CN107188537A - A kind of method that dust collected with town pavement sweeper filter cloth bag prepares purple sand process goods of furniture for display rather than for use - Google Patents
A kind of method that dust collected with town pavement sweeper filter cloth bag prepares purple sand process goods of furniture for display rather than for use Download PDFInfo
- Publication number
- CN107188537A CN107188537A CN201710573484.2A CN201710573484A CN107188537A CN 107188537 A CN107188537 A CN 107188537A CN 201710573484 A CN201710573484 A CN 201710573484A CN 107188537 A CN107188537 A CN 107188537A
- Authority
- CN
- China
- Prior art keywords
- dust
- raw ore
- purple sand
- lip river
- boccaro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of method that dust collected with sweeper filter cloth bag prepares purple sand process goods of furniture for display rather than for use, the dust that town pavement sweeper filter cloth bag is collected is poured into washing pool and washed, pulls out after water surface floating object, is filtered, is dried；Angstrom Lip river soil is put into ball mill with hydromica clay, ball milling is carried out, the native hydromica clay slurry in angstrom Lip river is obtained；Boccaro Raw Ore clinker and dust are added in the native hydromica clay slurry in angstrom Lip river, mixed, seals old, is sufficiently stirred for, is pressed into mud bar, mud bar is suppressed repeatedly and seals old, purple sand pug is made；Purple sand pug is made mold base, and is put into electrical kiln and is calcined, cooling, kiln discharge obtains purple sand process goods of furniture for display rather than for use.Advantage is：Technique is simple, and with low cost using road cleaning waste dust as raw material, the red stoneware product of firing is of good quality, and quality is fine and smooth, glossy, no cracking, and good hand touch can be as craft ornament, and makes full use of road cleaning waste dust, economic and environment-friendly.
Description
Technical field
The present invention relates to the side that a kind of dust collected with town pavement sweeper filter cloth bag prepares purple sand process goods of furniture for display rather than for use
Method.
Background technology
Purple sand process goods of furniture for display rather than for use is the ceramic between pottery and porcelain, and it is that pug is made using boccaro ore deposit as raw material
Fire, it has natural in color, and the characteristics of translucency and water colour are good, colour generation is good, feel is fine and smooth is to enjoy people in China
A kind of traditional arts and crafts for liking.
Sweeper is when cleaning town road, and the dust that the filter cloth bags of in-car cleaning systems is collected is without value, again
It is not disposable, arbitrarily stack and easily cause airborne dust, pollute environment.Although dust belongs to soil material with boccaro, with dirt
Soil does not allow easy-formation but for raw material, even if pug is made, and fires product surface and does not have gloss yet, translucency is poor, and water colour is bad, no
The characteristics of with craft ornament.
The content of the invention
Boccaro work is prepared the technical problem to be solved in the present invention is to provide a kind of dust collected with sweeper filter cloth bag
The method of skill goods of furniture for display rather than for use, can make full use of road cleaning waste dust, economic and environment-friendly, and the red stoneware product natural in color fired,
Water colour is good, can be used as craft ornament.
The present invention technical solution be：
A kind of method that dust collected with sweeper filter cloth bag prepares purple sand process goods of furniture for display rather than for use, it is comprised the following steps that：
(1) dust is collected and pre-processed
The dust that town pavement sweeper filter cloth bag is collected is poured into washing pool, and addition accounts for 3 times~5 times of dust quality
Water, stirs in washing pool and is washed for 8 minutes~12 minutes, pulled out after water surface floating object, filtering, dries；
(2) dispensing
According to weight percentage, by boccaro Raw Ore clinker 27%~33%, angstrom Lip river soil 12%~14%, hydromica clay
2%~3%, dust 53%~57% carries out dispensing as raw material, and the granularity of the boccaro Raw Ore clinker is 80 mesh, the dirt
The granularity of soil is the mesh of 40 mesh~60；
(3) pretreatment of angstrom Lip river soil and hydromica clay
Angstrom Lip river soil is put into ball mill with hydromica clay, by the gross mass and the mass ratio of water of angstrom Lip river soil and hydromica clay
100:27~100:30 add water, carry out ball milling, obtain 300 mesh sieve angstrom Lip river soil-hydromica clay slurry；
(4) pug is refined
Boccaro Raw Ore clinker and dust are added in an angstrom Lip river soil-hydromica clay slurry, mixed, old 2 are sealed
Month~3 months, it is sufficiently stirred for；Mud bar is pressed into, is sealed old 8 days~10 days, mud bar is suppressed repeatedly and seals old, is grasped repeatedly
Make 6 times~8 times, purple sand pug is made；
(5) embryo processed and calcine
Mold base is made in purple sand pug, and is put into progress calcining 12 hours in electrical kiln, calcining heat is 1050 DEG C~1100 DEG C, drop
Temperature more than 12 hours to 200 DEG C, kiln discharge obtains purple sand process goods of furniture for display rather than for use.
