CN107190251B - 一种镀金液及其制备方法 - Google Patents

一种镀金液及其制备方法 Download PDF

Info

Publication number
CN107190251B
CN107190251B CN201710463936.1A CN201710463936A CN107190251B CN 107190251 B CN107190251 B CN 107190251B CN 201710463936 A CN201710463936 A CN 201710463936A CN 107190251 B CN107190251 B CN 107190251B
Authority
CN
China
Prior art keywords
tetra
gold
ethylenediamine
bis
ethoxy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710463936.1A
Other languages
English (en)
Other versions
CN107190251A (zh
Inventor
贾丹枫
李卫明
黎小芳
刘彬云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Toneset Science & Technology Co Ltd
Original Assignee
Guangdong Toneset Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Toneset Science & Technology Co Ltd filed Critical Guangdong Toneset Science & Technology Co Ltd
Priority to CN201710463936.1A priority Critical patent/CN107190251B/zh
Publication of CN107190251A publication Critical patent/CN107190251A/zh
Application granted granted Critical
Publication of CN107190251B publication Critical patent/CN107190251B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种镀金液及其制备方法，包括水溶性金盐、屏蔽剂及具有如下通式（1）或（2）所示的胺类化合物：(1)(2)

Description

一种镀金液及其制备方法
技术领域
本发明属于镀金加工技术领域，具体涉及一种镀金液及其制备方法。
背景技术
黄金镀层具有优良的化学稳定性、导电性、可焊性及耐高温性，是现代工艺中高稳定性，高可靠元器件的理想镀层。
现有的化学镀金液，可以是含氰也可以不含氰，镀液的主要成分有络合剂、还原剂、稳定剂、屏蔽剂等。如CN1771352A公开了一种化学镀金液，金盐为水溶性非氰金盐，采用羟基烷基磺酸及其盐作为还原剂、亚硫酸和硫代硫酸的碱金属盐为络合剂，乙二胺或甘氨酸为胺化合物，镀液可获得优异的稳定性及较厚的金层，但是经过1~2次微蚀就容易出现掉金。EP 0630991A1中提到一种无氰还原型镀金液，金盐为氯金酸钠或亚硫酸金钠，采用抗坏血酸为还原剂，镀液组成为烷基胺或噻唑、咪唑、恶唑类化合物，镀液稳定性好，安全环保、但是无法耐2次微蚀而不掉金。
