CN107090231A - 一种仿冰雪路面在驾校训练中的应用 - Google Patents

一种仿冰雪路面在驾校训练中的应用 Download PDF

Info

Publication number
CN107090231A
CN107090231A CN201710463681.9A CN201710463681A CN107090231A CN 107090231 A CN107090231 A CN 107090231A CN 201710463681 A CN201710463681 A CN 201710463681A CN 107090231 A CN107090231 A CN 107090231A
Authority
CN
China
Prior art keywords
snow road
ice
paint
imitative ice
epoxy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710463681.9A
Other languages
English (en)
Inventor
刘晏廷
王永峰
吴敌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Meixing Technology Development Co Ltd
Original Assignee
Shenyang Meixing Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Meixing Technology Development Co Ltd filed Critical Shenyang Meixing Technology Development Co Ltd
Priority to CN201710463681.9A priority Critical patent/CN107090231A/zh
Publication of CN107090231A publication Critical patent/CN107090231A/zh
Pending legal-status Critical Current

Abstract

一种仿冰雪路面在驾校训练中的应用，仿冰雪路面施工工艺的仿冰雪路面环氧种类配方包括底漆、中涂、薄涂面涂，底漆是：E51型环氧树脂、活性稀释剂、去离子水、底材润湿剂、消泡剂、脂环胺固化剂；中间漆是：E51型环氧树脂、活性稀释剂、去离子水、防沉剂、消泡剂、流平剂、沉淀硫酸钡、石英粉、脂环胺固化剂；面漆是：E51型环氧树脂、活性稀释剂、去离子水、防沉剂、消泡剂、流平剂、颜料、沉淀硫酸钡、滑石粉、石英粉、脂环胺固化剂。该发明通过在驾校掌握这一技术的关键，靠平时的训练，学习潮湿路面和冰雪路面的性能，掌握在潮湿路面和冰雪路面的驾驶技术，杜绝车辆事故的发生，应用于建筑工程技术领域中。

Description

一种仿冰雪路面在驾校训练中的应用
技术领域
本发明涉及建筑工程技术领域中的一种仿冰雪路面在驾校训练中的应用。
背景技术
