CN107299275A - 一种球墨铸铁 - Google Patents

一种球墨铸铁 Download PDF

Info

Publication number
CN107299275A
CN107299275A CN201710520956.8A CN201710520956A CN107299275A CN 107299275 A CN107299275 A CN 107299275A CN 201710520956 A CN201710520956 A CN 201710520956A CN 107299275 A CN107299275 A CN 107299275A
Authority
CN
China
Prior art keywords
iron
spheroidal graphite
graphite cast
cast
niobium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710520956.8A
Other languages
English (en)
Inventor
胡宗道
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HUIHUANG MACHINERY MANUFACTURING CO LTD
Original Assignee
ANHUI HUIHUANG MACHINERY MANUFACTURING CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HUIHUANG MACHINERY MANUFACTURING CO LTD filed Critical ANHUI HUIHUANG MACHINERY MANUFACTURING CO LTD
Priority to CN201710520956.8A priority Critical patent/CN107299275A/zh
Publication of CN107299275A publication Critical patent/CN107299275A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种球墨铸铁，按重量百分比计，包括碳3%~4.1%、硅1.5%~2.5%、锰0.3%~0.8%、镍0.5%~1%、铜0.1%~0.4%、钼0.3%~0.8%、钒0.05%~0.25%、铬0.1%~0.4%、钨0.1%~0.3%、铌0.05%~0.2%，其余成分为铁。本发明制成的球墨铸铁耐高温，抗氧化性好，能够满足现代生产对球墨铸铁的要求。

Description

一种球墨铸铁
技术领域
本发明涉及一种球墨铸铁，属于球墨铸铁技术领域。
背景技术
球墨铸铁是通过球化和孕育处理得到球状石墨，有效地提高了铸铁的机械性能，特别是提高了塑性和韧性，从而得到比碳钢还高的强度。铸铁是含碳量大于2.11%的铁碳合金，由工业生铁、废钢等钢铁及其合金材料经过高温熔融和铸造成型而得到。球墨铸铁是20世纪五十年代发展起来的一种高强度铸铁材料，其综合性能接近于钢，正是基于其优异的性能，已成功地用于铸造一些受力复杂，强度、韧性、耐磨性要求较高的零件。球墨铸铁已迅速发展为仅次于灰铸铁的、应用十分广泛的铸铁材料。所谓“以铁代钢”，主要指球墨铸铁。
现代生产对球墨铸铁要求更高了，例如发动机铸件、烟囱铸件等，需要球墨铸铁有很好的耐高温抗氧化的能力才能胜任。
发明内容
为克服上述不足，本发明目的提供一种球墨铸铁。
本发明的方案如下：一种球墨铸铁，按重量百分比计，包括碳3%~4.1%、硅1.5%~2.5%、锰0.3%~0.8%、镍0.5%~1%、铜0.1%~0.4%、钼0.3%~0.8%、钒0.05%~0.25%、铬0.1%~0.4%、钨0.1%~0.3%、铌0.05%~0.2%，其余成分为铁，优选的，包括碳3.5%、硅2.1%、锰0.5%、镍0.8%、铜0.3%、钼0.5%、钒0.2%、铬0.25%、钨0.2%、铌0.1%，其余成分为铁。
本发明的有益效果：本发明具有良好的抗氧化性和耐高温性，能够很好的适应复杂环境，生产出的产品质量非常好。
具体实施方式
一种球墨铸铁，按重量百分比计，包括碳3%~4.1%、硅1.5%~2.5%、锰0.3%~0.8%、镍0.5%~1%、铜0.1%~0.4%、钼0.3%~0.8%、钒0.05%~0.25%、铬0.1%~0.4%、钨0.1%~0.3%、铌0.05%~0.2%，其余成分为铁，优选的，包括碳3.5%、硅2.1%、锰0.5%、镍0.8%、铜0.3%、钼0.5%、钒0.2%、铬0.25%、钨0.2%、铌0.1%，其余成分为铁。
尽管上文对本发明的具体实施方式给予了详细描述和说明，但是应该指明的是，我们可以依据本发明的构想对上述实施方式进行各种等效改变和修改，其所产生的功能作用仍未超出说明书所涵盖的精神时，均应在本发明的保护范围之内。

Claims (2)

1.一种球墨铸铁，其特征在于，按重量百分比计，包括碳3%~4.1%、硅1.5%~2.5%、锰0.3%~0.8%、镍0.5%~1%、铜0.1%~0.4%、钼0.3%~0.8%、钒0.05%~0.25%、铬0.1%~0.4%、钨0.1%~0.3%、铌0.05%~0.2%，其余成分为铁。
2.根据权利要求1所述一种球墨铸铁，其特征在于，按重量百分比计，包括碳3.5%、硅2.1%、锰0.5%、镍0.8%、铜0.3%、钼0.5%、钒0.2%、铬0.25%、钨0.2%、铌0.1%，其余成分为铁。
CN201710520956.8A 2017-06-30 2017-06-30 一种球墨铸铁 Pending CN107299275A (zh)