目前有些公司在进行化镍镀金时只在部分露铜位置进行镀金，对制成后化镍金板会需要增加一个OSP过程以保护其他未化镍金的铜部位，这样需要在经过几道微蚀工序后才能进入OSP工序，而微蚀液具有一定的氧化性和腐蚀性，虽然也有些公司能够在化镍金层增加一层保护膜，但是贴膜和去膜的过程较繁琐，需要耗费大量的人力物力，如果这些化镍金板耐微蚀槽液的腐蚀的性能较优，就可以省去过OSP过程中的贴膜及去膜过程而直接进入OSP工序。然而现有的镀金液大多存耐微蚀性较差等问题，不能满足现在化镍金板工艺的要求。
发明内容
为解决上述现有化学镀金液存在的耐微蚀液腐蚀性差等问题，本发明的目的在于提供一种镀金液，该镀金液金面外观优良，耐微蚀性好，能够经过4-5次微蚀而不出现甩金。
本发明是通过以下技术方案实现：
一种镀金液，包括水溶性金盐、屏蔽剂及具有如下通式（1）或（2）所示的胺类化合物：
(1) (2)
其中：R1、R2、R3、R4、R5、R6、R7、R8、R9相同或不同，彼此独立的代表-CH2OH、
-CH2CH2OH、-CH(OH)CH3、-CH2CH2CH2OH、-CH2CH(OH)CH3、-CH(OH)CH2CH3、
-CH(CH2OH)(CH3)、-C(CH3)2(OH)、-CH2CH2CH2CH2OH、-CH2CH2CH(OH)CH3、
-CH2CH(OH)CH2CH3、-CH(OH)CH2CH2CH3、-CH(OH)CH(CH3)2、-CH2C(OH)(CH3)2、
-CH2CH(CH3)(CH2OH)、-C(OH)(CH3)CH2CH3、-CH(CH2OH)CH2CH3、-CH(CH3)CH(OH)CH3、-CH(CH3)CH2CH2OH或-C(CH3)2(CH2OH)，优选为-CH2OH、-CH2CH2OH、-CH2CH2CH2OH、-CH2CH2CH2CH2OH；
其中n=1~6，m=1~5。
进一步优选的，所述胺类化合物为N,N,N',N'-四(羟甲基)乙二胺、N,N,N',N'-四(2-羟乙基)乙二胺、N,N,N',N'-四(1-羟乙基)乙二胺、N,N,N',N'-四(3-羟丙基)乙二胺、N,N,N',N'-四(2-羟丙基)乙二胺、N,N,N',N'-四(1-羟丙基)乙二胺、N,N,N',N'-四(1-羟甲基乙基)乙二胺、N,N,N',N'-四(1-羟基-1-甲基乙基)乙二胺、N,N,N',N'-四(4-羟丁基)乙二胺、N,N,N',N'-四(3-羟丁基)乙二胺、N,N,N',N'-四(2-羟丁基)乙二胺、N,N,N',N'-四(1-羟丁基)乙二胺、N,N,N',N'-四(1-羟基-2-甲基丙基)乙二胺、N,N,N',N'-四(2-羟基-2-甲基丙基)乙二胺、N,N,N',N'-四(3-羟基-2-甲基丙基)乙二胺、N,N,N',N'-四(1-羟基-1-甲基丙基)乙二胺、N,N,N',N'-四(1-羟甲基丙基)乙二胺、N,N,N',N'-四(2-羟基-1-甲基丙基)乙二胺、N,N,N',N'-四(3-羟基-1-甲基丙基)乙二胺、N,N,N',N'-四(2-羟基-1,1-二甲基乙基)乙二胺、N,N,N',N'-四(羟甲基)-1,3-丙二胺、N,N,N',N'-四(2-羟乙基)-1,3-丙二胺、N,N,N',N'-四(3羟丙基)-1,3-丙二胺、N,N,N',N'-四(4-羟丁基)-1,3-丙二胺、N,N,N',N'-四(羟甲基)-1,4-丁二胺、N,N,N',N'-四(2-羟乙基)-1,4-丁二胺、N,N,N',N'-四(3-羟丙基)-1,4-丁二胺、N,N,N',N'-四(4-羟丁基)-1,4-丁二胺、N,N,N',N'-四(羟甲基)-1,5-戊二胺、N,N,N',N'-四(2-羟乙基)-1,5-戊二胺、N,N,N',N'-四(3-羟丙基)-1,5-戊二胺、N,N,N',N'-四(4-羟丁基)-1,5-戊二胺、N,N,N',N'-四(羟甲基)-1,5-戊二胺、N,N,N',N'-四(2-羟乙基)-1,5-戊二胺、N,N,N',N'-四(3-羟丙基)-1,5-戊二胺、N,N,N',N'-四(4-羟丁基)-1,5-戊二胺、N,N,N',N'-四(羟甲基)-1,6-己二胺、N