The boccaro Raw Ore clinker is, by boccaro Raw Ore, to dry carry out weathering to boccaro Raw Ore at room temperature, by wind
Boccaro Raw Ore after change is impregnated with clear water, is placed 24h~36h, is dried at 80 DEG C~100 DEG C and it is cured, to wind
Raw Ore after change is cured 3 times~5 times repeatedly.
Silica quality percentage composition is 30%~40%, aluminium dioxide weight/mass percentage composition in the boccaro Raw Ore
It is 30%~40% for 10%~15%, ferrous oxide weight/mass percentage composition.
Angstrom Lip river soil, also known as halloysite, chemical general formula：Al2O32SiO2nH2O (n=4~6), monoclinic system or
Anorthic system, profile is in fine blank pipe shape or curling sheet；Structure is close with high territory, but there is intermediary water, and lattice is in c-axis side
Increase to thickness.
Beneficial effects of the present invention：
Technique is simple, and with low cost using road cleaning waste dust as raw material, the red stoneware product of firing is of good quality, and quality is fine and smooth,
It is glossy, no cracking, good hand touch can be as craft ornament, and makes full use of road cleaning waste dust, economic and environment-friendly.
Embodiment
Embodiment 1
(1) dust is collected and pre-processed
The dust that town pavement sweeper filter cloth bag is collected is poured into washing pool, the water for accounting for 3 times of dust quality is added, in water
Stirring is washed for 8 minutes in wash pool, is pulled out after water surface floating object, is filtered, is dried；
(2) boccaro Raw Ore is cured
Boccaro shale is chosen as Raw Ore, dioxide-containing silica is that 40wt%, aluminium dioxide content are in Boccaro shale
10wt%, ferrous oxide content are that 40wt%, content of titanium dioxide are that 0.2wt%, calcium oxide content are 1.5wt%；At room temperature
It is 10wt% to dry and weathering water content into boccaro Raw Ore is carried out to boccaro Raw Ore, by the boccaro Raw Ore after weathering with clearly
Water saturates, place 24h, are dried at 80 DEG C and it is cured, the Raw Ore after weathering cured repeatedly 5 times；The boccaro
Raw ore is red boccaro raw ore, purple boccaro raw ore, black boccaro raw ore or green boccaro raw ore；
(3) dispensing
Weigh raw material：Boccaro Raw Ore clinker 30kg, angstrom Lip river soil 14kg, hydromica clay 2kg, dust 54kg, the boccaro are former
The granularity for expecting ore deposit clinker is 80 mesh, and the granularity of the dust is the mesh of 40 mesh~60；
(4) pretreatment of angstrom Lip river soil and hydromica clay
Angstrom Lip river a soil 14kg and hydromica clay 2kg are put into ball mill, 4.32kg water is added, ball milling is carried out, obtained 300 mesh
Sieve angstrom Lip river soil-hydromica clay slurry；
(5) pug is refined
Boccaro Raw Ore clinker 30kg and dust 55kg are added in an angstrom Lip river soil-hydromica clay slurry, mixed, sealing
Old 2 months, it is sufficiently stirred for；Mud bar is pressed into, is sealed old 8 days, mud bar is suppressed repeatedly and seals old, is operated 6 times repeatedly,
Purple sand pug is made；
(6) embryo processed and calcine
Mold base is made in purple sand pug, and is put into progress calcining 12 hours in electrical kiln, calcining heat is 1080 DEG C, is cooled 12 hours
To 200 DEG C, kiln discharge obtains purple sand process goods of furniture for display rather than for use.The purple sand process goods of furniture for display rather than for use is of good quality, and quality is fine and smooth, glossy, no cracking, hand
Feel, there is fine particle sense.
