CN1071940A - 磷锌体系防锈涂料 - Google Patents

磷锌体系防锈涂料 Download PDF

Info

Publication number
CN1071940A
CN1071940A CN 91109882 CN91109882A CN1071940A CN 1071940 A CN1071940 A CN 1071940A CN 91109882 CN91109882 CN 91109882 CN 91109882 A CN91109882 A CN 91109882A CN 1071940 A CN1071940 A CN 1071940A
Authority
CN
China
Prior art keywords
coating
agent
antirusting
grease
pigment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 91109882
Other languages
English (en)
Inventor
李固
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEIYANG CHEMICAL PLANT NANJIAO DISTRICT TIANJIN CITY
Original Assignee
BEIYANG CHEMICAL PLANT NANJIAO DISTRICT TIANJIN CITY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEIYANG CHEMICAL PLANT NANJIAO DISTRICT TIANJIN CITY filed Critical BEIYANG CHEMICAL PLANT NANJIAO DISTRICT TIANJIN CITY
Priority to CN 91109882 priority Critical patent/CN1071940A/zh
Publication of CN1071940A publication Critical patent/CN1071940A/zh
Pending legal-status Critical Current

Abstract

一种钢铁表面防腐用磷锌体系防锈涂料，主要由 成膜聚合物10-15％、固化剂2-4％、增塑剂1-2％、 脱脂剂4-2％、磷化剂2-4％、防湿剂1-3％、颜料 10-15％、混合溶剂70-55％组成。其生产工艺及设 备与生产一般涂料所使用的工艺及设备完全相同。 本涂料附着力强，在金属表面带油带锈的条件下，涂 上本涂料后能起到优良的防锈作用。

Description

本发明属于一种钢铁表面防腐用的涂料，尤其是一种渗透型带锈防锈涂料。
目前解决钢铁及其制品的生锈问题普遍采用在钢铁表面涂以防腐涂料的办法。这种一般防腐涂料在使用前必须将金属表面的锈层及油污清除掉，否则不能使用。
本发明的目的是为了提供一种可以直涂在带锈带油的金属表面的磷锌体系防锈涂料，而且附着力强、防腐效果好。
本发明是由成膜聚合物10-15%、固化剂2-4%、增塑剂1-2%、脱脂剂4-2%、磷化剂2-4%、防湿剂1-3%、颜料10-15%、混合溶剂70-55%组成，其中的百分比均为重量百分比。
该涂料的制备是首先将聚合物在30-50℃的条件下溶于溶剂中，然后将颜料加入上述容剂中充分搅拌，再将固化剂、防湿剂、增塑剂、脱脂剂分别加聚合物溶液中，充分研磨，最后加入磷化剂。
附图是本发明的工艺流程图，本发明的具体工艺流程与附图完全相同。
生产本涂料的具体工艺参数及所使用的设备与生产一般防腐涂料的工艺及设备完全相同。以下结合实施例对本发明的技术特征进一步说明：
实施例：聚乙烯醇缩甲醛    80
618环氧树脂    40
对苯乙酚    20
磷酸三钠    30
一氨丙基三乙氧基硅烷    2
磷苯二甲三丁酚    2
氧化铁红    110
微硅粉    10
乙醇    350
异丙醇    350
水    6
利用上述配方所生产的涂料性能如下：
粘度    22秒（4＃/22℃）
细度    ≤60
遮盖力 55g/m2
表干    20-25分钟/25℃
硬度    0.52
冲击强度    50KgCm
附着力    1.5-2级（带油）
耐盐水性    浸48小时不起泡
本涂料与一般涂料相比，具有附着力强的特点，在金属表面带油带锈的条件下，涂上本涂料后能起到优良的防腐作用。

Claims (1)

  1. 一种钢铁表面防腐用磷锌体系防锈涂料，其特征在于由成膜聚合物10-15%、固化剂2-4%、增塑剂1-2%、脱脂剂4-2%、磷化剂2-4%、防湿剂1-3%、颜料10-15%、混合溶剂70-55%组成。上述中的百分比均为重量百分比。
CN 91109882 1991-10-28 1991-10-28 磷锌体系防锈涂料 Pending CN1071940A (zh)