CN107098676A - 一种高白瓷耐热直烧壶干烧配方及方法 - Google Patents
一种高白瓷耐热直烧壶干烧配方及方法 Download PDFInfo
- Publication number
- CN107098676A CN107098676A CN201610097946.3A CN201610097946A CN107098676A CN 107098676 A CN107098676 A CN 107098676A CN 201610097946 A CN201610097946 A CN 201610097946A CN 107098676 A CN107098676 A CN 107098676A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic whiteware
- dry combustion
- heat
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高白瓷耐热直烧壶干烧配方及方法,由如下重量分数的原料组成:广西高岭土25‑27份、江西长石20‑24份、澳洲锂辉石20‑24份、滑石1‑2份、大田石英7‑9份、锂瓷石27‑30份,采用烧成工艺,将配方原料混合,高温氧化烧1310度后还原再烧1330度,高白瓷具有可以无水直烧,没有上釉直接在胚体上盛水也不会渗水的优点。
Description
技术领域
本发明涉及直烧壶干烧技术领域,具体涉及一种高白瓷耐热直烧壶干烧配方及方法。
背景技术
随着社会的进步发展,人们对高品质的日用瓷器的要求越来越高,高温高白瓷日用瓷器以其品质细腻,光洁耐磨的性能受到消费者的青睐,具有广阔的市场,在耐热直烧壶的生产过程中,其配方是影响产品质量的关键,随着社会的发展,环保、资源节约型产品已成为当今新科技研发的方向,其制备成本也需要严格控制。
发明内容
针对以上问题,本发明提供了一种高白瓷耐热直烧壶干烧配方及方法,高白瓷具有可以无水直烧,没有上釉直接在胚体上盛水也不会渗水的优点,可以有效解决技术背景中的问题。
为了实现上述目的,本发明采用的技术方案如下:一种高白瓷耐热直烧壶干烧配方,由如下重量分数的原料组成:
广西高岭土25-27份、江西长石20-24份、澳洲锂辉石20-24份、滑石1-2份、大田石英7-9份、锂瓷石27-30份。
进一步地,该配方由如下重量分数的原料组成:
广西高岭土25份、江西长石20份、澳洲锂辉石20份、滑石1份、大田石英7份、锂瓷石27份。
另外本发明还设计了一种高白瓷耐热直烧壶干烧方法,采用烧成工艺,将配方原料混合,高温氧化烧1310度后还原再烧1330度。
本发明的有益效果:
本发明高白瓷具有可以无水直烧,没有上釉直接在胚体上盛水也不会渗水的优点。
具体实施方式
根据下述实施例,可以更好的理解本发明。然而,本领域的技术人员容易理解,实施例所描述的内容仅用于说明本发明,而不应当也不会限制权利要求书中所详细描述的本发明。
实施例1:
一种高白瓷耐热直烧壶干烧配方,由如下重量分数的原料组成:
广西高岭土25份、江西长石20份、澳洲锂辉石20份、滑石1份、大田石英7份、锂瓷石27份。
其方法为,采用烧成工艺,将配方原料混合,高温氧化烧1310度后还原再烧1330度。
实施例2:
一种高白瓷耐热直烧壶干烧配方,由如下重量分数的原料组成:
广西高岭土27份、江西长石24份、澳洲锂辉石24份、滑石2份、大田石英9份、锂瓷石30份。
其方法为,采用烧成工艺,将配方原料混合,高温氧化烧1310度后还原再烧1330度。
具体的,本发明烧成工艺是将硅酸盐制品在一定条件下进行热处理,使之发生一系列物理化学变化,形成预期的矿物组成和显微结构,从而达到固定外形并获得所要求性能的工序;生产硅酸盐制品的主要工序之一。将生坯或生料在高温下煅烧而成制品或熟料的过程。烧成时发生脱水、分解、化合等物理和化学变化,使制品具有充分机械强度和其他需要性能。一般在各种窑炉中进行,须注意火焰的气氛性质(还原性的或氧化性的)和烧成的温度范围等。
基于上述,本发明高白瓷具有可以无水直烧,没有上釉直接在胚体上盛水也不会渗水的优点。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种高白瓷耐热直烧壶干烧配方,其特征在于:由如下重量分数的原料组成:
广西高岭土25-27份、江西长石20-24份、澳洲锂辉石20-24份、滑石1-2份、大田石英7-9份、锂瓷石27-30份。
2.根据权利要求1所述的一种治疗红肿消毒药水制剂,其特征在于:由如下重量分数的原料组成:
广西高岭土25份、江西长石20份、澳洲锂辉石20份、滑石1份、大田石英7份、锂瓷石27份。
3. 一种高白瓷耐热直烧壶干烧方法,其特征在于:采用烧成工艺,将配方原料混合,高温氧化烧1310度后还原再烧1330度。