Embodiment 2
(1) dust is collected and pre-processed
The dust that town pavement sweeper filter cloth bag is collected is poured into washing pool, the water for accounting for 5 times of dust quality is added, in water
Stirring is washed for 12 minutes in wash pool, is pulled out after water surface floating object, is filtered, is dried；
(2) boccaro Raw Ore is cured
Boccaro shale is chosen as Raw Ore, dioxide-containing silica is that 35wt%, aluminium dioxide content are in Boccaro shale
12wt%, ferrous oxide content are that 35wt%, content of titanium dioxide are that 0.3wt%, calcium oxide content are 1.2wt%, at room temperature
It is 10wt% to dry and weathering water content into boccaro Raw Ore is carried out to boccaro Raw Ore, by the boccaro Raw Ore after weathering with clearly
Water saturates, place 36h, are dried at 100 DEG C and it is cured, the Raw Ore after weathering cured repeatedly 3 times；
(3) dispensing
Weigh raw material：Boccaro Raw Ore clinker 33kg, angstrom Lip river soil 12kg, hydromica clay 2kg, dust 53kg, the boccaro are former
The granularity for expecting ore deposit clinker is 80 mesh, and the granularity of the dust is the mesh of 40 mesh~60；
(4) pretreatment of angstrom Lip river soil and hydromica clay
Angstrom Lip river a soil 12kg and hydromica clay 2kg are put into ball mill, 4.2kg water is added, ball milling is carried out, obtained 300 mesh
Sieve angstrom Lip river soil-hydromica clay slurry；
(5) pug is refined
Boccaro Raw Ore clinker 33kg and dust 53kg are added in an angstrom Lip river soil-hydromica clay slurry, mixed, sealing
Old 3 months, it is sufficiently stirred for；Mud bar is pressed into, is sealed old 10 days, mud bar is suppressed repeatedly and seals old, 7 are operated repeatedly
It is secondary, purple sand pug is made；
(6) embryo processed and calcine
Mold base is made in purple sand pug, and is put into progress calcining 12 hours in electrical kiln, calcining heat is 1050 DEG C, is cooled 14 hours
To 200 DEG C, kiln discharge obtains purple sand process goods of furniture for display rather than for use.The purple sand process goods of furniture for display rather than for use is of good quality, and quality is fine and smooth, glossy, no cracking, hand
Feel, there is fine particle sense.
Embodiment 3
(1) dust is collected and pre-processed
The dust that town pavement sweeper filter cloth bag is collected is poured into washing pool, the water for accounting for 4 times of dust quality is added, in water
Stirring is washed for 10 minutes in wash pool, is pulled out after water surface floating object, is filtered, is dried；
(2) boccaro Raw Ore is cured
Boccaro shale is chosen as Raw Ore, dioxide-containing silica is that 30wt%, aluminium dioxide content are in Boccaro shale
15wt%, ferrous oxide content are that 30wt%, content of titanium dioxide are that 0.5wt%, calcium oxide content are 0.5wt%；At room temperature
It is 10wt% to dry and weathering water content into boccaro Raw Ore is carried out to boccaro Raw Ore, by the boccaro Raw Ore after weathering with clearly
Water saturates, place 30h, are dried at 90 DEG C and it is cured, the Raw Ore after weathering cured repeatedly 4 times；
(3) dispensing
Weigh raw material：Boccaro Raw Ore clinker 27kg, angstrom Lip river soil 13kg, hydromica clay 3kg, dust 57kg, the boccaro are former
The granularity for expecting ore deposit clinker is 80 mesh, and the granularity of the dust is the mesh of 40 mesh~60；
(4) pretreatment of angstrom Lip river soil and hydromica clay
Angstrom Lip river a soil 13kg and hydromica clay 3kg are put into ball mill, 4.5kg water is added, ball milling is carried out, obtained 300 mesh
Sieve angstrom Lip river soil-hydromica clay slurry；
(5) pug is refined
Boccaro Raw Ore clinker 27kg and dust 57kg are added in an angstrom Lip river soil-hydromica clay slurry, mixed, sealing
Old 2.5 months, it is sufficiently stirred for；Mud bar is pressed into, is sealed old 9 days, mud bar is suppressed repeatedly and seals old, 8 are operated repeatedly
It is secondary, purple sand pug is made；
(6) embryo processed and calcine
Mold base is made in purple sand pug, and is put into progress calcining 12 hours in electrical kiln, calcining heat is 1100 DEG C, is cooled 12 hours
To 200 DEG C, kiln discharge obtains purple sand process goods of furniture for display rather than for use.The purple sand process goods of furniture for display rather than for use is of good quality, and quality is fine and smooth, glossy, no cracking, hand
Feel, there is fine particle sense.
