CN107640943A - A kind of Self-decorating regeneration aggregate porous concrete product and preparation method thereof - Google Patents
A kind of Self-decorating regeneration aggregate porous concrete product and preparation method thereof Download PDFInfo
- Publication number
- CN107640943A CN107640943A CN201711015611.3A CN201711015611A CN107640943A CN 107640943 A CN107640943 A CN 107640943A CN 201711015611 A CN201711015611 A CN 201711015611A CN 107640943 A CN107640943 A CN 107640943A
- Authority
- CN
- China
- Prior art keywords
- aggregate
- self
- weight
- regeneration aggregate
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of Self-decorating regeneration aggregate porous concrete product and preparation method thereof, it is characterized in that：The product by regeneration aggregate pervious concrete basic unit with regeneration aggregate self-chambering finish coat is compound forms；Concrete or/and mortar class construction refuse regenerated aggregate, particle diameter≤2.36mm concrete or/and mortar class construction refuse regenerated aggregate and the water mixing that the basic unit is 2.36~9.5mm by Portland cement, particle diameter form；The surface layer by one or both of white cement, particle diameter≤2.36mm sintered brick and tile, glass and ceramic-like thing mixed above construction refuse regenerated decoration aggregate, and water mixing composition.Preparation method is：Basic unit and face stock are mixed respectively, then it is layered mat formation, be press-formed base, the demoulding, natural curing i.e. obtained.Inventive article has good mechanical property, water permeability and decorative effect, practical.
Description
Technical field
The invention belongs to the utilization of discarded object and the preparation of plastics products for building, and it is permeable to be related to a kind of Self-decorating regeneration aggregate
Concrete product and preparation method thereof.Self-decorating regeneration aggregate porous concrete product of the present invention is suitable for (sponge) urban road
Construction material.
Background technology
At present, China is in the peak period of socio-economic development critical stage and urbanization process, and country sets to basis
The continuous acceleration for applying investment and urbanization process brings two problems：When new construction to sandstone aggregate consumption maintain it is very high
Level, according to statistics, China's sandstone is produced per year, sales volume is more than 10,000,000,000 tons；Second, existent building transformation, dismounting produce a large amount of buildings
Rubbish, according to conservative estimation, following 10 years, China produces building waste every year will be more than 1,500,000,000 tons.In the prior art, sandstone bone
Material relies primarily on exploitation natural resources；And based on building waste is more to fill, heap is abandoned.Construction refuse regenerated, circulating and recovering is arrived
It is to alleviate the most effective approach that sandstone aggregate relied on natural resources and solved building waste pollution in building.However, building rubbish
Rubbish source is complex, mainly includes sintered brick and tile, glass, ceramics, concrete, mortar etc..Wherein concrete, mortar class are built
Building refuse can replace the use of parts of traditional sandstone without producing significant impact to concrete performance after broken processing；Sintering
Brick and tile class building waste is sintered article, and amount is big, Kong Duo, water imbibition is big, crush values are big, is not suitable as structural concrete aggregate
Large dosage uses；Glass, ceramics etc. are fine and close smooth, poor with concrete gel material matrix associativity.Building is limited above
High-valued, scale application of the garbage regeneration aggregate in commerical ready-mixed concrete.
In recent years, to solve the modern "urban disease"s such as waterlogging, level of ground water decline and heat island, country, which proposes, builds sponge city
City's strategy.Pervious concrete and its product have preferable mechanical property, water permeability and dicoration, turn into sponge urban road
The material of main part of construction.In the prior art, porous concrete product is mainly formed by porous base course and architectural surface are compound, permeable
Basic unit is formulated using Portland cement with conventional sandstone aggregate, and architectural surface is then generally required using white cement as gelling
Material, routine building are aggregate with sand and are aided with a variety of colors commercial pigments to reach decorative effect.Also there is technology using naturally
Color sand is that aggregate replaces routine building sand.Easily faded by facing decoration admixture, pigment of commercial pigments, and commercial pigments
It is expensive；Natural color smalt is natural locked resource, and collection can welding.
The content of the invention
The purpose of the present invention is intended to overcome in the prior art that construction refuse resource utilization rate is high, sandstone aggregate for building
A kind of deficiency that commercial pigments fugitive color, natural colour sand collection are not easy in short supply and porous concrete product, there is provided Self-decorating
Regeneration aggregate porous concrete product and preparation method thereof.Self-decorating regeneration aggregate porous concrete product of the present invention has preferable
Mechanical property, water permeability and decorative effect；In addition, surface layer is using sintered brick and tile, glass, the construction refuse regenerated bone of ceramic-like
Expect that, without filling any commercial pigments, facing decoration is natural, beautiful, generous, colour-fast, practical to decorate aggregate.
Present disclosure is：A kind of Self-decorating regeneration aggregate porous concrete product, it is characterized in that：The Self-decorating regenerates
The regeneration aggregate pervious concrete basic unit that aggregate porous concrete product is 50~65mm by thickness and thickness are 10~15mm's
The compound composition of regeneration aggregate self-chambering finish coat；
The regeneration aggregate pervious concrete basic unit by the parts by weight of Portland cement 20, particle diameter be 2.36mm~
9.5mm concrete or/and the parts by weight of mortar class construction refuse regenerated aggregate 56~72, particle diameter≤2.36mm concrete or/
Mix and form with the component raw material of the parts by weight of mortar class construction refuse regenerated aggregate 8~24 and the parts by weight of water 8；
The regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20, particle diameter≤2.36mm sintered brick and tile, glass, with
And the construction refuse regenerated parts by weight of decoration aggregate 80~120 of one or both of ceramic-like thing mixed above, and water 10
The component raw material mixing composition of parts by weight.
In present disclosure：The preparation method of the construction refuse regenerated aggregate is：Building waste is reclaimed, sub-elected
Concrete, mortar class building waste and sintered brick and tile, glass, ceramic-like building waste；Concrete, mortar class building waste are broken
It is broken, 2.36mm~9.5mm and≤2.36mm particle are filtered out respectively, as the regeneration aggregate pervious concrete basic unit with building
Building refuse regeneration aggregate；By sintered brick and tile, glass, ceramic-like construction waste crushing ,≤2.36mm particle is filtered out, as institute
Regeneration aggregate self-chambering finish coat is stated with construction refuse regenerated decoration aggregate.