,N,N',N'-四(2-羟乙基)-1,6-己二胺、N,N,N',N'-四(3-羟丙基)-1,6-己二胺、N,N,N',N'-四(4-羟丁基)-1,6-己二胺、N,N,N',N'',N''-五(羟甲基)二乙烯三胺、N,N,N',N'',N''-五(2-羟乙基)二乙烯三胺、N,N,N',N'',N''-五(3-羟丙基)二乙烯三胺、N,N,N',N'',N''-五(4-羟丁基)二乙烯三胺、N1,N1,N2,N3,N4,N4-六(羟甲基)三乙烯四胺、N1,N1,N2,N3,N4,N4-六(2-羟乙基)三乙烯四胺、N1,N1,N2,N3,N4,N4-六(3-羟丙基)三乙烯四胺、N1,N1,N2,N3,N4,N5,N5-七(羟甲基)四乙烯五胺、N1,N1,N2,N3,N4,N5,N6,N6-八(羟甲基)五乙烯六胺、N,N'-二(1-羟乙基)-N,N'-二(羟甲基)乙二胺、N,N-二(2-羟乙基)-N',N'-二(羟甲基)乙二胺、N,N-二(3-羟丙基)-N',N'-二(羟甲基)乙二胺、N,N-二(3-羟丙基)-N',N'-二(2-羟乙基)乙二胺、N,N-二(2-羟乙基)-N',N'-二(羟甲基)-1,3-丙二胺、N,N-二(3-羟丙基)-N',N'-二(2-羟乙基)-1,3-丙二胺、N,N'-二(1-羟丙基)-N,N'-二(羟甲基)-1,3-丙二胺、N,N,N'',N''-四(2-羟乙基)-N'-羟甲基二乙烯三胺、N,N,N4,N4-四(2-羟乙基)-N2,N3-二(羟甲基)三乙烯四胺或N,N-二(3-羟丙基)-N'',N''-二(2-羟乙基)-N'-羟甲基二乙烯三胺中的一种或几种。
更优选为N,N,N',N'-四(羟甲基)乙二胺、N,N,N',N'-四(2-羟乙基)乙二胺、N,N,N',N'-四(3-羟丙基)乙二胺、N,N,N',N'-四(4-羟丁基)乙二胺、N,N,N',N'-四(2-羟乙基)-1,3-丙二胺、N,N,N',N'-四(羟甲基)-1,4-丁二胺、N,N,N,'N'-四(2-羟乙基)-1,4-丁二胺、N,N,N',N'',N''-五(羟甲基)二乙烯三胺、N,N,N',N'',N''-五(2-羟乙基)二乙烯三胺、N,N,N',N'',N''-五(3-羟丙基)二乙烯三胺、N1,N1,N2,N3,N4,N4-六(2-羟乙基)三乙烯四胺、N,N-二(2-羟乙基)-N',N'-二(羟甲基)乙二胺、N,N-二(3-羟丙基)-N',N'-二(羟甲基)乙二胺、N,N-二(2-羟乙基)-N',N'-二(羟甲基)-1,3-丙二胺、N,N,N'',N''-四(2-羟乙基)-N'-羟甲基二乙烯三胺或N,N-二(3-羟丙基)-N'',N''-二(2-羟乙基)-N'-羟甲基二乙烯三胺中的一种或几种，最优选为N,N,N',N'-四(2-羟乙基)-1,3-丙二胺或N,N,N',N'-四(2-羟乙基)-1,4-丁二胺。
所述胺类化合物的用量为0.1g/l~50g/l，优选为1~20g/l。如果用量小于0.1 g/l，则耐微蚀性能达不到要求；如果用量大于50 g/l，则容易引起镀速不足。
所述水溶性金盐选自水溶性非氰金盐或水溶性含氰金盐中的一种或几种。本发明的镀金液中的水溶性金盐以渡液中的金浓度计，优选金浓度为0.1~5g/l。如果金浓度小于0.1g/l，则镀速不足；如果金浓度大于5g/l，浓度达到饱和，对镀速提升效果不明显，而金较为贵重，成本会增加。
所述水溶性非氰金盐选自亚硫酸金钾、亚硫酸金钠、亚硫酸金铵、硫代硫酸金钠、硫代硫酸金钾、硫代硫酸金铵、氯金酸钠、氯金酸钾、氯金酸铵、二氯金酸钠、二氯金酸钾、二氯金酸铵、硫氰酸金钠、硫氰酸金钾、硫氰酸金铵、硫代苹果酸钠、硫代苹果酸钾、硫代苹果酸铵、柠檬酸金钾、柠檬酸金钠、柠檬酸金铵中的一种或多种；
所述水溶性含氰金盐选自氰化亚金钾、氰化亚金钠、氰化亚金铵、四氰合金酸钾、四氰合金酸钠、四氰合金酸铵中的一种或多种。
