CN107099753B - 循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢 - Google Patents
循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢 Download PDFInfo
- Publication number
- CN107099753B CN107099753B CN201710241650.9A CN201710241650A CN107099753B CN 107099753 B CN107099753 B CN 107099753B CN 201710241650 A CN201710241650 A CN 201710241650A CN 107099753 B CN107099753 B CN 107099753B
- Authority
- CN
- China
- Prior art keywords
- percent
- molten steel
- hood
- fluidized bed
- circulating fluidized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中,各化学成分的重量百分比为:C:0.15~0.5%,Si:1.0~2.6%,Mn:1~1.5%,Cr:24~26%,Mo:0.8~1%,Ni:6~8%,Cu:0.8~1.9%,Nb:0.1~0.5%,W:2~6%,Co:0.1~0.5%,N:0.1~0.3%,Al:2~3.8%,S≤0.03%,P≤0.03%,余量为Fe。利用该材质制备的循环流化床锅炉风帽最高耐热温度可达1380℃,相对于ZG40Cr25Ni20而言,具有成本低、高温抗氧化性强、耐磨性好、高温不变形等特点。因此,该材质在循环流化床锅炉风帽等耐热耐磨部件应用前景广阔。
Description
技术领域
本发明涉及新材料领域,特别是一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢。
背景技术
循环流化床锅炉由于具有环保、燃烧充分、燃料可选择性广等优点,已成为煤和其他燃料能源综合利用发展的高新技术产品,是近几年应用最广泛的一种新型火力发电和供热锅炉。
风帽是循环流化床锅炉布风装置的关键部件,循环流化床锅炉正常运行时,风帽被高温床上面的燃料浸埋,风帽不仅受到高温烧蚀还要受到煤粉气流的磨损等多重影响。高温氧化、冲蚀磨损、腐蚀等多重因素,常常导致风帽帽顶烧坏失效,严重影响锅炉的安全经济运行。因此,风帽应具有良好的抗高温冲蚀磨损、抗高温氧化和腐蚀的能力,同时还应具备优异的抗蠕变能力和高温持久强度。传统风帽材质一般选用高Cr-Ni合金奥氏体耐热钢,因含有较多的Cr和Ni,制作成本高。同时,Ni是我国的稀有元素,Ni的大量使用不符合我国节能减排和经济可持续发展的要求。而且,高Cr-Ni合金奥氏体耐热钢风帽长期高温条件下,寿命短、易变形、不耐冲蚀等缺点。因此,科研工作者在风帽的材质方面进行了大量研究,试图开发一种低Ni含量、寿命长、高温持久强度高、耐冲蚀的耐热合金钢风帽。对于提高流化床锅炉运行效率、减少风帽更换频率、节约利用Ni资源、降低工人劳动强度等方面具有重要意义。
近年来,关于提高循环流化床锅炉风帽耐热和耐磨的性能方面进行了大量研究,国内开发了几种新的风帽合金材料和风帽结构。
中国专利公开号CN103173692公开的“高温合金、采用该合金制造的合金风帽及该风帽的制造工艺”,其风帽的化学成分重量百分比组成是:C:0.4~0.6%,Cr:25~29%,Ni:32~36%,Mo:2.3~2.7%,Si:1.4~1.7%,Mn:1.5~1.9%,Nb:1.3~1.6%,Re:0.1~0.3%,N:0.1~0.3%,Ti:0.1~0.3%,B:0.06~0.1%,Zr:0.1~0.2%,余量为Fe。这种风帽合金材料由于含有:Ni:32~36%,与25-20钢相比,Ni提高了60~80%,高温合金的平均硬度、高温抗氧化性能和高温抗腐蚀性能较25-20钢有明显提高。然而,虽然高温抗氧化性能和抗高温腐蚀性能较25-20钢有较大提高,大量Ni的加入明显增加了原材料成本,再加上该合金还含有Mo:2.3~2.7%、Nb:1.3~1.6% 、Zr:0.1~0.2%等贵重金属,所以该合金材料性价比并不高。再者,Ni、Mo、Nb、Zr属于稀有元素,大量使用稀有元素不符合我国节能减排的发展要求。
中国专利公开号CN201429075披露的“循环流化床锅炉陶瓷复合风帽”,该专利是通过对普通风帽加装工业陶瓷外罩,从而提高风帽的抗磨性能。同时,采用分层结构,解决了风帽使用过程中易堵易漏的难题,具有显著的经济效益和广阔的推广前景。然而,该专利采用陶瓷复合制备了风帽,虽然提高了风帽的抗磨性能和减少了风帽在使用过程中易堵易漏的难题,但是由于风帽采用耐热合金与陶瓷复合,必然存在制备工艺复杂、生产周期长、劳动成本高等问题,不适合风帽大批量生产。而且陶瓷硬度高、韧性差,在搬运过程中有易损坏的弊端。
发明内容
本发明的目的是要提供一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,具有成本低、高温抗氧化性强、耐磨性好、高温不变形等特点。
为达到上述目的,本发明是按照以下技术方案实施的:一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.15~0.5%,Si:1.0~2.6%,Mn:1~1.5%,Cr:24~26%,Mo: 0.8~1%,Ni:6~8%,Cu: 0.8~1.9%,Nb:0.1~0.5%,W:2~6%,Co: 0.1~0.5%,N:0.1~0.3%,Al:2~3.8%,S≤0.03%,P≤0.03%,余量为Fe。
