CN107083086A - A kind of high purely inorganic functional paint of air purifying property - Google Patents
A kind of high purely inorganic functional paint of air purifying property Download PDFInfo
- Publication number
- CN107083086A CN107083086A CN201710356235.8A CN201710356235A CN107083086A CN 107083086 A CN107083086 A CN 107083086A CN 201710356235 A CN201710356235 A CN 201710356235A CN 107083086 A CN107083086 A CN 107083086A
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic
- chlorine dioxide
- functional paint
- purifying property
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of high purely inorganic functional paint of air purifying property, it is mainly made up of the raw material of following weight parts：0~8 part of 0~15 part of 0~15 part of 0~15 part of 0.3~3 part of 5~35 parts of 3~15 parts of 30~60 parts of 100 parts of the aqueous solution, alkaline inorganic material, SILICA FUME, Ludox, sodium chloride, diatomite, attapulgite, sepiolite, bentonite and 0~25 part of inorganic filler containing chlorine dioxide, it is finished product that above-mentioned each raw material, which is pressed after respective parts by weight are disperseed and filtered by mixing, at a high speed,.The present invention be it is a kind of can with it is long-acting it is micro release chlorine dioxide purification air and sterilization purely inorganic functional paint, diatomite, attapulgite and sepiolite in formula etc., which possess multiple hole structure, can largely store chlorine dioxide, the solution of the present invention is perfectly realized.The present invention is entirely free of organic chemical industry's composition, possesses a variety of advantages such as environmental protection, highly effective air purification air, fire prevention, humidity and fungus-resistant.
Description
Technical field
The invention belongs to purification type inorganic coating technical field, a kind of high pure nothing of air purifying property is particularly related to
Machine functional paint.
Background technology
Chlorine dioxide is internationally recognized safe and nontoxic disinfectant, and without " three cause " effect, both carcinogenic, teratogenesis, cause are prominent
Become, while also not occurring chlorination with organic matter in disinfecting process generates the organic chloride or its that can produce three-induced effect
Its poisonous class material.Any influence, including the influence in terms of Physiology and biochemistry will not be produced during below 100ppm to human body.In sky
Most widely applied in gas purification, tap water purifying, food sterilization.But utilization of the chlorine dioxide in coating does not have but
It was found that, trace it to its cause and be primarily present following technological difficulties：
1st, chlorine dioxide is readily volatilized：Cause people custom think chlorine dioxide be most efficiently however be again it is most short-acting,
Row such as air cleaning industry can purify one week after or so with chlorine dioxide in first time and purify for the second time with cumulative effects,
Accumulated once again after two months and reach promising result, long-term micro bottleneck of the chlorine dioxide release as purification industry is asked
Topic.If wall covering can as chlorine dioxide release vehicle, will be the once great leap of indoor purifying, he is by pole
Big surmounts the passive adsorption function of diatom ooze, or even much surmounts the purification function of photocatalyst.
2nd, chlorine dioxide has strong oxidizing property：The many mixed modes with organic-inorganic of existing coating occur, and organic matter can not
The strong oxidizing property of chlorine dioxide is resistant to, and organic matter is general all poisonous, does not accomplish really nontoxic.In wet environment organic matter
Easily mouldy, mould virus is that another kind of important environment is poisoned.When high temperature particularly fire, have with the rising of temperature
The gas that machine thing is volatilized is inflammable and becomes severe toxicity, spreading for fire is not only resulted in, while being the lethal main cause of fire.
Only purely inorganic coating just can as chlorine dioxide dependable carriers, so as to realize environmental protection truly, fire prevention and anti-
It is mould antibacterial.
3rd, the control of optimal burst size：Optimal situation is that the chlorine dioxide of release is just anti-with the toxin such as indoor formaldehyde
Should be complete, or toxic gas be reduced to it is up to standard in the case of react complete.Actually since the high security of chlorine dioxide, he
The amount that can allow in air is very high.It is internationally recognized when concentration is less than 500ppm, its influence to human body can
To ignore, any influence, including the influence in terms of Physiology and biochemistry will not be produced during below 100ppm to human body.To skin also without
Any sensitization, in fact our release concentration will well below 500ppm, normally only in below 20ppm, therefore, two
Chlorine monoxid is also known as safe and nontoxic green disinfectant in the world.
Although inorganic coating patent of the prior art is named with inorganic coating, it is most of also to add it is organic into
Point, do not reach it is purely inorganic so that the advantages of environmental protection index, weather resistance, fire prevention, mould proof, anti-aging and humidity it is big give a discount
Button, organic-compound system can not also be resistant to the strong oxidizing property of chlorine dioxide at all.Although sub-fraction inorganic coating patent possesses pure
Inorganic standard, but have the shortcomings that workability is poor, it is most of to scratch, or exist film easy to crack, easy dry linting and
The limited many problems of grade of Storage period, cause the actual product conversion of patent very poor, do not see that popularization is successful substantially on the market
Purely inorganic coating, what is named with inorganic coating is organic-inorganic compo mostly, substantially with emulsion paint without too big difference.