目前，随着我国经济的快速发展，我国的公路建设事业也得到了迅猛发展，然而提高驾驶员应对因潮湿地表，如冰雪天、雨天、雾天和刹车淋水等造成的路面潮湿引起的车辆侧滑能力则需要司机极大的提高训练水平。汽车的侧滑现象是当今驾驶技术全面发展的一个至关重要的环节，如果不能掌握这项技术，在高速公路、雨季、泥泞路面、冰雪路行车都是非常危险的，而掌握这一技术的关键，不是靠临时的发挥，而是靠平时的训练。在山区汽车重车下坡行驶，超载运行尤其是拖带不制动装置的挂车超载运行时，即使使用辅助制动（如发动机制动、排气制动等）来降低车速，由于超载量过大，使车辆行驶的惯性力超过路面附着的极限，而产生滑移。这时，纵向与横向附着系数迅速下降，只要有很小的侧向力或急打方向盘就可能使后轴侧滑，发生急转弯。上述两种情况在潮湿路面和冰雪路面出现的概率很大，这时近年山区公路翻车等交通事故增多的主要原因。因此，研制一种仿冰雪路面在驾校训练中的应用是急需解决的新课题。
发明内容
本发明的目的在于提供一种仿冰雪路面在驾校训练中的应用，该发明通过在驾校掌握这一技术的关键，不是靠临时的发挥，而是靠平时的训练，充分学习和了解潮湿路面和冰雪路面的性能，掌握在潮湿路面和冰雪路面的驾驶技术，杜绝车辆事故的发生。
本发明的目的是这样实现的：一种仿冰雪路面在驾校训练中的应用，仿冰雪路面施工工艺的仿冰雪路面环氧种类配方包括底漆、中间漆、面漆，所述的仿冰雪路面环氧种类底漆配方百分比是：E51型环氧树脂82-88%、活性稀释剂7-10%、去离子水2%、底材润湿剂0.2%、消泡剂0.5 %、脂环胺固化剂1-5%；所述的仿冰雪路面环氧种类中间漆配方百分比是：E51型环氧树脂20-35%、活性稀释剂6-8%、去离子水1%、防沉剂0.5%、消泡剂0.6%、流平剂0.9%、沉淀硫酸钡10-15%、滑石粉2-5%、石英粉25-35%、脂环胺固化剂1-2%；所述的仿冰雪路面环氧种类面漆配方百分比是：E51型环氧树脂32-36%、活性稀释剂6-8%、去离子水2%、防沉剂0.7%、消泡剂0.6%、流平剂0.7%、颜料5%、沉淀硫酸钡6-8%、滑石粉5-7%、石英粉25-30%、脂环胺固化剂5-10%；
仿冰雪路面施工工艺的仿冰雪路面聚氨酯种类配方包括底漆、中间漆、面漆，所述的仿冰雪路面聚氨酯种类底漆配方百分比是：分散剂 0.5-0.9%、沉淀BASO4 20-35%、羟基丙烯酸乳液45-60%、防腐防霉剂0.1-0.2%、结合型增稠剂0.4-0.8%、聚氨酯增稠剂0.4-0.6%、水性脂肪族聚异氰酸酯固化剂5-10%；所述的仿冰雪路面聚氨酯种类中间漆配方百分比是：分散剂 0.5-0.9%、消泡剂0.1-0.3%、钛白粉6-8%、沉淀BASO4 20-25%、去离子水10-15%、羟基丙烯酸乳液35-46%、流平剂0.5-0.7%、防腐防霉剂 0.1-0.2%、结合型增稠剂0.4-0.8%、聚氨酯增稠剂0.4-0.6%、水性脂肪族聚异氰酸酯固化剂5-10%；所述的仿冰雪路面聚氨酯种类面漆配方百分比是：分散剂 0.5-0.8%、第一消泡剂0.1-0.3%、钛白粉6-8%、沉淀BASO4 20-25%、涂料专用耐磨粉1-2.5%、去离子水10-15%、羟基丙烯酸乳液35-42%、成膜助剂0.5-1%、第二消泡剂0.2-0.3%、润湿剂0.3-0.5%、流平剂0.5-0.6%、防腐防霉剂 0.1-0.2%、结合型增稠剂0.4-0.7%、聚氨酯增稠剂0.4-0.6%、水性脂肪族聚异氰酸酯固化剂5-10%；