In present disclosure：The strength grade of the Portland cement is not less than 42.5MPa.Such as：Southwestern water
Mud P.O425 Portland cements；The high victory P.O425R Portland cements in Sichuan；Lafarge SA's P.O525R ordinary silicons
Acid salt cement.
In present disclosure：The white cement is the P.W.52.5 levels of A Erbo Portlands (Anqing) Co., Ltd production
White cement (A Erbo boards) or P.W.42.5 levels white cement (A Erbo boards), preferably P.W.52.5 levels white cement (A Erbo boards).
In another content of the present invention：A kind of preparation method of Self-decorating regeneration aggregate porous concrete product, its feature
It is that step is：
A, dispensing：By the parts by weight of Portland cement 20, the concrete or/and mortar that particle diameter is 2.36mm~9.5mm
The parts by weight of class construction refuse regenerated aggregate 56~72, particle diameter≤2.36mm concrete or/and the construction refuse regenerated bone of mortar class
The proportioning of 8~24 parts by weight of material and the parts by weight of water 8 takes each component raw material, the original as regeneration aggregate pervious concrete basic unit
Material；
It is more than one or both of particle diameter≤2.36mm sintered brick and tiles, glass, ceramic-like mixed by the parts by weight of white cement 20
The construction refuse regenerated parts by weight of decoration aggregate 80~120 of compound, and the proportioning of the parts by weight of water 10 take each component raw material, as
The raw material of regeneration aggregate self-chambering finish coat；
B, it is stirred：The preparation raw material weighed by step a, respectively by the original of regeneration aggregate pervious concrete basic unit
Material, the raw material of regeneration aggregate self-chambering finish coat mix, and regeneration aggregate pervious concrete basic unit mixture, regeneration are made respectively
Aggregate self-chambering finish coat mixture；
C, cloth：By regeneration aggregate self-chambering finish coat mixture making in steel die bottom, placement thickness be 10mm~
15mm；Again by regeneration aggregate pervious concrete basic unit mixture making on regeneration aggregate self-chambering finish coat mixture it is compound,
Placement thickness is 50mm~65mm, obtains two-layer compound mixture；
D, it is molded：It is with 2~5MPa pressure that step c two-layer compound mixture is compressing again, the demoulding, shaping is made
Base substrate；
E, conserve：By molding blank be placed in the environment of 15~25 DEG C of temperature, humidity 50%~90% conserve 28d (my god),
Self-decorating regeneration aggregate porous concrete product is made.
In another content of the present invention：The preparation method of the construction refuse regenerated aggregate is：Building waste is reclaimed, point
Select concrete, mortar class building waste and sintered brick and tile, glass, ceramic-like building waste；By concrete, mortar class building rubbish
Rubbish crushes, and 2.36mm~9.5mm and≤2.36mm particle is filtered out respectively, as the regeneration aggregate pervious concrete basic unit
Use construction refuse regenerated aggregate；By sintered brick and tile, glass, ceramic-like construction waste crushing ,≤2.36mm particle is filtered out, is made
It is the regeneration aggregate self-chambering finish coat with construction refuse regenerated decoration aggregate.
In another content of the present invention：The strength grade of the Portland cement is not less than 42.5MPa.Such as：West
Southern cement P.O425 Portland cements；The high victory P.O425R Portland cements in Sichuan；Lafarge SA P.O525R is general
Logical portland cement.
In another content of the present invention：The white cement is the production of A Erbo Portlands (Anqing) Co., Ltd
P.W.52.5 levels white cement (A Erbo boards) or P.W.42.5 levels white cement (A Erbo boards), preferably P.W.52.5 levels white cement
(A Erbo boards).
Compared with prior art, the present invention has following features and beneficial effect：
(1) preparation of Self-decorating regeneration aggregate porous concrete product basic unit of the present invention and surface layer is all using building waste
Regeneration aggregate is aggregate, and the comprehensive utilization for the huge building waste of discharge capacity provides suitable approach, while has saved day
Right sandstone aggregate, the production of natural sand stone aggregate is avoided to environmental disruption；
(2) using the present invention, the features such as the intrinsic water imbibition of construction refuse regenerated aggregate, porous, preparation is become
The good candidate aggregate of pervious concrete and its product；In addition, the building waste itself such as sintered brick and tile, glass, ceramics has face
Color, Self-decorating positive effect, commercial pigments and natural colour sand can be replaced to be used to decorate porous concrete product surface layer；The present invention
Middle regeneration aggregate self-chambering finish coat decorates aggregate using sintered brick and tile, glass, ceramic-like building waste as regeneration, without adding industry
Pigment or natural colour sand, Self-decorating effect is directly realized, while the regeneration such as sintered brick and tile, glass, ceramics decoration aggregate makes
Discolouration phenomena will not occur during, facing decoration is natural, beautiful, generous, colour-fast；
(3) Self-decorating regeneration aggregate porous concrete product of the present invention has preferable mechanical property, water permeability and dress
Effect is adornd, particularly suitable for sponge urban water-through road construction, from building waste processing and recycling, natural resources saving and permeable
From the point of view of in terms of the performance of concrete product decorative effect, the present invention has very great society, economy and environmental benefit；
(4) product preparation process of the present invention is simple, and process is easy, and easily operation, practical.
Embodiment
The invention will be further described for example given below plan, but is not to be construed as to the scope of the present invention
Limitation, some nonessential improvement and tune that person skilled in art makes according to the content of the invention described above to the present invention
It is whole, still fall within protection scope of the present invention.
Embodiment 1：
A kind of Self-decorating regeneration aggregate porous concrete product, includes regeneration aggregate pervious concrete basic unit and regeneration aggregate
Self-chambering finish coat.Wherein regeneration aggregate pervious concrete basic unit is mixed by the parts by weight of Portland cement 20,2.36mm~9.5mm
Solidifying soil, the parts by weight of mortar class construction refuse regenerated aggregate 56 ,≤2.36mm concrete, the weight of mortar class construction refuse regenerated aggregate 24
Measure the component raw material mixing composition of part and the parts by weight of water 8；Wherein regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20 ,≤
The component of the construction refuse regenerated decoration parts by weight of aggregate 100 of 2.36mm sintered brick and tiles, glass, ceramic-like and the parts by weight of water 10 is former
Material mixing composition.
