 미네랄성분들이 세균의 원형질막을 파괴하여 항균기능을 발휘하여 악취 생산요인을 일차적으로 제거가 가능하며 그 외 발생하는 악취도 ZnO를 광촉매로 사용하여 화학적 방법으로 악취를 산화시켜 분해를 하여 악취를 소거 하게 된다. By the above-mentioned manufacturing method, the inorganic material contained in the inorganic material destroys the bacterial plasma membrane and exerts the antibacterial function, so that the odor producing factor can be removed firstly. In addition, And the odor is oxidized and decomposed by a chemical method to erase the odor.
상기의 기능성을 한국의류시험연구원과 FITI시험연구원에 의뢰하여 실험 결과를 확보하였다. The above-mentioned functionality was commissioned to the Korea Apparel Testing Institute and the FITI Testing Research Institute to obtain the experimental results.
<실시예><Examples>
맥반석과 제올라이트 2가지 이상의 광물을 선발하여 1차 분쇄에 의하여 50㎛의 파우더로 제조하고, 상기 두 종류의 분쇄된 광물을 1:1로 혼합하여 2차 분쇄하여 평균 입도가 1.08㎛의 금속산화물의 분말을 얻었다. 상기 2차 분쇄된 광물파우더 100중량부에 0.4중량부에 해당하는 징크옥사이드(ZnO)를 첨가하고, 상기 ZnO가 첨가된 2차 분쇄광물파우더 100중량부에 5중량부의 동백나무잎 추출물을 첨가하여 고르게 혼합하였다. 상기 혼합물을 폴리에스터 수지 99중량%에 최종 혼합물 1중량%가 되도록 고르게 혼합하여 압출기에 투입한 뒤 방사하여 스테이플 화이버를 수득하고, 폴리에스터 방적(spinning)을 실시하였다. 상기 필라멘트사는 65중량%의 면사와 35%의 폴리에스터와 함께 연신 과정을 수행 후 권축가공(crimping), 컷팅(cutting), 코밍(combing)을 거쳐 면과 함께 혼방사로 제조한다.Two or more minerals of elvan and zeolite were selected and made into a powder of 50 탆 by primary pulverization. The two kinds of pulverized minerals were mixed in a ratio of 1: 1 and then subjected to secondary pulverization to obtain a metal oxide having an average particle size of 1.08 탆 Powder was obtained. 0.4 part by weight of zinc oxide (ZnO) was added to 100 parts by weight of the second milled mineral powder, and 5 parts by weight of camellia leaf extract was added to 100 parts by weight of the second milled mineral powder to which ZnO was added And mixed evenly. The mixture was uniformly mixed with 99% by weight of polyester resin so as to be 1% by weight of the final mixture, put into an extruder, and then spun to obtain a staple fiber, and polyester spinning was carried out. The filament yarn is stretched together with 65% by weight of cotton yarn and 35% by weight of polyester, followed by crimping, cutting and combing to produce a blend yarn together with the cotton yarn.
<비교예><Comparative Example>
맥반석과 제올라이트 2가지 이상의 광물을 선발하여 1차 분쇄에 의하여 50㎛의 파우더로 제조하고, 상기 두 종류의 분쇄된 광물을 1:1로 혼합하여 2차 분쇄하여 평균 입도가 1.08㎛의 금속산화물의 분말을 얻었다. 이어서, 상기 2차 분쇄 광물파우더 무게 30 중량%에 혼합수지 70 중량%를 혼합하여 마스터배치 칩을 생산한 후, 상기 마스터 배치 칩과 폴리에스터 Virgin Chip 혼합물을 100 중량부로 하였을 때 97 중량부의 Virgin chip, 3중량부의 마스터 배치 칩을 혼합하여 압출기에 투입한 뒤 방사하여 스테이플 화이버를 수득하고, 폴리에스터 방적(spinning)을 실시하였다. 상기 필라멘트사는 65 중량%의 면사와 35%의 폴리에스터와 함께 연신 과정을 수행 후 권축가공(crimping), 컷팅(cutting), 코밍(combing)을 거쳐 면과 함께 혼방사로 제조한다.Two or more minerals of elvan and zeolite were selected and made into a powder of 50 탆 by primary pulverization. The two kinds of pulverized minerals were mixed in a ratio of 1: 1 and then subjected to secondary pulverization to obtain a metal oxide having an average particle size of 1.08 탆 Powder was obtained. Subsequently, the master batch chip was produced by mixing 70 wt% of the mixed resin with 30 wt% of the second powdered mineral powder, and then 100 parts by weight of the master batch chip and polyester virgin chip mixture was mixed with 97 parts by weight of Virgin chips , And 3 parts by weight of master batch chips were mixed and put in an extruder and then spun to obtain a staple fiber and polyester spinning was carried out. The filament yarn is stretched together with 65% by weight of cotton yarn and 35% by weight of polyester, followed by crimping, cutting and combing to produce a blend yarn together with the cotton yarn.