仿冰雪路面施工工艺的丙烯酸种类配方包括底漆、中间漆、面漆，所述的仿冰雪路面丙烯酸种类底漆配方百分比是：甲基丙烯酸甲酯11.6%、丙烯酸丁酯30%、丙烯酸羟乙酯6%、丙烯酸6.4%、苯乙烯8%、十二硫醇2%、甲戊酮32%、BPO引发剂4%；所述的仿冰雪路面丙烯酸种类中间漆配方百分比是：甲基丙烯酸甲酯11.6%、丙烯酸丁酯30%、丙烯酸羟乙酯6%、丙烯酸6.4%、十二硫醇2%、甲戊酮32%、三乙胺10%；去离子水2%；所述的仿冰雪路面丙烯酸种类面漆配方百分比是：甲基丙烯酸甲酯11.6%、丙烯酸丁酯30%、丙烯酸羟乙酯6%、丙烯酸6.2%、苯乙烯8%、十二硫醇2%、甲戊酮32%、BPO引发剂4%、；三乙胺0.1%；去离子水0.1%；
所述的仿冰雪路面环氧种类施工工艺是：
（1）打磨、清理地面
（a）材料进场前、清理现场，平整性差的地面要进行削峰、填谷处理；
（b）专业机械打磨，清除疙瘩、使地面平整，适度粗糙、增加粘结力；
（c）吸尘机吸尘清理；
（d）修补凹坑，填补伸缩缝；
（e）清除油圬、烘干处理；
（2）滚涂渗透型底漆
底漆的渗透使环氧涂层与地面形成“咬合”，增强环氧涂层的附着能力；
（3）满刮环氧石英砂浆
环氧树脂+石英砂调和成砂浆后满刮一遍使涂层与水泥地面这一整体进一步扩大、共同发挥整体的作用；
（4）满刮环氧腻子环氧树石英粉调和后满刮两遍腻子，填补小的凹坑和毛孔增加地面的光滑性；
（5）滚涂环氧色漆
（a）先打磨，消除刮腻子时留下的刮刀痕迹、腻子疙瘩；
（b）全方位吸尘不留死角，包括窗台、墙壁、设备、非施工区、有可能污染 施工区地面的灰尘全部要清洗干净，阻断灰尘污染源；
（c）涂刷环氧色漆,使地坪的丰满度、光泽度、饱满度、硬度达到要求；
（6）滚涂耐磨清漆罩光
提高光泽度，增强硬度延长使用寿命；高质量的环氧地坪，近乎完美；
所述的仿冰雪路面聚氨酯种类施工工艺是：
（1）基面处理，打磨表面、去除浮浆，要求干净、干燥，对局部有损坏的基面进行修补；
（2）涂刷高效能普通地坪底漆，要求均匀、无遗漏；
（3）用中涂配适量石英砂刮涂中涂层；
（4）待沙刮完后干后细磨、除尘；
（5）采用中涂拌石英粉刮涂腻子两遍；
（6）细磨、除尘；
（7）用面漆涂第一遍；
（8）细磨、除尘，用面漆涂第二遍（防滑）；
（9）在施工过程中及时成品保护，切勿洒水和溶剂面漆层；
（10）养护5天（养护期间不要自行使用,不要用水或化学品冲洗）；
所述的仿冰雪路面丙烯酸种类施工工艺是：
（1）施工时的天气要求
（a）施工时必须天气晴朗，阴雨天请勿施工；
（b）温度低于10℃，高于35℃时，不适合施工；
（c）大气相对湿度大于85%，最好也不要施工；
（d）基础养护时间不够或含水率大于5%也不应施工；
（e）基础未清洗干净也不能施工；
2、施工工序
表面处理→打磨→打底漆→施工中涂→分二次涂刮面层→划线→清场完工；
3、施工方法
（1）素地处理,依素地状况做好打磨、修补、除尘；
（2）水性底漆，采用渗透性及附着力特强水性环氧底漆滚涂一道，增强表面附着力；
（3）丙烯酸中涂，将丙烯酸中涂树脂加入适量的石英砂，用镘刀将基均匀涂布一道，增强地面的耐压及抗冲击性能及止滑效果；
（4）丙烯酸面漆，用有色面漆滚涂二道，使地面防尘防水，耐磨耐腐蚀、易清洁，完工后整体地面颜色均一，无空鼓；
（5）施工完成，24小时后方可上人，72小时后可重压（20℃为准，低温开放时间需适度延长）。
本发明的要点在于它的材料配方及施工工艺。
一种仿冰雪路面在驾校训练中的应用与现有技术相比，具有通过在驾校掌握这一技术的关键，不是靠临时的发挥，而是靠平时的训练，充分学习和了解潮湿路面和冰雪路面的性能，掌握在潮湿路面和冰雪路面的驾驶技术，杜绝车辆事故的发生等优点，将广泛的应用于建筑工程技术领域中。