The preparation method of Self-decorating regeneration aggregate porous concrete product is：
1) dispensing：By the parts by weight of Portland cement 20,2.36mm~9.5mm concrete, mortar class building waste again
The parts by weight of raw aggregate 56 ,≤2.36mm concrete, the parts by weight of mortar class construction refuse regenerated aggregate 24 and the parts by weight of water 8 are matched somebody with somebody
Than taking each component raw material, as regeneration aggregate pervious concrete basic unit raw material；By the parts by weight of white cement 20 ,≤2.36mm fired bricks
Watt, the proportioning of the construction refuse regenerated decoration parts by weight of aggregate 100 of glass, ceramic-like and the parts by weight of water 10 take each component raw material,
As regeneration aggregate Self-decorating face stock；
2) stir：Preparation raw material is weighed by step 1), respectively by regeneration aggregate pervious concrete basic unit raw material, Regenerated Bone
Expect that Self-decorating face stock mixes, regeneration aggregate pervious concrete basic unit's mixture and regeneration aggregate Self-decorating are made respectively
Surface layer mixture；
3) cloth：Regeneration aggregate self-chambering finish coat mixture making is not less than in steel die bottom, placement thickness
10mm, then by regeneration aggregate pervious concrete basic unit mixture making on surface layer mixture；
4) it is molded：It is compressing with 2~5MPa pressure, the demoulding；
5) conserve：Molding blank is not less than in 50% environment in 20 DEG C of temperature, humidity conserves 28d, that is, Self-decorating is made again
Raw aggregate porous concrete product.
Embodiment 2：
A kind of Self-decorating regeneration aggregate porous concrete product, includes regeneration aggregate pervious concrete basic unit and regeneration aggregate
Self-chambering finish coat.Wherein regeneration aggregate pervious concrete basic unit is mixed by the parts by weight of Portland cement 20,2.36mm~9.5mm
Solidifying soil, the parts by weight of mortar class construction refuse regenerated aggregate 64 ,≤2.36mm concrete, the weight of mortar class construction refuse regenerated aggregate 16
Measure the component raw material mixing composition of part and the parts by weight of water 8；Wherein regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20 ,≤
The component of the construction refuse regenerated decoration parts by weight of aggregate 100 of 2.36mm sintered brick and tiles, glass, ceramic-like and the parts by weight of water 10 is former
Material mixing composition.
The preparation method of Self-decorating regeneration aggregate porous concrete product is：
1) dispensing：By the parts by weight of Portland cement 20,2.36mm~9.5mm concrete, mortar class building waste again
The parts by weight of raw aggregate 64 ,≤2.36mm concrete, the parts by weight of mortar class construction refuse regenerated aggregate 16 and the parts by weight of water 8 are matched somebody with somebody
Than taking each component raw material, as regeneration aggregate pervious concrete basic unit raw material；By the parts by weight of white cement 20 ,≤2.36mm fired bricks
Watt, the proportioning of the construction refuse regenerated decoration parts by weight of aggregate 100 of glass, ceramic-like and the parts by weight of water 10 take each component raw material,
As regeneration aggregate Self-decorating face stock；
2) stir：Preparation raw material is weighed by step 1), respectively by regeneration aggregate pervious concrete basic unit raw material, Regenerated Bone
Expect that Self-decorating face stock mixes, regeneration aggregate pervious concrete basic unit's mixture and regeneration aggregate Self-decorating are made respectively
Surface layer mixture；
3) cloth：Regeneration aggregate self-chambering finish coat mixture making is not less than in steel die bottom, placement thickness
10mm, then by regeneration aggregate pervious concrete basic unit mixture making on surface layer mixture；
4) it is molded：It is compressing with 2~5MPa pressure, the demoulding；
5) conserve：Molding blank is not less than in 50% environment in 20 DEG C of temperature, humidity conserves 28d, that is, Self-decorating is made again
Raw aggregate porous concrete product.
Embodiment 3：
A kind of Self-decorating regeneration aggregate porous concrete product, includes regeneration aggregate pervious concrete basic unit and regeneration aggregate
Self-chambering finish coat.Wherein regeneration aggregate pervious concrete basic unit is mixed by the parts by weight of Portland cement 20,2.36mm~9.5mm
Solidifying soil, the parts by weight of mortar class construction refuse regenerated aggregate 72 ,≤2.36mm concrete, the weight of mortar class construction refuse regenerated aggregate 8
Measure the component raw material mixing composition of part and the parts by weight of water 8；Wherein regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20 ,≤
The component of the construction refuse regenerated decoration parts by weight of aggregate 100 of 2.36mm sintered brick and tiles, glass, ceramic-like and the parts by weight of water 10 is former
Material mixing composition.
The preparation method of Self-decorating regeneration aggregate porous concrete product is：
1) dispensing：By the parts by weight of Portland cement 20,2.36mm~9.5mm concrete, mortar class building waste again
The parts by weight of raw aggregate 72 ,≤2.36mm concrete, the parts by weight of mortar class construction refuse regenerated aggregate 8 and the parts by weight of water 8 are matched somebody with somebody
Than taking each component raw material, as regeneration aggregate pervious concrete basic unit raw material；By the parts by weight of white cement 20 ,≤2.36mm fired bricks
Watt, the proportioning of the construction refuse regenerated decoration parts by weight of aggregate 100 of glass, ceramic-like and the parts by weight of water 10 take each component raw material,
As regeneration aggregate Self-decorating face stock；
2) stir：Preparation raw material is weighed by step 1), respectively by regeneration aggregate pervious concrete basic unit raw material, Regenerated Bone
Expect that Self-decorating face stock mixes, regeneration aggregate pervious concrete basic unit's mixture and regeneration aggregate Self-decorating are made respectively
Surface layer mixture；
3) cloth：Regeneration aggregate self-chambering finish coat mixture making is not less than in steel die bottom, placement thickness
10mm, then by regeneration aggregate pervious concrete basic unit mixture making on surface layer mixture；
4) it is molded：It is compressing with 2~5MPa pressure, the demoulding；
5) conserve：Molding blank is not less than in 50% environment in 20 DEG C of temperature, humidity conserves 28d, that is, Self-decorating is made again
Raw aggregate porous concrete product.