所述屏蔽剂选自柠檬酸、柠檬酸钠、柠檬酸铵、柠檬酸钾、酒石酸、酒石酸钠、酒石酸钾、酒石酸铵、苹果酸、苹果酸钠、苹果酸钾、苹果酸铵、乳酸、乳酸钠、乳酸钾、乳酸铵、葡萄糖-δ-内酯、葡萄糖酸或琥珀酸羟基乙酸的一种或多种，用量为0~50g/l。
本发明上述的镀金液，还包括络合剂，所述络合剂选自氰化钠、氰化钾、亚硫酸氢钠、焦亚硫酸钠、亚硫酸钾、亚硫酸铵、硫代硫酸钠、硫代硫酸钾或硫代硫酸铵中的一种或多种，用量为0~100g/l。
本发明上述的镀金液，还包括稳定剂，所述稳定剂选自氮基三乙酸、次氮基三丙酸、甘氨酸、亚氨基乙二酸、乙二胺四乙酸、四二胺四丙酸、羟基乙二胺四乙酸、双羟基乙二胺四乙酸、羟乙基乙二胺三乙酸、二羟乙基乙二胺二乙酸、丙二胺四乙酸、二亚乙基三胺五乙酸、三亚乙基四安六乙酸、双甘氨肽、双羟乙基甘氨酸、羟乙基亚氨基乙二酸及其碱金属盐或铵盐，以及甲胺、乙胺、丙胺、丁胺、乙二胺、丙二胺、1,3-丙二胺、丁二胺、己二胺、庚二胺、二乙烯三胺、三乙烯四胺、四乙烯五胺、五乙烯六胺、四羟基亚乙基二胺、单乙醇胺、双乙醇胺、三乙醇胺、2-巯基苯并噻唑、6-乙氧基-2-巯基苯并噻唑、2-巯基苯并咪唑、2-巯基苯并恶唑、苯并三唑钠、四氢苯并三唑、甲基苯并三唑、硝基苯并三唑、吡啶、联吡啶或氨基吡啶中的一种或多种，用量为0~50g/l。
本发明上述的镀金液，还包括添加剂，所述添加剂选自二乙二醇丁醚、乙二醇丁醚、丙二醇丁醚、乙二醇甲醚、二乙二醇甲醚或二丙二醇甲醚中的一种或多种，用量为0~5g/l。
本发明所选用的添加剂适量添加可以达到改善金面颜色的作用，如果添加剂的用量超过5g/l，则会引起金面颜色变暗或无光泽感。
本发明还提供了上述镀金液的制备方法，包括如下步骤：
在室温条件下，先将络合剂、屏蔽剂、稳定剂、添加剂、胺类化合物混合均匀，调节pH为6.5-8.5，然后再加入水溶性金盐混合均匀，即得。
当使用本发明的镀金液进行镀金时，可采用常规方法。所述镀金液的温度为65-85℃，pH为6.5~8.5，镀覆时间为10~60min。
本发明与现有技术相比，具有如下有益效果：
本发明镀金液通过添加特定的胺类化合物，使镀金层金面颜色优良为金黄色，在保持较高沉积速率（0.05-0.09μm/10min）的同时，耐微蚀性优良，能耐4~5次微蚀而不出现甩金，可稳定应用于制品镀镍或镀镍合金后的镀金过程。
具体实施方式
下面通过具体实施方式来进一步说明本发明，以下实施例为本发明具体的实施方式，但本发明的实施方式并不受下述实施例的限制，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。
镀层外观：采用目测法观测镀层外观。
耐微蚀性能测试：采用微蚀液M进行耐微蚀测试（微蚀液M的组成为质量分数3%硫酸、质量分数1.0%的过氧化氢，质量分数0.02%氨基四唑和余量的水组成），具体操作过程为30℃下，将做好的镍金板垂直全部放置于槽液浸泡1min，然后水洗烘干，待板面冷却后用3M胶带进行测试，若无甩金，则记为耐1次微蚀，并继续进行耐微蚀测试，依此类推直至第N次出现甩金，记作耐N-1次微蚀不掉金。
具体实施例1：亚硫酸金钠（金浓度）2g/l，亚硫酸钠30g/l，柠檬酸钠20g/l，乙二胺20g/l，N,N,N',N'-四(羟甲基)乙二胺5g/l，pH 7.5，温度70℃，镀速为0.05~0.06μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例2：氰化亚金钾（金浓度）0.5g/l，柠檬酸钠20g/l，乙二胺10g/l，EDTA2Na 15g/l，N,N,N',N'-四(2-羟乙基)乙二胺5g/l， pH 6.5，温度80℃，镀速为0.05~0.06μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例3：氰化亚金钾（金浓度）0.5g/l，柠檬酸钠10g/l，N,N,N',N'-四(2-羟乙基)-1,3-丙二胺20g/l，pH 8.5，温度85℃，镀速为0.06~0.07μm/10min，外观为金黄色，耐5次微蚀不掉金。