用循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽的方法,包括以下步骤:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1650-1670℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.15~0.5%,Si:1.0~2.6%,Mn:1~1.5%,Cr:24~26%,Mo: 0.8~1%,Ni:6~8%,Cu: 0.8~1.9%,Nb:0.1~0.5%,W:2~6%,Co: 0.1~0.5%,N:0.1~0.3%,Al:2~3.8%,S≤0.03%,P≤0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1650-1670℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
与现有技术相比,本发明的耐热钢中加入了金属W,W的熔点是3410±20℃,所以,W是一种难熔金属,具有良好的高温强度,同时,W的加入使得研制的耐热钢在熔融碱金属和蒸气环境下,具有良好的耐蚀性能,并且,W只有在1000℃以上条件下,才出现氧化物挥发和液相氧化物,另外,该耐热钢组成还添加了少量或微量的Nb、Co、N、Al,可以形成复合固溶强化,该耐热钢具有良好的高温强度、耐磨性、抗氧化性和耐蚀性,其主要力学性能指标为:(1)常温条件下,抗拉强度≥900Mpa,屈服强度≥680Mpa,延伸率≥18%,冲击韧性:19~27j/cm2,硬度:HRC42~47;(2)1380℃条件下,抗拉强度≥38Mpa,延伸率大于17%,氧化增重≤0.40/m2﹒h,抗氧化性≥1380℃。
因此,利用该耐热钢制备的循环流化床锅炉风帽最高耐热温度可达1380℃,相对于ZG40Cr25Ni20而言,具有成本低、高温抗氧化性强、耐磨性好、高温不变形等特点,利用该耐热钢制备的循环流化床锅炉风帽的使用寿命是25-20钢制风帽的1.5倍以上。因此,该耐热钢在循环流化床锅炉风帽等耐热耐磨部件应用前景广阔。
具体实施方式
下面结合具体实施例对本发明作进一步描述,在此发明的示意性实施例以及说明用来解释本发明,但并不作为对本发明的限定。
实施例1
一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.41%,Si:1.51%,Mn:1.34%,Cr:24.01%,Mo: 0.81%,Ni:6.82%,Cu:1.31 %,Nb:0.24%,W:2.31%,Co:0.21 %,N:0.30%,Al:2.51%,S:0.02%,P:0.03%,余量为Fe。
使用本实施例的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽时其具体步骤如下:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1650℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.41%,Si:1.51%,Mn:1.34%,Cr:24.01%,Mo: 0.81%,Ni:6.82%,Cu:1.31 %,Nb:0.24%,W:2.31%,Co:0.21 %,N:0.30%,Al:2.51%,S:0.02%,P:0.03%,余量为Fe;
步骤三、注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1650℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
实施例2
一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.43%,Si:1.61%,Mn:1.41%,Cr:24.64%,Mo: 0.91%,Ni:7.30%,Cu:1.50 %,Nb:0.30%,W:2.00%,Co:0.10 %,N:0.23%,Al:3.10%,S:0.02%,P:0.03%,余量为Fe。
使用本实施例的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽时其具体步骤如下:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1670℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.43%,Si:1.61%,Mn:1.41%,Cr:24.64%,Mo: 0.91%,Ni:7.30%,Cu:1.50 %,Nb:0.30%,W:2.00%,Co:0.10 %,N:0.23%,Al:3.10%,S:0.02%,P:0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1670℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
实施例3
一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.42%,Si:1.51%,Mn:1.51%,Cr:25.11%,Mo: 0.81%,Ni:7.21%,Cu:1.40 %,Nb:0.20%,W:2.12%,Co:0.10 %,N:0.21%,Al:3.21%,S:0.02%,P:0.03%,余量为Fe。