Comparative example 1
(1) dust is collected and pre-processed
The dust that town pavement sweeper filter cloth bag is collected is poured into washing pool, the water for accounting for 5 times of dust quality is added, in water
Stirring is washed for 12 minutes in wash pool, is pulled out after water surface floating object, is filtered, is dried；
(2) boccaro Raw Ore is cured
By boccaro Raw Ore, it is 10wt% to dry weathering water content into boccaro Raw Ore is carried out to boccaro Raw Ore at room temperature,
Boccaro Raw Ore after weathering is impregnated with clear water, 24h is placed, is dried at 100 DEG C and it is cured, to the original after weathering
Material ore deposit is cured 5 times repeatedly；
(3) dispensing
By boccaro Raw Ore clinker 1.8kg, angstrom Lip river soil a 1.2kg, hydromica clay 0.8kg and dust 6.2kg are carried out as raw material
Dispensing, the granularity of the boccaro Raw Ore clinker is 80 mesh, and the granularity of the dust is the mesh of 40 mesh~60；
(4) pretreatment of angstrom Lip river soil and hydromica clay
Angstrom Lip river a soil 1.2kg and hydromica clay 0.8kg are put into ball mill, 0.54L water is added, ball milling is carried out, obtained 300
Mesh sieve angstrom Lip river soil-hydromica clay slurry；
(5) pug is refined
Boccaro Raw Ore clinker and dust are added in an angstrom Lip river soil-hydromica clay slurry, mixed, old 3 are sealed
Month, it is sufficiently stirred for；Mud bar is pressed into, is sealed old 8 days, mud bar is suppressed repeatedly and seals old, operates 8 times repeatedly, purple is made
Sand pug；
(6) embryo processed and calcine
Mold base is made in purple sand pug, and is put into progress calcining 12 hours in electrical kiln, calcining heat is 1100 DEG C, and cooling is obtained
Product.The product surface is coarse, matt, and after the completion of firing, part easily produces slight crack, the spy without handicraft
Point.
Comparative example 2
The method be the same as Example 1 of purple sand pug is prepared, the black purple sand pug of preparation is made mold base, and is put into electrical kiln and is forged
Burn, calcining heat is 1150 DEG C, cooling obtains purple sand process goods of furniture for display rather than for use.There is obvious bulky grain on the purple sand process goods of furniture for display rather than for use surface, and
And have foaming phenomena on craft ornament surface.
Claims (3)
1. a kind of method that dust collected with sweeper filter cloth bag prepares purple sand process goods of furniture for display rather than for use, it is characterized in that：
Comprise the following steps that：
(1) dust is collected and pre-processed
The dust that town pavement sweeper filter cloth bag is collected is poured into washing pool, and addition accounts for 3 times~5 times of dust quality
Water, stirs in washing pool and is washed for 8 minutes~12 minutes, pulled out after water surface floating object, filtering, dries；
(2) dispensing
According to weight percentage, by boccaro Raw Ore clinker 27%~33%, angstrom Lip river soil 12%~14%, hydromica clay
2%~3%, dust 53%~57% carries out dispensing as raw material, and the granularity of the boccaro Raw Ore clinker is 80 mesh, the dirt
The granularity of soil is the mesh of 40 mesh~60；
(3) pretreatment of angstrom Lip river soil and hydromica clay
Angstrom Lip river soil is put into ball mill with hydromica clay, by the gross mass and the mass ratio of water of angstrom Lip river soil and hydromica clay
100:27~100:30 add water, carry out ball milling, obtain 300 mesh sieve angstrom Lip river soil-hydromica clay slurry；
(4) pug is refined
Boccaro Raw Ore clinker and dust are added in an angstrom Lip river soil-hydromica clay slurry, mixed, old 2 are sealed
Month~3 months, it is sufficiently stirred for；Mud bar is pressed into, is sealed old 8 days~10 days, mud bar is suppressed repeatedly and seals old, is grasped repeatedly
Make 6 times~8 times, purple sand pug is made；
(5) embryo processed and calcine
Mold base is made in purple sand pug, and is put into progress calcining 12 hours in electrical kiln, calcining heat is 1050 DEG C~1100 DEG C, drop
Temperature more than 12 hours to 200 DEG C, kiln discharge obtains purple sand process goods of furniture for display rather than for use.
2. the method that the dust according to claim 1 collected with sweeper filter cloth bag prepares purple sand process goods of furniture for display rather than for use, its
It is characterized in：The boccaro Raw Ore clinker is, by boccaro Raw Ore, to dry carry out weathering to boccaro Raw Ore at room temperature, by weathering
Boccaro Raw Ore afterwards is impregnated with clear water, is placed 24h~36h, is dried at 80 DEG C~100 DEG C and it is cured, to weathering
Raw Ore afterwards is cured 3 times~5 times repeatedly.
3. the method that the dust according to claim 1 collected with sweeper filter cloth bag prepares purple sand process goods of furniture for display rather than for use, its
It is characterized in：Silica quality percentage composition is 30%~40%, aluminium dioxide weight/mass percentage composition in the boccaro Raw Ore
It is 30%~40% for 10%~15%, ferrous oxide weight/mass percentage composition.