附图说明
下面结合附图和实施例对本发明进行详细说明。
图1是本发明驾校在冰雪路面上的训练路面形式图一。
图2是本发明驾校在冰雪路面上的训练路面形式图二。
图3是本发明驾校在冰雪路面上的训练路面形式图三。
图4是本发明驾校在冰雪路面上的训练路面形式图四。
图5是本发明驾校在冰雪路面上的训练路面形式图五。
具体实施方式
参照附图，一种仿冰雪路面在驾校训练中的应用，仿冰雪路面施工工艺的仿冰雪路面环氧种类配方包括底漆、中间漆、面漆，所述的仿冰雪路面环氧种类底漆配方百分比是：E51型环氧树脂82-88%、活性稀释剂7-10%、去离子水2%、底材润湿剂0.2 %、消泡剂0.5%、脂环胺固化剂1-5%；所述的仿冰雪路面环氧种类中间漆配方百分比是：E51型环氧树脂20-35%、活性稀释剂6-8%、去离子水1%、防沉剂0.5%、消泡剂0.6%、流平剂0.9%、沉淀硫酸钡10-15%、滑石粉2-5%、石英粉25-35%、脂环胺固化剂1-2%；所述的仿冰雪路面环氧种类面漆配方百分比是：E51型环氧树脂32-36%、活性稀释剂6-8%、去离子水2%、防沉剂0.7%、消泡剂0.6%、流平剂0.7%、颜料5%、沉淀硫酸钡6-8%、滑石粉5-7%、石英粉25-30%、脂环胺固化剂5-10%。
仿冰雪路面施工工艺的仿冰雪路面聚氨酯种类配方包括底漆、中间漆、面漆，所述的仿冰雪路面聚氨酯种类底漆配方百分比是：分散剂 0.5-0.9%、沉淀BASO4 20-35%、羟基丙烯酸乳液45-60%、防腐防霉剂0.1-0.2%、结合型增稠剂0.4-0.8%、聚氨酯增稠剂0.4-0.6%、水性脂肪族聚异氰酸酯固化剂5-10%；所述的仿冰雪路面聚氨酯种类中间漆配方百分比是：分散剂 0.5-0.9%、消泡剂0.1-0.3%、钛白粉6-8%、沉淀BASO4 20-25%、去离子水10-15%、羟基丙烯酸乳液35-46%、流平剂0.5-0.7%、防腐防霉剂 0.1-0.2%、结合型增稠剂0.4-0.8%、聚氨酯增稠剂0.4-0.6%、水性脂肪族聚异氰酸酯固化剂5-10%；所述的仿冰雪路面聚氨酯种类面漆配方百分比是：分散剂 0.5-0.8%、第一消泡剂0.1-0.3%、钛白粉6-8%、沉淀BASO4 20-25%、涂料专用耐磨粉1-2.5%、去离子水10-15%、羟基丙烯酸乳液35-42%、成膜助剂0.5-1%、第二消泡剂0.2-0.3%、润湿剂0.3-0.5%、流平剂0.5-0.6%、防腐防霉剂 0.1-0.2%、结合型增稠剂0.4-0.7%、聚氨酯增稠剂0.4-0.6%、水性脂肪族聚异氰酸酯固化剂5-10%。
仿冰雪路面施工工艺的丙烯酸种类配方包括底漆、中间漆、面漆，所述的仿冰雪路面丙烯酸种类底漆配方百分比是：甲基丙烯酸甲酯11.6%、丙烯酸丁酯30%、丙烯酸羟乙酯6%、丙烯酸6.4%、苯乙烯8%、十二硫醇2%、甲戊酮32%、BPO引发剂4%；所述的仿冰雪路面丙烯酸种类中间漆配方百分比是：甲基丙烯酸甲酯11.6%、丙烯酸丁酯30%、丙烯酸羟乙酯6%、丙烯酸6.4%、十二硫醇2%、甲戊酮32%、三乙胺10%；去离子水2%；所述的仿冰雪路面丙烯酸种类面漆配方百分比是：甲基丙烯酸甲酯11.6%、丙烯酸丁酯30%、丙烯酸羟乙酯6%、丙烯酸6.2%、苯乙烯8%、十二硫醇2%、甲戊酮32%、BPO引发剂4%、；三乙胺0.1%；去离子水0.1%。
所述的仿冰雪路面环氧种类施工工艺是：