Embodiment 4：
A kind of Self-decorating regeneration aggregate porous concrete product, includes regeneration aggregate pervious concrete basic unit and regeneration aggregate
Self-chambering finish coat.Wherein regeneration aggregate pervious concrete basic unit is mixed by the parts by weight of Portland cement 20,2.36mm~9.5mm
Solidifying soil, the parts by weight of mortar class construction refuse regenerated aggregate 64 ,≤2.36mm concrete, the weight of mortar class construction refuse regenerated aggregate 16
Measure the component raw material mixing composition of part and the parts by weight of water 8；Wherein regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20 ,≤
The component of the construction refuse regenerated decoration parts by weight of aggregate 80 of 2.36mm sintered brick and tiles, glass, ceramic-like and the parts by weight of water 10 is former
Material mixing composition.
The preparation method of Self-decorating regeneration aggregate porous concrete product is：
1) dispensing：By the parts by weight of Portland cement 20,2.36mm~9.5mm concrete, mortar class building waste again
The parts by weight of raw aggregate 64 ,≤2.36mm concrete, the parts by weight of mortar class construction refuse regenerated aggregate 16 and the parts by weight of water 8 are matched somebody with somebody
Than taking each component raw material, as regeneration aggregate pervious concrete basic unit raw material；By the parts by weight of white cement 20 ,≤2.36mm fired bricks
Watt, the proportioning of the construction refuse regenerated decoration parts by weight of aggregate 80 of glass, ceramic-like and the parts by weight of water 10 take each component raw material, make
For regeneration aggregate Self-decorating face stock；
2) stir：Preparation raw material is weighed by step 1), respectively by regeneration aggregate pervious concrete basic unit raw material, Regenerated Bone
Expect that Self-decorating face stock mixes, regeneration aggregate pervious concrete basic unit's mixture and regeneration aggregate Self-decorating are made respectively
Surface layer mixture；
3) cloth：Regeneration aggregate self-chambering finish coat mixture making is not less than in steel die bottom, placement thickness
10mm, then by regeneration aggregate pervious concrete basic unit mixture making on surface layer mixture；
4) it is molded：It is compressing with 2~5MPa pressure, the demoulding；
5) conserve：Molding blank is not less than in 50% environment in 20 DEG C of temperature, humidity conserves 28d, that is, Self-decorating is made again
Raw aggregate porous concrete product.
Embodiment 5：
A kind of Self-decorating regeneration aggregate porous concrete product, includes regeneration aggregate pervious concrete basic unit and regeneration aggregate
Self-chambering finish coat.Wherein regeneration aggregate pervious concrete basic unit is mixed by the parts by weight of Portland cement 20,2.36mm~9.5mm
Solidifying soil, the parts by weight of mortar class construction refuse regenerated aggregate 64 ,≤2.36mm concrete, the weight of mortar class construction refuse regenerated aggregate 16
Measure the component raw material mixing composition of part and the parts by weight of water 8；Wherein regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20 ,≤
The component of the construction refuse regenerated decoration parts by weight of aggregate 120 of 2.36mm sintered brick and tiles, glass, ceramic-like and the parts by weight of water 10 is former
Material mixing composition.
The preparation method of Self-decorating regeneration aggregate porous concrete product is：
1) dispensing：By the parts by weight of Portland cement 20,2.36mm~9.5mm concrete, mortar class building waste again
The parts by weight of raw aggregate 64 ,≤2.36mm concrete, the parts by weight of mortar class construction refuse regenerated aggregate 16 and the parts by weight of water 8 are matched somebody with somebody
Than taking each component raw material, as regeneration aggregate pervious concrete basic unit raw material；By the parts by weight of white cement 20 ,≤2.36mm fired bricks
Watt, the proportioning of the construction refuse regenerated decoration parts by weight of aggregate 120 of glass, ceramic-like and the parts by weight of water 10 take each component raw material,
As regeneration aggregate Self-decorating face stock；
2) stir：Preparation raw material is weighed by step 1), respectively by regeneration aggregate pervious concrete basic unit raw material, Regenerated Bone
Expect that Self-decorating face stock mixes, regeneration aggregate pervious concrete basic unit's mixture and regeneration aggregate Self-decorating are made respectively
Surface layer mixture；
3) cloth：Regeneration aggregate self-chambering finish coat mixture making is not less than in steel die bottom, placement thickness
10mm, then by regeneration aggregate pervious concrete basic unit mixture making on surface layer mixture；
4) it is molded：It is compressing with 2~5MPa pressure, the demoulding；
5) conserve：Molding blank is not less than in 50% environment in 20 DEG C of temperature, humidity conserves 28d, that is, Self-decorating is made again
Raw aggregate porous concrete product.
Embodiment 6：
A kind of Self-decorating regeneration aggregate porous concrete product, includes regeneration aggregate pervious concrete basic unit and regeneration aggregate
Self-chambering finish coat.Wherein regeneration aggregate pervious concrete basic unit is mixed by the parts by weight of Portland cement 20,2.36mm~9.5mm
Solidifying soil, the parts by weight of mortar class construction refuse regenerated aggregate 72 ,≤2.36mm concrete, the weight of mortar class construction refuse regenerated aggregate 8
Measure the component raw material mixing composition of part and the parts by weight of water 8；Wherein regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20 ,≤
The component of the construction refuse regenerated decoration parts by weight of aggregate 120 of 2.36mm sintered brick and tiles, glass, ceramic-like and the parts by weight of water 10 is former
Material mixing composition.
The preparation method of Self-decorating regeneration aggregate porous concrete product is：
1) dispensing：By the parts by weight of Portland cement 20,2.36mm~9.5mm concrete, mortar class building waste again
The parts by weight of raw aggregate 72 ,≤2.36mm concrete, the parts by weight of mortar class construction refuse regenerated aggregate 8 and the parts by weight of water 8 are matched somebody with somebody
Than taking each component raw material, as regeneration aggregate pervious concrete basic unit raw material；By the parts by weight of white cement 20 ,≤2.36mm fired bricks
Watt, the proportioning of the construction refuse regenerated decoration parts by weight of aggregate 120 of glass, ceramic-like and the parts by weight of water 10 take each component raw material,
As regeneration aggregate Self-decorating face stock；
2) stir：Preparation raw material is weighed by step 1), respectively by regeneration aggregate pervious concrete basic unit raw material, Regenerated Bone
Expect that Self-decorating face stock mixes, regeneration aggregate pervious concrete basic unit's mixture and regeneration aggregate Self-decorating are made respectively
Surface layer mixture；
3) cloth：Regeneration aggregate self-chambering finish coat mixture making is not less than in steel die bottom, placement thickness
10mm, then by regeneration aggregate pervious concrete basic unit mixture making on surface layer mixture；
4) it is molded：It is compressing with 2~5MPa pressure, the demoulding；
5) conserve：Molding blank is not less than in 50% environment in 20 DEG C of temperature, humidity conserves 28d, that is, Self-decorating is made again
Raw aggregate porous concrete product.