具体实施例4：氰化亚金钾（金浓度）0.5g/l，N,N,N',N'-四(3-羟丙基)乙二胺20g/l，甘氨酸10g/l，pH 7.5，温度85℃，镀速为0.05~0.06μm/min，外观为金黄色，耐4次微蚀不掉金。
具体实施例5：氰化亚金钾（金浓度）1g/l，N,N,N',N'-四(羟甲基)-1,4-丁二胺10g/l，柠檬酸钠20g/l，pH 7.0，温度80℃，镀速为0.05~0.06μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例6：亚硫酸金钠（金浓度）1g/l，亚硫酸钠20g/l，硫代硫酸钠1g/l，柠檬酸钠10g/l，乙二胺20g/l，N,N,N',N'',N''-五(羟甲基)二乙烯三胺15g/l，pH 7.0，温度65℃，镀速为0.06~0.07μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例7：氰化亚金钾（金浓度）0.4g/l，氰化钾0.1g/l，柠檬酸钠20g/l，乙二胺10g/l，EDTA2Na 15g/l，N,N,N,'N'-四(2-羟乙基)-1,4-丁二胺20g/l， pH 7.5，温度85℃，镀速为0.05~0.06μm/10min，外观为金黄色，耐5次微蚀不掉金。
具体实施例8：氰化亚金钾（金浓度）1g/l，氰化钾0.1g/l， N,N,N',N'',N''-五(2-羟乙基)二乙烯三胺5g/l，pH 6.5，温度85℃，镀速为0.07~0.08μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例9：氰化亚金钾（金浓度）0.5g/l，柠檬酸钠20g/l，EDTA2Na 15g/l，N1,N1,N2,N3,N4,N4-六(2-羟乙基)三乙烯四胺20g/l，pH 7.5，温度85℃，镀速为0.05~0.06μm/min，外观为金黄色，耐4次微蚀不掉金。
具体实施例10：氰化亚金钾（金浓度）0.5g/l，柠檬酸钠20g/l，EDTA2Na 10g/l，N,N-二(2-羟乙基)-N',N'-二(羟甲基)乙二胺15g/l，pH 7.5，温度80℃，镀速为0.07~0.08μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例11：亚硫酸金钠（金浓度）1g/l，亚硫酸钠30g/l，硫代硫酸钠5g/l，柠檬酸钠10g/l，N,N-二(3-羟丙基)-N',N'-二(羟甲基)乙二胺5g/l，丙二醇甲醚0.5g/l，pH8.5，温度75℃，镀速为0.08~0.09μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例12：亚硫酸金钠（金浓度）1g/l，亚硫酸钠20g/l，硫代硫酸钠5g/l，柠檬酸钠15g/l，三乙醇胺5g/l，EDTA2Na 20g/l，N,N-二(2-羟乙基)-N',N'-二(羟甲基)-1,3-丙二胺2g/l，甘氨酸10g/l，二丙二醇甲醚1g/l，pH 7.5，温度70℃，镀速为0.06~0.07μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例13：氰化亚金钾（金浓度）0.5g/l，氰化钾0.1g/l，柠檬酸钠20g/l，N,N,N'',N''-四(2-羟乙基)-N'-羟甲基二乙烯三胺10g/l，pH 7.5，温度85℃，镀速为0.05~0.06μm/min，外观为金黄色，耐4次微蚀不掉金。