（1）打磨、清理地面
（a）材料进场前、清理现场，平整性差的地面要进行削峰、填谷处理；
（b）专业机械打磨，清除疙瘩、使地面平整，适度粗糙、增加粘结力；
（c）吸尘机吸尘清理；
（d）修补凹坑，填补伸缩缝；
（e）清除油圬、烘干处理；
（2）滚涂渗透型底漆
底漆的渗透使环氧涂层与地面形成“咬合”，增强环氧涂层的附着能力；
（3）满刮环氧石英砂浆
环氧树脂+石英砂调和成砂浆后满刮一遍使涂层与水泥地面这一整体进一步扩大、共同发挥整体的作用；
（4）满刮环氧腻子环氧树石英粉调和后满刮两遍腻子，填补小的凹坑和毛孔增加地面的光滑性；
（5）滚涂环氧色漆
（a）先打磨，消除刮腻子时留下的刮刀痕迹、腻子疙瘩；
（b）全方位吸尘不留死角，包括窗台、墙壁、设备、非施工区、有可能污染 施工区地面的灰尘全部要清洗干净，阻断灰尘污染源；
（c）涂刷环氧色漆,使地坪的丰满度、光泽度、饱满度、硬度达到要求；
（6）滚涂耐磨清漆罩光
提高光泽度，增强硬度延长使用寿命；高质量的环氧地坪，近乎完美。
所述的仿冰雪路面聚氨酯种类施工工艺是：
（1）基面处理，打磨表面、去除浮浆，要求干净、干燥，对局部有损坏的基面进行修补；
（2）涂刷高效能普通地坪底漆，要求均匀、无遗漏；
（3）用中涂配适量石英砂刮涂中涂层；
（4）待沙刮完后干后细磨、除尘；
（5）采用中涂拌石英粉刮涂腻子两遍；
（6）细磨、除尘；
（7）用面漆涂第一遍；
（8）细磨、除尘，用面漆涂第二遍（防滑）；
（9）在施工过程中及时成品保护，切勿洒水和溶剂面漆层；
（10）养护5天（养护期间不要自行使用,不要用水或化学品冲洗）。
所述的仿冰雪路面丙烯酸种类施工工艺是：
（1）施工时的天气要求
（a）施工时必须天气晴朗，阴雨天请勿施工；
（b）温度低于10℃，高于35℃时，不适合施工；
（c）大气相对湿度大于85%，最好也不要施工；
（d）基础养护时间不够或含水率大于5%也不应施工；
（e）基础未清洗干净也不能施工；
2、施工工序
表面处理→打磨→打底漆→施工中涂→分二次涂刮面层→划线→清场完工。
3、施工方法
（1）素地处理,依素地状况做好打磨、修补、除尘；
（2）水性底漆，采用渗透性及附着力特强水性环氧底漆滚涂一道，增强表面附着力；
（3）丙烯酸中涂，将丙烯酸中涂树脂加入适量的石英砂，用镘刀将基均匀涂布一道，增强地面的耐压及抗冲击性能及止滑效果；
（4）丙烯酸面漆，用有色面漆滚涂二道，使地面防尘防水，耐磨耐腐蚀、易清洁，完工后整体地面颜色均一，无空鼓；
（5）施工完成，24小时后方可上人，72小时后可重压（20℃为准，低温开放时间需适度延长）。
实施例一
用环氧种类施工工艺制成的仿冰雪路面是：
（1）打磨、清理地面
（a）材料进场前、清理现场，平整性差的地面要进行削峰、填谷处理；
（b）专业机械打磨，清除疙瘩、使地面平整，适度粗糙、增加粘结力；
（c）吸尘机吸尘清理；
（d）修补凹坑，填补伸缩缝；
（e）清除油圬、烘干处理；
（2）滚涂渗透型底漆
用82.3公斤E51型环氧树脂、10公斤活性稀释剂、2公斤去离子水、0.2 公斤底材润湿剂、0.5 公斤消泡剂、5公斤脂环胺固化剂制成环氧种类底漆，底漆的渗透使环氧涂层与地面形成“咬合”，增强环氧涂层的附着能力；
（3）满刮环氧石英砂浆
环氧树脂+石英砂调和成砂浆后满刮一遍使涂层与水泥地面这一整体进一步扩大、共同发挥整体的作用；