Embodiment 7：
A kind of Self-decorating regeneration aggregate porous concrete product, includes regeneration aggregate pervious concrete basic unit and regeneration aggregate
Self-chambering finish coat.Wherein regeneration aggregate pervious concrete basic unit is mixed by the parts by weight of Portland cement 20,2.36mm~9.5mm
Solidifying soil, the parts by weight of mortar class construction refuse regenerated aggregate 56 ,≤2.36mm concrete, the weight of mortar class construction refuse regenerated aggregate 24
Measure the component raw material mixing composition of part and the parts by weight of water 8；Wherein regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20 ,≤
The component of the construction refuse regenerated decoration parts by weight of aggregate 80 of 2.36mm sintered brick and tiles, glass, ceramic-like and the parts by weight of water 10 is former
Material mixing composition.
The preparation method of Self-decorating regeneration aggregate porous concrete product is：
1) dispensing：By the parts by weight of Portland cement 20,2.36mm~9.5mm concrete, mortar class building waste again
The parts by weight of raw aggregate 56 ,≤2.36mm concrete, the parts by weight of mortar class construction refuse regenerated aggregate 24 and the parts by weight of water 8 are matched somebody with somebody
Than taking each component raw material, as regeneration aggregate pervious concrete basic unit raw material；By the parts by weight of white cement 20 ,≤2.36mm fired bricks
Watt, the proportioning of the construction refuse regenerated decoration parts by weight of aggregate 80 of glass, ceramic-like and the parts by weight of water 10 take each component raw material, make
For regeneration aggregate Self-decorating face stock；
2) stir：Preparation raw material is weighed by step 1), respectively by regeneration aggregate pervious concrete basic unit raw material, Regenerated Bone
Expect that Self-decorating face stock mixes, regeneration aggregate pervious concrete basic unit's mixture and regeneration aggregate Self-decorating are made respectively
Surface layer mixture；
3) cloth：Regeneration aggregate self-chambering finish coat mixture making is not less than in steel die bottom, placement thickness
10mm, then by regeneration aggregate pervious concrete basic unit mixture making on surface layer mixture；
4) it is molded：It is compressing with 2~5MPa pressure, the demoulding；
5) conserve：Molding blank is not less than in 50% environment in 20 DEG C of temperature, humidity conserves 28d, that is, Self-decorating is made again
Raw aggregate porous concrete product.
The gained Self-decorating regeneration aggregate porous concrete product performance of embodiment 1~7 is shown in Table 1.
Table 1：Self-decorating regeneration aggregate porous concrete product performance：
Embodiment 8：
A kind of Self-decorating regeneration aggregate porous concrete product, the Self-decorating regeneration aggregate porous concrete product is by thickness
The compound composition of regeneration aggregate self-chambering finish coat that regeneration aggregate pervious concrete basic unit for 50mm is 10mm with thickness；
The regeneration aggregate pervious concrete basic unit by the parts by weight of Portland cement 20, particle diameter be 2.36mm~
9.5mm concrete or/and the parts by weight of mortar class construction refuse regenerated aggregate 56, particle diameter≤2.36mm concrete or/and sand
Starch the component raw material mixing composition of the parts by weight of class construction refuse regenerated aggregate 8 and the parts by weight of water 8；
The regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20, particle diameter≤2.36mm sintered brick and tile, glass, with
And the construction refuse regenerated parts by weight of decoration aggregate 80 of one or both of ceramic-like thing mixed above, and the parts by weight of water 10
Component raw material mixing composition.
Embodiment 9：
A kind of Self-decorating regeneration aggregate porous concrete product, the Self-decorating regeneration aggregate porous concrete product is by thickness
The compound composition of regeneration aggregate self-chambering finish coat that regeneration aggregate pervious concrete basic unit for 65mm is 15mm with thickness；
The regeneration aggregate pervious concrete basic unit by the parts by weight of Portland cement 20, particle diameter be 2.36mm~
9.5mm concrete or/and the parts by weight of mortar class construction refuse regenerated aggregate 72, particle diameter≤2.36mm concrete or/and sand
Starch the component raw material mixing composition of the parts by weight of class construction refuse regenerated aggregate 24 and the parts by weight of water 8；
The regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20, particle diameter≤2.36mm sintered brick and tile, glass, with
And the construction refuse regenerated parts by weight of decoration aggregate 120 of one or both of ceramic-like thing mixed above, and the weight of water 10
The component raw material mixing composition of part.
Embodiment 10：
A kind of Self-decorating regeneration aggregate porous concrete product, the Self-decorating regeneration aggregate porous concrete product is by thickness
The compound composition of regeneration aggregate self-chambering finish coat that regeneration aggregate pervious concrete basic unit for 57mm is 13mm with thickness；
The regeneration aggregate pervious concrete basic unit by the parts by weight of Portland cement 20, particle diameter be 2.36mm~
9.5mm concrete or/and the parts by weight of mortar class construction refuse regenerated aggregate 64, particle diameter≤2.36mm concrete or/and sand
Starch the component raw material mixing composition of the parts by weight of class construction refuse regenerated aggregate 16 and the parts by weight of water 8；
The regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20, particle diameter≤2.36mm sintered brick and tile, glass, with
And the construction refuse regenerated parts by weight of decoration aggregate 100 of one or both of ceramic-like thing mixed above, and the weight of water 10
The component raw material mixing composition of part.