具体实施例14：亚硫酸金钠（金浓度）1g/l，亚硫酸钠10g/l，硫代硫酸钠5g/l，N,N-二(3-羟丙基)-N'',N''-二(2-羟乙基)-N'-羟甲基二乙烯三胺15g/l，pH 7.5，温度70℃，镀速为0.07~0.08μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例15：亚硫酸金钠（金浓度）1g/l，亚硫酸钠30g/l，硫代硫酸钠5g/l，乙二胺10g/l，N,N,N',N'-四(2-羟乙基)乙二胺2g/l，pH 7.5，温度70℃，镀速为0.06~0.07μm/10min，外观为金黄色，耐4次微蚀不掉金。
具体实施例16：氰化亚金钾（金浓度）0.5g/l，柠檬酸钠20g/l，N,N,N',N'-四(1-羟丙基)乙二胺10g/l，pH 7.5，温度85℃，镀速为0.06~0.07μm/min，外观为金黄色，耐4次微蚀不掉金。
具体实施例17：氰化亚金钾（金浓度）0.5g/l，柠檬酸钠20g/l，N,N'-二(1-羟乙基)-N,N'-二(羟甲基)乙二胺5g/l，pH 6.5，温度85℃，镀速为0.06~0.07μm/min，外观为金黄色，耐4次微蚀不掉金。
具体实施例18：氰化亚金钾（金浓度）0.5g/l，柠檬酸钠20g/l，N,N,N',N'-四(1-羟丁基)乙二胺5g/l，pH 6.5，温度85℃，镀速为0.06~0.07μm/min，外观为金黄色，耐4次微蚀不掉金。
对比例1：氰化亚金钾（金浓度）0.5g/l，柠檬酸钠10g/l， pH 8.5，温度85℃，镀速为0.07~0.08μm/10min，外观为金黄色，耐2次微蚀不掉金。
对比例2：亚硫酸金钠（金浓度）1g/l，亚硫酸钠20g/l，硫代硫酸钠1g/l，柠檬酸钠10g/l，乙二胺20g/l，pH 7.0，温度65℃，镀速为0.06~0.07μm/10min，外观为金黄色，耐1次微蚀不掉金。
对比例3：氰化亚金钾（金浓度）0.5g/l，柠檬酸钠20g/l，EDTA2Na 10g/l，羟乙基乙二胺三乙酸15g/l，pH 7.5，温度80℃，镀速为0.07~0.08μm/10min，外观为金黄色，耐2次微蚀不掉金。

Claims (14)

1.一种镀金液，其特征在于，包括水溶性金盐、屏蔽剂及具有如下通式（1）或（2）所示的胺类化合物：
(1) (2)
其中：R1、R2、R3、R4、R5、R6、R7、R8、R9相同或不同，彼此独立的代表-CH2OH、
-CH2CH2OH、-CH(OH)CH3、-CH2CH2CH2OH、-CH2CH(OH)CH3、-CH(OH)CH2CH3、
-CH(CH2OH)(CH3)、-C(CH3)2(OH)、-CH2CH2CH2CH2OH、-CH2CH2CH(OH)CH3、
-CH2CH(OH)CH2CH3、-CH(OH)CH2CH2CH3、-CH(OH)CH(CH3)2、-CH2C(OH)(CH3)2、
-CH2CH(CH3)(CH2OH)、-C(OH)(CH3)CH2CH3、-CH(CH2OH)CH2CH3、-CH(CH3)CH(OH)CH3、-CH(CH3)CH2CH2OH或-C(CH3)2(CH2OH)；
其中n=1~6，m=1~5。
2.根据权利要求1所述的镀金液，其特征在于，R1、R2、R3、R4、R5、R6、R7、R8、R9相同或不同，彼此独立的代表-CH2OH、-CH2CH2OH、-CH2CH2CH2OH、-CH2CH2CH2CH2OH。