（4）用35公斤E51型环氧树脂、8公斤活性稀释剂、1公斤去离子水、0.5公斤防沉剂、0.6公斤消泡剂、0.9公斤流平剂、15公斤沉淀硫酸钡、5公斤滑石粉、32公斤石英粉、2公斤脂环胺固化剂制成环氧种类中间漆，满刮环氧腻子环氧树石英粉调和后满刮两遍腻子，填补小的凹坑和毛孔增加地面的光滑性；
（5）滚涂环氧色漆
（a）先打磨，消除刮腻子时留下的刮刀痕迹、腻子疙瘩；
（b）全方位吸尘不留死角，包括窗台、墙壁、设备、非施工区、有可能污染 施工区地面的灰尘全部要清洗干净，阻断灰尘污染源；
（c）用36公斤E51型环氧树脂、8公斤活性稀释剂、2公斤去离子水、0.7公斤防沉剂、0.6公斤消泡剂、0.7公斤流平剂、5公斤颜料、8公斤沉淀硫酸钡、7公斤滑石粉、27公斤石英粉、5公斤脂环胺固化剂制成环氧种类面漆，涂刷环氧色漆,使地坪的丰满度、光泽度、饱满度、硬度达到要求；
（6）滚涂耐磨清漆罩光
提高光泽度，增强硬度延长使用寿命；高质量的环氧地坪，近乎完美。
所述的仿冰雪路面环氧种类面漆配方百分比是：
实施例二
用聚氨酯种类施工工艺制成的仿冰雪路面是：
（1）基面处理，打磨表面、去除浮浆，要求干净、干燥，对局部有损坏的基面进行修补；
（2）用0.9公斤分散剂、35公斤沉淀BASO4、57.5公斤羟基丙烯酸乳液、0.2公斤防腐防霉剂、0.8公斤结合型增稠剂、0.6公斤聚氨酯增稠剂、5公斤水性脂肪族聚异氰酸酯固化剂制成聚氨酯种类底漆，涂刷高效能普通地坪底漆，要求均匀、无遗漏；
（3）用0.9公斤分散剂、0.3公斤消泡剂、8公斤钛白粉、25公斤沉淀BASO4、15公斤去离子水、43.5公斤羟基丙烯酸乳液、0.7公斤流平剂、0.2公斤防腐防霉剂、0.8公斤结合型增稠剂、0.6公斤聚氨酯增稠剂、5水性脂肪族聚异氰酸酯固化剂制成聚氨酯种类中间漆，用中涂配适量石英砂刮涂中涂层；
（4）待沙刮完后干后细磨、除尘；
（5）采用中涂拌石英粉刮涂腻子两遍；
（6）细磨、除尘；
（7）用面漆涂第一遍；
（8）细磨、除尘，用0.8公斤分散剂、0.3公斤第一消泡剂、8公斤钛白粉、25公斤沉淀BASO4、2.5公斤涂料专用耐磨粉、15公斤去离子水、39.5公斤羟基丙烯酸乳液、1公斤成膜助剂、0.3公斤第二消泡剂、0.5公斤润湿剂、0.6公斤流平剂、0.2公斤防腐防霉剂、0.7公斤结合型增稠剂、0.6公斤聚氨酯增稠剂、5公斤水性脂肪族聚异氰酸酯固化剂制成聚氨酯种类面漆，用面漆涂第二遍（防滑）；
（9）在施工过程中及时成品保护，切勿洒水和溶剂面漆层；
（10）养护5天（养护期间不要自行使用,不要用水或化学品冲洗）。
实施例三
用聚氨酯种类施工工艺制成的仿冰雪路面是：
所述的仿冰雪路面丙烯酸种类施工工艺是：
（1）施工时的天气要求
（a）施工时必须天气晴朗，阴雨天请勿施工；
（b）温度低于10℃，高于35℃时，不适合施工；
（c）大气相对湿度大于85%，最好也不要施工；
（d）基础养护时间不够或含水率大于5%也不应施工；
（e）基础未清洗干净也不能施工；
2、施工工序
表面处理→打磨→打底漆→施工中涂→分二次涂刮面层→划线→清场完工。
3、施工方法
（1）素地处理,依素地状况做好打磨、修补、除尘；
（2）用11.6公斤甲基丙烯酸甲酯、30公斤丙烯酸丁酯、6公斤丙烯酸羟乙酯、6.4公斤丙烯酸、8公斤苯乙烯、2公斤十二硫醇、32公斤甲戊酮、4公斤BPO引发剂制成聚氨酯种类底漆，水性底漆，采用渗透性及附着力特强水性环氧底漆滚涂一道，增强表面附着力；