<실험 1> 2차 분쇄에 의한 입도의 평균 크기≪
- 의뢰기관 : 한국의류시험연구원- Request Agency: Korea Clothing Testing Institute
- 시료 : 2차 분쇄광물- Samples: Secondary crushed mineral
- 실험기기 : Malvern Instruments- Laboratory Instruments: Malvern Instruments
실험 1 결과 실시예의 2차 분쇄된 광물의 크기를 분석하여 본 결과 평균 입도는 1.08 ㎛을 나타 내었으며, 3.12㎛이하 크기의 입도를 나타낸는 분쇄물이 99.2%인 것이 확인되었다. 97%가 3 ㎛ 이하의 크기로 쉽게 분쇄된 것이 도 2의 그래프와 도3의 현미경 사진으로 확인할 수 있었다.
본 발명과 같이 광물을 2가지 혼합하여 분쇄하였을 경우 분쇄에 투입되는 시간이 감소하고, 분쇄물의 99%가 3 ㎛입도가 되어 쉽게 분쇄가 가능하여 제작비용의 절감되었다.As in the case of the present invention, when two minerals are mixed and pulverized, the time required for pulverization is reduced, and 99% of the pulverized material has a particle size of 3 탆.
<실험 2> 2차 분쇄된 광물의 조성<Experiment 2> The composition of the second crushed mineral
- 시료 : 2차 분쇄광물- Samples: Secondary crushed mineral
- 실험기기 : KS L4007- Experimental instrument: KS L4007
- 실험방법 : XRF, XRD, ICP-OES- Experimental method: XRF, XRD, ICP-OES
실시예에서 2차 분쇄된 광물의 조성을 확인한 결과 표와 같이 나타났다.In the examples, the compositions of the second-mined minerals were confirmed as shown in the table.
상기 실시예와 비교예의 2차 분쇄된 광물파우더의 성분을 분석하여 표2와 같은 결과를 확인하였다. 상기 시험분석방법은XRF(X선 형광분석기)와 XRD(X선 회절분석기)에 의하여 조성과 결정을 확인하고 ICP-OES(Inductively Coupled Plasma Optical Emission Spectrometer: 유도결합플라즈마 분광분석기)에 의하여 미량에 대한 정량 분석을 하였다.The components of the second pulverized mineral powders of the above Examples and Comparative Examples were analyzed and the results as shown in Table 2 were confirmed. The test analysis method was confirmed by XRF (X-ray fluorescence spectrometer) and XRD (X-ray diffractometer), and the composition and crystal were confirmed by ICP-OES (Inductively Coupled Plasma Optical Emission Spectrometer) Quantitative analysis was performed.
상기와 같이 광물질의 대부분은 구성하는 것은 이산화규소(SiO2)이고, 일부 ZnO와 CuO가 미량으로 존재하고 있어 미미하게 항균효과를 나타낼 수 있다. 상기와 같이 원료에 포함된 상기 무기산화물들은 광물의 기본적은 금속산화물만이 존재하고 있으며 상기 광물의 특징인 흡착기능을 나타내고 있다. As described above, most of the minerals are silicon dioxide (SiO 2 ), and some ZnO and CuO exist in a trace amount, so that they can exhibit a slight antibacterial effect. As described above, the inorganic oxides included in the raw material are basically metal oxides of minerals and exhibit an adsorption function characteristic of the minerals.