It is particularly optimal 13 or so and the most pH value of formula of existing inorganic system does not reach 11-13.
Applicant retrieved five coating patents containing calcium hydroxide：1st, CN1179449A, calcium hydroxide ratio 80~
90%；2nd, CN101591481A, calcium hydroxide ratio 60~80%；3rd, CN101899232A, calcium hydroxide ratio 10~15%；
4th, CN102092989A, calcium hydroxide ratio 12~15%；5th, CN103709799A, calcium hydroxide ratio 10~22%.Wherein
Preceding two patents are because of calcium hydroxide too high levels, so as to cause insufficient strength, difficulty of construction to precipitate greatly, easily and there is colour-difference
The problems such as, the formula of rear three patents is generally not then the actual proportioning based on calcium hydroxide, so the painting made
Material is all difficult to reach ideal effect.
The content of the invention
The present invention applies to overcome the shortcomings of that prior art is present there is provided a kind of high purely inorganic function of air purifying property
Material, the present invention is the high-environmental wall covering that a kind of complete use inorganic mineral powder is constituted, and is entirely free of organic chemical industry's composition,
Possess a variety of advantages such as environmental protection, highly effective air purification air, fire prevention, humidity and fungus-resistant.
The present invention is achieved by the following technical solutions：A kind of high purely inorganic functional paint of air purifying property, it is led
To be made up of the raw material of following weight parts：30~60 parts of 100 parts of the aqueous solution, alkaline inorganic material, SILICA FUME 3 containing chlorine dioxide
~15 parts, 5~35 parts of Ludox, 0.3~3 part of sodium chloride, 0~15 part of diatomite, 0~15 part of attapulgite, sepiolite 0~15
0~25 part of part, 0~8 part of bentonite and inorganic filler, above-mentioned each raw material is disperseed by respective parts by weight by mixing, at a high speed
With after filtering be finished product.
As the preferred embodiment of the present invention, the high purely inorganic functional paint of air purifying property of the invention is main by following
The raw material composition of parts by weight：4~10 parts of 40~55 parts of 100 parts of the aqueous solution, alkaline inorganic material, SILICA FUME containing chlorine dioxide,
15~30 parts of Ludox, 1~2 part of sodium chloride, 2~10 parts of diatomite, 3~8 parts of attapulgite, 4~9 parts of sepiolite, bentonite 2
~4 parts and 15~22 parts of inorganic filler.
As the preferred forms of the present invention, the high purely inorganic functional paint of air purifying property of the invention is main by following
The raw material composition of parts by weight：5 parts of 50 parts of 100 parts of the aqueous solution, alkaline inorganic material, SILICA FUME, Ludox 25 containing chlorine dioxide
Part, 2 parts of sodium chloride, 6 parts of diatomite, 4 parts of attapulgite, 5 parts of sepiolite, 3 parts of bentonite and 20 parts of inorganic filler.
Alkaline inorganic material is calcium hydroxide, calcium oxide, potassium hydroxide, potassium oxide, sodium hydroxide, sodium oxide molybdena, hydroxide
Barium, barium monoxide, cobalt hydroxide, cobalt oxide, magnesium hydroxide, magnesia, lithium hydroxide, lithia, cement, gypsum, silicate, silicon
One or more mixtures in colloidal sol, sodium carbonate, sodium acid carbonate, calcium bicarbonate and magnesium chloride class inorganic alkaline material.
The aqueous solution containing chlorine dioxide is the aqueous solution of chlorine dioxide that concentration range is 0.001%~20%.Preferably,
The aqueous solution containing chlorine dioxide is the aqueous solution of chlorine dioxide that concentration range is 0.1%~1%.Ludox is that concentration is more than 30%
Ludox, SILICA FUME be mesh number be more than 6000 mesh SILICA FUME.
Table one：Traditional inorganic coating formation scheme substantially has following four pattern in the prior art：
It is can be found that in table one：The coating main film forming substance of false inorganic compounding be all emulsion and rubber powder etc. it is organic into
Point, substantially it is exactly emulsion paint.The coating of only calcium hydroxide composition has the utilization of more than 1,000 years in the coating of purely inorganic formula
History, can have larger development space at many aspects such as construction, storage, toning.So main for calcium hydroxide coating
Strength problem is overcome to have very big development prospect, his superpower bactericidal property and water resistance also necessarily have wider fortune
With.