使用本实施例的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽时其具体步骤如下:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1660℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.42%,Si:1.51%,Mn:1.51%,Cr:25.11%,Mo: 0.81%,Ni:7.21%,Cu:1.40 %,Nb:0.20%,W:2.12%,Co:0.10 %,N:0.21%,Al:3.21%,S:0.02%,P:0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1660℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
实施例4
一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.45%,Si:1.71%,Mn:1.42%,Cr:25.50%,Mo: 0.92%,Ni:7.51%,Cu:1.21 %,Nb:0.44%,W:5.81%,Co:0.16 %,N:0.25%,Al:3.52%,S:0.02%,P:0.03%,余量为Fe。
使用本实施例的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽时其具体步骤如下:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1670℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.45%,Si:1.71%,Mn:1.42%,Cr:25.50%,Mo: 0.92%,Ni:7.51%,Cu:1.21 %,Nb:0.44%,W:5.81%,Co:0.16 %,N:0.25%,Al:3.52%,S:0.02%,P:0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1670℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
实施例5
一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.42%,Si:1.54%,Mn:1.45%,Cr:26.14%,Mo: 0.81%,Ni:6.91%,Cu:1.52 %,Nb:0.31%,W:5.71%,Co:0.20 %,N:0.23%,Al:2.91%,S:0.02%,P:0.03%,余量为Fe。
使用本实施例的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽时其具体步骤如下:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1650℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.42%,Si:1.54%,Mn:1.45%,Cr:26.14%,Mo: 0.81%,Ni:6.91%,Cu:1.52 %,Nb:0.31%,W:5.71%,Co:0.20 %,N:0.23%,Al:2.91%,S:0.02%,P:0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1650℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
实施例6
一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.43%,Si:1.61%,Mn:1.51%,Cr:25.07%,Mo:0.97%,Ni:6.71%,Cu:1.82 %,Nb:0.41%,W:5.62%,Co:0.20 %,N:0.21%,Al:2.81%,S:0.02%,P:0.03%,余量为Fe。
使用本实施例的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽时其具体步骤如下:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1670℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.43%,Si:1.61%,Mn:1.51%,Cr:25.07%,Mo:0.97%,Ni:6.71%,Cu:1.82 %,Nb:0.41%,W:5.62%,Co:0.20 %,N:0.21%,Al:2.81%,S:0.02%,P:0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1670℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
实施例7
一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.41%,Si:1.41%,Mn:1.42%,Cr:24.81%,Mo: 0.91%,Ni:7.12%,Cu:1.51 %,Nb:0.37%,W:4.61%,Co:0.10 %,N:0.25%,Al:2.71%,S:0.02%,P:0.03%,余量为Fe。