<실험 3> 소취능력 검사<Experiment 3> Deodorizing ability test
- 의뢰기관 : 한국의류시험연구원, FITI시험연구원 - Request Agency: Korea Apparel Testing Institute, FITI Testing Institute
- 시료 : 실시예와 비교예의 혼방사.- Samples: blend of Examples and Comparative Examples.
- 시험가스 : 암모니아(NH4)- Test gas: ammonia (NH4)
- 실험방법 : 가스검지관법, 소취율 (%)- Test method: gas detection method, deodorization rate (%)
- 주입된 시험가스의 농도 : 500 ppm - Concentration of injected test gas: 500 ppm
- 시험환경 : 온도 22℃, 습도 48 % R. H.- Test environment: temperature 22 캜, humidity 48% R.H.
실험의 결과 실시예로 완성된 혼방사는 암모니아가스를 2시간 동안 가스검지관법으로 소취율을 검사한 결과 모든 실시예의 방적사는 99% 이상 소취되는 것을 확인 할 수 있었다. 또한 포름알데히드에 대한 소취율은 모두 27.6%를 나타내었다. 본 시험방법에 의해서 실시예는 2시간 측정결과이며 이후 계속적인 소취 능력이 유지되어 소취 능력이 멈추는 시간은 측정이 불가능 하였다. 하지만, 비교예의 경우 2시간은 같은 소취 능력이 발휘되는 것으로 확인 되었으나 이후 소취 능력이 감소하는 것으로 비교예와 같은 제조방법은 소취 능력이 아닌 악취의 흡착에 의한 탈취능력에 해당하여, 본 발명과 같이 ZnO가 첨가된 시료는 소취 능력이 우수한 이유는 광물의 흡착능력과 함께 소취 능력이 발휘 되는 것이 확인되었다. 상기 실시예는 폴리에스터 원액수지에 첨가한 후 용융방사하여 원사에 1%(O.W.F) 함유토록 하여 충분한 소취 능력을 검증할 수 있었다. As a result of the experiment, it was confirmed that the spinning yarn of all the examples was deodorized by 99% or more when the deodorizing rate of the mixed blend yarn was examined by gas detecting tube method for 2 hours. The deodorization rate of formaldehyde was 27.6%. According to the present test method, the result of the measurement was 2 hours, and the continuous deodorizing ability was maintained, so that the stopping time of the deodorizing ability could not be measured. However, in the comparative example, it is confirmed that the same deodorizing ability is exhibited for 2 hours, but the deodorizing ability is decreased after that. The same manufacturing method as the comparative example corresponds to the deodorizing ability by adsorption of odor, It was confirmed that the sample with ZnO added had excellent deodorizing ability and exhibited the deodorizing ability together with the adsorption ability of mineral. In the above example, 1% (O.W.F) was contained in the yarn by melt spinning after adding to the polyester resin solution, and sufficient deodorizing ability could be verified.
<실험 4> 항균능력 검사<Experiment 4> Antibacterial ability test
- 의뢰기관 : 한국의류시험연구원, FITI시험연구원 - Request Agency: Korea Apparel Testing Institute, FITI Testing Institute
- 시료 : 실시예와 비교예의 혼방사 - Samples: Blends of Examples and Comparative Examples
- 사용공시균주 : staphylococcus aureeus ATCC6538(황색포도상구균) - Disclosed strain: staphylococcus aureus ATCC6538 (Staphylococcus aureus)
- 측정방법 : 세균수/㎖, 정균 감소율 %- Measurement method: Number of bacteria / ml, reduction rate of bacterium%
본 발명과 같이 광물을 첨가하여 제작된 실시예와 비교예의 혼방사에 항균력을 확인하였다. 상기와 같은 조건으로 2곳의 시험연구원에서 검사한 결과 실시예는 모두 99%의 균감소율을 확인 할 수 있었다. 하지만, 비교예와 같이 제조한 방적사의 경우 항균력이 전혀 나타나지 않는 것을 확인할 수 있었다. 또한, 상기와 같은 혼방사의 경우 1시간 이내에 살균효과를 확인 할 수 있었다. The antibacterial activity was confirmed in the blended yarn of Examples and Comparative Examples prepared by adding minerals according to the present invention. As a result of testing by two test laboratories under the above conditions, all of the examples were able to confirm a 99% reduction in the number of bacteria. However, in the case of the spinning yarn manufactured as in the comparative example, it was confirmed that no antibacterial activity was exhibited at all. In addition, in the case of the above-mentioned blend yarn, the sterilizing effect could be confirmed within one hour.