（3）用11.6公斤甲基丙烯酸甲酯、30公斤丙烯酸丁酯、6公斤丙烯酸羟乙酯、6.4公斤丙烯酸、2公斤十二硫醇、32公斤甲戊酮、10公斤三乙胺；2公斤去离子水制成聚氨酯种类中间漆，丙烯酸中涂，将丙烯酸中涂树脂加入适量的石英砂，用镘刀将基均匀涂布一道，增强地面的耐压及抗冲击性能及止滑效果；
（4）用11.6公斤甲基丙烯酸甲酯、30公斤丙烯酸丁酯、6公斤丙烯酸羟乙酯、6.2公斤丙烯酸、8公斤苯乙烯、2公斤十二硫醇、32公斤甲戊酮、4公斤BPO引发剂、0.1公斤三乙胺、0.1公斤去离子水制成聚氨酯种类面漆，丙烯酸面漆，用有色面漆滚涂二道，使地面防尘防水，耐磨耐腐蚀、易清洁，完工后整体地面颜色均一，无空鼓；
（5）施工完成，24小时后方可上人，72小时后可重压（20℃为准，低温开放时间需适度延长）。

Claims (6)

1.一种仿冰雪路面在驾校训练中的应用，仿冰雪路面施工工艺的仿冰雪路面环氧种类配方包括底漆、中间漆、面漆，其特征在于：所述的仿冰雪路面环氧种类底漆配方百分比是：E51型环氧树脂 82-88%、活性稀释剂7-10% 、去离子水2%、底材润湿剂0.2 %、消泡剂0.5 %、脂环胺固化剂1-5%；所述的仿冰雪路面环氧种类中间漆配方百分比是：E51型环氧树脂 20-35%、活性稀释剂6-8% 、去离子水1%、防沉剂0.5%、消泡剂0.6%、流平剂0.9%、沉淀硫酸钡10-15%、滑石粉2-5%、石英粉25-35%、脂环胺固化剂1-2%；所述的仿冰雪路面环氧种类面漆配方百分比是：E51型环氧树脂 32-36%、活性稀释剂6-8% 、去离子水2%、防沉剂0.7%、消泡剂0.6%、流平剂0.7%、颜料5%、沉淀硫酸钡6-8%、滑石粉5-7%、石英粉25-30%、脂环胺固化剂5-10%。
2.一种仿冰雪路面在驾校训练中的应用，仿冰雪路面施工工艺的仿冰雪路面聚氨酯种类配方包括底漆、中间漆、面漆，其特征在于：所述的仿冰雪路面聚氨酯种类底漆配方百分比是：分散剂 0.5-0.9%、沉淀BASO4 20-35%、羟基丙烯酸乳液45-60%、防腐防霉剂0.1-0.2%、结合型增稠剂0.4-0.8%、聚氨酯增稠剂0.4-0.6%、水性脂肪族聚异氰酸酯固化剂5-10%；所述的仿冰雪路面聚氨酯种类中间漆配方百分比是：分散剂 0.5-0.9%、消泡剂0.1-0.3%、钛白粉6-8%、沉淀BASO4 20-25%、去离子水10-15%、羟基丙烯酸乳液35-46%、流平剂0.5-0.7%、防腐防霉剂 0.1-0.2%、结合型增稠剂0.4-0.8%、聚氨酯增稠剂0.4-0.6%、水性脂肪族聚异氰酸酯固化剂5-10%；所述的仿冰雪路面聚氨酯种类面漆配方百分比是：分散剂0.5-0.8%、第一消泡剂0.1-0.3%、钛白粉6-8%、沉淀BASO4 20-25%、涂料专用耐磨粉1-2.5%、去离子水10-15%、羟基丙烯酸乳液35-42%、成膜助剂0.5-1%、第二消泡剂0.2-0.3%、润湿剂0.3-0.5%、流平剂0.5-0.6%、防腐防霉剂 0.1-0.2%、结合型增稠剂0.4-0.7%、聚氨酯增稠剂0.4-0.6%、水性脂肪族聚异氰酸酯固化剂5-10%。