Research finds that single dependence calcium hydroxide intensity is extremely difficult to ideal tensile strength, when calcium hydroxide and superfine
Excellent performance is shown after silica flour and Ludox mixing, special silico-calcium 3 D stereo net is formed.To realize coating simultaneously
Antisolvent precipitation, the performance such as plumpness, anti-dry linting and cracking resistance smeared also needs to coordinate concave convex rod, sepiolite and bentonit etc. pure
Inorganic constituents.
Conventional patent is mostly without third party's data evidence, and practical study finds existing purely inorganic coating, in formula
The problem of performance difference of construction and product is most crucial in the case of incomplete.In the presence of hardly possible construction, smear insufficient strength, Yi Kai
Split, easy dry linting, basic color whiteness not enough and the defect such as later stage color representation power difference, cause basic neither one patent to realize
Successful commodity conversion and popularization.It is existing that promoted most of still with organic emulsion or rubber powder are named with inorganic coating
Film forming, is basically emulsion paint.The top environmental protection of inorganic coating, A grade prevent fires, the advantages of anti-mildew is antibacterial, water-fast and ageing-resistant
Do not embody at all, and organic-compound system can not also be resistant to the strong oxidizing property of chlorine dioxide at all.
The beneficial effects of the invention are as follows：The present invention is that one kind can be with long-acting micro release chlorine dioxide purification air and sterilization
Purely inorganic functional paint, in order to realize above-mentioned target, applicant has found chlorine dioxide in the pure of pH value 11-13 through studying for a long period of time
Micro slow release can be realized under inorganic environment, while diatomite, attapulgite and sepiolite in formula etc. possesses porous
Hole structure can also largely store chlorine dioxide, this scheme is perfectly realized.The present invention is with high-purity calcium hydroxide
Micro mist, SILICA FUME and Ludox are main film forming substance, and huge breakthrough is realized in terms of intensity and workability.This hair
It is bright to be made up of completely inorganic constituents, without any organic principle, the toxin such as the formaldehydeless VOC free of real meaning are reached, are prevented fires
Grade reaches A1 grades, and pH value is in 11-13 or so, super antibacterial.
The main production process of inorganic coating of the present invention is relatively simple, and the mainly stirring to various mineral dusts was mixed
Filter.Conventional purification type coating in the prior art, the passive adsorption function of such as diatom ooze, photocatalyst needs what light irradiation just had to urge
Change the functions such as reaction weaker, so the slow release method of chlorine dioxide of the present invention can not surmount substantially, the security of chlorine dioxide
By verifying for a long time.The present invention is the high-environmental wall covering that a kind of complete use inorganic mineral powder is constituted, completely not
Containing organic chemical components, possess a variety of advantages such as environmental protection, highly effective air purification air, fire prevention, humidity and fungus-resistant.Present invention warp
The examining report that national testing agency provides is as follows：
Table two：Testing agency：National building materials test center
Table three：Testing agency：National building materials Quality Supervision and Inspection Center
Table four：Testing agency：National Fire building materials quality Supervision Test Center
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1：A kind of high purely inorganic functional paint of air purifying property, it is mainly by the raw material group of following weight parts
Into：0.3 part of 5 parts of 3 parts of 30 parts of 100 parts of the aqueous solution, alkaline inorganic material, SILICA FUME, Ludox, sodium chloride containing chlorine dioxide,
10 parts of 2 parts of diatomite, 1 part of attapulgite, 3 parts of sepiolite, 8 parts of bentonite and inorganic filler, by above-mentioned each raw material by respective
Parts by weight are finished product after disperseing and filter by mixing, at a high speed.Wherein alkaline inorganic material is calcium hydroxide, containing titanium dioxide
The aqueous solution of chlorine is the aqueous solution of chlorine dioxide that concentration range is 0.1%.Ludox is the Ludox that concentration is more than 30%, micro- silicon
Powder is the SILICA FUME that mesh number is more than 6000 mesh.
Embodiment 2：A kind of high purely inorganic functional paint of air purifying property, it is mainly by the raw material group of following weight parts
Into：2 parts of 25 parts of 5 parts of 50 parts of 100 parts of the aqueous solution, alkaline inorganic material, SILICA FUME, Ludox, sodium chloride, silicon containing chlorine dioxide
20 parts of 6 parts of diatomaceous earth, 4 parts of attapulgite, 5 parts of sepiolite, 3 parts of bentonite and inorganic filler, by above-mentioned each raw material by respective heavy
Amount part is finished product after disperseing and filter by mixing, at a high speed.Alkaline inorganic material is calcium oxide, potassium hydroxide and sodium carbonate
Mixture, the aqueous solution containing chlorine dioxide be concentration range be 1% aqueous solution of chlorine dioxide, Ludox is that concentration is more than
30% Ludox, SILICA FUME is the SILICA FUME that mesh number is more than 6000 mesh.