도 4에 나타난 것과 같이 실시예의 시료를 첨가하지 않은 경우 처음 접종한 것과 같은 1.5 x 104으로 나타났다. 또한, 비교예와 같이 ZnO가 첨가되지 않은 방적사의 경우 항균력을 거의 나타내지 않는 것을 확인 할 수 있었다. 이는 상기 광물만으로는 항균력을 나타내지 못하며, ZnO가 첨가 되었을 때 항균력이 발휘 된다는 것을 확인할 수 있었다. As shown in FIG. 4, when the sample of the example was not added, it was found to be 1.5 x 10 4 which was the same as that of the first inoculation. In addition, it was confirmed that the spinning yarn to which ZnO was not added showed little antibacterial activity as in the comparative example. This indicates that the above-mentioned minerals alone do not exhibit antibacterial activity, and that the antibacterial activity is exerted when ZnO is added.
또한, 본 발명에 의해 실시예에서 ZnO를 첨가한 분쇄물과 비교예의 2차 분쇄된 광물의 항균력을 비교 분석한 결과 실시예의 ZnO를 첨가한 분쇄물 시료는 92.5%의 항균력을 18시간에 걸쳐 나타나는 것을 확인 하였고, 비교예의 2차 분쇄된 광물의 시료는 항균력을 전혀 나타내지 않는 것을 확인하였다. 이는 본 발명에서 식물성 추출물이 첨가되고 고르게 방적가공을 실시한 결과 99%를 넘는 결과를 가져 오는 것을 확인하였다. Further, according to the present invention, the antibacterial activity of the ZnO-added pulverized product and the comparative example of the pulverized product of ZnO-added pulverized product of Comparative Example was 92.5% , And it was confirmed that the samples of the secondary pulverized minerals of the comparative examples did not show any antibacterial activity. It was confirmed that the addition of the vegetable extract in the present invention and the uniform spinning treatment resulted in more than 99%.
본 발명과 같이 제조할 경우 첨가된 금속산화무기물은 원료가 흡착, 산화작용을 하여 소취를 하며 동시에 소취 성분을 갖는 식물추출물이 중화반응, 부가반응, 포접 작용과 미량의 방향성 성분이 냄새를 제거하는 소취의 모든 작용도 같이 포함되어 기타의 화합물이나 혼방사의 코팅가공을 통한 기능성 개선이 없이 우수한 소취 능력과 항균능력을 나타냄으로써 제조 단가와 시간이 절감되는 우수한 특성의 원단에 제조가 가능하다.In the case of the production according to the present invention, the metal oxide inorganic material added is adsorbed and oxidized by the raw material to deodorize, and at the same time, the plant extract having the deodorant ingredient is neutralized, added and contained, and a small amount of aromatic component removes the odor It also includes all the functions of deodorant, so it can produce excellent deodorizing ability and antimicrobial ability without improving functionalities through coating process of other compounds or blended yarn, thereby manufacturing fabrics having excellent properties such as reduced manufacturing cost and time.