使用本实施例的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽时其具体步骤如下:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1670℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.41%,Si:1.41%,Mn:1.42%,Cr:24.81%,Mo: 0.91%,Ni:7.12%,Cu:1.51 %,Nb:0.37%,W:4.61%,Co:0.10 %,N:0.25%,Al:2.71%,S:0.02%,P:0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1670℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
实施例8
一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.47%,Si:1.62%,Mn:1.54%,Cr:24.61%,Mo: 0.94%,Ni:7.45%,Cu:1.62 %,Nb:0.30%,W:4.12%,Co:0.19 %,N:0.25%,Al:3.23%,S:0.02%,P:0.03%,余量为Fe。
使用本实施例的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽时其具体步骤如下:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1650℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.47%,Si:1.62%,Mn:1.54%,Cr:24.61%,Mo: 0.94%,Ni:7.45%,Cu:1.62 %,Nb:0.30%,W:4.12%,Co:0.19 %,N:0.25%,Al:3.23%,S:0.02%,P:0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1650℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
实施例9
一种循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢,该耐热钢中各化学成分的重量百分比为:C:0.46%,Si:1.54%,Mn:1.35%,Cr:25.64%,Mo: 0.87%,Ni:6.95%,Cu:1.73%,Nb:0.43%,W:3.00%,Co:0.16%,N:0.21%,Al:3.52%,S:0.02%,P:0.03%,余量为Fe。
使用本实施例的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽时其具体步骤如下:
步骤一、制备型壳:首先根据风帽的图纸制做蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为1660℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.46%,Si:1.54%,Mn:1.35%,Cr:25.64%,Mo: 0.87%,Ni:6.95%,Cu:1.73%,Nb:0.43%,W:3.00%,Co:0.16%,N:0.21%,Al:3.52%,S:0.02%,P:0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1660℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。
本发明的技术方案不限于上述具体实施例的限制,凡是根据本发明的技术方案做出的技术变形,均落入本发明的保护范围之内。
Claims (1)
1.一种用循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢制备风帽的方法,其特征在于:所述的循环流化床锅炉风帽用稀土高铬镍钨多元合金耐热钢其各化学成分的重量百分比为:C:0.15~0.5%,Si:1.0~2.6%,Mn:1~1.5%,Cr:24~26%,Mo:0.8~1%,Ni:6~8%,Cu:0.8~1.9%,Nb:0.1~0.5%,W:2~6%,Co:0.1~0.5%,N:0.1~0.3%,Al:2~3.8%,S≤0.03%,P≤0.03%,余量为Fe;该耐热钢具有良好的高温强度、耐磨性、抗氧化性和耐蚀性,其主要力学性能指标为:(1)常温条件下,抗拉强度≥900MPa,屈服强度≥680MPa,延伸率≥18%,冲击韧性:19~27J/cm2,硬度:HRC42~47;(2)1380℃条件下,抗拉强度≥38MPa,延伸率>17%;该风帽的制备方法包括以下步骤:
步骤一、制备型壳:首先根据风帽的图纸制作蜡模,把蜡模和浇注系统进行粘结,组合成模组,随后,将模组脱蜡和焙烧制备成型壳;
步骤二、熔炼:将生铁、铜、铝、钴、废钢、硅铁合金、锰铁合金、钨铁合金、镍、铌铁合金、铬铁合金、钼铁合金、氮化铬铁和钛铁加入熔炉进行熔炼得到钢液,熔炼温度为 1650~1670℃,然后调整钢液成分,使钢液中各化学成分的重量百分比为:C:0.15~0.5%,Si:1.0~2.6%,Mn:1~1.5%,Cr:24~26%,Mo:0.8~1%,Ni:6~8%,Cu:0.8~1.9%,Nb:0.1~0.5%,W:2~6%,Co:0.1~0.5%,N:0.1~0.3%,Al:2~3.8%,S≤0.03%,P≤0.03%,余量为Fe;
步骤三、浇注成型:提前将型壳和浇包进行预热400℃以上,浇包采用茶壶包,型壳在钢水出炉前从加热炉拿出,等待浇注,钢液出钢温度控制在1650~1670℃,钢液出炉后,用打渣剂打三遍渣釉,然后进行浇注;
步骤四、脱壳与清理:将浇注完的铸件使用震动脱壳机脱壳、清砂,用无齿锯切割浇冒口,检测合格后入库。