3.一种仿冰雪路面在驾校训练中的应用，仿冰雪路面施工工艺的丙烯酸种类配方包括底漆、中间漆、面漆，其特征在于：所述的仿冰雪路面丙烯酸种类底漆配方百分比是：甲基丙烯酸甲酯11.6%、丙烯酸丁酯30%、丙烯酸羟乙酯6%、丙烯酸6.4%、苯乙烯8%、十二硫醇2%、甲戊酮32%、BPO引发剂4%；所述的仿冰雪路面丙烯酸种类中间漆配方百分比是：甲基丙烯酸甲酯11.6%、丙烯酸丁酯30%、丙烯酸羟乙酯6%、丙烯酸6.4%、十二硫醇2%、甲戊酮32%、三乙胺10%；去离子水2%；所述的仿冰雪路面丙烯酸种类面漆配方百分比是：甲基丙烯酸甲酯11.6%、丙烯酸丁酯30%、丙烯酸羟乙酯6%、丙烯酸6.2%、苯乙烯8%、十二硫醇2%、甲戊酮32%、BPO引发剂4%、；三乙胺0.1%；去离子水0.1%。
4.根据权利要求1所述的一种仿冰雪路面在驾校训练中的应用，其特征在于：所述的仿冰雪路面环氧种类施工工艺是：
（1）打磨、清理地面
（a）材料进场前、清理现场，平整性差的地面要进行削峰、填谷处理；
（b）专业机械打磨，清除疙瘩、使地面平整，适度粗糙、增加粘结力；
（c）吸尘机吸尘清理；
（d）修补凹坑，填补伸缩缝；
（e）清除油圬、烘干处理；
（2）滚涂渗透型底漆
底漆的渗透使环氧涂层与地面形成“咬合”，增强环氧涂层的附着能力；
（3）满刮环氧石英砂浆
环氧树脂+石英砂调和成砂浆后满刮一遍使涂层与水泥地面这一整体进一步扩大、共同发挥整体的作用；
（4）满刮环氧腻子环氧树石英粉调和后满刮两遍腻子，填补小的凹坑和毛孔增加地面的光滑性；
（5）滚涂环氧色漆
（a）先打磨，消除刮腻子时留下的刮刀痕迹、腻子疙瘩；
（b）全方位吸尘不留死角，包括窗台、墙壁、设备、非施工区、有可能污染 施工区地面的灰尘全部要清洗干净，阻断灰尘污染源；
（c）涂刷环氧色漆,使地坪的丰满度、光泽度、饱满度、硬度达到要求；
（6）滚涂耐磨清漆罩光
提高光泽度，增强硬度延长使用寿命；高质量的环氧地坪，近乎完美。
5.根据权利要求2所述的一种仿冰雪路面在驾校训练中的应用，其特征在于：所述的仿冰雪路面聚氨酯种类施工工艺是：
（1）基面处理，打磨表面、去除浮浆，要求干净、干燥，对局部有损坏的基面进行修补；
（2）涂刷高效能普通地坪底漆，要求均匀、无遗漏；
（3）用中涂配适量石英砂刮涂中涂层；
（4）待沙刮完后干后细磨、除尘；
（5）采用中涂拌石英粉刮涂腻子两遍；
（6）细磨、除尘；
（7）用面漆涂第一遍；
（8）细磨、除尘，用面漆涂第二遍；
（9）在施工过程中及时成品保护，切勿洒水和溶剂面漆层；
（10）养护5天。
6.根据权利要求3所述的一种仿冰雪路面在驾校训练中的应用，其特征在于：所述的仿冰雪路面丙烯酸种类施工工艺是：
（1）施工时的天气要求
（a）施工时必须天气晴朗，阴雨天请勿施工；
（b）温度低于10℃，高于35℃时，不适合施工；
（c）大气相对湿度大于85%，最好也不要施工；
（d）基础养护时间不够或含水率大于5%也不应施工；
（e）基础未清洗干净也不能施工；
2、施工工序
表面处理→打磨→打底漆→施工中涂→分二次涂刮面层→划线→清场完工；
3、施工方法
（1）素地处理,依素地状况做好打磨、修补、除尘；
（2）水性底漆，采用渗透性及附着力特强水性环氧底漆滚涂一道，增强表面附着力；
（3）丙烯酸中涂，将丙烯酸中涂树脂加入适量的石英砂，用镘刀将基均匀涂布一道，增强地面的耐压及抗冲击性能及止滑效果；
（4）丙烯酸面漆，用有色面漆滚涂二道，使地面防尘防水，耐磨耐腐蚀、易清洁，完工后整体地面颜色均一，无空鼓；
（5）施工完成，24小时后方可上人，72小时后可重压。
CN201710463681.9A 2017-06-19 2017-06-19 一种仿冰雪路面在驾校训练中的应用 Pending CN107090231A (zh)