상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the present invention as defined by the following claims It can be understood that
10 : 광물 20 : Virgin Chip
30 : 익스트루더 40 : 도징펌프
50 : 연신 60 : 권취10: Minerals 20: Virgin Chip
30: Extruder 40: dosing pump
50: stretching 60: winding
Claims (5)
맥반석, 현무암, 운석류 및 제올라이트를 포함하는 광물질 중에서 2가지 내지 4가지의 광물을 선발하여 준비하는 단계;
상기 선발된 광물들을 개별적으로 1차 분쇄하는 단계;
상기 준비된 광물을 동량으로 혼합하여 2차 분쇄하여 평균 입도가 3㎛ 이하의 금속산화물의 분말을 얻는 단계;
상기 2차 분쇄된 광물 분말 100 중량부에 징크옥사이드(ZnO) 0.2 ~ 0.5 중량부를 첨가하는 단계;
상기 징크옥사이드가 첨가된 2차 분쇄광물 분말 100중량부에 식물추출물 4 내지 7 중량부를 첨가하여 고르게 혼합하는 단계; 및
PET 수지 97 ~ 99.9 중량부에 상기 식물추출물이 혼합된 광물 분말 0.3 ~ 3 중량부를 고르게 혼합하여 압출기에 투입한 뒤 방사하는 단계;
상기 방사된 필라멘트사는 면 60 ~ 85 중량%에 광물이 첨가된 폴리에스터 15 ~ 40 중량%로 혼방사로 연사(twisting)하는 단계;
상기 연사단계를 거친 후 권축가공(crimping), 컷팅(cutting), 코밍 (combing)을 거쳐 면과 함께 혼방사로 제조하는 단계;
상기 혼방사로 원단을 직조하는 단계;
를 포함하는 것을 특징으로 하는 무기계 금속산화 광물을 함유하여 소취율이 높은 내의류 제조방법.
The fabric having a high deodorization rate,
Selecting two or four kinds of minerals among minerals including quartz, quartz, basalt, rhyolite and zeolite;
Separately first crushing the selected minerals;
Mixing and mixing the prepared minerals in an equal amount to obtain a metal oxide powder having an average particle size of 3 탆 or less;
Adding 0.2 to 0.5 parts by weight of zinc oxide (ZnO) to 100 parts by weight of the second pulverized mineral powder;
Adding 4 to 7 parts by weight of the plant extract to 100 parts by weight of the powder of the secondary crushed mineral to which zinc oxide is added, And
0.3 to 3 parts by weight of a mineral powder mixed with the plant extract is uniformly mixed in 97 to 99.9 parts by weight of a PET resin, and the mixture is injected into an extruder and then irradiated;
Twisting the blended filament yarn into a blended yarn with 60 to 85% by weight of the cotton and 15 to 40% by weight of the polyester to which the mineral is added;
A step of crimping, cutting, and combing the yarn after the twisting step to produce a blended yarn together with the yarn;
Weaving the fabric with the blend yarn;
Wherein the inorganic metal oxide mineral is characterized in that it contains an inorganic metal oxide mineral and has a high deodorization rate.
상기 식물추출물은 소취 기능을 갖는 식물성오일을 함유하는 동백나무과의 추출물인 것을 특징으로 하는 무기계 금속산화 광물을 함유하여 소취율이 높은 내의류 제조방법.
The method of claim 1,
Wherein the plant extract is an extract of a camellia tree containing a vegetable oil having a deodorizing function and contains an inorganic metal oxide mineral and has a high deodorization rate.
상기 내의류의 하나인 소취율이 높은 팬티를 제조함에 있어서,
남·녀 착용자의 국부가 접하는 내저부(100)로 재단된 일부의 원단을 소취율이 높은 내의 원단으로 구성된 것을 특징으로 하는 무기계 금속산화 광물을 함유하여 소취율이 높은 내의류 제조방법.
The method according to claim 1,
In producing a panty with a high deodorization rate, which is one of the above-mentioned undergarments,
Wherein a part of the fabric cut by the inner bottom part (100) contacting with the local part of the wearer of men and women is composed of a fabric having a high deodorization rate and having a high deodorization rate.
상기 내의류의 하나인 소취율이 높은 러닝셔츠를 제조함에 있어서,
착용자의 겨드랑이가 접하는 소매부(110)로 재단된 일부의 원단을 소취율이 높은 내의 원단으로 구성된 것을 특징으로 하는 무기계 금속산화 광물을 함유하여 소취율이 높은 내의류 제조방법.
The method according to claim 1,
In manufacturing a running shirt having a high deodorization rate, which is one of the above-mentioned undergarments,
Characterized in that a part of the fabric cut by the sleeves (110) to which the wearer's side is touched is made of a fabric having a high deodorization rate, and the inorganic metal oxide mineral is contained, and the deodorization ratio is high.
An undergarment containing an inorganic metal oxide mineral and having a high deodorization rate, which is produced by the method of claim 1.