3.根据权利要求1所述的镀金液，其特征在于，所述胺类化合物为N,N,N',N'-四(羟甲基)乙二胺、N,N,N',N'-四(2-羟乙基)乙二胺、N,N,N',N'-四(1-羟乙基)乙二胺、N,N,N',N'-四(3-羟丙基)乙二胺、N,N,N',N'-四(2-羟丙基)乙二胺、N,N,N',N'-四(1-羟丙基)乙二胺、N,N,N',N'-四(1-羟甲基乙基)乙二胺、N,N,N',N'-四(1-羟基-1-甲基乙基)乙二胺、N,N,N',N'-四(4-羟丁基)乙二胺、N,N,N',N'-四(3-羟丁基)乙二胺、N,N,N',N'-四(2-羟丁基)乙二胺、N,N,N',N'-四(1-羟丁基)乙二胺、N,N,N',N'-四(1-羟基-2-甲基丙基)乙二胺、N,N,N',N'-四(2-羟基-2-甲基丙基)乙二胺、N,N,N',N'-四(3-羟基-2-甲基丙基)乙二胺、N,N,N',N'-四(1-羟基-1-甲基丙基)乙二胺、N,N,N',N'-四(1-羟甲基丙基)乙二胺、N,N,N',N'-四(2-羟基-1-甲基丙基)乙二胺、N,N,N',N'-四(3-羟基-1-甲基丙基)乙二胺、N,N,N',N'-四(2-羟基-1,1-二甲基乙基)乙二胺、N,N,N',N'-四(羟甲基)-1,3-丙二胺、N,N,N',N'-四(2-羟乙基)-1,3-丙二胺、N,N,N',N'-四(3羟丙基)-1,3-丙二胺、N,N,N',N'-四(4-羟丁基)-1,3-丙二胺、N,N,N',N'-四(羟甲基)-1,4-丁二胺、N,N,N',N'-四(2-羟乙基)-1,4-丁二胺、N,N,N',N'-四(3-羟丙基)-1,4-丁二胺、N,N,N',N'-四(4-羟丁基)-1,4-丁二胺、N,N,N',N'-四(羟甲基)-1,5-戊二胺、N,N,N',N'-四(2-羟乙基)-1,5-戊二胺、N,N,N',N'-四(3-羟丙基)-1,5-戊二胺、N,N,N',N'-四(4-羟丁基)-1,5-戊二胺、N,N,N',N'-四(羟甲基)-1,5-戊二胺、N,N,N',N'-四(2-羟乙基)-1,5-戊二胺、N,N,N',N'-四(3-羟丙基)-1,5-戊二胺、N,N,N',N'-四(4-羟丁基)-1,5-戊二胺、N,N,N',N'-四(羟甲基)-1,6-己二胺、N,N,N',N'-四(2-羟乙基)-1,6-己二胺、N,N,N',N'-四(3-羟丙基)-1,6-己二胺、N,N,N',N'-四(4-羟丁基)-1,6-己二胺、N,N,N',N'',N''-五(羟甲基)二乙烯三胺、N,N,N',N'',N''-五(2-羟乙基)二乙烯三胺、N,N,N',N'',N''-五(3-羟丙基)二乙烯三胺、N,N,N',N'',N''-五(4-羟丁基)二乙烯三胺、N1,N1,N2,N3,N4,N4-六(羟甲基)三乙烯四胺、N1,N1,N2,N3,N4,N4-六(2-羟乙基)三乙烯四胺、N1,N1,N2,N3,N4,N4-六(3-羟丙基)三乙烯四胺、N1,N1,N2,N3,N4,N5,N5-七(羟甲基)四乙烯五胺、N1,N1,N2,N3,N4,N5,N6,N6-八(羟甲基)五乙烯六胺、N,N'-二(1-羟乙基)-N,N'-二(羟甲基)乙二胺、N,N-二(2-羟乙基)-N',N'-二(羟甲基)乙二胺、N,N-二(3-羟丙基)-N',N'-二(羟甲基)乙二胺、N,N-二(3-羟丙基)-N',N'-二(2-羟乙基)乙二胺、N,N-二(2-羟乙基)-N',N'-二(羟甲基)-1,3-丙二胺、N,N-二(3-羟丙基)-N',N'-二(2-羟乙基)-1,3-丙二胺、N,N'-二(1-羟丙基)-N,N'-二(羟甲基)-1,3-丙二胺、N,N,N'',N''-四(2-羟乙基)-N'-羟甲基二乙烯三胺、N,N,N4,N4-四(2-羟乙基)-N2,N3-二(羟甲基)三乙烯四胺或N,N-二(3-羟丙基)-N'',N''-二(2-羟乙基)-N'-羟甲基二乙烯三胺中的一种或几种。