Embodiment 3：A kind of high purely inorganic functional paint of air purifying property, it is mainly by the raw material group of following weight parts
Into：3 parts of 35 parts of 15 parts of 60 parts of 100 parts of the aqueous solution, alkaline inorganic material, SILICA FUME, Ludox, sodium chloride containing chlorine dioxide,
15 parts of 15 parts of diatomite, 14 parts of attapulgite, 13 parts of sepiolite, 5 parts of bentonite and inorganic filler, by above-mentioned each raw material by respective
Parts by weight after mixing, scattered at a high speed and filtering i.e. finished product.Alkaline inorganic material is calcium hydroxide, containing chlorine dioxide
The aqueous solution be concentration range be 0.01% aqueous solution of chlorine dioxide, Ludox be concentration be more than 30% Ludox, micro- silicon
Powder is the SILICA FUME that mesh number is more than 6000 mesh.
The present invention is compounded the 3 D stereo silico-calcium structure for forming solid by calcium hydroxide, SILICA FUME and Ludox, with top
Divide and ratio is core, the change and addition of a small amount of inorganic constituents are included in patent claims protection domain, skill
Art scheme comprising the present invention whole formula components, ratio scope and prioritization scheme, do not rise on a small quantity main binding effect and
The composition of catharsis changes, in the claims for being also contained in the present invention.
Finally it should be noted that above content is merely illustrative of the technical solution of the present invention, rather than to present invention protection
The limitation of scope, simple modification or equivalent substitution that one of ordinary skill in the art is carried out to technical scheme,
All without departing from the spirit and scope of technical solution of the present invention.
Claims (7)
1. a kind of high purely inorganic functional paint of air purifying property, it is characterised in that：The high purely inorganic work(of air purifying property
Energy coating is mainly made up of the raw material of following weight parts：100 parts of the aqueous solution, alkaline inorganic material 30~60 containing chlorine dioxide
Part, 3~15 parts of SILICA FUME, 5~35 parts of Ludox, 0.3~3 part of sodium chloride, 0~15 part of diatomite, 0~15 part of attapulgite,
0~25 part of 0~15 part of sepiolite, 0~8 part of bentonite and inorganic filler, by above-mentioned each raw material by respective parts by weight through overmulling
It is finished product after conjunction, scattered at a high speed and filtering.
2. a kind of high purely inorganic functional paint of air purifying property according to claim 1, it is characterised in that：The high-altitude
The purely inorganic functional paint of gas purifying property is mainly made up of the raw material of following weight parts：100 parts of the aqueous solution, alkali containing chlorine dioxide
It is 40~55 parts of inorganic material of property, 4~10 parts of SILICA FUME, 15~30 parts of Ludox, 1~2 part of sodium chloride, 2~10 parts of diatomite, recessed
15~22 parts of convex 3~8 parts of rod soil, 4~9 parts of sepiolite, 2~4 parts of bentonite and inorganic filler.
3. a kind of high purely inorganic functional paint of air purifying property according to claim 2, it is characterised in that：The high-altitude
The purely inorganic functional paint of gas purifying property is mainly made up of the raw material of following weight parts：100 parts of the aqueous solution, alkali containing chlorine dioxide
50 parts of inorganic material of property, 5 parts of SILICA FUME, 25 parts of Ludox, 2 parts of sodium chloride, 6 parts of diatomite, 4 parts of attapulgite, sepiolite 5
20 parts of part, 3 parts of bentonite and inorganic filler.
4. a kind of high purely inorganic functional paint of air purifying property according to claim 1, it is characterised in that：The alkalescence
Inorganic material is calcium hydroxide, calcium oxide, potassium hydroxide, potassium oxide, sodium hydroxide, sodium oxide molybdena, barium hydroxide, barium monoxide, hydrogen
Cobalt oxide, cobalt oxide, magnesium hydroxide, magnesia, lithium hydroxide, lithia, cement, gypsum, silicate, Ludox, sodium carbonate,
One or more mixtures in sodium acid carbonate, calcium bicarbonate and magnesium chloride class inorganic alkaline material.
5. a kind of high purely inorganic functional paint of air purifying property according to claim 1, it is characterised in that：It is described to contain two
The aqueous solution of chlorine monoxid is the aqueous solution of chlorine dioxide that concentration range is 0.001%~20%.
6. a kind of high purely inorganic functional paint of air purifying property according to claim 5, it is characterised in that：It is described to contain two
The aqueous solution of chlorine monoxid is the aqueous solution of chlorine dioxide that concentration range is 0.1%~1%.
7. a kind of high purely inorganic functional paint of air purifying property according to claim 1, it is characterised in that：The silicon is molten
Glue is the Ludox that concentration is more than 30%, and the SILICA FUME is the SILICA FUME that mesh number is more than 6000 mesh.