Embodiment 11~17：
A kind of Self-decorating regeneration aggregate porous concrete product, the Self-decorating regeneration aggregate porous concrete product is by thickness
The compound structure of regeneration aggregate self-chambering finish coat that regeneration aggregate pervious concrete basic unit for 50~65mm is 10~15mm with thickness
Into；Each specific thickness of layer (mm) see the table below in each embodiment：
The regeneration aggregate pervious concrete basic unit by the parts by weight of Portland cement 20, particle diameter be 2.36mm~
9.5mm concrete or/and mortar class construction refuse regenerated aggregate (abbreviation regeneration aggregate 1 in following table) 56~72 parts by weight, grain
Footpath≤2.36mm concrete or/and mortar class construction refuse regenerated aggregate (abbreviation regeneration aggregate 2 in following table) 8~24 weight
The component raw material of part and the parts by weight of water 8 mixing composition；The specific parts by weight dosage of each raw material see the table below in each embodiment：
The regeneration aggregate self-chambering finish coat by the parts by weight of white cement 20, particle diameter≤2.36mm sintered brick and tile, glass, with
And the construction refuse regenerated parts by weight of decoration aggregate 80~120 of one or both of ceramic-like thing mixed above, and water 10
The component raw material mixing composition of parts by weight；The specific parts by weight dosage of each raw material see the table below in each embodiment：
In above-described embodiment：The preparation method of the construction refuse regenerated aggregate is：Building waste is reclaimed, sub-elected mixed
Solidifying soil, mortar class building waste and sintered brick and tile, glass, ceramic-like building waste；Concrete, mortar class building waste are broken
It is broken, 2.36mm~9.5mm and≤2.36mm particle are filtered out respectively, as the regeneration aggregate pervious concrete basic unit with building
Building refuse regeneration aggregate；By sintered brick and tile, glass, ceramic-like construction waste crushing ,≤2.36mm particle is filtered out, as institute
Regeneration aggregate self-chambering finish coat is stated with construction refuse regenerated decoration aggregate.
In above-described embodiment：The strength grade of the Portland cement is not less than 42.5MPa.Such as：Southwestern cement
P.O425 Portland cements；The high victory P.O425R Portland cements in Sichuan；The common silicic acid of Lafarge SA P.O525R
Salt cement.
In above-described embodiment：The white cement is that the P.W.52.5 levels of A Erbo Portlands (Anqing) Co., Ltd production are white
Cement (A Erbo boards) or P.W.42.5 levels white cement (A Erbo boards), preferably P.W.52.5 levels white cement (A Erbo boards).
Embodiment 18：
A kind of preparation method of Self-decorating regeneration aggregate porous concrete product, step are：
A, dispensing：By the parts by weight of Portland cement 20, the concrete or/and mortar that particle diameter is 2.36mm~9.5mm
The parts by weight of class construction refuse regenerated aggregate 56, particle diameter≤2.36mm concrete or/and the weight of mortar class construction refuse regenerated aggregate 8
The proportioning of amount part and the parts by weight of water 8 takes each component raw material, the raw material as regeneration aggregate pervious concrete basic unit；
It is more than one or both of particle diameter≤2.36mm sintered brick and tiles, glass, ceramic-like mixed by the parts by weight of white cement 20
The construction refuse regenerated parts by weight of decoration aggregate 80 of compound, and the proportioning of the parts by weight of water 10 take each component raw material, as regeneration
The raw material of aggregate self-chambering finish coat；
B, it is stirred：The preparation raw material weighed by step a, respectively by the original of regeneration aggregate pervious concrete basic unit
Material, the raw material of regeneration aggregate self-chambering finish coat mix, and regeneration aggregate pervious concrete basic unit mixture, regeneration are made respectively
Aggregate self-chambering finish coat mixture；
C, cloth：By regeneration aggregate self-chambering finish coat mixture making in steel die bottom, placement thickness 10mm；Again
By regeneration aggregate pervious concrete basic unit mixture making on regeneration aggregate self-chambering finish coat mixture compound, placement thickness
For 50mm, two-layer compound mixture is obtained；
D, it is molded：It is with 2MPa pressure that step c two-layer compound mixture is compressing again, the demoulding, parison is made into
Body；
E, conserve：By molding blank be placed in the environment of 25 DEG C of temperature, humidity 50% conserve 28d (my god), that is, be made self-chambering
Adorn regeneration aggregate porous concrete product.
Embodiment 19：
A kind of preparation method of Self-decorating regeneration aggregate porous concrete product, step are：
A, dispensing：By the parts by weight of Portland cement 20, the concrete or/and mortar that particle diameter is 2.36mm~9.5mm
The parts by weight of class construction refuse regenerated aggregate 72, particle diameter≤2.36mm concrete or/and mortar class construction refuse regenerated aggregate 24
The proportioning of parts by weight and the parts by weight of water 8 takes each component raw material, the raw material as regeneration aggregate pervious concrete basic unit；
It is more than one or both of particle diameter≤2.36mm sintered brick and tiles, glass, ceramic-like mixed by the parts by weight of white cement 20
The construction refuse regenerated parts by weight of decoration aggregate 120 of compound, and the proportioning of the parts by weight of water 10 take each component raw material, as regeneration
The raw material of aggregate self-chambering finish coat；
B, it is stirred：The preparation raw material weighed by step a, respectively by the original of regeneration aggregate pervious concrete basic unit
Material, the raw material of regeneration aggregate self-chambering finish coat mix, and regeneration aggregate pervious concrete basic unit mixture, regeneration are made respectively
Aggregate self-chambering finish coat mixture；
C, cloth：By regeneration aggregate self-chambering finish coat mixture making in steel die bottom, placement thickness 15mm；Again
By regeneration aggregate pervious concrete basic unit mixture making on regeneration aggregate self-chambering finish coat mixture compound, placement thickness
For 65mm, two-layer compound mixture is obtained；
D, it is molded：It is with 5MPa pressure that step c two-layer compound mixture is compressing again, the demoulding, parison is made into
Body；
E, conserve：By molding blank be placed in the environment of 15 DEG C of temperature, humidity 90% conserve 28d (my god), that is, be made self-chambering
Adorn regeneration aggregate porous concrete product.