4.根据权利要求3所述的镀金液，其特征在于，所述胺类化合物为N,N,N',N'-四(羟甲基)乙二胺、N,N,N',N'-四(2-羟乙基)乙二胺、N,N,N',N'-四(3-羟丙基)乙二胺、N,N,N',N'-四(4-羟丁基)乙二胺、N,N,N',N'-四(2-羟乙基)-1,3-丙二胺、N,N,N',N'-四(羟甲基)-1,4-丁二胺、N,N,N,'N'-四(2-羟乙基)-1,4-丁二胺、N,N,N',N'',N''-五(羟甲基)二乙烯三胺、N,N,N',N'',N''-五(2-羟乙基)二乙烯三胺、N,N,N',N'',N''-五(3-羟丙基)二乙烯三胺、N1,N1,N2,N3,N4,N4-六(2-羟乙基)三乙烯四胺、N,N-二(2-羟乙基)-N',N'-二(羟甲基)乙二胺、N,N-二(3-羟丙基)-N',N'-二(羟甲基)乙二胺、N,N-二(2-羟乙基)-N',N'-二(羟甲基)-1,3-丙二胺、N,N,N'',N''-四(2-羟乙基)-N'-羟甲基二乙烯三胺或N,N-二(3-羟丙基)-N'',N''-二(2-羟乙基)-N'-羟甲基二乙烯三胺中的一种或几种。
5.根据权利要求4所述的镀金液，其特征在于，所述胺类化合物为N,N,N',N'-四(2-羟乙基)-1,3-丙二胺或N,N,N',N'-四(2-羟乙基)-1,4-丁二胺。
6.根据权利要求1-5任一项所述的镀金液，其特征在于，所述胺类化合物的用量为0.1g/l~50g/l。
7.根据权利要求6所述的镀金液，其特征在于，所述胺类化合物的用量为1~20g/l。
8.权利要求1所述的镀金液，其特征在于，所述水溶性金盐选自水溶性非氰金盐或水溶性含氰金盐中的一种或几种，其中金浓度为 0.1~5g/l。
9.根据权利要求8所述的镀金液，其特征在于，所述水溶性非氰金盐选自亚硫酸金钾、亚硫酸金钠、亚硫酸金铵、硫代硫酸金钠、硫代硫酸金钾、硫代硫酸金铵、氯金酸钠、氯金酸钾、氯金酸铵、二氯金酸钠、二氯金酸钾、二氯金酸铵、硫氰酸金钠、硫氰酸金钾、硫氰酸金铵、硫代苹果酸钠、硫代苹果酸钾、硫代苹果酸铵、柠檬酸金钾、柠檬酸金钠或柠檬酸金铵中的一种或多种；所述水溶性含氰金盐选自氰化亚金钾、氰化亚金钠、氰化亚金铵、四氰合金酸钾、四氰合金酸钠或四氰合金酸铵中的一种或多种。
10.根据权利要求1所述的镀金液，其特征在于，所述屏蔽剂选自柠檬酸、柠檬酸钠、柠檬酸铵、柠檬酸钾、酒石酸、酒石酸钠、酒石酸钾、酒石酸铵、苹果酸、苹果酸钠、苹果酸钾、苹果酸铵、乳酸、乳酸钠、乳酸钾、乳酸铵、葡萄糖-δ-内酯、葡萄糖酸或琥珀酸羟基乙酸的一种或多种，用量为0~50g/l。
11.根据权利要求1所述的镀金液，其特征在于，还包括络合剂，所述络合剂选自氰化钠、氰化钾、亚硫酸氢钠、焦亚硫酸钠、亚硫酸钾、亚硫酸铵、硫代硫酸钠、硫代硫酸钾或硫代硫酸铵中的一种或多种，用量为0~100g/l。
12.根据权利要求1所述的镀金液，其特征在于，还包括稳定剂，所述稳定剂选自氮基三乙酸、次氮基三丙酸、甘氨酸、亚氨基乙二酸、乙二胺四乙酸、四二胺四丙酸、羟基乙二胺四乙酸、双羟基乙二胺四乙酸、羟乙基乙二胺三乙酸、二羟乙基乙二胺二乙酸、丙二胺四乙酸、二亚乙基三胺五乙酸、三亚乙基四安六乙酸、双甘氨肽、双羟乙基甘氨酸、羟乙基亚氨基乙二酸及其碱金属盐或铵盐，以及甲胺、乙胺、丙胺、丁胺、乙二胺、丙二胺、1,3-丙二胺、丁二胺、己二胺、庚二胺、二乙烯三胺、三乙烯四胺、四乙烯五胺、五乙烯六胺、四羟基亚乙基二胺、单乙醇胺、双乙醇胺、三乙醇胺、2-巯基苯并噻唑、6-乙氧基-2-巯基苯并噻唑、2-巯基苯并咪唑、2-巯基苯并恶唑、苯并三唑钠、四氢苯并三唑、甲基苯并三唑、硝基苯并三唑、吡啶、联吡啶或氨基吡啶中的一种或多种，用量为0~50g/l。
13.根据权利要求1所述的镀金液，其特征在于，还包括添加剂，所述添加剂选自二乙二醇丁醚、乙二醇丁醚、丙二醇丁醚、乙二醇甲醚、二乙二醇甲醚或二丙二醇甲醚中的一种或多种，用量为0~5g/l。
14.根据权利要求1-13任一项所述的镀金液的制备方法，其特征在于，包括如下步骤：在室温条件下，先将络合剂、屏蔽剂、稳定剂、添加剂、胺类化合物混合均匀，调节pH为6.5-8.5，然后再加入水溶性金盐混合均匀，即得。
CN201710463936.1A 2017-06-19 2017-06-19 一种镀金液及其制备方法 Active CN107190251B (zh)