Embodiment 20：
A kind of preparation method of Self-decorating regeneration aggregate porous concrete product, step are：
A, dispensing：By the parts by weight of Portland cement 20, the concrete or/and mortar that particle diameter is 2.36mm~9.5mm
The parts by weight of class construction refuse regenerated aggregate 64, particle diameter≤2.36mm concrete or/and mortar class construction refuse regenerated aggregate 16
The proportioning of parts by weight and the parts by weight of water 8 takes each component raw material, the raw material as regeneration aggregate pervious concrete basic unit；
It is more than one or both of particle diameter≤2.36mm sintered brick and tiles, glass, ceramic-like mixed by the parts by weight of white cement 20
The construction refuse regenerated parts by weight of decoration aggregate 100 of compound, and the proportioning of the parts by weight of water 10 take each component raw material, as regeneration
The raw material of aggregate self-chambering finish coat；
B, it is stirred：The preparation raw material weighed by step a, respectively by the original of regeneration aggregate pervious concrete basic unit
Material, the raw material of regeneration aggregate self-chambering finish coat mix, and regeneration aggregate pervious concrete basic unit mixture, regeneration are made respectively
Aggregate self-chambering finish coat mixture；
C, cloth：By regeneration aggregate self-chambering finish coat mixture making in steel die bottom, placement thickness 12mm；Again
By regeneration aggregate pervious concrete basic unit mixture making on regeneration aggregate self-chambering finish coat mixture compound, placement thickness
For 57mm, two-layer compound mixture is obtained；
D, it is molded：It is with 4MPa pressure that step c two-layer compound mixture is compressing again, the demoulding, parison is made into
Body；
E, conserve：By molding blank be placed in the environment of 20 DEG C of temperature, humidity 70% conserve 28d (my god), that is, be made self-chambering
Adorn regeneration aggregate porous concrete product.
Embodiment 21：
A kind of preparation method of Self-decorating regeneration aggregate porous concrete product, step are：
A, dispensing：By the parts by weight of Portland cement 20, the concrete or/and mortar that particle diameter is 2.36mm~9.5mm
The parts by weight of class construction refuse regenerated aggregate 56~72, particle diameter≤2.36mm concrete or/and the construction refuse regenerated bone of mortar class
The proportioning of 8~24 parts by weight of material and the parts by weight of water 8 takes each component raw material, the original as regeneration aggregate pervious concrete basic unit
Material；
It is more than one or both of particle diameter≤2.36mm sintered brick and tiles, glass, ceramic-like mixed by the parts by weight of white cement 20
The construction refuse regenerated parts by weight of decoration aggregate 80~120 of compound, and the proportioning of the parts by weight of water 10 take each component raw material, as
The raw material of regeneration aggregate self-chambering finish coat；
B, it is stirred：The preparation raw material weighed by step a, respectively by the original of regeneration aggregate pervious concrete basic unit
Material, the raw material of regeneration aggregate self-chambering finish coat mix, and regeneration aggregate pervious concrete basic unit mixture, regeneration are made respectively
Aggregate self-chambering finish coat mixture；
C, cloth：By regeneration aggregate self-chambering finish coat mixture making in steel die bottom, placement thickness be 10mm~
15mm；Again by regeneration aggregate pervious concrete basic unit mixture making on regeneration aggregate self-chambering finish coat mixture it is compound,
Placement thickness is 50mm~65mm, obtains two-layer compound mixture；
D, it is molded：It is with 2~5MPa pressure that step c two-layer compound mixture is compressing again, the demoulding, shaping is made
Base substrate；
E, conserve：By molding blank be placed in the environment of 15~25 DEG C of temperature, humidity 50%~90% conserve 28d (my god),
Self-decorating regeneration aggregate porous concrete product is made.
Embodiment 22~28：
A kind of preparation method of Self-decorating regeneration aggregate porous concrete product, step are：
A, dispensing：By the parts by weight of Portland cement 20, the concrete or/and mortar that particle diameter is 2.36mm~9.5mm
The parts by weight of class construction refuse regenerated aggregate 56~72, particle diameter≤2.36mm concrete or/and the construction refuse regenerated bone of mortar class
The proportioning of 8~24 parts by weight of material and the parts by weight of water 8 takes each component raw material, the original as regeneration aggregate pervious concrete basic unit
Material；The specific parts by weight dosage of each raw material is the same as any in embodiment 11~17, omission in each embodiment；
It is more than one or both of particle diameter≤2.36mm sintered brick and tiles, glass, ceramic-like mixed by the parts by weight of white cement 20
The construction refuse regenerated parts by weight of decoration aggregate 80~120 of compound, and the proportioning of the parts by weight of water 10 take each component raw material, as
The raw material of regeneration aggregate self-chambering finish coat；The specific parts by weight dosage of each raw material is appointed with embodiment 11~17 in each embodiment
One, omit；
B, it is stirred：The preparation raw material weighed by step a, respectively by the original of regeneration aggregate pervious concrete basic unit
Material, the raw material of regeneration aggregate self-chambering finish coat mix, and regeneration aggregate pervious concrete basic unit mixture, regeneration are made respectively
Aggregate self-chambering finish coat mixture；
C, cloth：By regeneration aggregate self-chambering finish coat mixture making in steel die bottom, placement thickness be 10mm~
15mm；Again by regeneration aggregate pervious concrete basic unit mixture making on regeneration aggregate self-chambering finish coat mixture it is compound,
Placement thickness is 50mm~65mm, obtains two-layer compound mixture；In each embodiment the specific thickness of each layer with embodiment 11~
It is any in 17, omit；Each specific thickness of layer (mm) can also see the table below in each embodiment：
D, it is molded：It is with 2~5MPa pressure that step c two-layer compound mixture is compressing again, the demoulding, shaping is made
Base substrate；
E, conserve：By molding blank be placed in the environment of 15~25 DEG C of temperature, humidity 50%~90% conserve 28d (my god),
Self-decorating regeneration aggregate porous concrete product is made.
In above-described embodiment 18~28：The preparation method of the construction refuse regenerated aggregate is：Building waste is reclaimed, point
Select concrete, mortar class building waste and sintered brick and tile, glass, ceramic-like building waste；By concrete, mortar class building rubbish
Rubbish crushes, and 2.36mm~9.5mm and≤2.36mm particle is filtered out respectively, as the regeneration aggregate pervious concrete basic unit
Use construction refuse regenerated aggregate；By sintered brick and tile, glass, ceramic-like construction waste crushing ,≤2.36mm particle is filtered out, is made
It is the regeneration aggregate self-chambering finish coat with construction refuse regenerated decoration aggregate.
In above-described embodiment 18~28：The strength grade of the Portland cement is not less than 42.5MPa.Such as：West
Southern cement P.O425 Portland cements；The high victory P.O425R Portland cements in Sichuan；Lafarge SA P.O525R is general
Logical portland cement.
In above-described embodiment 18~28：The white cement is the production of A Erbo Portlands (Anqing) Co., Ltd
P.W.52.5 levels white cement (A Erbo boards) or P.W.42.5 levels white cement (A Erbo boards), preferably P.W.52.5 levels white cement
(A Erbo boards).
In above-described embodiment：Used each raw material is commercially available prod.
In above-described embodiment：It is especially not dated in used percentage, be weight (quality) percentage or
Well known to a person skilled in the art percentage；Described weight (quality) part can be gram or kilogram.
In above-described embodiment：Technological parameter (temperature, humidity, pressure, thickness etc.) each component raw material dosage in each step
It is scope Deng numerical value etc., any point is applicable.
The technology contents being not specifically delineated in present invention and above-described embodiment are compared with technology.
Above-described embodiment only have selected different proportion raw material and prepare Self-decorating regeneration aggregate porous concrete product, for this
Those skilled in the art can easily make different modifications on the basis of these embodiments, and described herein one
As principle be applied in other embodiments and need not pass through performing creative labour, therefore, the invention is not restricted to above-described embodiment；Ability
Field technique personnel do not depart from improvement that scope made and modification all should be in the guarantors of the present invention according to the announcement of the present invention
Within the scope of shield；It can implement described in present invention and there is the good result.
Claims (8)
1. a kind of Self-decorating regeneration aggregate porous concrete product, it is characterized in that：The Self-decorating regeneration aggregate pervious concrete system
The regeneration aggregate self-chambering facing that the regeneration aggregate pervious concrete basic unit that product are 50~65mm by thickness is 10~15mm with thickness
The compound composition of layer；
The regeneration aggregate pervious concrete basic unit is 2.36mm~9.5mm's by the parts by weight of Portland cement 20, particle diameter
Concrete or/and the parts by weight of mortar class construction refuse regenerated aggregate 56~72, particle diameter≤2.36mm concrete or/and mortar class
The component raw material of the parts by weight of construction refuse regenerated aggregate 8~24 and the parts by weight of water 8 mixing composition；
The regeneration aggregate self-chambering finish coat is by the parts by weight of white cement 20, particle diameter≤2.36mm sintered brick and tile, glass, Yi Jitao
The construction refuse regenerated parts by weight of decoration aggregate 80~120 of one or both of porcelain class thing mixed above, and the weight of water 10
The component raw material mixing composition of part.
2. the Self-decorating regeneration aggregate porous concrete product as described in claim 1, it is characterized in that：It is described construction refuse regenerated
Aggregate processing method is：Building waste is reclaimed, sub-elects concrete, mortar class building waste and sintered brick and tile, glass, pottery
Porcelain class building waste；By concrete, mortar class construction waste crushing, filter out 2.36mm~9.5mm's and≤2.36mm respectively
Particle, as the regeneration aggregate pervious concrete basic unit construction refuse regenerated aggregate；By sintered brick and tile, glass, ceramic-like
Construction waste crushing ,≤2.36mm particle is filtered out, as the regeneration aggregate self-chambering finish coat with construction refuse regenerated dress
Adorn aggregate.
3. the Self-decorating regeneration aggregate porous concrete product as described in claim 1, it is characterized in that：The normal silicate water
The strength grade of mud is not less than 42.5MPa.
4. the Self-decorating regeneration aggregate porous concrete product as described in claim 1, it is characterized in that：The white cement is A Er
Rich Portland（Anqing）The P.W.52.5 levels white cement or P.W.42.5 level white cements of Co., Ltd's production.
A kind of 5. preparation method of Self-decorating regeneration aggregate porous concrete product, it is characterized in that step is：
A, dispensing：Built by the parts by weight of Portland cement 20, the concrete that particle diameter is 2.36mm~9.5mm or/and mortar class
The parts by weight of building refuse regeneration aggregate 56~72, particle diameter≤2.36mm concrete or/and mortar class construction refuse regenerated aggregate 8~
The proportioning of 24 parts by weight and the parts by weight of water 8 takes each component raw material, the raw material as regeneration aggregate pervious concrete basic unit；
By the parts by weight of white cement 20, one or both of particle diameter≤2.36mm sintered brick and tiles, glass, ceramic-like thing mixed above
The construction refuse regenerated parts by weight of decoration aggregate 80~120, and the proportioning of the parts by weight of water 10 takes each component raw material, as regeneration
The raw material of aggregate self-chambering finish coat；
B, it is stirred：The preparation raw material weighed by step a, respectively by the raw material of regeneration aggregate pervious concrete basic unit, again
The raw material of raw aggregate self-chambering finish coat mixes, and regeneration aggregate pervious concrete basic unit mixture, regeneration aggregate are made respectively
Self-chambering finish coat mixture；
C, cloth：By regeneration aggregate self-chambering finish coat mixture making in steel die bottom, placement thickness is 10mm~15mm；
Again by regeneration aggregate pervious concrete basic unit mixture making on regeneration aggregate self-chambering finish coat mixture it is compound, making is thick
Spend for 50mm~65mm, obtain two-layer compound mixture；
D, it is molded：It is with 2~5MPa pressure that step c two-layer compound mixture is compressing again, the demoulding, parison is made into
Body；
E, conserve：Molding blank is placed in the environment of 15~25 DEG C of temperature, humidity 50%~90% and conserves 28d, that is, is made certainly
Decorate regeneration aggregate porous concrete product.
6. the preparation method of the Self-decorating regeneration aggregate porous concrete product as described in claim 5, it is characterized in that：It is described to build
The preparation method of building refuse regeneration aggregate is：Building waste is reclaimed, sub-elects concrete, mortar class building waste and fired brick
Watt, glass, ceramic-like building waste；By concrete, mortar class construction waste crushing, filter out respectively 2.36mm~9.5mm and
≤ 2.36mm particle, as the regeneration aggregate pervious concrete basic unit construction refuse regenerated aggregate；By sintered brick and tile, glass
Glass, ceramic-like construction waste crushing ,≤2.36mm particle is filtered out, as regeneration aggregate self-chambering finish coat building rubbish
Rubbish regeneration decoration aggregate.
7. the preparation method of the Self-decorating regeneration aggregate porous concrete product as described in claim 5, it is characterized in that：It is described general
The strength grade of logical portland cement is not less than 42.5MPa.
8. the preparation method of the Self-decorating regeneration aggregate porous concrete product as described in claim 5, it is characterized in that：It is described white
Cement is A Erbo Portlands（Anqing）The P.W.52.5 levels white cement or P.W.42.5 level white cements of Co., Ltd's production.